• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1102-1107
• /
• 1999

SiC-Si3N4 composites were prepared by mixing $\alpha$-Si3N4 powder to $\alpha$-SiC powder in the range of 10 to 30 vol% with 10vol% interval. 6wg% Al2O3 and 6wt% Y2O3 were respectively added as sintering aids. Hot pressing was performed at 1,80$0^{\circ}C$ for 1 hour with 25 MPa pressure. In the case of adding 20vol% of $\alpha$-Si3N4 powder the relative density to theoretical value and the flexural strength were 99.1% and 34,420 MPa respectively and the worn amount was 2.09$\times$10-3 mm2 which were the highest values in the all range of he composition. Although the composite containig 10 vol% of $\alpha$-Si3N4 powder showed the highest fracture toughness(KIC) of 4.65MN/m3/2 the reduction of the wear resistance in this composite is likely to be affected by the homogeneity and the uniformity of the grain coalescence and growth during the sintering process.

• Journal of the Korean Ceramic Society
• /
• v.45 no.1
• /
• pp.1-29
• /
• 2008

In last two decades, an impressive progress has been recorded in terms of developing new materials or refining existing material composition/microstructure in order to obtain better performance in biomedical applications. The success of such efforts clearly demands better understanding of various concepts, e.g. biocompatibility, host response, cell-biomaterial interaction. In this article, we review the fundamental understanding that is required with respect to biomaterials development, as well as various materials and their properties, which are relevant in applications, such as hard tissue replacement. A major emphasize has been placed to present various design aspects, in terms of materials processing, of ceramics and polymer based biocomposites, Among the bioceramic composites, the research results obtained with Hydroxyapatite (HAp)-based biomaterials with metallic (Ti) or ceramic (Mullite) reinforcements as well as $SiO_2-MgO-Al_2O_3-K_2O-B_2O_3-F$ glass ceramics and stabilized $ZrO_2$ based bioinert ceramics are summarized. The physical as well as tribological properties of Polyethylene (PE) based hybrid biocomposites are discussed to illustrate the concept on how can the physical/wear properties be enhanced along with biocompatibility due to combined addition of bioinert and bioactive ceramic to a bioinert polymeric matrix. The tribological and corrosion properties of some important orthopedic metallic alloys based on Ti or Co-Cr-Mo are also illustrated. At the close, the future perspective on orthopedic biomaterials development and some unresolved issues are presented.

• Journal of Powder Materials
• /
• v.20 no.4
• /
• pp.285-290
• /
• 2013

$Ti_2AlN$ composites are a laminated compounds that posses unique combination of typical ceramic properties and typical metallic(Ti alloy) properties. In this paper, the powder synthesis, SPS sintering, composite characteristics and machinability evaluation were systematically conducted. The random orientation characteristics and good crystallization of the $Ti_2AlN$ phase are observed. The electrical and thermal conductivity of $Ti_2AlN$ is higher than that of Ti6242 alloy. A machining test was carried out to compare the effect of material properties on micro electrical discharge drilling for $Ti_2AlN$ composite and Ti6242 alloy. Also, mixture table as a kind of tables of orthogonal arrays was used to know how parameter is main effective at experimental design. Consequently, hybrid $Ti_2AlN$ ceramic composites showed good machining time and electrode wear shape under micro ED-drilling process. This conclusion proves the feasibility in the industrial applications.

• Journal of Powder Materials
• /
• v.28 no.5
• /
• pp.381-388
• /
• 2021

Zirconia has excellent mechanical properties, such as high fracture toughness, wear resistance, and flexural strength, which make it a candidate for application in bead mills as milling media as well as a variety of components. In addition, enhanced mechanical properties can be attained by adding oxide or non-oxide dispersing particles to zirconia ceramics. In this study, the densification and mechanical properties of YSZ-TiC ceramic composites with different TiC contents and sintering temperatures are investigated. YSZ - x vol.% TiC (x=10, 20, 30) system is selected as compositions of interest. The mixed powders are sintered using hot pressing (HP) at different temperatures of 1300, 1400, and 1500℃. The densification behavior and mechanical properties of sintered ceramics, such as hardness and fracture toughness, are examined.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2003.10a
• /
• pp.59-65
• /
• 2003

Four kinds of $Si_3N_4$-based ceramic cutting tools with different sintering time were fabricated to investigante the effect of sintering time on the microstructure, mechanical properties, grain sizes and the cutting performance. An endeavor was also made to determine the relation among mechanical property, Brain size and tool life. $Si_3N_4$ home made cutting tool sintered for 1 hour under $1760^{\circ}$ temperature and 25MPa pressure showed the best cutting performance among selected ceramic tools during machining both Bray cast iron and heat treated SCM440. Multiple linear regression model was used to estimate the tool lift from mechanical property, grain size and showed good result. It was also shown that hardness imposed the biggest offect on tool life.

