• Corrosion Science and Technology
• /
• v.13 no.4
• /
• pp.152-156
• /
• 2014

This study was undertaken to examine the electrochemical corrosion properties of an $Co_{80}Nb_{10}B_{10}$ and $Co_{82}Nb_8B_{10}$ amorphous alloys prepared by melt-spinning method under various conditions. The potentiodynamic polarization responses at various levels of pH (pH 2, pH 7, pH 12) showed that the corrosion current rate of $Co_{80}Nb_{10}B_{10}$ alloy is lower than that of $Co_{82}Nb_8B_{10}$ alloy in all levels of pH, implying the general corrosion resistance of the alloy with higher Nb content is better than that with higher Co content. The pitting potential of $Co_{80}Nb_{10}B_{10}$ alloy was also better than that of $Co_{82}Nb_8B_{10}$, evidenced by the higher pitting potential. Nb is thought to be effective in increasing the protectiveness of the passive film and hence to improve the corrosion resistance of Co-Nb-B alloys.

• Journal of Powder Materials
• /
• v.12 no.6 s.53
• /
• pp.433-440
• /
• 2005

The hydrogen sorption speed of $Zr_{57}V_{36}Fe_7$ nanocrystalline and amorphous alloys was evaluated at room temperature. Nanocrystalline alloys of $Zr_{57}V_{36}Fe_7$ were prepared by planetary ball milling. The hydrogen sorption speed of nanocrystalline alloys was higher than that of the amorphous alloy. The enhanced sorption speed of nanocrystalline alloys was explained in terms of surface oxygen stability which has been known to retard the activation of amorphous alloys. The retardation can be reduced by formation of nanocrystals, which results in the observed increase in sorption properties.

• Journal of the Korean Society for Heat Treatment
• /
• v.15 no.2
• /
• pp.76-81
• /
• 2002

The melt-spun amorphous $Fe_{77-X}P_{13}C_4B_4Al_2Mo_X$(x=4~10) and $Fe_{82-X}P_XC_4B_4Al_2Mo_8$(x=9~15) alloys were found to exhibit a large supercooled liquid region(${\Delta}T_x$) exceeding 40 K before crystallization. The largest ${\Delta}T_x$ for the glassy alloys containing Mo reaches as large as 65 K for the $Fe_{69}P_{13}C_4B_4Al_2Mo_8$ alloy. The corrosion behavior of the amorphous $Fe_{77-X}P_{13}C_4B_4Al_2Mo_X$(x=4~15) and $Fe_(82-X)P_XC_4B_4Al_2Mo_8$ (x=9~17) alloys were examined by electrochemical measurements in 9M $H_2SO_4$ solution at 303 K. The addition of Mo(or P) for replacing some portion of Fe is effective in improving the corrosion resistance of the investigated Fe-based glassy alloys. They are spontaneously passivated and have a wide passive region with low passive current density.

• Journal of the Korean Magnetics Society
• /
• v.17 no.3
• /
• pp.128-132
• /
• 2007

The thermal and magnetic properties of amorphous (FeCo)SiBNb ribbon alloys with high glass forming ability have been investigated. The glass forming ability was enhanced by Co substitution in amorphous ($Fe_{1-X}Co_X)_{72}Si_4B_{20}Nb_4$ alloys with the thickness of about $40{\mu}m$. With the increase in Co content, the temperature range of supercooled liquid phase increased indicating the high glass forming ability of the Co-added alloys. Further the ac permeability increased, and the core loss decreased considerably by Co substitution, while small change in $B_8$ (magnetic flux density at 800 A/m) was observed. The frequency characteristics of permeability deteriorated as compared to conventional amorphous ribbon alloys with the thickness of about $20\;{\mu}m$ due to the increased skin effect.

• Applied Microscopy
• /
• v.21 no.2
• /
• pp.57-66
• /
• 1991

The main purpose of this paper was to investigate the change of rapidly solidified microstructures and dispersoid behavior according to heat-treatment in the Al-Fe-V-Si-(Mn) alloys. It was found that (111) preferred orientation identified by X-ray diffraction and fine subgrain/large grain were observed in the rapidly solidified Al-Fe-V-Si-(Mn) alloys. Cell boundary of the zone A was composed of the microcrystalline, whereas that of the zone B was amorphous. Decomposition of the Al-Fe-V-Si-(Mn) alloys occurred at about $300^{\circ}C$. These alloys exhibited excellent thermal stability at the elevated temperature. Microstructure of the zone B was more stable than that of the zone A. The spherical dispersoid and 5-fold symmetry phase was also more thermally stable than the amorphous structure of cell boundary.

