• Applied Science and Convergence Technology
• /
• 제24권4호
• /
• pp.117-124
• /
• 2015

A direct growth method of graphene on insulating substrate without catalyst etching and transfer process was developed using Au/Ni/a-C catalyst system. During the growth process, behavior of the Au/Ni catalyst was investigated using EDX, XPS, SEM, and Raman spectroscopy. The Au/Ni catalyst layer was evaporated during growth process of graphene. The graphene film was composed mono-layer flakes. The transmittance of the graphene film was ~80.6%.

• 상하수도학회지
• /
• 제13권3호
• /
• pp.101-106
• /
• 1999

This research aims to compare immobilized catalysts prepared by various methods and determine suitable $TiO_2$ catalyst for water purification. Sol-gel method by Anderson and powder coation method by Tanaka ate famous in the methods to immobilize catalyst. Therefore, the $TiO_2$ catalyst for this research was prepared by sol-gel method and powder coating method. Its structure was tested by X-ray diffractometer (XRD), Scanning electron microseope (SEM). Durability of a catalyst-support couple in an solution was investigated. too. Experimental results were summarized as following; i) Optimum ratio of Ti : $H_2O$ : $H^+$ to obtain stable sol was 1 : 10 : 0.1 and the XRD patterns of $TiO_2$ film immobilized by sol-gel method which were fired at $700^{\circ}C$ showed that the catalyst had an anatase structure. ii) The particle size of $TiO_2$ prepared by sol-gel method was less than $5{\mu}$, but it was observed that coated side was not unifiom. iii) Sol-gel method was very effective to obtain $TiO_2$ catalyst of thin film, but spreadability and durability of a catalyst-support couple in a solution were than $TiO_2$ film immobilized by powder coating method. iv) The particle size of $TiO_2$ immobilized by powder coating method was a little larger than it prepared by sol-gel method, but spreadability and uniformity of $TiO_2$ film and durability of a catalyst-support couple in a solution were better than it immobilized by sol-gel method.

• 마이크로전자및패키징학회지
• /
• 제6권2호
• /
• pp.45-49
• /
• 1999

이온빔 보조 증착법을 이용하여 제작한 $SnO_2$박막을 기저 물질로한 가연성 센서에 catalyst로 ultra-thin Pd layer를 이온빔 스퍼터링으로 흡착시켰다. 가연성 기체의 센싱 메카니즘에서 Pd 촉매의 역할을 정확하게 조사하기 위해서 진공 및 공기 상에서 annealing 함으로서 Pd 촉매의 초기 산화 상태를 조절하였다. 촉매가 순수한 금속 Pd 클러스터 상태로 존재하는 $SnO_2$센서의 경우에는 PdO 클러스터가 있는 것에 비해 높은 감응성을 보였다. 이것은 PdO 클러스터가 표면 acceptor로 작용을 하는 것으로 생각되며 $SnO_2$로 부터 Pd sub-channel을 통해 전자를 받아 센서의 감도를 낮추고 응답시간을 늦추는 것으로 생각된다.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제51권12호
• /
• pp.567-572
• /
• 2002

In these days, diesel vehicle or power plant emits $NO_X\; and SO_2$ which cause air pollution like acid-rain, ozone layer destroy and optical smoke, therefore there are many kinds of methods considered for removing them such as SCR, catalyst, plasma process, and plasma-catalyst hybrid process. T$TiO_2$ is commonly used as catalyst to remove $NO_X$ gas because it have very excellent chemical characteristic as photo catalyst. In this paper, $NO_X$ sensing characteristic of $TiO_2$ thin film deposited by R.F Magnetron sputtering is investigated. A finger shaped electrode on $Al_2$O$_3$ substrate is designed and $TiO_2$ is deposited on the electrode by the magnetron sputtering deposition system. Chemical composition of the deposited $TiO_2$ thin film is $TiO_{1.9}$ by RBS analysis. When the UV is irradiated on it with flowing air, capacitance of $TiO_2$ thin film increases, however, when NO gas is put into the system with air, it immediately decreases because of photo chemical reaction. and it monotonously decreases with increasing NO concentration.

