• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.20 no.3
• /
• pp.571-576
• /
• 2016

Asymmetric double gate(DG) MOSFET has the different top and bottom gate oxides thicknesses. It is analyzed the deviation of subthreshold swing(SS) and conduction path for the ratio of top and bottom gate oxide thickness of asymmetric DGMOSFET. SS varied along with conduction path, and conduction path varied with top and bottom gate oxide thickness. The asymmetric DGMOSFET became valuable device to reduce the short channel effects like degradation of SS. SSs were obtained from analytical potential distribution by Poisson's equation, and it was analyzed how the ratio of top and bottom oxide thickness influenced on conduction path and SS. SSs and conduction path were greatly influenced by the ratio of top and bottom gate oxide thickness. Bottom gate voltage cause significant influence on SS, and SS are changed with a range of 200 mV/dec for $0<t_{ox2}/t_{ox1}<5$ under bottom voltage of 0.7 V.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.41 no.11
• /
• pp.7-13
• /
• 2004

Experimental results are presented for the degradation of 3 nm-thick gate oxide under -2.5V $\leq$ V$_{g}$ $\leq$-4.0V stress and 10$0^{\circ}C$ conditions using P and NMOSFETs that are annealed with hydrogen or deuterium gas at high-pressure (5 atm). The degradation mechanisms are highly dependent on stress conditions. For low gate voltage, hole-trapping is found to dominate the reliability of gate oxide both in P and NMOSFETs. With increasing gate voltage to V$_{g}$ =-4.0V, the degradation becomes dominated by electron-trapping in NMOSFETs, however, the generation rate of "hot" hole was very low, because most of tunneling electrons experienced the phonon scattering before impact ionization at the Si interface. Statistical parameter variations as well as the gate leakage current depend on and are improved by high-pressure deuterium annealing, compared to corresponding hydrogen annealing. We therefore suggest that deuterium is effective in suppressing the generation of traps within the gate oxide. Our results therefore prove that hydrogen related processes are at the origin of the investigated oxide degradation.gradation.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.1
• /
• pp.6-11
• /
• 2005

In this paper, two types of vertical SIT(Static Induction Transistor) structures are proposed to improve their electrical characteristics including the blocking voltage. Besides, the two dimensional numerical simulations were carried out using ISE-TCAD to verify the validity of the device and examine the electrical characteristics. First, a trench gate region oxide power SIT device is proposed to improve forward blocking characteristics. Second, a trench gate-source region power SIT device is proposed to obtain more higher forward blocking voltage and forward blocking characteristics at the same size. The two proposed devices have superior electrical characteristics when compared to conventional device. In the proposed trench gate oxide power SIT, the forward blocking voltage is considerably improved by using the vertical trench oxide and the forward blocking voltage is 1.5 times better than that of the conventional vertical power SIT. In the proposed trench gate-source oxide power SIT, it has considerable improvement in forward blocking characteristics which shows 1500V forward blocking voltage at -10V of the gate voltage. Consequently, the proposed trench oxide power SIT has the superior stability and electrical characteristics than the conventional power SIT.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.287-287
• /
• 2011

ITRS(international technology roadmap for semiconductors)에 따르면 MOS (metal-oxide-semiconductor)의 CD(critical dimension)가 45 nm node이하로 줄어들면서 poly-Si/SiO2를 대체할 수 있는 poly-Si/metal gate/high-k dielectric이 대두되고 있다. 일반적으로 metal gate를 식각시 정확한 CD를 형성시키기 위해서 plasma를 이용한 RIE(reactive ion etching)를 사용하고 있지만 PIDs(plasma induced damages)의 하나인 PICD(plasma induced charging damage)의 발생이 문제가 되고 있다. PICD의 원인으로 plasma의 non-uniform으로 locally imbalanced한 ion과 electron이 PICC(plasma induced charging current)를 gate oxide에 발생시켜 gate oxide의 interface에 trap을 형성시키므로 그 결과 소자 특성 저하가 보고되고 있다. 그러므로 본 연구에서는 이에 차세대 MOS의 metal gate의 식각공정에 HDP(high density plasma)의 ICP(inductively coupled plasma) source를 이용한 중성빔 시스템을 사용하여 PICD를 줄일 수 있는 새로운 식각 공정에 대한 연구를 하였다. 식각공정조건으로 gas는 HBr 12 sccm (80%)와 Cl2 3 sccm (20%)와 power는 300 w를 사용하였고 200 eV의 에너지로 식각공정시 TEM(transmission electron microscopy)으로 TiN의 anisotropic한 형상을 볼 수 있었고 100 eV 이하의 에너지로 식각공정시 하부층인 HfO2와 높은 etch selectivity로 etch stop을 시킬 수 있었다. 실제 공정을 MOS의 metal gate에 적용시켜 metal gate/high-k dielectric CMOSFETs의 NCSU(North Carolina State University) CVC model로 effective electric field electron mobility를 구한 결과 electorn mobility의 증가를 볼 수 있었고 또한 mos parameter인 transconductance (Gm)의 증가를 볼 수 있었다. 그 원인으로 CP(Charge pumping) 1MHz로 gate oxide의 inteface의 분석 결과 이러한 결과가 gate oxide의 interface trap양의 감소로 개선으로 기인함을 확인할 수 있었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.8
• /
• pp.687-694
• /
• 2008

