• Journal of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.103-109
• /
• 2012

Micro-cracks with a width less than 0.1 mm in precast concrete panels do not cause structural problem, but they can cause problems in long term durability and concrete surfaces aesthetic, requiring additional repair costs. In this paper, polymer cement concrete is used to increase flexural tensile strength and to prevent micro-cracks due to construction loads on LB-DECK panels. Using 5% polymer-cement ratio, the panel crack moment is increased by improving flexural tensile strength and controlling visible micro-cracks during construction stage of LB-DECK.

• Transactions of Materials Processing
• /
• v.21 no.6
• /
• pp.354-359
• /
• 2012

Effects of a nitriding treatment on the tensile and high cycle fatigue properties were investigated by conducting ion-nitriding and gas nitro-caburizing treatments on the spheroidized SCr430B medium-carbon steel and performing tensile and tension-tension high cycle fatigue tests. The nitrided samples showed much lower strength and ductility compared to those in the initial as-spheroidized state and premature fracture occurred at the hardened layers. The micro-voids in the compound layer caused fatigue crack initiation. Thus, the removal of the compound layer with micro-voids remarkably improved the fatigue resistance to even beyond that of the as-spheroidized sample.

• Structural Engineering and Mechanics
• /
• v.82 no.6
• /
• pp.713-724
• /
• 2022

Effects of coal tensile strength and plow configuration on the coal fragmentation process was modeled by two-dimensional particles flow code (PFC2D). Three tensile strength values, 0.5, 1,5 and 3.5 MPa were considered in this numerical study. The cutters of plow penetrated in the coal for 4 mm at a rate of 0.016 m/s. According to the PFC manual, the local damping factor was 0.7. Three failure mechanism of coal during the fragmentation process by plow were modelled. The coal material beneath the cutters showed the elastic, plastic and fracturing behaviors in this analysis. In all the models, the plastic zone was fractured and some micro-cracks were induced but the elastic zone remained undamaged. It was observed that the tensile strength affected the failure mechanism of coal significantly and as it increased the extent of the fractured zone underneath the plow cutter decreased during the fragmentation process.

• Transactions of Materials Processing
• /
• v.18 no.1
• /
• pp.45-51
• /
• 2009

Shape memory alloy has been used to improve the tensile strength of composite by the occurrence of compressive residual stress in matrix using its shape memory effect. In order to fabricate shape memory alloy composite, TiNi alloy fiber and Al2024 sheets were used as reinforcing material and matrix, respectively. In this study, TiNi/Al2024 shape memory alloy composite was made by using hot press method. In order to investigate bonding condition between TiNi reinforcement and Al matrix, the micro-structure of interface was observed by using optical microscope and diffusion layer of interface was measured by using Electron Probe Micro Analyser. And the mechanical properties of composite with three parameters(volume fraction of fiber, cold rolling amount and test temperature) were obtained by tensile test. The most optimum bonding condition for fabrication the TiNi/Al2024 composite material was obtained as holding for 30min. under the pressure of 60MPa at 793K. The strength of composite material increased considerably with the volume fraction of fiber up to 7.0%. And the tensile strength of this composite increased with the reduction ratio and it also depends on the volume fraction of fiber.

• Geomechanics and Engineering
• /
• v.29 no.6
• /
• pp.627-643
• /
• 2022

Water-rock interactions have a significant influence on the mechanical behavior of rocks. In this study, uniaxial compression and tension tests on different water-treated sandstone samples were conducted. Acoustic emission (AE) monitoring and micro-pore structure detection were carried out. Water-rock interactions and their effects on rock mechanical behavior were discussed. The results indicate that water content significantly weakens rock mechanical strength. The sensitivity of the mechanical parameters to water treatment, from high to low, are Poisson ratio (𝜇), uniaxial tensile strength (UTS), uniaxial compressive strength (UCS), elastic modulus (E), and peak strain (𝜀). After water treatment, AE activities and the shear crack percentage are reduced, the angles between macro fractures and loading direction are minimized, the dynamic phenomenon during loading is weakened, and the failure mode changes from a mixed tensile-shear type to a tensile one. Due to the softening, lubrication, and water wedge effects in water-rock interactions, water content increases pore size, promotes crack development, and weakens micro-pore structures. Further damage of rocks in fractured and caved zones due to the water-rock interactions leads to an extra load on the adjoining coal and rock masses, which will increase the risk of dynamic disasters.