• Journal of Korea Foundry Society
• /
• v.22 no.5
• /
• pp.252-256
• /
• 2002

Ni-Nb-Ti-Zr amorphous alloys were manufactured using melt-spinning methods. Amorphous formability, the supercooled liquid region before crystallization and mechanical properties were examined. The value of the reduced glass transition temperature and the supercooled liquid region of $Ni_{62}Nb_{10}Ti_{13}Zr_{15}$ alloy were relatively high and were 0.612 and 76 K respectively. However, amorphous bulk alloy rod was not formed using the Cu-mold die casting. The mechanical properties were in the range of $800{\sim}900DPN$ of hardness and $2.5{\sim}2.8$ GPa of tensile strength in the whole composition range.

• Transactions of Materials Processing
• /
• v.14 no.9 s.81
• /
• pp.751-755
• /
• 2005

This paper is concerned with spring back after sheet forming of bulk amorphous alloys in the super cooled liquid state. The temperature-dependence and strain-rate dependence of Newtonian/non-Newtonian viscosities as well as the stress overshoot/undershoot behavior of amorphous alloys are reflected in the thermo-mechanical Finite Element simulations. Hemispherical deep drawing operations are simulated for various forming conditions such as punch velocity, die comer radius, friction, blank holder force, clearance and initial funning temperature. Here, spring back by an instantaneous elastic unloading was followed by thermal deformation during cooling, and two modes of spring back are examined in detail. It could be concluded that the superior sheet formability of an amorphous alloy can be obtained by taking the proper forming conditions for loading/unloading.

• Korean Journal of Metals and Materials
• /
• v.48 no.8
• /
• pp.699-704
• /
• 2010

We investigated the cryogenic temperature plasticity of a bulk amorphous alloy. Experiments showed that as temperature decreases, the plasticity of the alloy increases, such that the alloy exhibited ~20% of plastic strain when tested at $-196^{\circ}C$. This enhancement in the plasticity at cryogenic temperatures was associated with the formation of abundant shear bands distributed uniformly over the entire surface of the sample. Nonetheless, the serrations, the characteristic feature of the plastic deformation of amorphous alloys, were unclear at $-196^{\circ}C$. In this study, both the enhanced plasticity and the unclear serrations exhibited by the amorphous alloy at cryogenic temperatures were clarified by exploring shear banding behaviors in the context of the velocity and the viscosity of a propagating shear band.

• Korean Journal of Metals and Materials
• /
• v.46 no.2
• /
• pp.53-57
• /
• 2008

This study examined the role of excess free volume on the corrosion resistance of an amorphous alloy. Corrosion behaviors were monitored on the amorphous alloys, of which amount of free volume was controlled via the isothermal annealing below the glass transition temperature, using immersion tests and potentiodynamic polarization tests in HCl aqueous solutions. It was found that the corrosion resistance of the amorphous alloy is improved by reducing the amount of excess free volume. The possible reason explaining the experimental result was discussed from the viewpoint of the internal energy associated with the annihilation of excess free volume.

• 한국전기화학회:학술대회논문집
• /
• 2005.07a
• /
• pp.335-340
• /
• 2005

Amorphous $MgNi_{1-x}Ti_x$ alloys with the composition of x=0.02, 0.03, 0.05 and 0.07 were synthesized by mechanical alloying. The synthesized alloys were investigated by electrochemical test, XRD and SEM. As increasing Ti concentration, the initial discharge capacity was raised more than that of nanocrystalline Mg-Ni 289 mAh/g, but the electrodes were degraded faster. Comparing to other synthesized alloys, $MgNi_{0.95}Ti_{0.05}$ alloy showed the highest initial discharged capacity 474 mAh/g and maintained $54\%$ of the initial capacity after 10 cycles.