• The korean journal of orthodontics
• /
• v.31 no.1 s.84
• /
• pp.137-147
• /
• 2001

Acidic primer is the bonding agent which combines the conditioning and priming agent into the single solution and was originally developed for the dentin bonding system. It is less harmful to the tooth structure and more convenient to manipulate than the traditional etching procedure. The Purpose of this study is to evaluate the shear bond strength of various bonding materials when the enamel is treated with acidic primer for the bracket bonding procedure. Fifty recently extracted human premolars were randomly separated into five groups -Group I using Clearfil Liner Bond 2 adhesive system to the enamel treated with acidic primer, Group II using Transbond XT adhesive system to the enamel treated with acidic primer, Group III using panavia 21 adhesive system to the enamel treated with acidic primer, Group IV using Fuji-Ortho LC adhesive system to the enamel treated with acidic primer, Group V using Transbond XT adhesive system to the enamel treated with 37$\%$ phosphoric acid. The shear bond strength was measured with Instron universal testing machine after storing in $37^{\circ}C$ water bath for 48 hours. After debonding, the teeth and brackets were examined under scanning electron microscope (SEM) and assessed with the adhesive remnant index (ARI). The results were as follows : 1. There were no significant differences in shear bond strength between group III ($8.69{\pm}2.72MPa$), group IV (9.7 ± 3.16 MPa), and group V ($10.48{\pm}2.60MPa$) (p>0.05). 2. The shear bond strength of group III and group IV was significantly higher than that of group I ($1.09{\pm}0.53MPa$), and Group II ($2.70{\pm}1.46MPa$) (p<0.05). 3. The ARI of group IV ($2.1{\pm}1.1$) and group V ($2.9{\pm}0.3$) was significantly higher than that of group I ($0.2{\pm}0.4$), group II ($0.3{\pm}0.9$) and group III ($0.2{\pm}0.4$) (p<0.05). 4. There were no significant difference between the ARI of group IV and group V (p>0.05). This result suggests that the combination of acidic primer and some bonding adhesive can provide sufficient shear bond strength for clinical orthodontics.

• The korean journal of orthodontics
• /
• v.26 no.2 s.55
• /
• pp.175-186
• /
• 1996

The purpose of this study was to examine the effects of mechanical and thermal fatigue on the shear bond strength(SBS) of stainless steel mesh brackets bonded to human premolar teeth with 3 no-mix adhesives. The stainless steel mesh bracket was Ormesh(Ormco, .022 slot) and three types of no-mix adhesives were Ortho-one(Bisco), $Monolok^2$(RMO), $System\;1^+$(Ormco). The $10^6$ loadcycles of $17.4{\times}10^2sin2{\pi}ftlg{\cdot}cm$ and the 1,000 thermocycles of 15 second dwell time in each bath of $5^{\circ}C\;and\;55^{\circ}C$ were acturated as mechanical and thermal fatigue stress, and SBS were measured after each fatigue test. The fracture sites were analyzed by stereoscope and scanning electron microscope. The results obtained were summarized as follows; 1. Before thermocycles, $Monolok^2$ showed the highest Knoop hardness number(KHN, $64.03kg/mm^2$) and $System\;1^+$ showed the lowest value($31.60kg/mm^2$). After thermocycling, $Monolok^2$ also showed the highest KHN($38.03kg/mm^2$) and $system\;1^+$ showed the minimum($20.87kg/mm^2$). The KHN of Ortho-one, $Monolok^2,\;System\;1^+$ significantly decreased after thermocycling (P<0.01). 2. In static shear bond test, three adhesives had no significant differences in the SBS(P>0.01). 3. After thermocycling test, $Monolok^2$ showed the maximum SBS($19.34{\pm}2.75MPa$) and Ortho-one showed the minimum SBS($13.66{\pm}2.23MPa$). The SBS of Ortho-one(P<0.01) and $System\;1^+$(P<0.05) significantly decreased after $10^3$ thermocycles. 4. The SBS of three adhesives after $10^6$ loadcycles were similar and were not significantly decreased compared with static group(P>0.01). 5. The failure sites were usually bracket/resin interface in all groups irrespective of experimental conditions.

