• Title/Summary/Keyword: all ceramic

Search Result 1,146, Processing Time 0.023 seconds

Effects of Particle Size on Properties of PZT -Based Thick Films (입자 크기가 PZT계 압전 후막의 물성에 미치는 영향)

  • 김동명;김정석;천채일
    • Journal of the Korean Ceramic Society
    • /
    • v.41 no.5
    • /
    • pp.375-380
    • /
    • 2004
  • Pb(Ni$\_$1/3/Nb$\_$2/3/)O$_3$-PbZrO$_3$-PbTiO$_3$ thick films were screen-printed on platinized alumina substrates and fired at 800-1000$^{\circ}C$. Two kinds of powders with different particle size were prepared by attrition and ball milling methods. Effects of particle size of starting material on the microstructure and electrical properties of the thick films were investigated. Average particle size of attrition milled-powder (0.44 ${\mu}$m) was much smaller than that of ball milled-powder (2.87 ${\mu}$m). Average grain size of the thick film prepared from attrition-milled powder was smaller than that of the thick film prepared from ball-milled powder at the sintering temperature of 800$^{\circ}C$. However, the difference in average particle size became smaller with increasing the sintering temperature. Thick films prepared from attrition-milled powders showed more uniform and denser microstructures at all firing temperatures. Thick films prepared from attrition-milled powders had better electrical properties at the firing temperature above 900$^{\circ}C$ than thick films prepared from ball-milled powders. Dielectric constant, remanent polarization and coercive field of the thick film prepared from attrition-milled powders and fired at 900$^{\circ}C$ were 559, 16.3 ${\mu}$C/cm$^2$, and 51.3 kV/cm, respectively.

Effect of High Concentration Carbon Dioxide and Pre-Cooling Treated with Solid Carbon Dioxide on the Storability of Radish Sprout in MA Storage (고체 이산화탄소를 이용한 고농도 이산화탄소와 예냉 처리가 싹채소의 저장성에 미치는 영향)

  • Kang, Ho-Min;Choi, In-Lee;Kim, Il-Seop;Park, Keun-Woo
    • Journal of Bio-Environment Control
    • /
    • v.18 no.3
    • /
    • pp.285-290
    • /
    • 2009
  • The solid carbon dioxide used for prolongation shelf life of radish sprout that was just 7days. The developed equipment for treated carbon dioxide consisted of solid carbon dioxide evaporated part and high carbon dioxide and low temperature treated part that can hold products. The inner temperature of equipment decreased temperature to below $5^{\circ}C$ from room temperature for 10minutes and carbon dioxide concentration increased to 80%. The radish sprouts treated 4 different conditions that was nontreated condition (control), solid carbon dioxide put into package (CO2-1), solid carbon dioxide treated before storage using the developed equipment (CO2-2), solid carbon dioxide treated before storage and during storage, and sprout packaged with solid carbon dioxide (CO2-3). These radish sprout packaged with $25{\mu}m$ ceramic film stored at $8^{\circ}C$. The high carbon dioxide treatment did not affect the fresh weight loss. The carbon dioxide and oxygen content in package changed 40% and 10%, respectively in CO2-1 and CO2-2 at 1day after treatments. But carbon dioxide content of all treatments was decreased to 5% and stabilized. The high carbon dioxide showed the effect of reduction ethylene production, but did not affect to visual quality and offodor.

The Properties of Permeability and Freeze-Thaw Resistance of Water-Permeable Paving Brick Using Wastes (폐기물을 이용한 투수블록의 투수성 및 동결융해저항 특성)

