• 제목/요약/키워드: amorphous alumina

Search Result 80, Processing Time 0.06 seconds

Preparation of Alumina by the Sol-Gel Process (II) Characteristics of Powders Obtained by Polymeric Alumina Sol (졸겔법에 의한 알루미나의 제조(II) : 중합졸로부터 제조한 분말의 특성)

  • 이해욱;김창은;김구대;정형진
    • Journal of the Korean Ceramic Society
    • /
    • v.28 no.9
    • /
    • pp.705-711
    • /
    • 1991
  • Alumina precursor sol was obtained by the reaction of Al(OC4H9)3 and acetylacetone in the solvent followed by the partial hydrolysis. This sol was measured by viscosity and the effect of pH. The powders obtained from this sol were calcined at the various temperatures. The transition of crystals and crystal state were investigated at the various temperatures. The powders dried at 90$^{\circ}C$ showed amorphous and ${\gamma}$-Al2O3 at 900$^{\circ}C$, ${\alpha}$-Al2O3 mono-phase at 1050$^{\circ}C$ respectively. As a result of Al27-MASNMR analysis, amorphous and ${\alpha}$-Al2O3 powders showed 6-coordinated Al, ${\gamma}$-Al2O3 4-coordinated Al respectively.

  • PDF

Microstructural Analysis of Anodic Oxide Layers Formed in a Boric Acid Solution for Al Electrolytic Capacitor Foils (붕산용액에서 형성된 알루미늄 전해콘덴서용 박의 화성피막 조직분석)

  • Kim, Seong-Gap;Kim, Seong-Su;O, Han-Jun;Jo, Nam-Don;Ji, Chung-Su
    • Korean Journal of Materials Research
    • /
    • v.11 no.4
    • /
    • pp.329-334
    • /
    • 2001
  • Microstructures of barrier-type oxide layers on aluminum was studied by XRD, TEM and RBS. Fer formation of oxide layer. aluminum was anodized in a boric acid solution. The thickness of the oxide film subjected to applied voltage increased linearly at ratio of 1.54nm/V. For oxide layer anodized at 300V, amorphous structure of oxide layer was not transformed after heat treatment at 50$0^{\circ}C$ , while for oxide layers anodized at higher voltages the amorphous structure crystallized into a ${\gamma}$-alumina without any heat treatment. It was also found that the amorphous structure of oxide layer formed at 100V transformed into crystalline structure by electron irradiation. The structure was identified as ${\gamma}$-alumina.

  • PDF

Synthesis of High Purity Alumina by Controlled Precipitation Method from Clay Minerals (I) Preparation of Aluminum Sulfate Hydrate and Alumina from Clay Minerals (점토 광물로부터 제어 침전법에 의한 고순도 알루미나의 합성 (I) 점토 광물로부터 수화 황산 알루미늄 및 알루미나의 제조)

  • No, Tae-Hwan;Lee, Heon-Su;Son, Myeong-Mo;Park, Hui-Chan
    • Korean Journal of Materials Research
    • /
    • v.2 no.1
    • /
    • pp.3-11
    • /
    • 1992
  • Aluminum sulfate hydrate was prepared using sulfuric acid from Ha-dong kaolin. The effects of calcination-temperature and calcination-time of kaolin, reaction-temperature and reaction-time, and sulfuric acid concentration on the formation of aluminum sulfate hydrate were investigated. The precipitation condition of aluminum sulfate hydrate from sulfuric acid solution was determined. Also, the products heat-treated at different temperatures have been investigated by X-ray diffraction, thermogravimetry, differential thermal analysis, Fourier transform infrared spectrophotometer, scanning electron microscopy, particle size distribution analysis and chemical analysis. In the optimum condition, the conversion of aluminum oxide in kaolin to aluminum sulfate hydrate was 60%. From the results of XRD, TG-DTA, and FT-IR, it is suggested that the aluminum sulfate hydrate is thermally decomposed as follows ; $Al_2(SO_4)_3{\cdot}18H_2O{\rightarrow}Al_2(SO_4)_3{\cdot}6H_2O{\rightarrow}Al_2(SO_4){\rightarrow}\;amorphous\;alumina{\rightarrow}{\gamma}-alumina{\rightarrow}{\delta}-alumina{\rightarrow}{\theta}-alumina{\rightarrow}{\alpha}-alumina$. The purity of alumina powder prepared by calcining aluminum sulfate hydrate at $1200^{\circ}C$ was 99.99 percent.