• Journal of Korean Academy of Oral and Maxillofacial Radiology
• /
• v.23 no.2
• /
• pp.229-250
• /
• 1993

This study was performed to investigate the morphological and structural changes of bone tissues and the effects of irradiation on the mandibular bodies of rats which were fed low calcium diets. In order to carry out this experiment, 160 seven-week old Sprague-Dawley strain rats weighing about 150 gm were selected and equally divided into one normal diet group of 80 rats and one low calcium diet group with the remainder. These groups were then subdivided into two groups, 40 were assigned rats for each subdivided group, exposed to radiation. The Group 1 was composed of forty non-irradiated rats with normal diet, Group 2 of forty irradiated rats with normal diet, Group 3 forty non-irradiated rats with low calcium diet, and Group 4 forty irradiated rats with low calcium diet. The two irradiation groups received a single dose of 20 Gy on the jaw area only and irradiated with a cobalt-50 teletherapy unit. The rats with normal and low calcium diet groups were serially terminated by ten on the 3rd, the 7th, the 14th, and the 21st day after irradiation. After termination, both sides of the dead rats mandible were removed and fixed with 10% neutral formalin. The bone density of mandibular body was measured by use of bone mineral densitometer(Model DPX -alpha, Lunar Corp., U.SA). Triga Mark ill nuclear reactor in Korea Atomic Research Institute was used for neutron activation and then calcium contents of mandibular body were measured by using a 4096 multichannel analyzer (EG and G ORTEC 919 MCA, U.SA). Also the mandibular body was radiographed with a soft X-ray apparatus(Hitex Co., Ltd., Japan). Thereafter, the obtained microradiograms were observed by a light microscope and were used for the morphometric analysis using a image analyzer(Leco 2001 System, Leco Co., Canada). The morphometric analysis was performed for parameters such as the total area, the bone area, the inner and outer perimeters of the bone. The obtained results were as follows: 1. In the morphometric analysis, total area and outer perimeter of the mandibular bodies of Group 3 were a little smaller than that of Group 1. The mean bone width and bone area were much smaller than that of Group 1 and the inner perimeter of Group 3 was much longer than that of Group 1. The total area and outer perimeter of Group 2 and Group 4 showed little difference. The mean bone width and bone area of Group 4 were smaller than that of Group 2 and the inner perimeter of Group 4 was longer than that of Group 2. 2. The remarkable decreases of the number and thickness of trabeculae and also the resorption of endosteal surface of cortical bone could be seen in the microradiogram of Group 3, Group 4 since the 3rd day of experiment. On the 21st day of experiment, the above findings could be more clearly seen in Group 4 than in Group 3. 3. The bone mineral density of Group 3 was lesser than that of Group 1 and the bone mineral density of Group 4 was lesser than that of Group 2 on the 7th, 14th, 21st days. The irradiation caused the bone mineral density to be decreased regardless of diet. In the case of Groups with low calcium diet, the bone mineral density was much decreased on the 21st day than on the 3rd day of experiment. 4. The calcium content in mandible of Group 3 was smaller than that of Group 1 throughout the experiment. roup 4 showed the least amount of calcium content. The irradiation caused the calcium content to be decreased regardless of diet. In the case of Groups with low calcium diet, the calcium content was much decreased on the 21st day than on the 3rd day of experiment. In conclusion, the present study demonstrated that morphological changs and decrease of bone mass due to resorption of bone by low calcium diet, and that the resorption of bone could be found in the spongeous bone and endosteal surface of cortical bone. So the problem of resorption of bone must be considered when the old and the postmenopausal women are taken radiotherapy because the irradiation seems to be accelerated the resorption of osteoporotic bone.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.2
• /
• pp.232-247
• /
• 2005

