• Journal of the Korean Solar Energy Society
• /
• v.39 no.1
• /
• pp.33-40
• /
• 2019

Al-doped ZnO (AZO) thin films were synthesized on Si(100) wafers via plasma enhanced metal organic chemical vapor deposition (PE-MOCVD) method using diethyl zinc (DEZ) and N-methylpyrrolidine alane (MPA) as precursors. Effects of Al/Zn mixing ratio, plasma power on the surface morphology, crystal structure, and electrical property were investigated with SEM, XRD and 4-point probe measurement respectively. Growth rate of the film decreased slightly with increasing the Al/Zn mixing ratio, however electrical property was enhanced and resistivity of the film decreased greatly about 2 orders from $9.5{\times}10^{-1}$ to $8.0{\times}10^{-3}{\Omega}cm$ when the Al/Zn mixing ratio varied from 0 to 9 mol%. XRD analysis showed that the grain size increased with increasing the Al/Zn mixing ratio. Growth rate and electrical property were enhanced in a mild plasma condition. Resistivity of AZO film decreased down to $7.0{\times}10^{-4}{\Omega}cm$ at an indirect plasma of 100 W condition which was enough value to use for the transparent conducting oxide (TCO) material.

• Applied Chemistry for Engineering
• /
• v.7 no.6
• /
• pp.1078-1086
• /
• 1996

The peroxo-polytungstic acid was formed by the direct reaction of tungsten powder with the hydrogen peroxide solution. Peroxo-polytungstic powder were prepared by rotary evaporator using the fabricated on to ITO coated glass as substrate by dip-coating method using $2g/10mL(W-IPA/H_2O)$ sol solution. A substrate was dipped into the sol solution and after a meniscus had settled, the substrate was withdrawn at a constant rate of the 3mm/sec. Thicker layer could be built up by repeated dipping/post-treatment 15 times cycles. The layers dried at the temperature of $65{\sim}70^{\circ}C$ during the withdrawn process, and then tungsten oxides thin film was formed by final heating treatment at the temperature of $230{\sim}240^{\circ}C$ for 30min. A linear rotation between the thickness of thin film and the number of dipping/post-treatment cycles for tungsten oxides thin films made by dip-coating was found. The thickness of thin film had $60{\AA}$ after one dipping. From the patterns of XRD, the structure of tungsten oxides thin film identified as amorphous one and from the photographs of SEM, the defects and the moderate cracks were observed on the tungsten oxides thin film, but the homogeneous surface of thin films were mostly appeared. The electrochemical characteristic of the $ITO/WO_3$ thin film electrode were confirmed by the cyclic voltammetry and the cathodic Tafel polaization method. The coloring bleaching processes were clearly repeated up to several hundreds cycles by multiple cyclic voltammetry, but the dissolved phenomenon of thin film revealed in $H_2SO_4$ solution was observed due to the decrease of the current densities. The diffusion coefficient was calculated from irreversible Randles-Sevick equation from the data obtained by the cyclic voltammetry with various scan rates.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1996.02a
• /
• pp.102-102
• /
• 1996

This paper represents a new type low power High Frequency technological ion source (HF TIS) for ion - beam processing: the surface modification of materials, cleaning of surface, sputtering, coating of thin films, and polishing. The operational principle of HF TIS is based on the excitation of electrostatic waves in plasma located in the external magnetic field. Low power HF TIS with diameter 92 rom gives the opportunity to obtain beams of inert and chemically reactive gases with currents range from 5 to 150 mA (current density $0.015\;~\;3.5\;mA/\textrm{m}^2$) and ion beam energy 100 ~ 2500 eV at a HF power level 10 ~ 150 W. Three grid concave type ion optical system (IOS) is used for extraction and formation ofion beam.n beam.

