• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2004.11a
• /
• pp.433-434
• /
• 2004

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.76-76
• /
• 2000

• Corrosion Science and Technology
• /
• v.12 no.2
• /
• pp.102-112
• /
• 2013

A very high-temperature gas reactor (VHTR) is one of the next generation nuclear reactors owing to its safety, high energy efficiency, and proliferation-resistance. Heat is transferred from the primary helium loop to the secondary helium loop through an intermediate heat exchanger (IHX). Under VHTR environment Alloy 617 is being considered a candidate Ni-based superalloy for the IHX of a VHTR, owing to its good creep resistance, phase stability and corrosion resistance at high temperature. In this study, high-temperature corrosion tests were carried out at 850 - $950^{\circ}C$ in air and impure helium environments. Alloy 617 specimens showed a parabolic oxidation behavior for all temperatures and environments. The activation energy for oxidation was 154 kJ/mol in helium environment, and 261 kJ/mol in an air environment. The scanning electron microscope (SEM) and energy-dispersive x-ray spectroscopy (EDS) results revealed that there were a Cr-rich surface oxide layer, Al-rich internal oxides and depletion of grain boundary carbide after corrosion test. The thickness and depths of degraded layers also showed a parabolic relationship with the time. A corrosion rate of $950^{\circ}C$ in impure helium was higher than that in an air environment, caused by difference in the outer oxide morphology.

• Journal of the Korean Ceramic Society
• /
• v.19 no.3
• /
• pp.179-186
• /
• 1982

This research is to aim at the study of sintering mechanism through the observation of microstructure by scanning electron microscopy, after the mixture of 30wt% $Al_2O_3$ (White Alundum) powder is fired in air at the temperature range of 1350~150$0^{\circ}C$ in order to sinter $Al_2O_3$-Al through the oxidation of Al powder. The results obtained in this experiment are as follows: 1. While the compressive strength of $Al_2O_3$(WA) body fired at $1450^{\circ}C$ for 5hrs in air is 150kg/$\textrm{cm}^2$, that of Al-$Al_2O_3$ body fired at 135$0^{\circ}C$, $1400^{\circ}C$ for 5hrs in air is 1100kg/$\textrm{cm}^2$, 1600kg/$\textrm{cm}^2$ respectively, and the higher the firing temperature, the more the compressive strength increases. These results from the sintering effect between $Al_2O_3$(WA) grains and surrounding Al-oxidation layer. 2. While the compressive strength of Al2O3(WA) body fired at 150$0^{\circ}C$ for 5hrs in air is 250kg/$\textrm{cm}^2$, the compressive strength of Al-$Al_2O_3$body fired under the same condition is 2050kg/$\textrm{cm}^2$ and water absorption 9.0%, porosity 23.3%, bulk density 2.60gr/$cm^3$. It is assumed that these results come from not only the grain growth of oxidized Al grains but also the increase of bonding strength between $Al_2O_3$(WA) grains.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.6
• /
• pp.772-779
• /
• 2011

New type of syngas generator based on the partial oxidation of biogas in volumetric permeable matrix reformers was suggested as an effective, adaptable and relatively simple way of syngas and hydrogen production for various low-scale applications. The use of biogas as an energy source reduces the chance of possible emission of two greenhouse gases, $CH_4$ and $CO_2$, into the atmosphere at the same time. Its nature of being a reproducible energy source makes its use even more attractive. Parametric screening studies were achieved as air ratio, biogas component ratio, input gas temperature, Steam/Carbon ratio. As the air ratio was low, the production of the hydrogen and carbon monoxide increased in the condition that 3D matrix reformer maintains the stable driving. As it was the simulation biogas in which the carbon dioxide content is high, the flammable range became narrow. And the flammable range was extended if the injected gas was preheated. The stable driving was possible in the low air ratio. The amount of hydrogen production was increased as S/C ratio increased.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.2
• /
• pp.43-52
• /
• 2021

The Ni-based superalloy, Inconel 740, was corroded between 800 and 1100℃ for up to 100 hr in air and Ar-0.2%SO₂ gas in order to study its corrosion behavior in air and sulfur/oxygen environment. It displayed relatively good corrosion resistance in both environment, because its corrosion was primarily dominated by not sulfidation but oxidation especially in Ar-0.2%SO₂ gas. Such was attributed to the thermodynamic stability of oxides of alloying elements when compared to corresponding sulfides. The scales consisted primarily of Cr₂O₃, together with some NiAl₂O₄, MnCr₂O₄, NiCrMnO₄, and rutile-TiO₂. Sulfur from SO₂ gas made scales prone to spallation, and thicker. It also widened the internal corrosion zone when compared to air. The corrosion resistance of IN740 was mainly indebted to the formation of protective Cr₂O₃-rich oxides, and suppression of the sulfide formation.

