• Journal of the Society of Disaster Information
• /
• v.19 no.1
• /
• pp.138-145
• /
• 2023

Purpose: In accordance with the increase in the number of buildings repaired and reinforced following deterioration from when a fire occurs in a previously reinforced building, the impact on the structure after the fire is analyzed to establish standards for repair and reinforcement measures. Method: After curing for 28 days, the process was to measure the compressive strength and induce destruction through a compressor, repair and reinforce it with epoxy, and conduct a re-compressive strength test on some specimens after curing for 3 days to understand the degree of strength restoration. The rest of the repaired and reinforced specimens as well as the unrepaired and unreinforced specimens were then put into an oven and heated according to the temporal and temperate conditions listed below, and then the compressive strength was tested to estimate the impact of fire. Result: After reinforcing the yielded specimen with epoxy, the process was to then put it in an oven and heat it at different temperatures over time. It was found that there was a decrease in the strength of the reinforcement more than that of the actual specimen. Conclusion: Based on this, it was found that a building repaired and reinforced with epoxy resin is actually more dangerous than a general unrepaired building when it is damaged by fire, and thus, that it must be prepared for fire vulnerabilities.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.9
• /
• pp.604-609
• /
• 2020

There are various methods of finishing concrete surfaces, and when considering workability, the spray method is effective, but rebound occurs. The allocation of rebound occurrence control should be adjusted according to the materials used. Thus, a basic study was conducted on multiple techniques for reducing the rebound incidence that are suitable for surface finishing materials containing a photocatalyst. A prior study derived the reduction effect and optimal mix ratio for photocatalytic performance. Based on that study, the rebound reduction was verified according to the specifications of the content and the mechanical durability characteristics of the mixed materials. Rebound, compressive strength, flexural rigidity, and table flow tests were done. The flow was fixed at 170±10 mm considering the workability of the mortar spray equipment. For the experimental variables, the rebound number was adjusted to the silica sand variables relative to the cement weight, and silica sands No. 5 and No. 7 were used. The results show the highest compression strength in the final S-1 variable, and the amount of rebound was minimized. These results were sufficiently filled with the bindings of the silica pores, which increased the binding force between the aggregates, resulting in a lower amount of rebound.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.3
• /
• pp.65-73
• /
• 2013

Recently the exterior attaching reinforcement method is being often used by using FRP (Fiber Reinforced Polymer) as a method of strengthening concrete structure. this FRP exterior attaching reinforcement method has several advantages like high intensity, stiffness, good durability and easy installment comparing to its weight. but its structure is airtight covered by reinforcement material whose water permeability is low and water can't be discharged, thus it may provoke a damage to the structure after a long while. the main purposes of this study are to develop GFRP reinforcement material which can discharge the surface water properly and to measure its special functions. for this, we have changed the normal reinforcement material to water permeable structure and measured its water permeance modulus by an indoor test which shows the process of water permeance with the parameter of contained GFRP quantity. also tried to verify the measured value of the water permeance modulus in theory by analyzing the numbers on water permeance process. the test result showed that the biggest quantity of water, 0.5129 g/h $m^2$ was discharged when the fiber contained quantity reached at 75% and the tensile strength was also biggest by 476.6MPa at 75%, so it appeared that COSREM GP panel with 75% fiber contained quantity is the best in ventilation and structure.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.3
• /
• pp.19-26
• /
• 2017

Concrete is a construction material with porous media and corroded steel inside affects negatively to durability and structural safety. This study aims a derivation of quantitative relationship between measured HCP (Half Cell Potential) and corrosion amount considering cover depth and W/C (water to cement) ratio. For the work, cement mortar specimens with 3 different W/C ratios and 4 different cover depths are prepared, HCPs are measured with 3 different corrosion level. HCP measurement significantly increases in the saturated condition and linear relationship is observed between corrosion level and acceleration period. With increasing corrosion level and W/C ratio, and decreasing cover depth, HCP measurement increases. Considering total corrosion level and HCP measurements, relatively low COV(Coefficient of Variation) of 0.67 is evaluated through multi-linear regression analysis, however higher COVs over 0.90 can be obtained considering level of HCP measurement. In the room condition, corrosion level can be evaluated through measured HCP in the given conditions of cover depth, W/C ratio. diameter of steel inside.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.6
• /
• pp.65-72
• /
• 2016

