• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.30 no.3
• /
• pp.46-56
• /
• 1998

The objective of this study was to investigate the relationship between water vapor diffusion properties and the pore structure of paper. Gas-phase molecular diffusivity of water vapor through pores was determined based on the kinetic theory of gas. A mathematical model was derived to characterize the dimensional changes of the pore caused by the fiber-swelling mechanism. A modified-Fickean diffusion model was designed to simulate the water-vapor diffusion phenomena in porous paper web. Structural characterisocs of paper pores including the tortuosity and the shape factor was studied on a theoretical basis of Knudsen flow diffusion. Results are summarized as follows: 1. The theoretical water vapor diffusivity in gas-phase was 0.092$cm^2$ /min, 2. Porosity was inversely proportional to the degree of wet-swelling of paper, 3. Solid-phase water-diffusivity of fiber was 1.2 $ \times 10^{-5}cm^2/min$, 4. Modified diffusion model was fairly consistent to the experimental data (from part I), and 5. The Fickean pore tortuosity, ranging from 1,000 to 2,500, was in inverse proportion to the porosity of paper, and the Knudsen shape factor and length-angle factor for micro-pores in paper were 0.5~3.5 and about 340, respectively.

• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.51-57
• /
• 2008

we have demonstrated structural evolution and optical properties of Si-nanowires (NWs) synthesized on Si (111) substrates with nanoscale Au-Si islands by rapid thermal chemical vapor deposition (RTCVD). The Au-Si nano-islands (10-50nm in diameter) were employed as a liquid-droplet catalysis to grow Si-NWs via vapor-liquid-solid mechanism. The Si-NWs were grown by a mixture gas of SiH4 and H2 at a pressure of 1.0 Torr and temperatures of $500{\sim}600^{\circ}C$. Scanning electron microscopy measurements showed that the Si-NWs are uniformly sized and vertically well-aligned along <111> direction on Si (111) surfaces. The resulting NWs are ${\sim}60nm$ in average diameter and ${\sim}5um$ in average length. High resolution transmission microscopy measurements indicated that the NWs are single crystals covered with amorphous SiOx layers of ${\sim}3nm$ thickness. In addition, the optical properties of the NWs were investigated by micro-Raman spectroscopy. The downshift and asymmetric broadening of the Si main optical phonon peak were observed in Raman spectra of Si-NWs, which indicates a minute stress effects on Raman spectra due to a slight lattice distortion led by lattice expansion of Si-NW structures.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.112-113
• /
• 2014

The submicron-rods of $Cu_2O$ with diameters of 100-700 nm and lengths of $2-8{\mu}m$ were synthesized by radio frequency magnetron sputtering. The abundance of Cu species, which is modulated by the $Ar/O_2$ ratio during the sputtering process affect directly to the growths of the $Cu_2O$ branches on the bodies of the submicron-rods. Transmission electron microscopy and elemental mapping reveal that metallic Cu are existed on the heads of the $Cu_2O$ rods. The growth rate, catalyst phase and shape reveal that vapor-quasiliquid-solid was the growth mechanism of the formations of those structures.

• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.686-690
• /
• 2010

$TiO_2$ nanowires were self-catalytically synthesized on bare Si(100) substrates using metallorganic chemical vapor deposition. The nanowire formation was critically affected by growth temperature. The $TiO_2$ nanowires were grown at a high density on Si(100) at $510^{\circ}C$, which is near the complete decomposition temperature ($527^{\circ}C$) of the Ti precursor $(Ti(O-iPr)_2(dpm)_2)$. At $470^{\circ}C$, only very thin (< $0.1{\mu}m$) $TiO_2$ film was formed because the Ti precursor was not completely decomposed. When growth temperature was increased to $550^{\circ}C$ and $670^{\circ}C$, the nanowire formation was also significantly suppressed. A vaporsolid (V-S) growth mechanism excluding a liquid phase appeared to control the nanowire formation. The $TiO_2$ nanowire growth seemed to be activated by carbon, which was supplied by decomposition of the Ti precursor. The $TiO_2$ nanowire density was increased with increased growth pressure in the range of 1.2 to 10 torr. In addition, the nanowire formation was enhanced by using Au and Pt catalysts, which seem to act as catalysts for oxidation. The nanowires consisted of well-aligned ~20-30 nm size rutile and anatase nanocrystallines. This MOCVD synthesis technique is unique and efficient to self-catalytically grow $TiO_2$ nanowires, which hold significant promise for various photocatalysis and solar cell applications.