  • PDF

Preparation of Alumina Coated Zirconia Powder by Hydrolysis of Aluminum Butoxide (가수분해법에 의한 알루미나 코팅 지르코니아 분말의 제조)

  • Lee, Jong-Kook;Kim, Yoon-Soo;Kim, Hwan
    • Journal of the Korean Ceramic Society
    • /
    • v.32 no.12
    • /
    • pp.1401-1407
    • /
    • 1995
  • Zirconia powder coated with alumina was prepared by hydrolysis of alumina butoxide. The coated powder was obtained by a hydrolysis reaction between the adsorbed water on the surface of zirconia particles and aluminum sec-butoxide. Amorphous aluminum hydroxide was uniformly coated on the surface of zirconia particles with the thickness of about 30 nm. The shape and distribution of aluminum hydroxide was varied with an existence of surfactant. The coated layer of aluminum hydroxide consists of the fine particle size, and the zirconia powder coated by alumina hydroxide have the large specific surface area of 120 $m^2$/g, compared with that of starting zirconia powder.

  • PDF

Preparation of High-capacity Ceramic Catalytic Support from Gibbsite (깁사이트를 이용한 고기능 세라믹 촉매담체의 제조)

  • Park, Byung-Ki;Suh, Jeong-Kwon;Lee, Jung-Min;Suhr, Dong-Soo
    • Journal of the Korean Ceramic Society
    • /
    • v.39 no.3
    • /
    • pp.245-251
    • /
    • 2002
  • We prepared γ-alumina beads using the amorphous alumina, obtained by fast calcination of gibbsite, and its were immersed in aqueous solution of the mixture of 21.87% nitric acid and 28.57% acetic acid. The beads thus were hydrothermaly treated at 200$^{\circ}$C for 3h, and were investigated changes of crystal, pore characteristics, $N_2$ adsorption and desorption isotherms, mechanical strengths and thermal resistance. Acicular platelet crystals of 0.1∼0.3${\mu}$m were transformed into acicular boehmite crystals of 1∼2${\mu}$m having the same crystal structure. Through this changes, we found that reversible phase transformation due to hydrothermal reaction took placed between boehmite and ${\gamma}$-alumina. In comparison to the ${\gamma}$-alumina bead before hydrothermal treatment, $N_2$ adsorption capacity was increased from 450㎖/g to 670㎖/g, and pore volume between 100${\AA}$ and 1000${\AA}$ was increased form 0.15㎖/g to 0.77㎖g, and mechanical strength was increased form 1.4MPa to 2.2MPa. Also, it showed the remarkable thermal resistance which sustained ${\theta}$-alumina crystal structure and pores between 100${\AA}$ and 1000${\AA}$ at 1000$^{\circ}$C in 40vol% steam.