Service life evaluation for RC Structures exposed to chloride attack is very important, however the previous two methods(deterministic and probabilistic method) show a big difference. The paper presents a service life simulation using deterministic and probabilistic method with time-dependent diffusion coefficient. Three different cases are considered for diffusion coefficient, concrete cover depth, and surface chloride content respectively, and then the PDF(probability of durability failure) and the related service life are obtained. Through adopting time-dependent diffusion, the discrepancy between the two methods can be reduced, which yields reasonable service life. When diffusion coefficient increases from $2.5{\times}10^{-12}m^2/sec$ to $7.5{\times}10^{-12}m^2/sec$, the service life decreases to 25.5~35.6% level, and cover depth does from 75 mm to 125 mm, it increases to 267~311% level as well. In the case of surface chloride content from $5.0kg/m^3$ to $15.0kg/m^3$, it changes to 40.9~54.5%. The effect of cover depth is higher than the others by 8~10 times and also implies it is a key parameter to service life extension.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.3
• /
• pp.1-7
• /
• 2018

As part of a research dedicated to the field evaluation of the durability of concrete subjected to freezing-thawing, this study analyzes the relationship between the surface roughness and the relative dynamic elastic modulus through image analysis. Four mix compositions with water-to-binder ratios (W/B) of 40%, 50%, 60% and 70% and without AE agent were considered to provoke early freezing. The basic physical properties of the mixes including the relative dynamic elastic modulus and the compressive strength were first evaluated experimentally according to W/B. Then, tests were performed to measure the surface roughness followed by photographs and SEM image analysis. The measured surface roughness tended to increase with larger number of freezing-thawing cycles regardless of W/B. The relative dynamic elastic modulus appeared to increase gradually with the number of cycles for the relatively denser mixes with W/B of 40% and 50%. Besides, the surface roughness increased only at rupture for the mixes with W/B of 60% and 70%. Moreover, the analysis of the photographs of the surface of the mixes with W/B of 40% and 50% revealed that the degradation progressed gradually from the surface with the freezing-thawing cycles. However, for the mixes with W/B of 60% and 70%, apparent change of the surface remained very insignificant until rupture at which damage like cracking could be observed. Consequently, the analysis of surface photograph or the measurement of the surface roughness presented some limitation in assessing the degree of freezing-thawing-induced degradation in case of relatively porous specimens. On the other hand, the photograph and surface roughness appeared to be sufficient for assessing such degradation for the mixes with W/B of 40% and 50%. Accordingly, the image of the surface and the surface roughness are potentially applicable on site for the assessment of freezing-thawing damages in relatively dense mixes.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.11 no.1
• /
• pp.1604-1615
• /
• 1969

