• Journal of Dental Rehabilitation and Applied Science
• /
• v.30 no.1
• /
• pp.16-22
• /
• 2014

Purpose: The purpose of this study was to assess the marginal and mesial fitness of zirconia single copings and 3-unit fixed partial dentures (FPDs) manufactured with an identical model. Materials and Methods: An epoxy model in which the maxillary right 2nd premolar is lost and maxillary 1st premolar and 2nd molar are formed as abutments was manufactured and scanned by using a laser scanner. A ten units of zirconia single copings were manufactured for maxillary 1st premolar and 2nd molar, respectively and the same number of 3-unit FPDs were manufactured. For the measurements of fitness, the manufactured silicone replicas were divided into four parts and the fitness were measured by digital microscope at measurement points (P1, P2, P3, P4 and P5) of each plane. The measured gaps were classified into three categories: marginal gap (MG, P1), axial gap (AG, average of P2 and P3), occlusal gap (OG, average of P4 and P5). Results: The ranges of MG, AG and OG for single copings were 18.47 - 40.54 ${\mu}m$, 39.73 - 73.61 ${\mu}m$ and 116.90 - 134.69 ${\mu}m$, respectively. The ranges of MG, AG and OG for 3-unit FPDs were 45.95 - 87.44 ${\mu}m$, 23.78 - 57.00 ${\mu}m$ and 99.89 - 131.06 ${\mu}m$, respectively. Conclusion: The result of the study shows that the MGs for 3-unit FPDs were higher than those of single copings, though they are within the range of clinical acceptance, indicating that the use of more homogeneous zirconia block and modification of sintering processes are needed to ensure the prevention of increase of gap in 3-unit FPDs.

• The Journal of Advanced Prosthodontics
• /
• v.11 no.5
• /
• pp.253-261
• /
• 2019

PURPOSE. To evaluate the influence of cyclic loading on phase transformation of zirconia abutments and to compare the effectiveness of three different quantitative ageing assessment techniques. MATERIALS AND METHODS. Thirty two Y-TZP prostheses fabricated from two brands, InCoris ZI and Ceramill ZI, were cemented to titanium bases and equally divided into two subgroups (n=8): control group without any treatment and aged group with cyclic loading between 20 N and 98 N for 100,000 cycles at 4 Hz in distilled water at $37^{\circ}C$. The tetragonal-to-monoclinic phase transformation was assessed by (i) conventional x-ray diffraction (XRD), (ii) micro x-ray diffraction (${\mu}XRD$), and (iii) micro-Raman spectroscopy. The monoclinic-phase fractions (M%) were compared by two-way ANOVA. RESULTS. InCoris Zi presented significantly higher M% than Ceramill Zi in both control and aged groups (P<.001). Both materials exhibited significant phase transformation with monoclinicphase of 1 to 3% more in aged groups than controls for all three assessment techniques. The comparable M% was quantified by both ${\mu}XRD$ and XRD. The highest M% was assessed with micro-Raman. CONCLUSION. Cyclic loading produced significant phase transformation in tested Y-TZP prostheses. The micro-Raman spectroscopy could be used as an alternative to XRD and ${\mu}XRD$.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.6
• /
• pp.479-488
• /
• 2016

PURPOSE. The aim of this study was to test the modulus of elasticity (E) across the interfaces of yttria stabilized zirconia (YTZP) / veneer multilayers using nanoindentation. MATERIALS AND METHODS. YTZP core material (KaVo-Everest, Germany) specimens were either coated with a liner (IPS e.max ZirLiner, Ivoclar-Vivadent) (Type-1) or left as-sintered (Type-2) and subsequently veneered with a pressable glass-ceramic (IPS e.max ZirPress, Ivoclar-Vivadent). A $5{\mu}m$ (nominal tip diameter) spherical indenter was used with a UMIS CSIRO 2000 (ASI, Canberra, Australia) nanoindenter system to test E across the exposed and polished interfaces of both specimen types. The multiple point load - partial unload method was used for E determination. All materials used were characterized using Scanning Electron Microscopy (SEM) and X - ray powder diffraction (XRD). E mappings of the areas tested were produced from the nanoindentation data. RESULTS. A significantly (P<.05) lower E value between Type-1 and Type-2 specimens at a distance of $40{\mu}m$ in the veneer material was associated with the liner. XRD and SEM characterization of the zirconia sample showed a fine grained bulk tetragonal phase. IPS e-max ZirPress and IPS e-max ZirLiner materials were characterized as amorphous. CONCLUSION. The liner between the YTZP core and the heat pressed veneer may act as a weak link in this dental multilayer due to its significantly (P<.05) lower E. The present study has shown nanoindentation using spherical indentation and the multiple point load - partial unload method to be reliable predictors of E and useful evaluation tools for layered dental ceramic interfaces.

