• Macromolecular Research
• /
• v.16 no.5
• /
• pp.467-472
• /
• 2008

Rigid polyurethane foams (RPUFs) were fabricated from crude MDI (CMDI) and polypropylene glycols (PPGs) of various isocyanate indices with a physical blowing agent (HFC 365mfc). There was a tendency for the gel time to decrease and the tack-free time to increase with increasing index value. With increasing index value the foam density and compression strength decreased and the glass transition temperature, dimension stability and thermal insulation increased, while the cell size and closed cell content were virtually unchanged. Allophanate crosslinks and condensation reactions between the isocyanate groups, which are favored with a high index value, exerted significant effects on the properties of RPUFs.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.5 no.4
• /
• pp.110-120
• /
• 1997

One of the most important factor for the comfort of the passenger vehicles is the minimization of the compressible transmissibility during the running vehicles. Seat foam materials of I2 series(index 95 and the contents of isocyanate TDI was changed in percentages 75, 70, 65, 60, 50, 40) and DI series(density 50kg/$\textrm{m}^3$, index was changed 100, 95, 90) showed the significant differences in their transmissibility depended upon their chemical constitution such as index and contents of isocyanate TDI. The minimum trasmissibility of seat foam materials of I2 series was found from the materials with the contents of 65% isocyanate TDI and the index 95 at the frequency 4.79~5.31Hz. Also the minimum transmissibility of seat foam materials of DI series was found from the materials with the index 90 and the density of 50kg/$\textrm{m}^3$ at the frequency of 4.79~5.31Hz.

• Elastomers and Composites
• /
• v.55 no.1
• /
• pp.20-25
• /
• 2020

The effect of the isocyanate index (NCO index) on the particle size and particle size distribution of a waterborne polyurethane dispersion (WPUD) with polycarbonate-diol was determined. The WPUDs were prepared using a conventional acetone process with polycarbonate-polyol (M_n = 2028), 4,4'-methylenebis(cyclohexyl isocyanate) (H₁₂MDI), 2,2-bis(hydroxymethyl) propionic acid (DMPA), and dibutyltin dilaurate catalyst. At NCO index values below 1.5, the number average particle diameter of the WPUDs significantly increased with the NCO index, whereas the particle diameter slightly varied at higher NCO indexes. The dependency of the WPUD viscosity on the NCO index exhibited similar behavior to that of the particle size. The relative values of the full width at half maximum of the WPUD particle distribution curves at various NCO indexes were not influenced by the NCO index.

• Applied Chemistry for Engineering
• /
• v.19 no.4
• /
• pp.427-431
• /
• 2008

The rigid polyurethane foams (PUF) were prepared using polyols with 90, 110, 130, and 150 isocyanate index. The effect of sea water on the physical properties of PUF with the increase in isocyanate (NCO) index and ageing time was investigated. Tensile strengths and compressive strengths of the PUFs decreased up to 10% and 7% with an increase in ageing time, respectively. Cell morphology of the PUF under sea water was turned out to be the same as that in the ambient condition. It was observed that $T_g$ and tensile modulus of the PUF under sea water increased. The results showed an additional cross-link reaction of non-reacted MDI and the change of NCO peak as observed from FT-IR spectrum.

• Journal of Integrative Natural Science
• /
• v.7 no.1
• /
• pp.5-10
• /
• 2014

A study that copolymerized Ag nanoparticle and furfuryl isocyanate with the crosslinking agent EGDMA (ethylene glycol dimethacrylate), HEMA (2-hydroxyethyl methacrylate), MMA (methyl methacrylate), MA (methacrylic acid) and the initiating agent AIBN (azobisisobutyronitrile) is presented. Measurement of the physical characteristics of the produced macromolecule showed that the water content is 32.08~32.67%, refractive index 1.446~1.448, visible light transparency 83.2~67.6%, contact angle $68.2{\sim}83.5^{\circ}$ and tensile strength 0.541~0.755 kgf. It is also demonstrated that the addition of Ag nanoparticles is associated with the reduction of UV-B transmittance and increase in tensile strength. The results show that the produced copolymer can be used as a material for ophthalmic lenses with durability and UV-blocking properties.

