• Journal of Powder Materials
• /
• v.16 no.1
• /
• pp.43-49
• /
• 2009

Titanium carbides are widely used for cutting tools and grinding wheels, because of their superior physical properties such as high melting temperature, high hardness, high wear resistance, good thermal conductivity and excellent thermal shock resistance. The common synthesizing method for the titanium carbide powders is carbo-thermal reduction from the mixtures of titanium oxide($TiO_2$) and carbon black. The purpose of the present research is to fabricate nano TiC powders using titanium salt and titanium hydride by the mechanochemical process(MCP). The initial elements used in this experiment are liquid $TiCl_4$(99.9%), $TiH_2$(99.9%) and active carbon(<$32{\mu}m$, 99.9%). Mg powders were added to the $TiCl_4$ solution in order to induce the reaction with Cl-. The weight ratios of the carbon and Mg powders were theoretically calculated. The TiC and $MgCl_2$ powders were milled in the planetary milling jar for 10 hours. The 40 nm TiC powders were fabricated by wet milling for 4 hours from the $TiCl_4$+C+Mg solution, and 300 nm TiC particles were obtained by using titanium hydride.

• Journal of the Mineralogical Society of Korea
• /
• v.30 no.3
• /
• pp.127-136
• /
• 2017

High pressure has been applied to check the pressure effect on the powdered $TiO_2$-complex, which was synthesized for ultra-violet rays cutoff and antimicrobial applications. $TiO_2$-complex consists of anatase, rutile and silver chloride. Grain size was determined to be ~34 nm. Both anatase and rutile begin structural phase transitions to $ZrO_2$ (baddeleyite)-type crystal structures at 14~16 GPa, then sustain their phases up to 22.7 GPa. Under decompression to 0.0001 GPa (ambient pressure), rutile transforms to another phase with ${\alpha}-PbO_2$ structure, while anatase retains its high pressure structure upon complete decompression. Silver chloride peaks disappear at the low pressures.

• Journal of the Korean Ceramic Society
• /
• v.22 no.2
• /
• pp.39-43
• /
• 1985

This study presents the results of an overall effort to detemine the applicability of the chemical wet process informing lead titanate electronic ceramics. Although pure lead titanate has not proven to be an important technological materials when prepared via conventional processing procedures this work is interesting as a study of chemical wet processing and a way of preparing pbTiO3 for study. The result obtained from this experiment were as follows ; Optimum synthesis condition which synthesize PbTiO3 by chemical wet process was obtained by firing at 50$0^{\circ}C$ after mixing $Pb(OH)_2$- gel and $Ti(OH)_4$ -gel at 7$0^{\circ}C$ for 4 hours.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.172-172
• /
• 2009

$BaTiO_3$는 perovskite 구조를 가지는 대표적인 강유전체 재료로서 MLCC(Multi Layer Ceramic Capacitor), PTC thermistor등에 널리 사용되어지고 있다. 최근 고용량 MLCC 의 상업화와 함께 나노크기를 갖는 tetragonal phase의 $BaTiO_3$ 입자를 합성하기 위한 다양한 제조방법이 제시되고 있다. 또한 유전 특성과 온도특성 및 신뢰성을 향상시키기 위해 많은 첨가제들이 연구되어지고 있다. 따라서 이 번 연구에서는 선행 연구를 통해 얻어진 high energy mill을 이용한 고상반응법으로 제조된 $BaTiO_3$를 사용하였으며, 제조된 $BaTiO_3$ 분말에 glass frit를 첨가하여 소결온도 및 유전특성의 변화를 관찰하였다. 제조된 $BaTiO_3$ 분말은 200nm이하의 구형화와 균일한 입자크기를 보였으며, 선행연구를 통해 최적화된 glass frit의 양인 2.53wt%를 첨가하였고 1170, 1200, $1230^{\circ}C$에서 소결하여 소결온도에 따른 변화를 관찰하였다. 실험방법으로는 원료를 혼합하기 위하여 24시간 ball-mill을 이용하여 혼합하였으며, $\Phi15$로 성형하여 소결을 진행하였다. 실험진행 결과 모든 시편에서의 비유전율은 glass frit가 첨가되지 않은 조성보다 높게 나타났으며, $1200^{\circ}C$에서 소결한 시편의 비유전율($\varepsilon_r$)은 2300으로 glass frit가 첨가되지 않은 조성과 비교하여 21% 증가하여 최대치를 나타냈다. 또한 소결온도 $1200^{\circ}C$ 이상에서의 모든 시편에서는 95% 이상의 상대밀도를 나타내어, glass frit가 소결조제로써의 역할을 하는 것으로 나타났다. 따라서 본 연구를 통해 glass frit첨가로 인한 소결온도 감소 및 유전특성이 증가하는 것을 확인 하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.259-270
• /
• 1997