Purpose. The purposes of this investigation were to discover the possibility of clinical application in the areas of dental implants and bone grafts by investigating the bone formation histologically around specimen which was depending on the intensity of magnetic field of neodymium magnet inside of the specimens. Material and method. 1. Measurement of magnetic intensity - placed the magnet inside of the specimen, and measured the intensity of magnetic field around the 1st thread and 3rd thread of specimen 20 times by using a Gaussmeter(Kanetec Co., Japan). 2. Surgical Procedure - Male rabbit was anesthetised by constant amount of Ketamine (0.25ml/kg) and Rompun (0.25ml/kg). After incising the flat part of tibia, and planted the specimens of titanium implant, control group was stitched without magnet, while experimental groups were placed a magnedisc 500(Aichi Steel Co., Japan) or magnedisc 800(Aichi Steel Co., Japan) into it, fixed by pattern resin and stitched. 3. Management after the surgery - In order to prevent it from the infection of bacteria and for antiinflammation, Gentamycin and Ketopro were injected during 1 week from operation day, and dressed with potadine. 4. Preparation of histomorphometric analysis - At 2, 4 and 8 weeks after the surgery, the animals were sacrificed by excessed Ketamine, and then, specimens were obtained including the operated part and some parts of tibia, and fixed it to 10% of PBS buffer solution. After embedding specimens in Technovit 1200 and B.P solution, made a H-E stain. Samples width was 75$\mu$m . In histological findings through the optical microscope and using Kappa image base program(Olympus Co. Japan), the bone contact ratio and bone area ratio of each parts of specimens were measured and analyzed. 5. Statistical analysis - Statistical analysis was accomplished with Mann Whitney U-test. Results and conclusion. 1. In histomorphometric findings, increased new bone formation was shown in both control & experimental groups through the experiment performed for 2, 4 & 8 weeks. After 4 weeks, more osteoblasts and osteoclasts with significant bone remodeling were shown in experimental groups. 2. In histomorphometric analysis, the bone contact ratios were 38.5% for experimental group 1, 29.5% for experimental group 2 and 11.9% for control group. Experimental groups were higher than control group(p<0.05) (Fig. 6, Table IV). The bone area ratios were 60.9% for experimental group 2, 46.4% for experimental group 1 and 36.0% for control group. There was no significantly statistical difference between experimental groups and control group(p<0.05) (Fig. 8, Table VII) 3. In comparision of the bone contact ratios at each measurement sites according to magnetic intensity, experimental group 2(5.6mT) was higher than control group at the 1st thread (p<0.05) and experimental group 1 (1.8mT) was higher than control group at the 3rd thread(p<0.05) (Fig. 7, Table V, VI). 4. In comparision of the bone area ratios at each measurement sites according to magnetic intensity, experimental group 2(5.6mT) was higher than control group and experimental group 1 (4.0mT) at the 1st thread(p<0.1) and experimental group 2(4.4mT) was higher than experimental group 1 (1.8mT) at the 3rd thread(p<0.1) (Fig. 9, Table IX, X). Experiment group 2 was largest, followed by experiment group l and control group at the 3rd thread of implant. There was a significant difference at the 1st thread of control group & experiment group 2, and at 1st thread & 3rd thread of experiment group 1 & 2, and not at control group experiment group 1.(p<0.1)

• Journal of Periodontal and Implant Science
• /
• v.23 no.3
• /
• pp.577-594
• /
• 1993

The ultimate goal of periodontal therapy is the regeneration of the periodontium that have been destroyed as a result of periodontal disease. This study were done in order to determine the healing status of periodontium under Polytetrafluoroethylene and millipore fillter combined with fibrin and the effect of the guided tissue regeneration procedures were performed as follows : 1) flap operation using PTFE membrane(control group) 2) flap operation using PTFE membrane which was fixed with fibrin(experimental group 1) 3) flap operation using millipore filter which was fixed with suture(experimental group II) 4) flap operation using millipore filter which was fixed with fibrin(experimental group II) After 1, 2, 4, 8, 12 weeks, dogs were sacrificed by perfusion technique and tissue block was excised including the tooth and prepared for light microscope with H-E & Masson’s trichrome staining. The result were as follows : In control and experimental group, there is no siginificant difference on epithelial cell down growth within 1st week, but more epithelial cell downgrowth in millipore or millipore combined with fibrin group. In this experiment, there were no significant difference in new cementum and alveolar bone formation whether PTFE membrane was fixed with suture or fibrin. In control and each experimental group, bone maturation appeared in 4 weeks, bone width increased bucco-lingually in control and experimental 1 group especially. Both control group and experimental group showed mild mew cementum formation on root surface and irregular arrangement of collagen fiber at 4 weeks, that showed obvious increased cementum formation at 8 weeks, and that was observed the functional arrangement of collagen fiber between new cementum and new alveolar bone at 12 weeks.

