• Journal of the Korea Furniture Society
• /
• v.12 no.2
• /
• pp.1-10
• /
• 2001

As finger joint method has a high rate of yield and high strength and ease in working, it has been widely used as an end joint method for solid wood and wood based-material. Therefore, we end-joined the material of Pinus densiflora, Quercus variabilis and populus euramericana with polyvinyl acetate adhesive and resorcinol phenol resin adhesive. The effect of difference (0, 0.15, 0.3, 0.45mm) between the dimensions of tip width and root width of the finger (DTRW) on bending strength properties was as follows: 1. In the case of polyvinyl acetate adhesive, DTRW had no effect on bending modulus of elasticity(MOE) and modulus of rupture(MOR) of the three kinds of species, because their bonding layers were destroyed by slippage, not their woody parts. 2. In the case of resorcinol phenol resin adhesive, the material of Quercus variabilis showed an optimal result at 0.15 or 0.3 of DTRW, while the poplar did at 0 of DTRW 3. The differences in efficiency ratio of bending MOR of populus euramericana, Pinus densiflora and Quercus variabilis species according to the kind of adhesive were 13-29%, 23-30% and 45-53%, respectively.

• Korean Journal of Materials Research
• /
• v.23 no.9
• /
• pp.489-494
• /
• 2013

In this study, by using nickel chloride solution as a raw material, a nano-sized nickel oxide powder with an average particle size below 50 nm was produced by spray pyrolysis reaction. A spray pyrolysis system was specially designed and built for this study. The influence of nozzle tip size on the properties of the produced powder was examined. When the nozzle tip size was 1 mm, the particle size distribution was more uniform than when other nozzle tip sizes were used and the average particle size of the powder was about 15 nm. When the nozzle tip size increases to 2 mm, the average particle size increases to roughly 20 nm, and the particle size distribution becomes more uneven. When the tip size increases to 3 mm, particles with an average size of 25 nm and equal to or less than 10 nm coexist and the particle size distribution becomes much more uneven. When the tip size increases to 5 mm, large particles with average size of 50 nm partially exist, mostly consisting of minute particles with average sizes in the range of 15~25 nm. When the tip size increases from 1 mm to 2 mm, the XRD peak intensities greatly increase while the specific surface area decreases. When the tip size increases to 3 mm, the XRD peak intensities decrease while the specific surface area increases. When the tip size increases to 5 mm, the XRD peak intensities increase again while the specific surface area decreases.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.197-197
• /
• 2011

In this study, in contrast with cases in which Scanning Tunneling Microscopy (STM) tip-induced reactions were instigated by the tunneling electrons, the local electric field, or the mechanical force between a tip and a surface, we found that the tungsten oxide (WO3) covered tungsten (W) tip of a STM acted as a chemical catalyst for the S-H dissociative adsorption of phenylthiol and 1-octanethiol onto a Ge(100) surface. By varying the distance between the tip and the surface, the degree of the tip-catalyzed adsorption could be controlled. We have found that the thiol head-group is the critical functional group for this catalysis and the catalytic material is the WO3 layer of the tip. After removing the WO3 layer by field emission treatment, the catalytic activity of the tip has been lost. 3-mercapto isobutyric acid is a chiral bi-functional molecule which has two functional groups, carboxylic acid group and thiol group, at each end. 3-Mercapto Isobutyric Acid adsorbs at Ge(100) surface only through carboxylic acid group at room temperature and this adsorption was enhanced by the tunneling electrons between a STM tip and the surface. Using this enhancement, it is possible to make thiol group-terminated surface where we desire. On the other hand, surprisingly, the WO3 covered W tip of STM was found to act as a chemical catalyst to catalyze the adsorption of 3-mercapto isobutyric acid through thiol group at Ge(100) surface. Using this catalysis, it is possible to make carboxylic acid group-terminated surface where we want. This functional group-selective adsorption of bi-functional molecule using the catalysis may be used in positive lithographic methods to produce semiconductor substrate which is terminated by desired functional groups.

