• Journal of the Mineralogical Society of Korea
• /
• v.28 no.2
• /
• pp.95-108
• /
• 2015

Nano-sized iron colloids are formed as acid mine drainage is exposed to surface environments and is introduced into surrounding water bodies. These iron nanomaterials invoke aesthetic contamination as well as adverse effects on aqueous ecosystems. In order to control them, the characteristics of their behaviour should be understood first, but the cumulative research outputs up to now are much less than the expected. Using zero-valent iron (ZVI) and magnetite, this study aims to investigate the behaviour of iron nanomaterials according to the change in the composition and pH of background electrolyte and the concentration of natural organic matter (NOM). The size and surface zeta potential of iron nanomaterials were measured using dynamic light scattering. Characteristic behaviour, such as aggregation and dispersion was compared each other based on the DLVO (Derjaguin, Landau, Verwey, and Overbeek) theory. Whereas iron nanomaterials showed a strong tendency of aggregation at the pH near point of zero charge (PZC) due to electrostatic attraction between particles, their dispersions became dominant at the pH which was higher or lower than PZC. In addition, the behaviour of iron nanomaterials was likely to be more significantly influenced by cations than anions in the electrolyte solutions. Particularly, it was observed that divalent cation influenced more effectively than monovalent cation in electrostatic attraction and repulsion between particles. It was also confirmed that the NOM enhanced the dispersion nanomaterials with increasing the negative charge of nanomaterials by coating on their surface. Under identical conditions, ZVI aggregated more easily than magnetite, and which would be attributed to the lower stability and larger reactivity of ZVI.

• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.607-613
• /
• 2004

This study was to investigate the surface properties of electrochemically oxidized Ti-6Al-7Nb alloy by anodic spark discharge technique. Anodizing was performed at current density 30 $mA/cm^2$ up to 300 V in electrolyte solutions containing $DL-{\alpha}$-glycerophosphate disodium salt hydrate($DL-{\alpha}$-GP) and calcium acetate (CA). Hydrothermal treatment was done at $300^{\circ}C$ for 2 hrs to produce a thin outermost layer of hydroxyapatite (HA). The bioactivity was evaluated from HA formation on the surfaces in a Hanks' solution with pH 7.4 at $36.5^{\circ}C$ for 30 days. The size of micropores and the thickness of oxide film increased and complicated multilayer by increasing the spark forming voltage. Needle-like HA crystals were observed on anodic oxide film after the hydrothermal treatment at $300^{\circ}C$ for 2 hrs. When increasing $DL-{\alpha}$-GP in electrolyte composition, the precipitated HA crystals showed the shape of thick and shorter rod. However, when increasing CA, the more fine needle shape HA crystals were appeared. The bioactivity in Hanks' solution was accelerated when the oxide films composed with strong anatase peak with presence of rutile peak. The increase of amount of Ca and P was observed in groups having bioactivity in Hanks' solution. The Ca/P ratio of the precipitated HA layer was equivalent to that of HA crystal and it was closer to 1.67 as increasing the immersion time in Hanks' solution.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.30 no.5
• /
• pp.809-815
• /
• 1997

A series of experiments were conducted to study effects of osmolality and $Ca^{2+}$ on sperm motility in marbled sole, Limanda yokohamae. Spermatozoa were immotile when the milt was mixed with solutions (electrolyte or non-electrolyte) of lower osmolality than the average seminal plasma osmolality (351 mOsm/kg), but became motile after mixing milt with an hyperosmotic solution. However, with the osmolality above 1,639 mOsm/kg spermatozoa ceased their movement. When the milt was suspended in the $Ca^{2+}$ free artificial seawater (ASW) containing ethylenglycoltriamine (EGTA), the percentage of motile spermatozoa decreased in proportion to the increase of EGTA. Most spermatozoa were quiescent in a medium containing 3 mM EGTA. The motility of spermatozoa prevented by 3 mM EGTA was recovered by the subsequent addition of $Ca^{2+}$ over the concentration of 0.25 mM. Effects of calmodulin antagonist, trifluoperazin (TFP) on spermatozoa were examined to elucidate the possible functions of calmodulin in sperm motility. TFP immobilized spermatozoa 5n ASW at the concentration of 0.5 M. These findings suggest that calcium is an effective external factor in the initiation process of sperm motility.