• Journal of the Korean Vacuum Society
• /
• v.5 no.1
• /
• pp.25-32
• /
• 1996

An ERD-TOF system is constructed for the nondestructive depth profiling of light elements in thin films in the range of several thousand angstroms. The particles, recoiled by 10 $MeV^{35}Cl$ projectiles, were detected by a Time-Of-Flight spectrometer composed of a MCP (Micro Channel Plate) and a SSB (Silicon Surface Barrier) detector. A two parameter data acquisition system composed of two PC's was constructed for registering simultaneous time and energy signals. A $Si_3N_4$/poly-Si/$SiO_2$/Si sample was anlayzed and the result is compared with RBS. The detection limit, maximum probable depth and depth resolution for light elements in silicon are about $4\times10^{14}atoms/\textrm{cm}^2$, 5, 000$\AA$ and 100$\AA$, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.444-444
• /
• 2011

Recently, patterned magnetic films and elements attract a wide interest due to their technological potentials in ultrahigh-density magnetic recording and spintronic devices. Among those patterned magnetic structures, magnetic anti-dot patterning induces a strong shape anisotropy in the film, which can control the magnetic properties such as coercivity, permeability, magnetization reversal process, and magneto-resistance. While majority of the previous works have been concentrated on anti-dot arrays with a single magnetic layer, there has been little work on multilayered anti-dot arrays. In this work, we report on study of the magnetic properties of bilayered anti-dot system consisting of upper perforated Co layer of 40 nm and lower continuous Ni layer of 5 nm thick, fabricated by photolithography and wet-etching processes. The magnetic hysteresis (M-H) loops were measured with a superconducting-quantum-interference-device (SQUID) magnetometer (Quantum Design: MPMS). For comparison, investigations on continuous Co thin film and single-layer Co anti-dot arrays were also performed. The magnetic-domain configuration has been measured by using a magnetic force microscope (PSIA: XE-100) equipped with magnetic tips (Nanosensors). An external electromagnet was employed while obtaining the MFM images. The MFM images revealed well-defined periodic domain networks which arise owing to the anisotropies such as magnetic uniaxial anisotropy, configurational anisotropy, etc. The inclusion of holes in a uniform magnetic film and the insertion of a uniform thin Ni layer, drastically affected the coercivity as compared with single Co anti-dot array, without severely affecting the saturation magnetization ($M_s$). The observed changes in the magnetic properties are closely related to the patterning that hinders the domain-wall motion as well as to the magneto-anisotropic bilayer structure.

• Journal of the Korean Ceramic Society
• /
• v.49 no.6
• /
• pp.620-624
• /
• 2012

The role of moisture remaining inside the deposition chamber during the formation of the cubic boron nitride (c-BN) phase in BN film was investigated. BN films were deposited by an unbalanced magnetron sputtering (UBM) method. Single-crystal (001) Si wafers were used as substrates. A hexagonal boron nitride (h-BN) target was used as a sputter target which was connected to a 13.56 MHz radiofrequency electric power source at 400 W. The substrate was biased at -60 V using a 200 kHz high-frequency power supply. The deposition pressure was 0.27 Pa with a flow of Ar 18 sccm - $N_2$ 2 sccm mixed gas. The inside of the deposition chamber was maintained at a moisture level of 65% during the initial stage. The effects of the evacuation time, duration time of heating the substrate holder at $250^{\circ}C$ as well as the plasma treatment on the inside chamber wall on the formation of c-BN were studied. The effects of heating as well as the plasma treatment very effectively eliminated the moisture adsorbed on the chamber wall. A pre-deposition condition for the stable and repeatable deposition of c-BN is suggested.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.60-60
• /
• 2000

The adhesion interface formation between copper and poly(ethylene terephthalate)(PET), poly(methyl methacrylate)(PMMA) and Polyimide films was treated using Ion assisted reaction system to sequential sputter deposition by High-Frequency ion source. The ion beam modification system used a new type of low power HF ion thruster for space application as new low thruster electric propulsion system. Low power HF ion thruster with diameter 100mm gives the opportunity to obtain beams of Ar+ with currents 20~150 mA (current density 0.5~3.5 mA/cm2) and energy 200~2500eV at HF power level 10~150 W. Using Ar as a working gas it is possible to obtain thrust within 3~8 mN. Contact angles for untreated films were over 95$^{\circ}$ and 80 for Pet, 10o for PMMA and 12o for PI samples as a condition of ion assisted reaction at the ion dose of 10$\times$1016 ions/cm2, the ion beam potential of 1.2 keV and 4 ml/min for environmental gas flow rate. 900o peel tests yielded values of 15 to 35 for PET, 18 to 40 and 12 to 36 g/min. respectively. High resolution X-ray photoelectron spectrocopy is the Cls region for Cu metal on these polymer substrates showed increases in C=O-O groups for polymide, whereas PET and PMMA treated samples showed only C=O groups with increase the ion dose. Finally, unstable polymer surface can be changed from hydrophobic to hydrophilic formation such as C-O and C=O that were confirmed by the XPS analysis, conclusionally, the ion assisted reaction is very effective tools to attach reactive ion species to form functional groups on C-C bond chains of PET, PMMA and PI.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.1
• /
• pp.88-93
• /
• 2024