  • 신대용;한상목;김경남;이현종
    • Journal of the Korean Ceramic Society
    • /
    • v.41 no.3
    • /
    • pp.210-215
    • /
    • 2004
  • Porous ceramics for water-permeable paving brick was prepared by the sintering of mixed materials comprising of sewage sludge ash, waste porcelain fragment, waste glaze and low-grade clay at 1,000$^{\circ}C$ for 2 h, and the physical $.$mechanical properties, the permeability and the freeze-thaw resistance of specimens with preparation parameters were investigated. The physical mechanical properties were increased in specimens while porosity and permeability were decreased with increasing sewage sludge ash content and sintering temperature on the properties of specimens showed the opposite results. The bulk density, porosity, compressive strength and permeability (passed charge) of 30A60F specimens with 30 wt% of sewage sludge ash content, waste porcelain fragment size with 1∼2 mm and sintered at 1,000$^{\circ}C$ for 2 h were 2.17, 46.2%, 221 kgf/$\textrm{cm}^2$ and 3,150 coulombs, respectively. The permeability was increased with increasing waste porcelain fragment size, however compressive strength was decreased. The freeze-thaw resistance of 30A60F specimen with 1∼2 mm of fragment size was superior to that of the other specimens. The 30A60F specimens can be used for the water-permeable paving brick with the high permeability and adequate strength. The heavy metals included in the all specimens showed lower than the standard level.

Physical Properties of Sintered Body for Coal Fly Ash-clay Slip of Varying Dispersion State (석탄회-점토계 슬립의 분산상태에 따른 소결체의 물리적 특성)

  • 강승구;이기강;김유택;김정환
    • Journal of the Korean Ceramic Society
    • /
    • v.40 no.7
    • /
    • pp.677-682
    • /
    • 2003
  • The physical properties of sintered body made from 3 kinds of slip, F (Flocculated), M (Moderate), and D (Dispersed) for coal fly ash 70-clay 30 (wt%) were studied in terms of slip states and pore size distribution of sintered bodies. The floc particle size distribution for slip F was wider than slip D and the slip F contained flocs larger than 11 $\mu\textrm{m}$. The pore size distribution of the green body of all slips ranged over 1∼4 $\mu\textrm{m}$. The pores smaller than 1 $\mu\textrm{m}$ almost disappeared during the sintering process, while the larger pore of 2.5∼3 $\mu\textrm{m}$ growed by 1 $\mu\textrm{m}$. The pore distribution for the green body of slip F became a narrow in width and high in height after sintering and the large pore limit in a slip F sintered body was 5.1 $\mu\textrm{m}$ which is smaller than that of other slip. The slip F rather flocculated was favorable over slip D well dispersed, in offering a higher compressive strength. From these results, the mechanical strength of sintered body is dependent on the pore distribution which could be controlled by dispersion state of the slips.

Magnetic Properties of Co-substituted Ba-ferrite Powder by Sol-gel Method (졸-겔법에 의한 Cobalt 치환된 Ba-ferrite 분말의 자기적 특성)

  • Choi, Hyun-Seung;Park, Hyo-Yul;Yoon, Seog-Young;Shin, Hak-Gi;Kim, Tae-Ok
    • Journal of the Korean Ceramic Society
    • /
    • v.39 no.8
    • /
    • pp.789-794
    • /
    • 2002
  • In this study, nano-sized Si-C-N precursor powders were synthesized by Chemical Vapor Condensation Method(CVC) using TMS(Tetramethylsilane: $Si(CH_3)_4$), $NH_3$ and $H_2$ gases under the various reaction conditions of the reaction temperature, TMS/$NH_3$ ratio and TMS/$H_2$ ratio. XRD and FESEM were used to analysis the crystalline phase and the average particle size of the synthesized powders. It was found that the obtained powders under the considering conditions were all spherical amorphous powder with the particle size of 87∼130 nm. The particle size was decreased as the reaction temperature increased and TMS/$NH_3$ and TMS/$H_2$ ratio decreased. As the results of EA analysis, it was found that the synthesized powders had been formed the powders composed of Si, N, C and H. Through FT-IR results, it was found that the synthesized powders were Si-C-N precursor powders with Si-C, Si-N and C-N bonds.