• Journal of the Korean Society of Safety
• /
• v.38 no.5
• /
• pp.8-14
• /
• 2023

Lithium ions can induce the thermal runaway phenomenon and lead to reignition due to electrical, mechanical, and environmental factors such as high temperature, smoke generation, explosions, or flames, which is extremely likely to create safety concerns. Therefore, one of the ways to improve the flame retardancy of the electrolyte is to use a flame-retardant additive. Comparing the associated characteristic value of existing substances with the required experimental value, it was found that these values were either considerably different or were not documented. It is vital to know a substance's combustion characteristic values, flash point, explosion limit, and autoignition temperature (AIT) as well as its combustion characteristics before using it. In this research, the flash point and AIT of materials were measured by mixing a highly volatile and flammable substance, diethyl carbonate (DEC), with flame-retardant dimethyl methylphosphonate (DMMP). The flash point of DEC, which is a pure substance, was 29℃, and that for DMMP was 65℃. Further, the lower explosion limit calculated using the measured flash point of DEC was 1.79 Vol.%, while that for DMMP was 0.79 Vol.%. The AIT was 410℃ and 390℃ for DEC and DMMP, respectively. In particular, since the AIT of DMMP has not been discussed in any previous study, it is necessary to ensure safety through experimental values. In this study, the experimental and regression analysis revealed that the average absolute deviation (ADD) for the flash point of the DEC+DMMP DEC+DMMP system is 0.58 sec and that the flash point tends to increase according to changes in the composition employed. It also revealed that the AAD for the AIT of the mixture was 3.17 sec and that the AIT tended to decrease and then increase based on changes in the composition.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.2
• /
• pp.121-128
• /
• 2017

For an investigation on the effect of the shape of electrodes in alkaline water electrolysis, two kinds of stack with circular and square electrode array are used to visualize both for behaviors of hydrogen bubble around the electrodes and for measurements of hydrogen production from these two stacks. The electrolytes for the hydrogen production experiment were applied for 20 wt%, 25 wt%, 30 wt% and 35 wt% of KOH alkaline aqueous solutions. As a result, the adhesion length of bubbles attached around the square electrode in the visualization experiment was found to be 1.7 times longer compared with the attached around the circular electrode. In the hydrogen production experiments, the volume of hydrogen production of the stack by using circular electrode array was approximately 3% more than that of the stack with square electrode array. These observations may be caused by the effect of the bubbles attached to the around the electrodes obstructing mass transfer such as hydrogen exhaust and electrolyte supply.

• Applied Chemistry for Engineering
• /
• v.24 no.2
• /
• pp.121-125
• /
• 2013

In this work, we prepared the carbon paper from chopped carbon fibers using a gas diffusion matrix in polymer electrolyte membrane fuel cells by wet processing. The process of making carbon paper using wet processing is consisted of the three steps involving the dispersion of chopped carbon fibers, the preparation of the carbon fiber web, the impregnating of phenol resin. This work was focused on finding the optimal surfactant to make the carbon paper with 2D orientation of carbon fibers by investigating the dispersion state of carbon fibers in different dispersion solutions. Furthermore, the effect of phenol resin and carbon black contents on properties of electric conductivity was analyzed. As a result, it is confirmed that the carbon fiber was well dispersed when using sodium dodecyl sulfate as a surfactant, and the carbon paper with 8 wt% of phenol and 5 wt% of carbon black contents showed the most excellent electrical property.

• Resources Recycling
• /
• v.11 no.1
• /
• pp.19-25
• /
• 2002

For $ZnSO_4$-$Na_2$$SO_4$-$H_2$ $SO_4$-$NaOH-H_2$O system, pH of solutions with different electrolyte concentrations was measured at $25^{\circ}C$ and ionic equilibria were analyzed by using K-value method. Activity of water and activity coefficients of solutes were calculated by Pitzer equation. The equilibrium concentration and activity coefficients of solutes were calculated from initial experimental conditions. At high ionic strength of 4m, the pH values calculated were in good agreement with those measured. In the experimental ranges of ionic strength of solution from 3.5 to 4.3 m, the mean activity coefcient of $ZnSO_4$calculated agreed well with those obtained from literature.