• Tribology and Lubricants
• /
• v.35 no.5
• /
• pp.286-293
• /
• 2019

In friction and wear tests that use friction force microscopy (FFM), the wear debris transfer to the tip apex that changes tip radius is a crucial issue that influences the friction and wear performances of films and coatings with nanoscale thicknesses. In this study, FFM tests are performed for bilayer $MoS_2$ film to obtain a better understanding of how geometrical and chemical changes of tip apex influence the friction and wear properties of nanoscale molecular layers. The critical load can be estimated from the test results based on the clear distinction of the failure area. Scanning electron microscopy and energy-dispersive spectroscopy are employed to measure and observe the geometrical and chemical changes of the tip apex. Under normal loads lower than 1000 nN, the reuse of tips enhances the friction and wear performance at the tip-sample interface as the contact pair changes with the increase of tip radius. Therefore, the reduction of contact pressure due to the increase of tip radius by the transfer of $MoS_2$ or Mo-dominant wear debris and the change of contact pairs from diamond/$MoS_2$ to partial $MoS_2$ or Mo/$MoS_2$ can explain the critical load increase that results from tip reuse. We suggest that the wear debris transfer to the tip apex should be considered when used tips are repeatedly employed to identify the tribological properties of ultra-thin films using FFM.

• Korean Journal of Materials Research
• /
• v.23 no.2
• /
• pp.81-88
• /
• 2013

In this study, using a tin chloride solution as the raw material, a nano-sized tin oxide powder with an average particle size below 50 nm is generated by a spray pyrolysis process. The properties of the tin oxide powder according to the nozzle tip size are examined. Along with an increase in the nozzle tip size from 1 mm to 5 mm, the generated particles that appear in the shape of droplets maintain an average particle size of 30 nm. When the nozzle tip size increases from 1 mm to 2 mm, the average size of the generated particles is around 80-100 nm, and the ratio of the independent particles with a compact surface structure increases significantly. When the nozzle tip size is at 3 mm, the majority of the generated particles maintain the droplet shape, the average size of the droplet-shaped particles increases remarkably compared to the cases of other nozzle tip sizes, and the particle size distribution also becomes extremely irregular. When the nozzle tip size is at 5 mm, the ratio of droplet-shaped particles decreases significantly and most of the generated particles are independent ones with incompact surface structures. Along with an increase in the nozzle tip size from 1 mm to 3 mm, the XRD peak intensity increases, whereas the specific surface area decreases greatly. When the nozzle tip size increases up to 5 mm, the XRD peak intensity decreases significantly, while the specific surface area increases remarkably.

• Plant Resources
• /
• v.6 no.3
• /
• pp.233-241
• /
• 2003

The shoot tip and young leaf of Rhodiola sachalinensis were cultured to invest the plant growth regulator condition for callus induction, shoot and root regeneration. When the shoot tip was sterilized in 2.0% of NaOCl for 20min., the contamination rate was the lowest. And the survival rate of the culture material was good in carbenicillin 500mg/L treatment group. Callus was obtained from shoot tip and young leaf segments. NAA 0.1-1.0mg/L and 2,4-D 0.1-0.5mg/L alone treatment were shown to have a good response on callus induction from shoot tip culture. In the case of young leaf culture, NAA and 2,4-D 0.1-0.5mg/L alone treatment were good in callus induction. In culturing shoot tip NAA 0.5mg/L and BA 0.5mg/L, NAA1.0mg/L and BA 0.lmg/L combination treatment was good in shoot regeneration. The regenerated shoots were rooted on MS medium supplemented with NAA and BA combination treatment. Especially, NAA 1.0mg/L and BA 0.1mg/L combination treatment was effective for root regeneration.