Synthesis and Characterization of Si-C-N Precursor by Using Chemical Vapor Condensation Method (화학기상응축법을 이용한 Si-C-N Precursor 분말의 합성 및 특성평가)

  • Kim, Hyoung-In;Kim, Dae-Jung;Hong, Jin-Seok;So, Myoung-Gi
    • Journal of the Korean Ceramic Society
    • /
    • v.39 no.8
    • /
    • pp.783-788
    • /
    • 2002
  • In this study, nano-sized Si-C-N precursor powders were synthesized by Chemical Vapor Condensation Method(CVC) using TMS(Tetramethylsilane: Si($CH_3)_4$), $NH_3$ and $H_2$ gases under the various reaction conditions of the reaction temperature, TMS/$NH_3$ ratio and TMS/$H_2$ ratio. XRD and FESEM were used to analysis the crystalline phase and the average particle size of the synthesized powders. It was found that the obtained powders under the considering conditions were all spherical amorphous powder with the particle size of 87∼130 nm. The particle size was decreased as the reaction temperature increased and TMS/$NH_3$ and TMS/$H_2$ ratio decreased. As the results of EA analysis, it was found that the synthesized powders had been formed the powders composed of Si, N, C and H. Through FT-IR results, it was found that the synthesized powders were Si-C-N precursor powders with Si-C, Si-N and C-N bonds.

Formation and Color of the Spinel Solid Solution in CoO-ZnO-$Fe_2O_3$-$TiO_2$-$SnO_2$ System (CoO-ZnO-$Fe_2O_3$-$TiO_2$-$SnO_2$계 Spinel 고용체의 생성과 발색에 관한 연구)

  • 이응상;이진성
    • Journal of the Korean Ceramic Society
    • /
    • v.28 no.11
    • /
    • pp.897-907
    • /
    • 1991
  • This study was conducted to research the formation and the color development of CoO-ZnO-Fe2O3-TiO2-SnO2 system for the purpose of synthesizing the spinel pigments which are stable at high temperature. After preparing CoO-ZnO-Fe2O3, in which CoO causes the color, as a basic composition, $\chi$CoO.(1-$\chi$)ZnO.Fe2O3 system, $\chi$CoO.(1-$\chi$)ZnO.TiO2 system and $\chi$CoO.(1-$\chi$)ZnO.SnO2 system were prepared with $\chi$=0, 0.2, 0.5, 0.7, 1.0 mole ratio respectively. The manufacturing was carried out at 128$0^{\circ}C$ for 90 minutes. These specimens were analyzed by the reflectance measurement and the X-ray diffraction analysis and the results were summarized as follows: 1. All of the specimens formed the spinel structure and were colored with stable yellow or blue. 2. As the content of CoO and Fe2O3 in the specimens being increased, the reflectance of each specimen was measured becoming lower and the colors were changed from yellow to greyish blue and from blue to dark blue. 3. As the substituting amount of Co2+ ion for Zn2+ ion in $\chi$CoO-ZnO-TiO2-SnO2 system being increased, the colors were changed from blue to greyish blue. The colors were changed from yellow to grayish green owing to the tetrahedral Co2+ ions being increased, the octahedral Co2+ ions being decreased with increasing the amount of Sn4+ ions. 4. CoO-ZnO-Fe2O3-TiO2-SnO2 system, in which Zn2+ was substituted with Co2+ and Fe3+ was substituted with Ti4+ and Sn4+, easily formed the spinel structure without regard to the amount of substitution or the ion owing to the selectivity of the coordination number: 4 of Zn2+, 4 of Co2+, 6 of Fe3+ or 6 of Ti4+ and Sn4+.

  • PDF

The Electrical Properties of Bi2O3 Doped BaTi4O9 Ceramic Thick Film Monopole Antenna (Bi2O3가 첨가된 BaTi4O9 세라믹 후막 모노폴 안테나의 전기적 특성)