• Korean Journal of Materials Research
• /
• v.21 no.4
• /
• pp.192-195
• /
• 2011

The electro-deposition of compound semiconductors has been attracting more attention because of its ability to rapidly deposit nanostructured materials and thin films with controlled morphology, dimensions, and crystallinity in a costeffective manner (1). In particular, low band-gap $A_2B_3$-type chalcogenides, such as $Sb_2Te_3$ and $Bi_2Te_3$, have been extensively studied because of their potential applications in thermoelectric power generator and cooler and phase change memory. Thermoelectric $Sb_xTe_y$ films were potentiostatically electrodeposited in aqueous nitric acid electrolyte solutions containing different ratios of $TeO_2$ to $Sb_2O_3$. The stoichiometric $Sb_xTe_y$ films were obtained at an applied voltage of -0.15V vs. SCE using a solution consisting of 2.4 mM $TeO_2$, 0.8 mM $Sb_2O_3$, 33 mM tartaric acid, and 1M $HNO_3$. The stoichiometric $Sb_xTe_y$ films had the rhombohedral structure with a preferred orientation along the [015] direction. The films featured hole concentration and mobility of $5.8{\times}10^{18}/cm^3$ and $54.8\;cm^2/V{\cdot}s$, respectively. More negative applied potential yielded more Sb content in the deposited $Sb_xTe_y$ films. In addition, the hole concentration and mobility decreased with more negative deposition potential and finally showed insulating property, possibly due to more defect formation. The Seebeck coefficient of as-deposited $Sb_2Te_3$ thin film deposited at -0.15V vs. SCE at room temperature was approximately 118 ${\mu}V/K$ at room temperature, which is similar to bulk counterparts.

• Journal of Electrochemical Science and Technology
• /
• v.8 no.3
• /
• pp.206-214
• /
• 2017

SnS films have been prepared by electrodeposition technique onto Cu and ITO substrates using acidic solutions containing tin chloride and sodium thiosulfate with sodium citrate as an additive. The effects of sodium citrate on the electrochemical behavior of electrolyte bath containing tin chloride and sodium thiosulfate were investigated by cyclic voltammetry and chronoamperometry techniques. Deposited films were characterized by XRD, FTIR, SEM, optical, photoelectrochemical, and electrical measurements. XRD data showed that deposited SnS with sodium citrate on both substrates were polycrystalline with orthorhombic structures and preferential orientations along (111) directions. However, SnS films with sodium citrate on Cu substrate exhibited a good crystalline structure if compared with that deposited on ITO substrates. FTIR results confirmed the presence of SnS films at peaks 1384 and $560cm^{-1}$. SEM images revealed that SnS with sodium citrate on Cu substrate are well covered with a smooth and uniform surface morphology than deposited on ITO substrate. The direct band gap of the films is about 1.3 eV. p-type semiconductor conduction of SnS was confirmed by photoelectrochemical and Hall Effect measurements. Electrical properties of SnS films showed a low electrical resistivity of $30{\Omega}cm$, carrier concentration of $2.6{\times}10^{15}cm^{-3}$ and mobility of $80cm^2V^{-1}s^{-1}$.

• Journal of Soil and Groundwater Environment
• /
• v.9 no.1
• /
• pp.54-62
• /
• 2004

In order to enhance the efficiency of removal a series of ElectroKinetic Remediation (EKR) tests on ferrous soil contaminated by lead are carried out using acids, chelates and surfactant as flushing agents. The test results indicate that pH in the electrolyte rapidly reached at steady state as the introduce of flushing solution of the lower pH, the type of flushing solution have no effect the distribution of electrical voltage within the sample but the increasing of solution concentration increases it at x/L=0.9. In the distribution of the residual lead in the sample SDS is the highest. Also, the removal efficiency for acetic acid concentration of 1mM Is the highest but the concentration of acetic acid significantly have no effect.