• Journal of the Korean Society of Safety
• /
• v.23 no.5
• /
• pp.30-34
• /
• 2008

To evaluate the mechanical properties of in-service materials, tensile properties measurement using small-scaled specimen has been carried out. Tensile testing specimens with various dimensions, including standard and sub-size specimen specified in ASTM and ISO and small-scaled specimen, were prepared. Tensile strain in small-scaled specimen was measured using micro-ESPI system set up in this study. This system was used in the specimen with the parallel length of 2 mm and in subsequently measuring the strain under tensile loading. From each type of tensile specimen, stress-strain curves were determined. The dimension effect of the tensile properties was investigated comparing the tensile results obtained from standard specimens and small-scaled specimens. It was shown that the tensile strength for the small-scaled specimen is lower by 15% than those for the standard specimen.

• Journal of the Semiconductor & Display Technology
• /
• v.3 no.2
• /
• pp.23-26
• /
• 2004

Thin film is one of the most general structures used in micro-electro-mechanical systems (MEMS). To measure the mechanical properties of SU-8 film, tensile testing was adopted which offers not only elastic modulus but also yield strength and plastic deformation by load-displacement curve. Tensile testing system was constructed with linear guided servo motor for actuation, load cell for force measurement and dual microscope for strain measurement.

• Journal of the korean Society of Automotive Engineers
• /
• v.9 no.3
• /
• pp.76-84
• /
• 1987

A study has been made to clarify the microstructural effect on static tensile properties of the dual phase steel, in which the martensitic phase encapsulated islands of ferritic phase. The main results are as follows: Yield strength is associated with the degree of plastic constraint factor and tensile strength increases with increasing of strain hardening exponent. Also, the variation of ductility is dependent upon the amount of micro-brittle facets.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.41-45
• /
• 2011

SnAgCu lead-free solder alloy is considered as the best alternative to eutectic tin-lead solder. However, the detailed material properties of SnAgCu solder are not available in public. Hence, this paper presents an estimation of mechanical properties of SnAgCu lead-free solder. In particular, the weight percent of Ag was varied as 1.0wt%, 2.5wt%, 3.0wt%, and 4.5wt% in order to estimate the effect of Ag in the Sn-xAg-0.5Cu ternary alloy system. For this purpose, four types of SnAgCu bars were first molded by casting and then standard specimens were cut out of molded bars. Micro-Vickers hardness, tensile tests were finally performed to estimate the variations in mechanical properties according to the weight percent of Ag. Test results reveal that the higher the weight percent of Ag is, the higher the hardness, yield strength, and ultimate tensile strength become. More material properties will be further investigated in the future work.

• Advances in concrete construction
• /
• v.13 no.3
• /
• pp.265-279
• /
• 2022

The roughness of substrate concrete interfaces before new concrete placement has a major effect on the interface bond behaviour. However, there are challenges associated with the consistency of the final roughness interface prepared using conventional roughness preparation methods which influences the interface bond performance. In this study, five quantitative interface roughness textures with different roughness tooth angles, depths, and tooth distribution were created to ensure consistency of interface roughness and to evaluate the bond behaviour at a precast and new concrete interface using the splitting tensile test, slant shear test, and double-shear test. In addition, smooth interface specimens and two separate the pitting interface roughness were also utilized. Obtained results indicate that the quantitative roughness has a very limited effect on the interface tensile bond strength if no extra micro-roughness or bonding agent is added at the interface. The roughness method however causes enhanced shear bond strength at the interface. Increased tooth depth improved both the tensile and shear bond strength of the interfaces, while the tooth distribution mainly influenced the shear bond strength. Major failure modes of the test specimens include interface failure, splitting cracks, and sliding failure, and are influenced by the tooth depth and tooth distribution. Furthermore, the interface properties were obtained and presented while a comparison between the different testing methods, in terms of bond strength, was performed.