• Analytical Science and Technology
• /
• v.30 no.6
• /
• pp.319-328
• /
• 2017

The identification of explosive residues on specimens obtained from an explosion event is a crucial factor for assessing the cause of the explosion. In order to detect the components of explosives, the explosive residues deposited on surfaces are commonly extracted using swabbing materials pre-wetted with an organic solvent. The residues are then analyzed with analytical instruments such as LC/MS and CE/MS. Most conventionally used swabbing media such as cotton swabs or cotton tip swabs seem unsuitable for extracting explosive residues from the surface of a large area of clothes because the swabbing materials tend to be damaged easily, and because only a relatively small amount of explosives is collected. To overcome these problems, we have introduced a novel wiper ($215{\times}210mm$, single layer, Yuhan-Kimberly, Republic of Korea) as a swabbing material to recover representative organic explosives, namely, TNT, RDX, tetryl, HMX, PETN, and NG, from a large area of clothes. Different sides of the wiper, which was folded in half five times, was used to swab the surface of a clothing. We compared this novel wiper with a cotton swab and a cotton tip swab in terms of the recovery efficiency for the aforementioned organic explosives by pre-wetting with methanol, acetone, and acetonitrile, respectively. We identified that this novel wiper collected a significantly higher amount of organic explosive residues than a cotton swab or a cotton tip swab when using methanol as an extracting solvent.

• Korean Journal of Metals and Materials
• /
• v.46 no.8
• /
• pp.495-505
• /
• 2008

With the high proportion of zinc coated steels in body-in-white assembly, newly developed surface roughness textured galvannealed steel sheets have been introduced. In this study, zinc coated and surface roughness textured steel sheets were welded by resistance spot welding to investigate its weldability including electrode wear test. Based on the results of tensile-shear test, nugget diameter changes, and electrode tip growth test, it was clear that both surface roughness textured steels (GA-T and GA-E) showed good weldability. Also, there was no large difference in weldability and electrode wear behavior between GA-T and GA-E steels which have different surface roughness morphology. An analysis of electrode degradation showed Fe and Zn penetration through the electrode tip surface at 2400 welds reached $55{\sim}60{\mu}m$ and $75{\sim}80{\mu}m$, respectively. Therefore, there is no significant effect of surface roughness morphology on spot weldability of surface roughness textured galvannealed steel sheets. However, slight difference in thickness of alloying layers existing on electrode tip was found between GA-T and GA-E steels.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.7
• /
• pp.1373-1380
• /
• 1992

The local cyclic strain distribution near the crack tip has been investigated by the fine Dot Grid Strain Measurement Method, which had been suggested strain measurement method to resolve experimental difficulties by authors. It has been found that the magnitude of the local cyclic strain distribution(.DELTA..epsilon.$_{eq}$ )near a crack tip has been varied by the applied cyclic load level and material, but the shape of the local cyclic strain distribution near the crack tip has been experimentally scrarcely altered : that is .DELTA..epsilon.$_{eq}$ = .DELTA.A.f(.theta.). $r^{-1}$ . Consequently, the local cyclic strain field near the crack tip could be favorably characterized by a single parameter fatigue strain intensity factor .DELTA.A. In addition, with the viewpoint that .DELTA.A depends on material and load level, .DELTA.A has been applied to evaluate the fatigue crack propagation rate and usefulness of the result has been considered. As a result, it has been ascertained that .DELTA.A has been a useful parameter to evaluate the fatigue crack propagation rate.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.11
• /
• pp.1207-1214
• /
• 2014

Under excessive plasticity, the fracture toughness of a material depends on its size and geometry. Under fully yielded conditions, the stresses in a material near its crack tip are not unique but rather depend on the geometry. Therefore, the single-parameter J-approach is limited to a high-constraint crack geometry. The JQ theory has been proposed for establishing the crack geometry constraints. This approach assumes that the crack-tip fields have two degrees of freedom. In this study, the crack-tip stress field of a fully circumferential surface-cracked pipe under combined loads is investigated on the basis of the JQ theory by using finite element analysis. The combined loads are a tensile axial force and the thermal gradient in the radial direction. Q-stresses of the crack geometry and its loading state are used to determine the constraint effects. The constraint effects of secondary loading are found to be greater than those of primary loading. Therefore, thermal shock is believed to be the most severe loading condition of constraint effects.