• Mycobiology
• /
• v.42 no.1
• /
• pp.59-65
• /
• 2014

Entomopathogenic fungi are promising pest-control agents but their industrial applicability is limited by their thermosusceptibility. With an aim to increase the thermotolerance of Isaria fumosorosea SFP-198, moisture absorbents were added to dried conidial powder, and the relationship between its water potential and thermotolerance was investigated. Mycotized rice grains were dried at $10^{\circ}C$, $20^{\circ}C$, $30^{\circ}C$, and $40^{\circ}C$ and the drying effect of each temperature for 24, 48, 96, and 140 hr was determined. Drying for 48 hr at $10^{\circ}C$ and $20^{\circ}C$ reduced the moisture content to < 5% without any significant loss of conidial thermotolerance, but drying at $30^{\circ}C$ and $40^{\circ}C$ reduced both moisture content and conidial thermotolerance. To maintain thermotolerance during storage, moisture absorbents, such as calcium chloride, silica gel, magnesium sulfate, white carbon, and sodium sulfate were individually added to previously dried-conidial powder at 10% (w/w). These mixtures was then stored at room temperature for 30 days and subjected to $50^{\circ}C$ for 2 hr. The white carbon mixture had the highest conidial thermotolerance, followed by silica gel, magnesium sulfate, and then the other absorbents. A significant correlation between the water potential and conidial thermotolerance was observed in all conidia-absorbent mixtures tested in this study (r = -0.945). Conidial thermotolerance in wet conditions was evaluated by adding moisturized white carbon (0~20% $H_2O$) to conidia to mimic wet conditions. Notably, the conidia still maintained their thermotolerance under these conditions. Thus, it is evident that conidial thermotolerance can be maintained by drying mycotized rice grains at low temperatures and adding a moisture absorbent, such as white carbon.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.314-322
• /
• 1997

The thin film processing and the applicability as a IMD material of SiO2 aerogels providing ultralow dielec-tric properties were studied. The SiO2 aerogel films with 0.5g/㎤ density (78% porosity) and 4000~21000$\AA$ thickness could be prepared at 25$0^{\circ}C$ and 1160 psig by supercritical drying of wet-gel films, which were spin-coated at the spin rate of 1000~7000 rpm on p-Si(111) wafer under the isopropanol atmosphere. The optimum viscosity of polymeric SiO2 sols for spin coating was in the range of 10~14 cP. The main fac-tors being able to control the film thickness and microstructures were found to be sol concentration, spin rpm, and aging time of wet-gel films. The dielectric constant of the SiO2 aerogel thin film was around 2.0 low enough to be applied to the next generation semiconductor device beyond the giga level.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.5
• /
• pp.411-417
• /
• 2020

In this study, we introduce a Na β"-alumina composite thick film as a solid electrolyte, to reduce the resistance of electrolyte for a Na/S battery. An alumina/zirconia composite material was used to enhance the mechanical properties of the electrolyte. A solid electrolyte of about 40 ㎛ thick was successfully fabricated through the conversion and tape-casting methods. In order to investigate the effect of the surface treatment process of the solid electrolyte on the battery performance, the electrolyte was polished by dry and wet processes, respectively, and then the Na/S batteries were prepared for analyzing the battery characteristics. The battery with the dry process performed much better than the battery made with the wet process. As a result, the battery manufactured by the dry process showed excellent performance. Therefore, it is confirmed that the surface treatment process of the solid electrolyte has an important effect on the battery capacity and coulombic efficiency, as well as the interface reaction.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.188-194
• /
• 1997

Wet gel with surface modification by TMCS was redispersed in EtOH and redispersed silica sol for coat-ing was prepared. After spin coating of redispersed sol was conducted on silicon substrate, processes of drying(8$0^{\circ}C$) and heat treatment(>25$0^{\circ}C$) were, followed at ambient pressure. The influence of heat treat-ment of properties of film was observed, changing temperature at heat treatment. The optimum redisp-ersion condition for stable silica sol was wet gel:EtOH=1g:110$m\ell$ and the concentration and viscosity of redispersed silica sol with average particle size of 30nm were 0.11 M, 2.0-2.2 cP respectively. Crack-free thin film with the refractive index of 1.14 and thickness of 400 nm was obtained through drying at 8$0^{\circ}C$ and subsequent heat treatment at 45$0^{\circ}C$ for 2 hrs respectively after spin coating of 1500rpm, 10 times.

• Geomechanics and Engineering
• /
• v.33 no.1
• /
• pp.29-40
• /
• 2023

Xanthan gum and starch compound biopolymer (XS), an environmentally friendly soil-binding material produced from natural resources, has been suggested as a slope protection material to enhance soil strength and erosion resistance. Insufficient wet strength and the consequent durability concerns remain, despite XS biopolymer-soil treatment showing high strength and erosion resistance in the dried state, even with a small dosage of soil mass. These concerns need to be solved to improve the field applicability and post-stability of this treatment. This study explored the utilization of an alkaline-based cation crosslinking method using calcium hydroxide and sodium hydroxide to induce non-thermal gelation, resulting in the enhancement of the wet strength and durability of biopolymer-treated soil. Laboratory experiments were conducted to assess the unconfined compressive strength and cyclic wetting-drying durability performance of the treated soil using a selected recipe based on a preliminary gel formation test. The results demonstrated that the uniformity of the gel structure and gelling time varied depending on the ratio of crosslinkers to biopolymer; consequently, the strength of the soil was affected. Subsequently, site soil treated with the recipe, which showed the best performance in indoor assessment, was implemented on the field slope at the bridge abutment via compaction and pressurized spraying methods to assess feasibility in field implementation. Moreover, the variation in surface soil hardness was monitored periodically for one year. Both slopes implemented by the two construction methods showed sufficient stability against detachment and scouring, with a higher soil hardness index than the natural slope for a year.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.407.1-407.1
• /
• 2016