• Journal of the Korean Ceramic Society
• /
• v.44 no.4 s.299
• /
• pp.202-207
• /
• 2007

High-Quality 1-Dimensional InN single crystalline have been grown by Halide Vapor-Phase Epitaxy on the Au catalyst coated Si substrate using the vapor-liquid-solid growth mechanism. We have been grown 1-dimension InN nanowires having controlled the growth conditions for substrate temperature and gases flow rate. The grown InN nanowire of characteristics for morphologies, crystal structure, and element analysis were carried out by SEM, HR-TEM, and EDS respectively. And the defects of InN crystalline were analyzed by indexing of selective area diffraction pattern with attached HR-TEM. We have successfully obtained the defect-free 1-dimensional InN single crystalline nanowire at the atmosphere pressure.

• Journal of Powder Materials
• /
• v.13 no.5 s.58
• /
• pp.305-312
• /
• 2006

Amorphous carbon nanotubes were synthesized by a reaction of benzene, ferrocene and Na mixture in a small autoclave at temperatures as low as $400^{\circ}C$. The resulting carbon nanotubes were short and straight, but their inner hole was filled with residual products. The addition of quartz to the reacting mixture considerably promoted the formation of carbon nanotubes. A careful examination of powder structure suggested that the nanotubes in this process were mainly formed by surface diffusion of carbon atoms at the surface of solid catalytic particles, not by VLS(vapor-liquid-solid) mechanism.

• Journal of the Korean Vacuum Society
• /
• v.16 no.4
• /
• pp.279-285
• /
• 2007

We have demonstrated structural evolution and optical properties of the Si-NWs on Si (111) substrates with synthesized nanoscale Au-Si islands by rapid thermal chemical vapor deposition(RTCVD). Au nano-islands (10-50nm in diameter) were employed as a liquid-droplet catalysis to grow Si-NWs via vapor-liquid-solid mechanism. Si-NWs were grown by a mixture gas of $SiH_4\;and\;H_2$ at pressures of $0.1{\sim}1.0$Torr and temperatures of $450{\sim}650^{\circ}C$. SEM measurements showed the formation of Si-NWs well-aligned vertically for Si (111) surfaces. The resulting NWs are 30-100nm in diameter and $0.4{\sim}12um$ in length depending on growth conditions. HR-TEM measurements indicated that Si-NWs are single crystals convered with about 3nm thick layers of amorphous oxide. In addition, optical properties of NWs were investigated by micro-Raman spectroscopy. The downshift and asymmetric broadening of the Si optical phonon peak with a shoulder at $480cm^{-1}$ were observed in Raman spectra of Si-NWs.

• Journal of the Korean Ceramic Society
• /
• v.45 no.3
• /
• pp.142-145
• /
• 2008

The growth of amorphous silica nanowires by on-site feeding of silicon and oxygen is reported. The nanowires were grown on a nickel-coated oxidized silicon substrate without external silicon or oxygen sources. Transmission electron microscopy observation revealed that the nanowires, which have diameters of less than 50 nm and a length of several micrometers, were grown using a traditional vapor-liquid-solid mechanism. Blue photoluminescence was observed from these nanowires at room temperature. An approach to grow nanowires without external precursors may be useful when integrating nanowires into devices structures. This can benefit the fabrication of nanowire-based nanodevices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.115-116
• /
• 2005

Si nanowires (NWs) were fabricated in vacuum furnace by using a Nd:YAG pulsed laser with the wavelength of 325 nm. Commercial p-type Si wafer is used for target, and any catalytic materials are not used. Scanning electron microscopy (SEM) images indicate that the diameters of Si NWs ranged from 10 to 150 nm. Si NWs have various size and shape with a substrate position inside a furnace, and their morphologic construction is reproducible. The formation mechanism of the NWs is discussed.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.462-462
• /
• 2013

Gallium Oxide (Ga2O3) has been widely investigated for the optoelectronic applications due to its wide bandgap and the optical transparency. Recently, with the development of fabrication techniques in nanometer scale semiconductor materials, there have been an increasing number of extensive reports on the synthesis and characterization of Ga2O3 nano-structures such as nano-wires, nanobelts, and nano-dots. In contrast to typical vaporliquid-solid growth mode with metal catalysts to synthesis 1-dimensional nano-wires, there are several difficulties in fabricating the nanostructures by using sputtering techniques. This is attributed to the fact that relatively low growth temperatures and higher growth rate compared with chemical vapor deposition method. In this study, Ga2O3 chestnut burr were synthesized by using radio-frequency magnetron sputtering method. In contrast to typical sputtering method with sintered ceramic target, a Ga2O3 powder (99.99% purity) was used as a sputtering target. Several samples were prepared with varying the growth parameters, especially he growth time and the growth temperature to investigate the growth mechanism. Samples were characterized by using XRD, SEM, and PL measurements. In this presentation, the details of fabrication process and physical properties of Ga2O3 nano chestnut burr will be reported.