• The Journal of Korean Academy of Prosthodontics
• /
• v.52 no.4
• /
• pp.312-316
• /
• 2014

Purpose: The aim of this study was to compare the fracture toughness of currently available resin cements for zirconia restorations and evaluate the effect of water storage on fracture toughness of those resin cements. Materials and methods: Single-edge notched specimens ($3mm{\times}6mm{\times}25mm$) were prepared from three currently available dual cure resin cements for zirconia restorations (Panavia F 2.0, Clearfil SA luting and Zirconite). Each resin cement was divided into four groups: immersed in distilled water at $37^{\circ}C$ for 1 (Control group), 30, 90, or 180 days (n=5). Specimens were loaded in three point bending at a cross-head speed of 0.1 mm/s. The maximum load at specimen failure was recorded and the fracture toughness ($K_{IC}$) was calculated. Data were analyzed using one-way ANOVA and multiple comparison $Scheff{\acute{e}}$ test (${\alpha}$=.05). Results: In control group, the mean $K_{IC}$ was $3.41{\pm}0.64MN{\cdot}m^{-1.5}$ for Panavia F, 2.0, $3.07{\pm}0.41MN{\cdot}m^{-1.5}$ for Zirconite, $2.58{\pm}0.30MN{\cdot}m^{-1.5}$ for Clearfil SA luting respectively, but statistical analysis revealed no significant difference between them. Although a gradual decrease of $K_{IC}$ in Panavia F 2.0 and gradual increases of KIC in Clearfil SA luting and Zirconite were observed with storage time, there were no significant differences between immersion time for each cement. Conclusion: The resin cements for zirconia restorations exhibit much higher $K_{IC}$ values than conventional resin cements. The fracture toughness of resin cement for zirconia restoration would not be affected by water storage.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.318-324
• /
• 2015

Purpose: This study compared shear bond strengths of five self-adhesive cements with phosphate monomer to zirconium oxide ceramic with and without airborn particle abrasion. Materials and methods: One hundred zirconia samples were air-abraded ($50{\mu}mAl_2O_3$). One hundred composite resin cylinders were fabricated. Composite cylinders were bonded to the zirconia samples with either Permacem 2.0 (P), $Clearfil^{TM}$ SA Luting (C), $Multilink^{(R)}$ Speed (M), $RelyX^{TM}$ U200 Automix (R), G-Cem $LinkAce^{TM}$ (G). All bonded specimens were stored in distilled water ($37^{\circ}C$) for 24 h and half of them were additionally aged by thermocycling ($5^{\circ}C$, $55^{\circ}C$, 5,000 times). The bonded specimens were loaded in shear force until fracture (1 mm/min) by using Universal Testing Machine (Model 4201, Instron Co, Canton, MA, USA). The failure sites were inspected under field-emission scanning electron microscopy. The data was analyzed with ANOVA, Tukey HSD post-hoc test and paired samples t-test ($\alpha$=.05). Results: Before and after thermocycling, $Multilink^{(R)}$ Speed (M) revealed higher shear-bond strength than the other cements. G-Cem $LinkAce^{TM}$ (G) showed significantly lower bond strengths after thermocycling than before treatment (P<.05), but the other groups were not significantly different (P>.05). Conclusion: Most self-adhesive cements with phosphate monomer showed high shear bond strength with zirconia ceramic and weren't influenced by thermocycling, so they seem to valuable to zirconia ceramic bonding.