To evaluate the possibility as a multi-level memory medium for the Ge₂Sb₂Te₅/TiN/W-doped Ge₂Sb₂Te₅ cell structure, the crystallization rate and stabilization characteristics according to voltage (V)- and current (I)- pulse sweeping were investigated. In the cell structures prepared by a magnetron sputtering system on a p-type Si (100) substrate, the Ge₂Sb₂Te₅ and W-doped Ge₂Sb₂Te₅ thin films were separated by a barrier metal, TiN, and the individual thicknesses were varied, but the total thickness was fixed at 200 nm. All cell structures exhibited relatively stable multi-level states of high-middle-low resistance (HR-MR-LR), which guarantee the reliability of the multilevel phase-change random access memory (PRAM). The amorphousto-multilevel crystallization rate was evaluated from a graph of resistance (R) vs. pulse duration (T) obtained by the nanoscaled pulse sweeping at a fixed applied voltage (12 V). For all structures, the phase-change rates of HR→MR and MR→LR were estimated to be approximately t<20 ns and t<40 ns, respectively, and the states were relatively stable. We believe that the doublestack structure of an appropriate Ge-Sb-Te film separated by barrier metal (TiN) can be optimized for high-speed and stable multilevel PRAM.

• Journal of Sensor Science and Technology
• /
• v.8 no.2
• /
• pp.115-123
• /
• 1999

A micro-gas sensor with heater and sensing electrode on the same plane was fabricated on phosphosilicate glass(PSG, 800nm)/$Si_3N_4$ (150nm) dielectric membrane. PSG film was provided by atmospheric pressure chemical vapor deposition(APCVD), and $Si_3N_4$ film by low pressure chemical vapor deposition (LPCVD). Total area of the fabricated device was $3.78{\times}3.78mm^2$. The area of diaphragm was $1.5{\times}1.5mm^2$, and that of the sensing layer was $0.24{\times}0.24mm^2$. Finite-element simulation was employed to estimate temperature distribution for a square-shaped diaphragm. The power consumption of Pt heater was about 85mW at $350^{\circ}C$. Tin thin films were deposited on the silicon substrate by thermal evaporation at room temperature and $232^{\circ}C$, and tin oxide films($SnO_2$) were prepared by thermal oxidation of the metallic tin films at $650^{\circ}C$ for 3 hours in oxygen ambient. The film analyses were carried out by SEM and XRD techniques. Effects of humidity and ambient temperature on the resistance of the sensing layer were found to be negligible. The fabricated micro-gas sensor exhibited high sensitivity to butane gas.

• Proceedings of the KOSOMBE Conference
• /
• v.1997 no.05
• /
• pp.47-50
• /
• 1997

We synthesized N-Hydroxysuccinimidyl (NHS) azidobenzoate as a cross-linking reagent for immobilization of peptide onto the solid surface. Thin polystyrene(PS) films spin-coated with a NHS azidobenzoate solution were exposed with ultraviolet light at 245nm$(3.3mW/cm^2)$ for 5 min. The NHS active ester groups became covalently attached to the polymer via photogenerated, highly reactive nitrene intermediates derived from NHS azidobenzoate. Using this technique, it is demonstrated that well-defined surface regions can be functionalized with a minimum observable feature size of 1mm for UV exposure. Through reaction of this functionalized PS surface with primary amine-containing biomolecules, biological molecule had been immobilized on the polymer surface.