• Journal of the Korean Society of Food Science and Nutrition
• /
• v.33 no.7
• /
• pp.1224-1229
• /
• 2004

The blend films of poly(3-hydroxybutyric acid) (PHB) with chitosan were prepared and water vapor transmission rate, oxygen permeability and lipid permeability of the PHB/chitosan films were measured. Additionally, the biodegradability of the PHB/chitosan films was also evaluated. Water vapor transmission rate and oxygen permeability of the films decreased by the addition of chitosan. The addition of polyethylene glycol (PEG, plasticizer), however, increased the water vapor transmission rate and oxygen permeability of the films. In the evaluation of lipid permeability, all the films except PHB (the film made of only PHB) and PHB-P (the film made of PHB and PEG) did not permeate beef tallow for 24 hours. The consumed oxygen for PHB/chitosan films during incubation was greater than that for the control on the biodegradability determination of the films, which implies that PHB/chitosan films were degraded by the microorganisms. The higher PHB ratio of the films was, the faster biodegradation of the films occurred.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.873-880
• /
• 2009

Water-vapor permeation through metallic barriers deposited on polymer substrates has been an important technological issue because the performance of the barrier is critical to the reliability of flexible organic devices. For the development of long-lifetime flexible organic devices, two different sets of samples were designed and demonstrated from the viewpoint of the water-vapor transmission rate (WVTR). Aluminum (Al) and polyethylene terephthalate (PET) were chosen for the barrier layer and the polymer substrate, respectively. Two stacking structures, a single-layer (Al/PET) structure and a double-layer (Al/PET/Al) structure, were used for the WVTR measurement. For the single-layer structure, the WVTR decreases as the thickness of the barrier layer increases. Compared to the single-layer sample, the double-layer sample showed superior WVTR performance (by nearly three times) when the total thickness of the Al barrier was greater than 100 nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.244-247
• /
• 2002

In order to evaluate the water ingress to URD power cables with the jacketing materials and the cable structures, water vapor transmission (WVT) tests were carried out by the ASTM and the TEPCO's specification. All polyolefin compounds showed the superior water suppression to conventional PVC. Especially, linear polyethylenes have very low WVT. In case of cable structures, Allaminate cables showed the significant water suppression due to the watertight structure. Accordingly, it can be concluded that jacketing material and cable structure play an important role in the water suppression of URD power cables.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.41 no.1
• /
• pp.84-97
• /
• 2017

Water vapor and thermal transmission properties of high emotional garments are important to evaluate wear comfort; in addition, the measuring methods of these properties are also critical for breathable and warm suit fabrics. In this study, the water vapor and thermal properties of composite yarn fabrics made of CoolMax, Tencel, and Bamboo fibers with filaments were measured and compared according to the measuring method. Water Vapor Transmittance (WVT) of the fabric woven by the sheath/core composite yarn in the warp direction was the highest due to the small staple fiber volume in the sheath/core yarn structure and high air voids in the sheath/core yarn fabrics. This property was also the highest in fabrics woven by bamboo staple yarns in the weft direction, and was the lowest on hi-multi filament fabrics. However, water vapor resistance ($R_{ef}$) of these fabrics by KSK ISO 11092 showed the opposite results to the water vapor transmittance method ($CaCl_2$ method); in addition, its correlation coefficient was low. The correlation coefficient between $R_{ef}$ and the drying rate was 0.719; therefore, the measurement mechanism of $R_{ef}$ is analogous to the drying property measurement. The thermal conductivity of the fabrics woven with compact staple yarn showed a high value; however, the hi-multi filament fabric showed low thermal conductivity. Therefore, fiber characteristics affect thermal properties more than yarn structure. The correlation between thermal property and moisture transport was also low. This study showed that: water vapor transmittance was active at the loose yarn structure, dry heat transport was vigorous at the compact yarn structure, and heat transport was affected more by fiber characteristics than yarn structure. In conclusion, sheath/core composite yarns were relevant to the high absorptive cool suit along with siro-fil and CoolMax/Bamboo staple yarns that were relevant to the heat diffusive cool suit.

• Journal of Pharmaceutical Investigation
• /
• v.39 no.2
• /
• pp.93-95
• /
• 2009

To compare the water vapor transmission rate (WVTR) of PVA/Dextran blended hydrogel obtained by European Pharmacopiea (EP) and Japanese Industrial Standards 1099 (JIS) method, the hydrogels with various PVA/Dextran rates were prepared and their WVTR values were then checked. As dextran in the hydrogel was increased, the WVTR of hydrogel was increased. The WVTR of hydrogels were 660-1500 and $730-1900\;g/m^2$-day in EP and JIS method, respectively. There were no significant differences between the WVTRs of the hydrogels obtained by EP and those obtained by JIS method. Thus, JIS method was recommended as a WVTR method of hydrogel due to relatively simpler and shorter time.