• Journal of dental hygiene science
• /
• v.13 no.2
• /
• pp.135-141
• /
• 2013

One factor for successful prognosis of finished dental prosthesis is good marginal fit. The purpose of this study in vitro investigation was to compare the marginal fit of all-ceramic crown before and after porcelain veneering, to evaluate the influence of high temperature of the porcelain firing on the fit. For this experiment, model of abutment tooth of maxillary right central incisor was prepared. Ten working models were produced. Ten zirconia cores were made by dental computer aided design/computer aided manufacturing system. The marginal fit of specimens were examined using silicone replica technique. Silicone replicas were sectioned four times and were measured through a digital microscope (${\times}160$). Marginal fit is a distance connected between edge end part of specimen and abutment margin. Each specimens was measured twice, the first measurement was done prior to veneering porcelain firing, while the second measurement was done after the porcelain firing to evaluate this process. Statistical analyses were performed with paired t-test. $Mean{\pm}SD$ marginal fit was $60.8{\pm}14.2{\mu}m$ for zirconia core and $86.1{\pm}13.3{\mu}m$ for all-ceramic crown. They were statistically significant differences (p<0.001). But all specimens showed a marginal fit where the gap widths ranged within the clinical recommendation ($120{\mu}m$), all-ceramic crown production using the zirconia core was adequate.

• Journal of Technologic Dentistry
• /
• v.31 no.2
• /
• pp.23-30
• /
• 2009

All-ceramic restorations have gained acceptance among clinicians and patients because of their superior esthetics. Most all-ceramic systems have a 2-layer structure, using a weak veneering ceramic over a strong supporting core. often, failure of all-ceramic restorations occurs when the veneering ceramic fractures, exposing the core material. The purpose of this study was to compare the shear bond strength of heat press ceramic system (Zirpress) to zirconia core with various surface treatments. 10 metal cores and 50 zirconia cores were fabricated and divided into six groups according to surface treatment such as Zirliner application, aluminium oxide blasting, and 9.5% HF etching. Sixty specimens were prepared using Zirpress, veneered 8mm height and 3mm in diameter, over the zirconia cores (n=10). The shear bond strength test was performed in a universal testing machine with a crosshead speed of 1/min. Ultimate shear bond strength data were analyzed with One-way ANOVA and the Scheffe's test (p=.05). Within the limits of this study, the following conclusions were drawn: The mean shear bond strengths (MPa) were: 12.93 for $110{\mu}m$ aluminium oxide blasting/Rexillium III/IPS e.Max Zirpress; 14.92 for $50{\mu}m$ aluminium oxide blasting ${\pm}9.5%$ HF etching/Zirconis core/IPS e.Max Zirpress; 16.37 for $110{\mu}$ aluminium oxide blasting + 9.5% HF etching/Zirconis core/IPS e.Max Zirpress; 12.89 for $200{\mu}$ aluminium oxide blasting + 9.5% HF etching/Zirconis core/IPS e.Max Zirpress; 19.30 for 9.5% HF etching/Zirconis core/IPS e.Max Zirpress; 19.55 for Zirliner/Zirconis core/IPS e.Max Zirpress. The mean shear bond strength for ZNTZH (Zirliner/Zirconis core) and ZNTEH (9.5% HF etching/Zirconis core) were significantly superior to MS110H ($110{\mu}$ aluminium oxide blasting/Rexillium III) and ZS200EH ($200{\mu}$ aluminium oxide blasting + 9.5% HF etching/Zirconis core) (p<0.05).

• Journal of Periodontal and Implant Science
• /
• v.33 no.1
• /
• pp.1-11
• /
• 2003

Hydroxyapatite(HA) has been extensively used as bone graft materials and tooth implant surface coating materials because of its biocompatibility and osteoconductive properties. However, as HA is intrinsically poor in mechanical properties, zirconia($ZrO_2$) was incorporated with HA as reinforcing phases for improvement of mechanical properties. The purpose of this study was to investigate the biological activities of HA-coated zirconia through the cell proliferation test, measurements of alkaline phosphatase activity, and histologic examination. Four kinds of tested blocks were prepared according to the pore size (300-500${\mu}m$/500-700${\mu}m$) and the porosity (70%/90%). Cell proliferation and alkaline phosphatase activity was measured at 1, 7, 14 days. The number of cells proliferate after 7, 14 days were significantly increased in all groups when compared with that of the first day, but there was no significant difference between the 4 groups at each time period. At the 7 day, alkaline phosphatase activities of cells cultured in 4 groups were higher than that of the first day, but there was no significant difference between the 4 groups at each time period. The human gingival fibroblast and MG 63 cell was used to evaluate the cell cytotoxicity using MTT test. The materials tested in the current study turned out to be non-cytotoxic. In histologic examination(SEM), at 1 day there were many cells attached on the surfaces of all kinds of tested blocks. The number of cells were increased over time. At the 14 day, there were more cells proliferated than 1 day and some of the pores of blocks were partially filled with the proliferated cells. The in vitro response of osteoblast-like cells to the HA-coated zirconia showed comparable effect on transformation comparable to hydroxyapatite.