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1303-1305
• /
• 1998

In order to reduce or avoid oxidation problem at operation the interconnects in SOFCs have so far mostly been made of ceramic material. It has high chemical stability both under cathode and anode condition, relatively thermal expansion coefficient that matchs that of electrolyte material YSZ. But this material shown rather weak in the low oxygen atmosphere and thermal shock, and it has lower mechanical strength than alloys. To avoid these problems one may consider to use metals or alloys as materials for interconnects. Metallic interconnects are advantageous because of their high thermal and electronic conductivities. But it has some problems, Those are high thermal expansion and oxidation at high temperature in air. To solve these problems in the interconnection material in this study, $LaCrO_3$-dispersed Cr alloys for metallic interconnector of SOFC have been investigated as a fuction of $LaCrO_3$ content in the range of 5 to 25 vol.%. The Cr alloy were prepared by mixing Cr and $LaCrO_3$ powders in high-energy ball mill for 48h and by sintering under Ar atmosphere with 5vol.% $H_2$ for 10h at $1500^{\circ}C$. The alloys had a relative density of 95% and above. The Cr alloys in composed of two kind of small $LaCrO_3$ and large Cr particles. As the $LaCrO_3$ content increased, the Cr particle size decreased but the $LaCrO_3$ particle size remained contant. Also the oxidation tests show that the $LaCrO_3$-dispersed Cr is very resistant to oxidation in air. These results means that $LaCrO_3$-dispersed Cr is a useful material for metallic interconnect of planar SOFC.

• Applied Chemistry for Engineering
• /
• v.32 no.3
• /
• pp.237-242
• /
• 2021

Simultaneous removal technologies of multi-pollutants such as particulate matters (PMs), NOx, SOx, VOCs and ammonia have received consistent attention due to the enhancement of pollutant abatement efficiency in addition to the stringent environmental regulation and emission standard. Pretreatment of insoluble NO by an ozone oxidation can be considered to be more effective route for saving space occupation as well as operation cost in comparison with that of traditional selective catalytic reduction (SCR) process. Moreover the primary advantage of ozone oxidation process is that the simultaneous removal with acidic gas including SOx is also available. Herein, we highlight recent studies of multi-pollutant abatement via ozone oxidation process and the promising research topics for better application in industrial sectors.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.499-502
• /
• 2001

Functionally gradient NiCrAlY/$ZrO_2$-$Y_2$$O_3$ and NiCrAlY/$ZrO_2$- $CeO_2$-$Y_2$$O_3$ coatings were prepared by APS. The as-sprayed microstructure consisted of metal-rich and ceramic-rich regions, between which $Al_2$$O_3$-rich layers existed owing to the oxidation during APS. During oxidation between 900 and $1100^{\circ}C$ in air, the pre-existing $Al_2$$O_3$-rich scales grew, due mainly to the preferential reaction of Al with inwardly transporting oxygen along the heterogeneous phase boundaries. As the amount of ceramics in the coating increased, the oxidation resistance increased.

• Journal of the Korean Ceramic Society
• /
• v.17 no.4
• /
• pp.197-202
• /
• 1980

The oxidation mechanism of the not sintered pellets and sintered bodies of $Si_3N_4$ was investigated. in air over the temperature range of 800~130$0^{\circ}C$. The $\beta$-cristobalite was instantaneously formed and covered the particles of powder packed in the not sintered and weakly sintered porous $Si_3N_4$ bodies by molecular diffusion of oxygen through the porous Si3N4 bodies and an immediate oxidation. The diffusion of oxygen ion through the formed $\beta$-cristobalite surface layer is assumed to control the further oxidation of the $Si_3N_4$ particles of the porous $Si_3N_4$ bodies. The diffusion coefficients and activation energies of oxygen ion through the $\beta$-cristobalite layer were obtained by the use of a derived equation.