• The Journal of Korean Academy of Prosthodontics
• /
• v.19 no.1
• /
• pp.17-27
• /
• 1981

This study was conducted to determine the chemical composition and the mechanical properties of four commercially available low gold-based crown and bridge alloy produced in Korea. Four dental casting gold-silver-palladium alloys, i.e., A, B, C and D (code of alloys) were selected for the evaluation of chemical composition, ultimate tensile strength, elongation. values and Vickers hardness. The chemical composition of test specimens was analyzed by both emission spectrography and wet gravitation method with a 1.5gm of low gold ingot. The tensile properties and Vickers hardness was determined with cast specimens treated in following three conditions; as-cast, softening heat treatment and hardening heat treatment. The tensile testing bars were cast in accordance with the model designed by Gettleman and Harrison (1969) which was modified from the A. D. A. Specification No. 14 for dental chromium-cobalt casting alloy. Nine tensile test specimens were made from a split silicone mold for each of the test alloys to the size of 2.5mm in diameter and a gauge length of 10mm. All four alloys were handled in accordance with conventional methods used in Type III gold alloys. Ultimate tensile strength and elongation were measured on an Instron Universal Tensile Testing Machine (Model 1125, Japan) operated at a crosshead rate of 0.1cm/min. Elongation values were measured using Digital Measuring Microscope (MS-152, FUSOH, Japan). Vickers hardness was determined with a Vickers Hardness Tester (Model VKH-l, Japan) at a 1.0kg load on a mounted tensile test specimen. The following results were obtained from this study; 1. All tested alloys were composed of Au, Ag, Pd, Cu, Zn and Fe in common. The composition rate of gold for all four alloys was found in the range of $42{\sim}47$ weight % as shown below. Alloy A; Au 45%, Ag 40.2%, Pd 5.76%, others 9.04%. Alloy B; Au 47.1%, Ag 29.03%, Pd 6.98%, others 16.92%. Alloy C; Au 45%, .Ag 26.9%, Pd 6.83%, others 21.07%. Alloy D; Au 41.8%, Ag 34.4%, Pd 6.95%, others 16.85%. 3. The ultimate tensile strength of the four alloys was in the range of $31{\sim}82kg/mm^2$. The test results were shown in the below order from the highest value; As-cast condition; D, B, C, A. Softening heat treament; B, C, D, A. Hardening heat treatment; D, B, C, A. 4. The test :results of the elongation rate for each alloy were in the range of $0.5{\sim}18%$. The test results were shown in the below order from the highest value; As-cast condition; A, D, B, C. Softening heat treatment; A, C, D, B. Hardening heat treatment; C, D, B, A. 5. Vickers hardness for each of the four alloys was in the range of $120{\sim}230$. The test results were shown in the below order from the highest value; As-cast condition; C, B, D, A Softening heat treatment; D, B, C, A. Hardening heat treatment; D, A, C, B. 6. There were no differences in the physical properties between as-cast condition and softening heat treatment.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.4
• /
• pp.424-434
• /
• 2009

Statement of problem: Problems such as loosening and fractures of retained screws and fracture of implant fixture have been frequently reported in implant prosthesis. Purpose: Implant has weak mechanical properties against lateral loading compared to vertical occlusal loading, and therefore, stress analysis of implant fixture depending on its material and geometric features is needed. Material and methods: Total 28 of external hexed implants were divided into 7 of 4 groups; Group A (3i, FULL $OSSEOTITE^{(R)}$Implant), Group B (Nobelbiocare, $Br{\aa}nemark$ $System^{(R)}$Mk III Groovy RP), Group C (Neobiotec, $SinusQuick^{TM}$ EB), Group D (Osstem, US-II). The type III gold alloy prostheses were fabricated using adequate UCLA gold abutments. Fixture, abutment screw, and abutment were connected and cross-sectioned vertically. Hardness test was conducted using MXT-$\alpha$. For fatigue fracture test, with MTS 810, the specimens were loaded to the extent of 60-600 N until fracture occurred. The fracture pattern of abutment screw and fixture was observed under scanning electron microscope. A comparative study of stress distribution and fracture area of abutment screw and fixture was carried out through finite element analysis Results: 1. In Vicker's hardness test of abutment screw, the highest value was measured in group A and lowest value was measured in group D. 2. In all implant groups, implant fixture fractures occurred mainly at the 3-4th fixture thread valley where tensile stress was concentrated. When the fatigue life was compared, significant difference was found between the group A, B, C and D (P<.05). 3. The fracture patterns of group B and group D showed complex failure type, a fracture behavior including transverse and longitudinal failure patterns in both fixture and abutment screw. In Group A and C, however, the transverse failure of fixture was only observed. 4. The finite element analysis infers that a fatigue crack started at the fixture surface. Conclusion: The maximum tensile stress was found in the implant fixture at the level of cortical bone. The fatigue fracture occurred when the dead space of implant fixture coincides with jig surface where the maximum tensile stress was generated. To increase implant durability, prevention of surrounding bone resorption is important. However, if the bone resorption progresses to the level of dead space, the frequency of implant fracture would increase. Thus, proper management is needed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.4
• /
• pp.285-291
• /
• 2012