• Journal of Technologic Dentistry
• /
• v.36 no.2
• /
• pp.83-89
• /
• 2014

Purpose: This study is to evaluate the effect of modeling liquid on the shear-bond strength between zirconia core and veneering ceramic. Methods: Disk-shaped (diameter: 12.0mm; height: 3.0mm) zirconia were randomly divided into six groups according to the surface conditioning method and whether modeling liquid is used or not to be applied (N=60, n=10 per group): group 1-control group with distilled water(ZD); group 2-control group with modeling liquid(ZM); group 3-airborne particle abrasion with $110-{\mu}m$ $Al_2O_3$(AD) with distilled water; group 4-airborne particle abrasion with $110-{\mu}m$ $Al_2O_3$ with modeling liquid(AM); group 5-liner with distilled water(LD); group $6{\pounds}{\neq}liner$ with modeling liquid(LM). Contact angles were determined by the sessile drop method at room temperature using a contact angle measurement apparatus. The specimens were prepared using dentin veneering ceramics, veneered, 3mm high and 2.8mm in diameter, over the cores. The shear bond strength test was performed in a Shear bond test machine. Load was applied at a cross-head speed of 0.50mm/min until failure. The fractured zirconia surfaces were evaluated by using stereomicroscope (${\times}30$). Collected data were analyzed using SPSS(Statistical Package for Social Sciences) Win 12.0 statistics program. Results: ZD showed the highest contact angle($50.6{\pm}5.4^{\circ}$) and LD showed the lowest value($6.7{\pm}1.3^{\circ}$). Control groups and zirconia liner groups were significantly higher contact angle than liner groups(p<0.05). LD was the highest shear bond strength($43.9{\pm}3.8MPa$) and ZD was the lowest shear bond strength($24.8{\pm}4.9MPa$). Shear bond strengths of control groups and contact angle of liner groups were not significantly different((p>0.05). Liner groups presented adhesive failures. The others groups showed cohesive and adhesive failures. Conclusion: Modeling liquid groups showed lower contact angles and lower shear bond strength compared to those of distilled water groups.

• Journal of the Mineralogical Society of Korea
• /
• v.14 no.2
• /
• pp.99-110
• /
• 2001

A gem-quality yttria-stabilized zirconium oxide crystals were synthesized by the skull-melting method, using the RF electrical apparatus. Principal raw materials used were $ZrO_2$and 25 wt.% $Y_2O_3$as stabilizer and 0.03~0.05 wt.% $Nd_2O_3$decolorizing agent were added to it. The single crystals were approximately 20$\times$63 mm in size with chemical composition $Zr_{0.73}$ $Y_{0.27}$ $O_{1.87}$ . The crystals are isotropic with no appreciable anisotropism under a polarizing microscope. Their refractive indices are in the range of 2.15~2.18, specific gravity 5.85, Mohs' hardness 8~8.5, and reflectivity 13.47%. The zirconia crystals were confirmed to have cubic structure with Face-centered lattice(Z=4), space group Fm3m ($CaF_2$-type structure) and unit cell parameters are a=5.157 $\AA$. The optimal growing conditions for yttria-stabilized zirconia are 50 kW, 2.94 MHz in power and to use a crucible with 105 mm $\times$ 135 mm in size. When the lowering speed of the crucible was set 16mm/hr gave the best yield, 42%. Since the refractive index(2.15~2.18) of cubic zirconia is smaller than that of diamond, the angle between crown and pavilion should be fashioned to make it smaller than $40.5^{\circ}$ to show the maximum brilliancy and fire.