Electrochromism is defined as a phenomenon which involves persistently repeated change of optical properties between bleached state and colored state by simultaneous injection of electrons and ions, sufficient to induce an electrochemical redox process. Due to this feature, considerable progress has been made in the synthesis of electrochromic (EC) materials, improvements of EC properties in EC devices such as light shutter, smart window and variable reflectance mirrors etc. Among the variable EC materials, solid-state inorganics in particular, metal oxide semiconducting materials such as nickel oxide (NiO) have been investigated extensively. The NiO that is an anodic EC material is of special interest because of high color contrast ratio, large dynamic range and low material cost. The high performance EC devices should present the use of standard industrial production techniques to produce films with high coloration efficiency, rapid switching speed and robust reversibility. Generally, the color contrast and the optical switching speed increase drastically if high surface area is used. The structure of porous thin film provides a specific surface area and can facilitate a very short response time of the reaction between the surface and ions. The large variety of methods has been used to prepare the porous NiO thin films such as sol-gel process, chemical bath deposition and sputtering. Few studies have been reported on NiO thin films made by using sol-gel method. However, compared with dry process, wet processes that have the questions of the durability and the vestige of bleached state color limit the thin films practical use, especially when prepared by sol-gel method. In this study, we synthesis the porous NiO thin films on the fluorine doped tin oxide (FTO) glass by using sputtering and anodizing method. Also we compared electrical and optical properties of NiO thin films prepared by sol gel. The porous structure is promised to be helpful to the properties enhancement of the EC devices.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.6
• /
• pp.220-224
• /
• 2016

Anti-reflection (AR) thin films were fabricated on a glass substrate by using an ultrasonic spray. Glycidoxypropyl trimethoxysilane (GPTMS) and tetraethyl orthosilicate (TEOS) were used to synthesize a sol-gel hybrid coating solution. The moving speed of spray nozzle was changed from 15~25 mm/s to control the coating thickness of AR thin film. As the moving speed of spray nozzle increased, the thickness of AR thin film decreased from 138 nm to 86 nm. When the AR thin film was fabricated by nozzle moving speed of 20 mm/s, the refractive index and thickness of AR thin film was measured to be 1.31 and 104 nm, respectively. The average reflectance and transmittance of AR thin film coating glass was measured to be 0.75 % and 94 %, respectively into the visible light range of 380~780 nm.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.5
• /
• pp.801-804
• /
• 2006

[ $GdAlO_3(GAO)$ ] buffer layer for $YBa_2Cu_3O_{7-{\delta}}(YBCO)$ coated superconductor wire was fabricated by sol-gel processing. Precursor solution was prepared by dissolving 1:1 stoichiometric quantaties of gadolinium nitrate hexahydrate and aluminum nitrate nonahydrate in methanol. The solution was spin-coated on $SrTiO_3(STO)$(100) single crystal substrates and heated at $1000^{\circ}C$ for 2h in wet $N_2-5%\; H_2$, atmosphere. A SEM(scanning electron microscopy) observation of the surface morphology of the GAO layer has shown that it has a faceted morphology indicating epitaxy. It was shown from x-ray diffraction(XRB) that GAO buffer layer was highly c-axis oriented epitaxial thin film with both good out-of-plane($FWHM=0.29^{\circ}$ for the (002) reflection) and in-plane ($FWHM=1.10^{\circ}$ for the {112} reflection) alignment.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.12
• /
• pp.826-830
• /
• 2015

Transparent Ag nanowire conducting thin films with high surface hardness were fabricated by bar coating method. When coating speed was changed from 35 mm/sec to 50 mm/sec, the transmittance of coated glass increased from 65.3% to 80.8% in visible light range and the surface resistance was changed from $10.1{\Omega}/sq$ to $23.3{\Omega}/sq$. The surface hardness and adhesion of thin film were 5H and 5B.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.190-190
• /
• 2010

Zinc oxide is the most attractive material due to the large direct band gap (3.37 eV), excellent chemical and thermal stability, and large exciton binding energy (60 meV). Recently, ZnO nanorods were used as the high efficient antireflection coating layer of solar cells based on silicon (Si). In this reports, we studied the effects of rapid thermal annealing (RTA) treatment on optical properties of ZnO nanorods. For fabrication of ZnO nanorods, there are many methods such as hydrothermal method, sol-gel method, and metal organic chemical vapor deposition method. Among of them, we used the conventional wet chemical method which is simple and low temperature growth. In order to synthesize the ZnO nanorods, the ZnO films were deposited on Si substrate by RF magnetron sputtering at room temperature and the samples were dipped to aqua solution containing the zinc nitrate and hexamethylentetramines (HMT). The synthesis process was achieved in keeping with temperature of $90-95^{\circ}C$ and under constant stirring. The morphology of ZnO nanorods on glass and Si was characterized by scanning electron microscopy. For the analysis of antireflection performance, the reflectance and transmittance were measured by spectrophotometer. And for analyzing the effects of RTA treatment on ZnO nanorods, crystalline properties were investigated by X-ray diffraction measurements and optical properties was estimated by photoluminescence spectra.