• 한국의류학회지
• /
• 제27권7호
• /
• pp.843-850
• /
• 2003

Cu/PET film composites were prepared by electroless copper plating method. In order to improve adhesion between electroless plated Cu layer and polyester (PET) film, the effect of pretreatment conditions such as etching method, mixed catalyst composition were investigated. Chemical etching and plasma treatment increased surface roughness in decreasing order of Ar＞HCl＞O$_2$＞NH$_3$. However, adhesion of Cu layer on PET film increased in the following order: $O_2$＜Ar＜HCl＜NH$_3$. It indicated that appropriate surface roughness and introduction of affinitive functional group with Pd were key factors of improving adhesion of Cu layer. PET film was more finely etched by HCI tolution, resulting in an improvement in adhesion between Cu layer and PET film. Plasma treatment with NH$_3$produced nitrogen atoms on PET film, which enhances chemisorption of Pd$^{2+}$ on PET film, resulting in improved adhesion and shielding effectiveness of Cu layer deposited on the Pd catalyzed surface. Surface morphology of Cu plated PET film revealed that Pd/Sn colloidal particles became more evenly distributed in the smaller size by increasing the molar ratio of PdCl$_2$; SnCl$_2$from 1 : 4 to 1 : 16. With increasing the molar ratio of mixed catalyst, adhesion and shielding effectiveness of Cu plated PET film were increased.d.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2006년도 6th International Meeting on Information Display
• /
• pp.146-149
• /
• 2006

We developed new FED cathode film material that has catalysis function for graphite nano fiber. Using the cathode film with catalyst, we can simplify the FED process. It is composed of Cr, Fe-Ni catalyst. Fabricating FED panel with the film, we confirmed good emission performance of the panel.

• 한국재료학회지
• /
• 제17권10호
• /
• pp.548-554
• /
• 2007

[ $BaTiO_3$ ] thick film by an interfacial polymerization method was prepared at the liquid/liquid interface between benzyl alcohol saturated solution with the basic catalyst [diethyl amine ($NHEt_2$) or triethylamine ($NEt_3$)], and the water dissolved with $TiO_2$ and $Ba(CH_3COO)_2$. The film thickness increased gradually with an increase in diethyl amine($NHEt_2$) or triethylamine($NEt_3$) volume and the reaction time. The homogeneity of $BaTiO_3$ thick film after sintered at $600^{\circ}C$ was confirmed by EPMA analysis, which showed that both of Ba and Ti element were homogeneously distributed on the surface as well as in the perpendicular direction of the film. The thickness of $BaTiO_3$ film obtained by this process was $8.75\;{\mu}m$.

• 공업화학
• /
• 제26권4호
• /
• pp.400-405
• /
• 2015

Tetraethylorthosilicate (TEOS)를 전구체로서 이용하여 제조된 기존의 반사방지(AR; anti-reflective) 코팅막은 대부분 수분을 쉽게 흡수할 뿐만 아니라 낮은 내마모성을 갖는다. 본 연구에서는 AR 코팅막의 투과율, 소수성 및 내마모성을 향상할 목적으로 전구체로서 methyltrimethoxysilane (MTMS)를 사용하고 불소 실란, 산 촉매, 염기 촉매 및 산-염기 2단계 촉매를 첨가하여 다양한 AR 코팅막을 제조하였다. 제조된 AR 코팅막은 UV-Vis, 접촉각 측정기, AFM, 연필경도 및 부착성 시험을 통해 특성을 분석하였다. 그 결과, 경화온도가 $300^{\circ}C$일 때 코팅되지 않은 유리 기판의 투과율은 90.5%인 반면, AR 코팅된 유리 기판의 투과율은 94.8%로 증가하였다. 불소 실란을 첨가한 경우, 소수성이 크게 향상되었음을 나타내듯이 AR 코팅막 표면에서의 접촉각은 $96.3^{\circ}$에서 $108^{\circ}$까지 증가하였다. AR 코팅막의 내마모성은 산 촉매에 의해 향상되었으며, 그것의 투과율은 염기 촉매에 의해 증가하였다. 산-염기 2단계 촉매 반응에 의해 제조한 AR 코팅막의 경우, 상승 효과에 의해 촉매의 도입 없이 제조된 AR 코팅막과 비교하여 투과율 및 내마모성이 향상되었다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.1829-1832
• /
• 2008

This paper reports a novel gas sensing method by using a thermoelectric device, thermopile in this case, with an embedded tin oxide catalyst. By using a thin catalyst film, the response time and recovery time were remarkably improved. The fabricated gas sensor was characterized through detecting NOx gas with various concentrations.

• 센서학회지
• /
• 제19권1호
• /
• pp.58-61
• /
• 2010

This paper describes the fabrication and characteristics of NO sensor using ZnO thin film by RF magnetron sputter system. The sensitivity, working temperature, and response time of sputtered pure ZnO thin film and added catalysts such as Pt, Pd, Al, Ti on those films were measured and analyzed. The sensitivity of pure ZnO thin film at working temperature of $300^{\circ}C$ is 0.875 in NO gas concentration of 0.046 ppm. At same volume of the gas in chamber, measuring sensitivity of 1.87 at $250^{\circ}C$ was the case of Pt/ZnO thin film. The ZnO thin films added with catalyst materials were showed higher sensitivity, lower working temperature and faster adsorption characteristics to NO gas than pure ZnO thin film.