• Journal of Surface Science and Engineering
• /
• v.44 no.3
• /
• pp.95-104
• /
• 2011

Ti based nanocomposite films including V, Si and Nb (Ti-Me-N, Me=V, Si and Nb) were fabricated by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The pure Ti target was used for arc ion plating and other metal targets (V, Si and Nb) were used for sputtering process at a gas mixture of Ar/$N_2$ atmosphere. Mostly all of the films were grown with textured TiN (111) plane except the Si doped Ti-Si-N film which has strong (200) peak. The microhardness of each film was measured using the nanoindentation method. The minimum value of removal rate ($0.5{\times}10^{-15}\;m^2/N$) was found at Nb doped Ti-Nb-N film which was composed of Ti-N and Nb-N nanoparticles with small amount of amorphous phases.

• International Journal of Ocean System Engineering
• /
• v.2 no.2
• /
• pp.106-115
• /
• 2012

In the present study, TiN and CrN films were coated by arc ion plating equipment onto aluminum alloy substrate, A2024. The film thickness was about 4.65 ${\mu}m$. TiN and CrN films were analyzed by X-ray diffraction and energy dispersive X-ray equipments. The Young's modulus and the micro-Vickers hardness of aluminum substrate were modified by the ceramic film coatings. The difference in Young's modulus between substrate and coating film would affect on the wear resistance. The critical load, Lc, was 75.8 N for TiN and 85.5 N for CrN. It indicated from the observation of optical micrographs for TiN and CrN films that lots of cracks widely propagated toward the both sides of scratch track in the early stage of MODE I. TiN film began to delaminate completely at MODE II stage. The substrate was finally glittered at MODE III stage. For CrN film, a few crack can be observed at MODE I stage. The delamination of film was not still occurred at MODE II and then was happened at MODE III. This agrees with critical load measurement which the adhesive strength was greater for CrN film than for TiN film. Consequently, it was difficult for CrN to delaminate because the adhesive strength was excellent against Al substrate. The wear process, which the film adheres and the ball transfers, could be enhanced because of the increase in loading. The wear weight of ball was less for CrN than for TiN. This means that the wear damage of ball was greater for TiN than for CrN film. It is also obvious that it was difficult to delaminate because the CrN coating film has high toughness. The coefficient of friction was less for CrN coating film than for TiN film.

• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.193-198
• /
• 1998

This paper presents the effects of an initial braking velocity, a braking pressure, and the number of braking stop on the tribological behaviors for the three different C-C composites using an inertia dynamic-friction tester. The C-C composites were prepared through the processes of several cycles of pitch impregnation/carbonization with different friction surface texture such as continuous 8-harness satin fabric (ADD-1), chopped fiber (ADD-2) and chopped fiber (ADD-3) having higher fiber volume fraction on friction than ADD-2 by about 10%. ADD-1 exhibited a higher fraction coefficient (0.41~0.33) than those of ADD-2 and ADD-3 (0.32~0.26) under the various initial braking velocities and braking pressures. The fraction coefficients decreased with increasing the initial velocity and the braking pressures. Wear rate by the thickness change after every 25 stop indicated that ADD-2 and ADD-3 having 1.7~2.7 $\mu\textrm{m}$/stop/pair were much lower than that of ADD-1 showing 5.0~6.5 $\mu\textrm{m}$/stop/pair. All specimens showed a little bit lower wear rate during the middle stage than the initial and latter stages among 100 braking stops. ADD-1 showed higher friction coefficient and wear rate due to the active pull-out of the fibers, evidenced by thicker were film and wear debrises.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.12 no.4
• /
• pp.123-130
• /
• 2013

Zirconia is well known in industrial applications for its mechanical characteristics. DLC (diamond-like carbon) have high elastic modulus, high electric resistivity, high dielectric constant, high wear resistance, low friction coefficient, bio compatibility, chemically inert and thermally stable. Because of all these physical and chemical properties these types of coatings have become key procedure for thin coating. Friction coefficient of DLC films is already evaluated and the current work is a further advancement by calculating the fracture toughness and wear resistance of these coatings. In the present study DLC thin film coatings are developed on $ZrO_2$ alloy surface using Plasma Enhanced Chemical Vapor Deposition (PECVD) method. Vicker hardness test is employed and it was concluded that, DLC coatings increase the Vickers hardness of ceramics.

• Journal of Advanced Marine Engineering and Technology
• /
• v.34 no.7
• /
• pp.963-970
• /
• 2010

This study makes an estimate of the laser-assisted machining (LAM) of an economically viable process for manufacturing precision silicon nitride ceramic parts using a high-power diode laser (HPDL). The surface is locally heated by an intense laser source prior to material removal, and the resulting softening and damage of the workpiece surface simplify the machining of the ceramics. The most important advantage of LAM is its ability to produce much better workpiece surface quality compared to conventional machining. Also important are its larger material removal rates and longer tool life. The cutting force and surface temperature were measured on-line using a pyrometer and a dynamometer, respectively. Tool wear, chips and the surface of the workpiece were measured using optical microscopy, and the surface and fractured cross-section of $Si_3N_4$ were measured by SEM. During the LAM process, the cutting force and tool wear were reduced and oxidation of the machined surface was increased according to the increase in the laser power. Moreover, the more the feed rate increased, the more the cutting force and tool wear increased.