  • Jung Chun-Suk;Ahn Sang-Chul;Ahn Sung-Hun;Heo Dae-Young;Park Eun-Chul;Lee Jae-Shin
    • The Journal of Korean Institute of Electromagnetic Engineering and Science
    • /
    • v.15 no.9
    • /
    • pp.826-834
    • /
    • 2004
  • In this paper, we fabricated thick film monopole antennas using Bi$_2$O$_3$-doped BaTi$_4$$O_{9}$ ceramics for small size and broadband intenna. In the result, the high permittivity was fixed and the quality factor was also significantly decreased by the formation of secondary phase of Bi$_4$Ti$_3$O$_{12}$ repleced by addtion Bi. The antenna property influenced by the quality value more than the permittivity. The bandwidth of antenna was increased to 33 %. On the other hand, the gain was reduced to -4.3 dBi. Also radiation patterns were showed low dBi value by increasing of dielectric loss. Specially, Measured x-y plane radiation patterns was distorted as the dispersion of wavelength and high permittivity difference. But the result is showed execellent bandwidth because of low quality value in all formation range.nge.

${SO_4}^{2-}$ ion Removal from Solution by Crystal Precipitation on Surface Active Glasses (표면활성유리에의 결정석출을 이용한 용액중 황산염 이온 제거)

  • 남명식;김철영
    • Journal of the Korean Ceramic Society
    • /
    • v.35 no.12
    • /
    • pp.1286-1293
    • /
    • 1998
  • ${SO_4}^{2-}$ ions present in industrial waste water if combined with other metal ions in the water can cause serious scale problem in a transporting pipe. In this study therefore ${SO_4}^{2-}$ ions in an acidic solution have been removed by using surface active glasses. Glasses with various compositions of $SiO_2-Na_2O-B_2O_3-RO$ (R=Mg, Ca, Sr, Ba) system were reacted in a ${SO_4}^{2-}$ ion-containing solution with various pHs ranging from 1 to 4 for various time the reacted glass surfaces were analyzed by XRD and SEM and all ions in the reacted solution were also measured ${SO_4}^{2-}$ ions in the solution were combined with divalent ions leached out of glass and precipitated on the glass surface as sulfate crystals. In this was the surface ion could be removed from the acidic solution. The sulfate ion removal capacity is closely related to the solubility product con-stants of the newly formed sulfate crystals. Almost no sulfate crystal was formed on the MgO-containing glass while sulfate crystals were easily formed on the glass containing either SrO or BaO This indicates that those glasses have strong removal efficiency of ${SO_4}^{2-}$ ions from the solution.

  • PDF

Stabilization of Heavy Metals in Glasses Containing EAF Dust (전기로 분진이 첨가된 유리의 중금속 안정화 특성)

  • Eun, Hee-Tai;Kang, Seung-Gu;Kim, Yoo-Taek;Lee, Gi-Kang;Kim, Jung-Hwan
    • Journal of the Korean Ceramic Society
    • /
    • v.41 no.11
    • /
    • pp.851-857
    • /
    • 2004
  • The stabilizing characteristics of heavy metals in the silicate glass (SD), borosilicate glass (BD), and leadsilicate glass (PD) containing Electric Arc furnace (EAF) dust were studied by the Toxic Characterization Leaching Procedure (TCLP) test. Also, the dependence of the amount of EAF dust upon structural changes of SD, BD, and PD glasses and the TCLP results were investigated by the XRD and FT-IR spectroscopy. In the XRD results, all of SD, BD, and PD specimens containing dust up to 30 wt% were amorphous without crystallizing. In the TCLP test, the concentration of heavy metals leached from the glasses increased with the amount of EAF dust added. The SD specimen series showed the lowest heavy metal leaching and the heavy metal leachate of the PD specimens were lower than those of the BD specimens. But, the Pb leaching from the PD specimens was the highest in the PD glass composition due to the high Pb content. The value of oxygen/network former ratio could be used to compare the chemical durability within the same glass series, but not proper to do between the different glass series. Adding the EAF dust to the SD mother glass, decreased the Si-O-Si symmetry and increased the non-bridging oxygen, which weakened the structure and decreased the chemical durability of glasses. In the BD series glasses, the addition of EAF dust caused the structural changes from tetra-borate group to di-borate group and the formation of the 2-dimensional layer structure of pyre- and ortho- borate, which decreased the chemical durability of glasses. It is concluded that SD series glass among the 3 kinds of glasses is the most effective to stabilize the heavy metals of EAF dust.