Nano Particle Coatings on α-alumina Powders by a Carbonate Precipitation (Carbonate 침전법을 이용한 α-알루미나의 나노파티클 코팅)

  • Lim, Jong-Min;Kim, Sang-Woo
    • Journal of Powder Materials
    • /
    • v.14 no.2 s.61
    • /
    • pp.145-149
    • /
    • 2007
  • Nanocrystalline transient aluminas (${\gamma}$-alumina) were coated on core particles (${\gamma}$-alumina) by a carbonate precipitation and thermal-assisted combustion, which is environmentally friend. The ammonium aluminum carbonate hydroxide (AACH) as a precursor for coating of transient aluminas was produced from precipitation reaction of ammonium aluminum sulfate and ammonium hydrogen carbonate. The crystalline size and morphology of the synthetic, AACH, were greatly dependent on pH and temperature. AACH with a size of 5 nm was coated on the core alumina particle at pH 9. whereas rod shape and large agglomerates were coated at pH 8 and 11, respectively. The AACH was tightly bonded coated on the core particle due to formation of surface complexes by the adsorption of carbonates, hydroxyl and ammonia groups on the surface of the core alumina powder. The synthetic precursor successfully converted to amorphous- and ${\gamma}$-alumina phase at low temperature through decomposition of surface complexes and thermal-assisted phase transformation.

Composition Dependence and Optical Properties of Polymethyl Methacrylate/Alumina Nanocomposite in the IR Region Determined by Kramers-Kronig Relation

  • Ghamari, Misagh;Ghasemifard, Mahdi
    • Journal of the Korean Ceramic Society
    • /
    • v.54 no.2
    • /
    • pp.102-107
    • /
    • 2017
  • The dependence of the IR optical properties of PMMA/$Al_2O_3$ nanocomposite on the alumina content was investigated in the wavelength range of $3500-2800cm^{-1}$. The samples were prepared via emulsion polymerization technique using oleic acid as a coupling agent. Grafting density calculations were carried out by means of elemental analysis CHN to yield the best coupling agent content. FTIR analysis confirmed the existence of a chemical bond between aluminum oxide and oleic acid. The outcomes of XRD analyses showed the presence of cubic gamma aluminum oxide in the nanocomposite, in contrast to the amorphous nature of PMMA. TEM images showed the core-shell morphology of the particles other than pristine PMMA. Optical constants of the nanocomposite were calculated based on FTIR spectra and the Kramers-Kronig equations. The presence of nano alumina modified some of the optical indexes in IR region.

Preparation of Fe2O3 Supported γ-alumina Catalyst by Hydrothermal Method (수열법에 의한 Fe2O3 담지 감마알루미나 촉매제조)

  • 박병기;이정민;서동수
    • Journal of the Korean Ceramic Society
    • /
    • v.40 no.7
    • /
    • pp.683-689
    • /
    • 2003
  • The cylindrical ${\gamma}$-alumina pellets were prepared using amorphous alumina and pore generating agent. Its were immersed in aqueous solution of the mixture of Fe(NO$_3$)$_3$.9$H_2O$ and $CH_3$COOH, Fe(NO$_3$)$_3$.9$H_2O$ and $CH_3$COOH and HNO$_3$, and Fe(NO$_3$)$_3$.9$H_2O$ and HNO$_3$. The pellets thus were hydrothermally treated at 20$0^{\circ}C$ for 3 h in autoclave, and were investigated morphologies and changes of crystal pore characteristics, $N_2$ adsorption and desorption isotherms, active sites and mechanical strength etc. According to the preparation method, acicular platelet pseudo-boehmite crystals of 0.1~0.3 ${\mu}{\textrm}{m}$ size were transformed into acicular pseudo-boehmite cristals of 0.5~2 ${\mu}{\textrm}{m}$ size having the same crystal structure. When ${\gamma}$-alumina pellets were immersed in aqueous solution of the mixture of Fe(NO$_3$)$_3$.9$H_2O$ and $CH_3$COOH and then were hydrothermally treated, pore volume between 100 $\AA$ and 1000 $\AA$ was increased from 0.34 ㏄/g to 0.86 ㏄/g, and the gap of $N_2$ adsorption and desorption hysteresis loop was decreased due to increasement of pore size. New active site that could adsorb the C-H functional group was created on the catalist. Also, mechanical strength of catalyst was increased from 1.06 ㎫ to 1.36 ㎫.