Purpose: This study was conducted to identify the surface characteristics of titanium discs coated with MS275/PLGA by electrospray and which is effective to mesenchymal stem cell proliferation. Materials and methods: We used anodized surface coated with PLGA as a control group and anodized surface coated with MS275 $0.5{\mu}M$, $1{\mu}M$, $1.5{\mu}M$ as test groups. To examine that the coating particles are nanometer sized, FE-SEM was used and AFM was utilized to determine the difference of coating surface roughness. We checked the mesenchymal stem cell proliferation by using MTT assay on $1^{st}$, $4^{th}$, $7^{th}$ days. Results: There was no significant difference between control groups and test groups in AFM results (P>.05). In MTT assay results, mesenchymal stem cell proliferation was increased with time, at $7^{th}$ day, cell viability on discs coated with $1.5{\mu}M$ MS275 was significantly higher than control group (P<.05). As SEM showed, the number of cells on all discs was increased and the morphology of cell attachment was also wider and closer with time. Conclusion: Titanium surface coated with MS275/PLGA showed significantly higher cell proliferation and the more density of MS275 was dispersed on titanium discs, the faster cells grew.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.27 no.3
• /
• pp.419-430
• /
• 2000

The purpose of this study was to compare the microleakage pattern of preventive resin restoration using conventional composite resin and flowable composite resin that recently developed. 60 sound premolar teeth were allocated to three groups. Flowable composite resin was used for the experimental groups(Group I and II) and conventional resin for the control group(Group III). After composite filling and sealant application, all teeth were thermocycled and evaluated for microleakage under light microscope. Additionally, a variety of voids formed inside restorations were also evaluated. Data were analyzed statistically using Kruskal-Wallis test and/or Mann-Whitney U-test. The results of the present study were as follows. 1. Microleakage found in all samples was only limited to the interface of restoration margin and enamel. 2. The flowable composite resin groups (Group I, II) generally showed less microleakage than control groups (conventional preventive resin restoration) (p<0.05) 3. Various types of voids were observed in most specimens. Especially, there was a tendency for more and larger voids to be found in group I, II than group III (p<0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.2
• /
• pp.221-232
• /
• 2006

The purpose of this study was to investigate the effect of step-curing mode on polymerization shrinkage and contraction of composite resin restoration. Class I cavities were prepared on the extracted human premolars. The cavities were ailed with Filtek $Z-250^{TM}$ (hybrid resin, 3M ESPE, USA) and Filtek $flow^{TM}$ (flowable resin, 3M ESPE, USA) and cured with one of the following irradiation modes; Halogen 40sec with continuous curing, LED 10sec with continuous curing, and LED 13sec with step-curing. Contraction stress was measured with strain gauge which was connected to TML $Datalogger^{TM}$ (TDS-102, SOKKI, Japan) and resin-dentin interfaces were observed by scanning electron microscope. The results of present study can be summarized as follows : 1. Composite resin restoration showed transient expansion just after irradiation of curing light. Contraction stress was increased rapidly at the early phase of polymerization and reduced slowly as time elapsed (P<0.05) 2. $Filtek\;flow^{TM}$ showed lower contraction stress than Filtek $Z-250^{TM}$ regardless of curing modes. 3. LED step-curing mode showed lowest contraction stress in Filtek $Z-250^{TM}$ compared with other curing modes(P<0.05). 4. LED step-curing mode showed lowest contraction stress in $Filtek\;flow^{TM}$ compared with other curing modes(P<0.05), but difference in contraction stress was not so greate as in $Filtek\;Z-250^{TM}$. 5. Polymerization of composite resin by LED light with step-curing mode and halogen light with continuous ode resulted in better marginal sealing than LED light with continuous mode.