This experiment was carried out as one of the basic studies to improve the acid resistance of concrete and it was conducted to investigate some relations among physical properties such as basorption, ratio of water to cement, compressive strength, density and ratio of mix to weight losses of mortar when exposed to 0.1 N solution of hydrochrolic acid. The results obtained from the limited data secured so far in this experiment are summarized as follows: 1. The specimens used in the experiment were made of 5 cubic centimeters of mortar having such various ratios of mix by weight as 1 : 1, 1 : 3, 1 : 5, 1 : 7, 1 : 10. 2. Physical tests included compressive strengths at 7 days, 28 days, 3 months, and 6 month, and 5 hour boiling absorption test. 3. In acid test, every specimen was immersed into 0.1 N solution of hydrochrolic acid. The specimens exposed to the acid solution were weighed to determine the weight losses of the acid-corroded at one week interval for 7 weeks exposure, and the old acid solutions were also changed to fresh one when weighed the weight losses by acid attack at one week interval. 4. The correlative relations were found among physical properties and they are expressed by certain formulas as follows; i) Relation between ratio of mix and absorption Y = 1.036x + 13.53 where Y: absorption(%) X: ratio of mix ii) Relation between ratio of mix and ratio of water-cement Y = 0.204x + 0.214 where Y: ratio of water-cement. X: ratio of mix iii) Relation between ratio of water-cement and absorption Y = 5.01x + 12.53 where Y: absorption(%). X: ratio of water-cement iv) Relation between density and absorption Y = 50.6 - 0.0176X where Y: absorption(%). X: density($kg/m^3$) v) Relation between density and ratio of water cement Y = 7.2183 - 0.0033X where Y: ratio of water-cement . X: density($kg/m^3$) 5. After completing the acid exposure test the specimens were corroded and , the per cent ranges of weight losses varies from a minimum of 20.4 per cent at a 1 : 1 mix to a maximum of 92.0 per cent at a 1:10 mix 6. The correlative relations of physical properties of mortar to weight losses by acid attak were found and they are also expressed by certain formulas as follows: i) Relation between weight losses and ratio of mix Y = 8.59X + 8.63 where Y: weight losses(%), X: ratio of mix ii) Relation between wieght losses and absorption Y = 0.121x + 12.43 where Y: absorption(%). X: weight losses(%) iii) Relation between weight losses and ratio of w/c Y = 0.0226X + 0.07 where Y: ratio of w/c X: weight losses(%) iv) Relation between weight losses and compressive strength LogY = 3.6097 - 0.05058X + 0.00022$X^2$ where Y: compressive strength ($kg/cm^3$) X: weight losses(%) v) Relation between weight losses and density Y = 2153.1 - 6.62X where Y: density($kg/m^3$) X: weigh losses(%) 7. In order to make better acid resistant mortar, it could be concluded that a 1 : 3 mix or richer mixes, adequate mixing water to minnimize the ratio of water-cement considering the workability, 16 per cent or less absorption by 5 hour boiling water, 1,800 kilogram per cubic meter or denser density by absolute weight base and 200 kilogram per square meter or compressive strength at 20 day, etc are required so as to obtain acid-resistant mortar. In addition to the above, it might be recommonded to select the fine aggregate and to use better equipments such as a mechanical vibrator, a mechanical mixer etc. in concrete manufacturing works.

• Korean Journal of Heritage: History & Science
• /
• v.40
• /
• pp.357-386
• /
• 2007

At present, thirteen Buddhist bells of Unified Silla are known to the world: Six in Korea, five in Japan and two other bells, and three out of them are impossible to make out its original form. Therefore, we divided the form of Unified Silla Buddhist bells based on the ten other bells, and we tried out to prove the manufacturing technology by the comparison of the research material of Uncheon-dong bell and existing research materials of other bells, in other to find their linkage based on the alloy elemental composition. We divided Unified Silla Buddhist bell into two types: Type I has symmetric apsaras and regular patterns on its face and it was made in early Silla period; type II has asymmetric apsaras and irregular pattern arrangement and made in late Silla period. In particular, Uncheon-dong Buddhist bells is very similar to Komyoji[光明寺] temple bell from ninth century in Japan. It is peculiar that the apsaras on Uncheon-dong bell play vertical music instruments that are never seen in Unified Silla Buddhist bell. Most of Unified Silla Buddhist bell are compounded with Cu-Sn or Cu-Sn-Pb system. From eighth and ninth century, bells were cast with even composition of copper, tin and lead, and the bronze alloy ratio was similar to the record in Gogonggi[考工記], Jurye[周禮], a book from ancient China. Particularly, Uncheon-dong bell is in a rare case of Cu-Sn-Pb-As system. As had been rarely used in Unified Silla Buddhist bells, so we presented the relative research materials. As has the same nature as Pb. Because As easily volatilize at high temperature, it is hard to use. But it has its merit of solidity and durability. Pb enhances fluidity and thereby expresses the patterns more distinct; As makes the bell stronger. The result of lead isotope ratio could not exactly reveal a concrete producing center. However, over the analysis of our samples, hereby we suggest Uncheon-dong bell was made of materials from just one ore deposit.