• Journal of Integrative Natural Science
• /
• v.6 no.1
• /
• pp.1-7
• /
• 2013

Polyurethane resin containing isocyanate is marked by excellent tensile and mechanical strengths and this test aims to gauge its applicability as a medical high polymer. Tris [2-(acryloyloxy)ethyl]isocyanurate and hexamethylenediisocyanate were added to a basic mixing ratio of HEMA (2-hydroxyethyl methacrylate), MMA (methyl methacrylate), NVP (n-vinyl-2-pyrrolidone) and crosslink agent, EGDMA (ethylene glycol dimethacrylate) with increasing proportions and copolymerized respectively. Also, the basic physical properties of the polymerized high polymers including refraction rate, tensile strength, light transmission and water content were measured to confirm that they are appropriate as hydrogelcontact lenses. After measuring the physical properties of high performance polymers produced by adding tris [2-(acryloyloxy) ethyl]isocyanurate, it was found that the average tensile strengths of sample TRIS1 to TRIS10 were between 0.285 and 0.612 kgf, while the average values of refractive index were ranged from 1.441 to 1.449 with water content from 30.00 to 37.35%.The measurement of physical properties of the copolymers generated by adding hexamethylenediisocyanate showed that the average tensile strength of sample HEXA1 to HEXA10 ranged from 0.267 to 1.742 kgf, the refractive index ranged from 1.443 to 1.475 and water contents were in the range of 21.22 to 35.58%. In all combinations the transmission rates satisfied the transmittance of general hydrogel contact lenses. From theresults, it is possible to conclude that the produced copolymers can be used as contact lens materials with excellent tensile strength.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 2003.10a
• /
• pp.60-65
• /
• 2003

Semi-Rigid 폴리우레탄 foam의 한 종류인 PIR(Polyisocyanurate) foam은 당량적으로 과량의 MDI가 투입되어 생성된 Isocyanate Trimer(Isocyanurate)가 높은 Char Formation을 형성, 우수한 난연특성, 낮은 SMOKE INDEX, 높은 OXYGEN INDEX를 나타낸다. 국내엔 1988년 단열재용 폴리우레탄 foam으로는 최초로 미국의 UL Mark를 획득하여 건설, 건축등 관련업계에서 요구하는 난연특성 및 단열제로서의 제반요건에 부응하며 꾸준히 연구 개발되어 왔다.(중략)

• Journal of the Korean Applied Science and Technology
• /
• v.23 no.3
• /
• pp.264-271
• /
• 2006

PU type flame-retardant coatings (TBAO/L-75, TBAOL ; TBAO/N-100, TBAON) were prepared by blending bromine-containing modified polyester (TBAO) which was synthesized in our earlier work. with two kinds of isocyanate curing agents, Desmodur L-75 and Desmodur N-100. Physical properties of the prepared flame-retardant coatings were tested. TBAOL shows better hardness than TBAON, while TBAON shows better viscosity, accelerated weathering resistance, yellowness index and lightness index difference than TBAOL. There were no remarkable differences in fineness of grind, $60^{\circ}$ specular gloss, cross-hatch adhesion, and abrasion resistance of TBAOL and TBAON. There was no discernable difference in flame-retardancy between the two flame-retardant coatings, TBAOL and TBAON. When the content of tribromo acetic acid, which is flame-retarding component, was 30wt% the LOI value was in a range of $29{\sim}30%$, which indicates that the two coatings are good flame-retardant coatings.

• Journal of Integrative Natural Science
• /
• v.11 no.2
• /
• pp.113-120
• /
• 2018

This study was planned to prepare the high strength hydrogel ophthalmic lens containing isocyanate group and nanoparticles. HDI with carbon nanoparticles were used as additives for the basic combination of HEMA, MA and MMA, and the materials were copolymerized with EGDMA as the cross-linking agent and AIBN as the initiator. The mixture was heated at $100^{\circ}C$ for an hour to produce the high performance hydrogel ophthalmic lens by cast mold method. Measurement of the physical characteristics of the produced material showed that the refractive index was in the range of 1.4027~1.4600, water content 25.21~44.01%, contact angle $54.18{\sim}72.94^{\circ}$, visible light transmittance 53.03~92.09%, and tensile strength 0.1024~0.2359 kgf and breaking strength was 0.0872~0.2825 kgf. The results showed an increase of refractive index while the decrease in water content. And also, the breaking strength was highest when the addition ratio of HDI was 5%(wt). As a result of the absorbance measurement, no significant difference was observed in all the samples, so it can be judged that the stabilization of nanoparticles in the polymer was maintained.

• Polymer(Korea)
• /
• v.26 no.2
• /
• pp.193-199
• /
• 2002

The dichloro-polyester polyol (DCBAO) which was synthesized in our earlier work was cured at room temperature with two different type of curing agents including Desmodur N-3300 and Desmodur L-75 to get a polyurethane flame-retardant coatings (DCBAO/N-3300=DEBAN and DCBAO/L-75=DCBAL). We could not observe any deterioration of physical properties of the flame-retardant PU coatings (UCBAN and DCBAL) in comparison with the conventional PU coatings. Thermal resistance of DCBAL-type flame-retardant coatings, which was measured by yellowness index difference, was inferior to that of DCBAL-type PU coatings. We believe that this phenomena is attributed to the poor thermal resistance of Desmodur L-75 isocyanate. It was observed that the LOI values were 25∼26% for the PU coatings containing 20∼30 wt% of 2,4-dichlorobenzoic acid.