This paper is focused on the improvement of MOS device reliability related to deuterium process. The injection of deuterium into the gate oxide film was achieved through two kind of method, high-pressure annealing and low-energy implantation at the back-end of line, for the purpose of the passivation of dangling bonds at $SiO_2/Si$ interface. Experimental results are presented for the degradation of 3-nm-thick gate oxide ($SiO_2$) under both negative-bias temperature instability (NBTI) and hot-carrier injection (HCI) stresses using P and NMOSFETs. Annealing process was rather difficult to control the concentration of deuterium. Because when the concentration of deuterium is redundant in gate oxide excess traps are generated and degrades the performance, we found annealing process did not show the improved characteristics in device reliability, compared to conventional process. However, deuterium ion implantation at the back-end process was effective method for the fabrication of the deuterated gate oxide. Device parameter variations under the electrical stresses depend on the deuterium concentration and are improved by low-energy deuterium implantation, compared to conventional process. Our result suggests the novel method to incorporate deuterium in the MOS structure for the reliability.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.8
• /
• pp.609-615
• /
• 2011

This paper is studied for the improvement of the characteristics of gate oxide with 3-nm-thick gate oxide by deuterium ion implantation methode. Deuterium ions were implanted to account for the topography of the overlaying layers and placing the D peak at the top of gate oxide. A short anneal at forming gas to nitrogen was performed to remove the damage of D-implantation. We simulated the deuterium ion implantation to find the optimum condition by SRIM (stopping and range of ions in matter) tool. We got the optimum condition by the results of simulation. We compare the electrical characteristics of the optimum condition with others terms. We also analyzed the electrical characteristics to change the annealing conditions after deuterium ion implantation. The results of the analysis, the breakdown time of the gate oxide was prolonged in the optimum condition. And a variety of annealing, we realized the dielectric property that annealing is good at longer time. However, the high temperature is bad because of thermal stress.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.8
• /
• pp.365-370
• /
• 2001

We have proposed and fabricated a new poly-Si TFT employing air-cavities at the edges of gate oxide in order to reduce the vertical electric field induced near the drain due to low dielectric constant of air. Air-cavity has been successfully fabricated by employing the wet etching of gate oxide and APCVD (Atmospheric pressure chemical vapor deposition) oxide deposition. Our experimental results show that the leakage current of the proposed TFT is considerably reduced by the factor of 10 and threshold voltage shift under high gate bias is also reduced because the carrier injection into gate insulator over the drain depletion region is suppressed.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.6 no.1
• /
• pp.99-102
• /
• 2002

Pinholes on the thermally grown oxide, which is called gate oxide, on silicon substrate under polysilicon layer are found and its mechanism is analyzed in this paper. The oxide under a polysilicon layer is broken during the plasma etching process of other polysilicon layer. Both polysilicon layers are separated with 0.8${\mu}{\textrm}{m}$ thick oxide deposited by CVD (Chemical Vapor Deposition). Since broken oxide points are found scattered around an arc occurrence point, it is assumed that an extremely high electric field generated near the arc occurrence point makes the gate oxide broken. 1'he arc occurrence point has been observed on the alignment key and is the mark of low yield. It is found that any arc occurrence can cause chips to fail by breaking the gate oxide, even if are occurrence points are found on scribeline.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.47 no.4
• /
• pp.13-19
• /
• 2010

MOSFET with deuterium-incorporated gate oxide shows enhanced reliability compared to conventional MOSFET. We present an alternative process whereby deuterium is delivered to the location where the gate oxide reside by an implantation process. Deuterium ions were implanted using two different energies to account for the topography of the overlaying layers and placing the D peak at the top of gate oxide. A short anneal at forming gas was performed to remove the D-implantation damage. We have observed that deuterium ion implantation into the gate oxide region can successfully remove the interface states and the bulk defects. But the energy and the dose of the deuterium implant need to be optimized to maintain the Si substrates dopant activation, while generating deuterium bonds inside gate oxide. CV and IV characteristics studies also determined that the deuterium implant dose not degrade the transistor performance.

• Journal of Information Display
• /
• v.11 no.4
• /
• pp.165-168
• /
• 2010

A solution-processed multicomponent oxide, yttrium hafnium zinc oxide (YHZO), was synthesized and deposited as a gate insulator. The YHZO film annealed at $600^{\circ}C$ contained an amorphous phase based on the results of thermogravimetry, differential thermal analysis, and X-ray diffraction. The electrical characteristics of the YHZO film were analyzed by measuring the leakage current. The high dielectric constant (16.4) and high breakdown voltage (71.6 V) of the YHZO films resulted from the characteristics of $HfO_2$ and $Y_2O_3$, respectively. To examine if YHZO can be applied to thin-film transistors (TFTs), indium gallium zinc oxide TFTs with a YHZO gate insulator were also fabricated. The desirable characteristics of the YHZO films when used as a gate insulator show that the limitations of the general binary-oxide-based materials and of the conventional vacuum processes can be overcome.