• Applied Chemistry for Engineering
• /
• v.29 no.4
• /
• pp.484-487
• /
• 2018

In this paper, the optical and electrical properties of ytterbium films were studied for water vapor transmission rate (WVTR) analysis of encapsulation films used in organic electronic devices. Ytterbium thin films show a wide range of light transmittance (70-10%) and resistivity ($6.0-0.16m{\Omega}{\cdot}cm$) depending on various film thicknesses (20-100 nm). The Yb thin films were oxidized with moisture and its transmittance and resistance changed in real time. As a result, the WVTR of parylene and aluminum nitride (AlN) laminated thin encapsulation film was measured to be $4.3{\times}10^{-3}g/m^2{\cdot}day$ with the 25 nm thick ytterbium thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.52-56
• /
• 2001

Experiments of 2 type on insulating compounds accomplished to change PVC using in URD(Underground) power cable jacketing. one was DB (Dielectric Breakdown) test on the pure base resins and the others were WVT(Water Vapor Transmission) test on the compounds which contained C/B(Carbon Black), anti-oxidant to base resin. a kind of specimens made by pressing to resin of pellet or lump form was HDPE(High Density Polyethylene), MDPE(Medium Density Polyehylene), LDPE(Low Density Polyethylene), LLDPE(Linear Low Density Polyethylene), PVC (Polyvinyl Chloride). As a results of AC DB and WVT test, we saw that strength of Insulation was HDPE > LLDPE ≒ MDPE > LDPE and WVT ratio was HDPE < LLDPE < MDPE < LLDPE ≒ LDPE${\ll}$PVC. WVT of PVC using for jacket showed characteristic 15 times more than MDPE or LLDPE. Therefore, to development of watertightness cable, our works present need of Changing in insulating materials

• Journal of the Korean Society of Clothing and Textiles
• /
• v.17 no.4
• /
• pp.577-586
• /
• 1993

Pesticide protective clothing has not been frequently worn due to its lack of thermal comfort. It is important to develop fabrics which can allow the wearer to work in comfort. One of the possible way to achieve the goal is to produce fabrics with a water- and oil-repellent finish which would resist pesticide penetration but maintain some breathability. The purpose of this study were to evaluate the pesticide barrier properties of untreated and water- and oil-repellent finished nonwoven fabrics. Three types of nonwoven fabrics(Tyvek, Sontara and Kimlon) were used as test specimens. By pad-dry-cure method, each of the specimen was treated with fluorocarbon. The pesticide barrier properties (amount of pesticide penetration and residue) were measured by the gas chromatography. The performance properties of untreated and treated specimens were evaluated with respects to water pepellency(KS K 0590), oil repellency(AATCC 118), water resistance(KS K 0591, AATCC 42), water vapor transmission (KS A 1013) and air permeability(KS K 0570). The results of this study were as follows : 1) The untreated Sontara showed much more amount of pesticide penetration than untreated Tyvek and Kimlon, while the treated Sontara showed little amount of pesticide penetration. 2) After laundering, the amount of pesticide residue in the untreated and treated Sontara was less than that in Tyvek and in Kimlon. 3) Water- and oil-repellent finish improved water repellency, oil repellency, and water resistance of specimens. 4) The untreated Sontara and Kimlon showed higher water vapor transmission and air permeability than untreated Tyvek. Water vapor transmission and air permeability of treated specimen decreased compared to those of untreated.

• Journal of the Korean Ceramic Society
• /
• v.56 no.6
• /
• pp.601-605
• /
• 2019

This work reports the preparation of ceramic hybrid films with illite-polyethylene composites analyzed as a function of concentration of added illite in polyethylene. The enhancement of oxygen and water-vapor transmission rate of illite-polyethylene film was evaluated to determine its influence on the freshness in fruit packaging. Particle size of illite materials was controlled in the range of 1~10 ㎛ and then mixed with LDPE to form the masterbatch. Ceramic hybrid films were prepared through a blown film making process. To determine the dispersity and abundancy of illite materials in the polyethylene matrix, various characterizations of illite-PE hybrid masterbatch and films were performed using SEM, TGA, and FT-IR. The oxygen and water-vapor transmission rate of illite-polyethylene film was found to be two times higher than that of LDPE film.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.8
• /
• pp.687-694
• /
• 2002

In order to replace the jacket material for URD power cables, the 6 kinds of polyethylene compounds were manufactured and evaluated. The characteristics of the compounds were investigated by water vapor transmission (WVT) test, thermal and mechanical test. In WVT test, all the polyethylene compounds showed the superior water resistance to conventional PVC. The molecular structure and density of polyethylene play an important role in WVT. Also, the polyethylene compounds showed the suitable characteristics in thermal and mechanical test. Especially, the linear polyethylene compounds showed the superior characteristics to LDPE ones. Due to the fillers in compounds, the abrasion resistance was decreased and the cut-through resistance was increased. From this study, it can be considered that the polyethylene compounds may be suitable to jacket material for URD power cables.