Reaction kinetics for the solid-state reaction of $\alpha-Al_2O_3$ with amorphous $TiO_2$ to produce $Al_2TiO_5$ (Tialite) was studied in the temperature range of $1200~1300^{\circ}C$. Rate of kinetic reaction were determined by using $TiO_2$-coated $Al_2O_3$ compact containing 50 mol% $TiO_2$ and heating the reactant mixtures in MgO at definite temperature for various times. Amount of products and unreacted reactants were determined by X-ray diffractometry. Data from the volume fraction and ratio of peak intensities of $\beta-Al_2TiO_5$ indicated that the reaction of $\alpha-Al_2O_3$ with $TiO_2$ to form pseudobrookite starts between 1280 and $1300^{\circ}C$. The activation energy for solid-state reaction was determined by using the Arrhenius equation ; The activation energy was 622.4 kJ/mol.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.2
• /
• pp.77-82
• /
• 2011

The surface of $Li[Ni_{0.35}Co_{0.3}Mn_{0.35}]O_2$ cathode was modified by $[Li,La]TiO_3$ coating using pH controlled coating solution. At low pH values (acidic solution), cathode powders, which is oxides, have a positive surface charge, whereas, they have a negative surface charge at high pH values. As a result, their charge could affect the formation of the coating layer on the surface of cathode powder. To determine the optimal pH value, the surface coating of the pristine powder was carried out at various pH values of the coating solution. The surface morphology of coated samples was characterization by SEM and TEM analyses. Impedance analysis and cyclic voltammogram presented that internal resistance of the cell was dependent upon the pH of coating solution.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.493-497
• /
• 1999

$TiO_2$ Powders were prepared by sol-gel method to testify the characteristics as the photocatalysts. The relationship between processing conditions (R-value (molar ratio of water to alkoxide)), heat treatment temperature, microstructures (crystalline phases), and properties (surface area, particle size) was examined. The optimal conditionsto improve the activity of photocatalyst for photobleaching of dyes in aqueous solution, Were determined.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.141-141
• /
• 2003

Dichlorobenzen과 같은 휘발성 유기물질(Volatile Organic Compound)은 산업폐수 및 폐가스, 폐기물등이 다양한 형태로 대기 중에 존재하면서 심각한 환경문제를 유발시키고 있다 따라서, 본 연구에서는 TiO$_2$에 SiO$_2$를 첨가하여 열처리시 anatase상에서 rutile상으로 전이되는 것을 제어하며 비표면적을 크게 하여 휘발성유기 물질에 대한 광촉매 활성을 증진시키고자 두가지 합성방법, 즉 졸겔 공정과 수열합성 공정을 사용하여, 공정조건을 변화시키면서, 광촉매활성이 가장 우수한 실험조건을 결정하였다.

• Journal of Powder Materials
• /
• v.24 no.6
• /
• pp.472-476
• /
• 2017

Porous W-10 wt% Ti alloys are prepared by freeze-drying a $WO_3-TiH_2$/camphene slurry, using a sintering process. X-ray diffraction analysis of the heat-treated powder in an argon atmosphere shows the $WO_3$ peak of the starting powder and reaction-phase peaks such as $WO_{2.9}$, $WO_2$, and $TiO_2$ peaks. In contrast, a powder mixture heated in a hydrogen atmosphere is composed of the W and TiW phases. The formation of reaction phases that are dependent on the atmosphere is explained by a thermodynamic consideration of the reduction behavior of $WO_3$ and the dehydrogenation reaction of $TiH_2$. To fabricate a porous W-Ti alloy, the camphene slurry is frozen at $-30^{\circ}C$, and pores are generated in the frozen specimens by the sublimation of camphene while drying in air. The green body is hydrogen-reduced and sintered at $1000^{\circ}C$ for 1 h. The sintered sample prepared by freeze-drying the camphene slurry shows large and aligned parallel pores in the camphene growth direction, and small pores in the internal walls of the large pores. The strut between large pores consists of very fine particles with partial necking between them.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.700-704
• /
• 2000

Titanium hydroxide precipitate was obtained by the reaction of 0.5M TiOCl2 and 5M NH4OH solutions, then anatase TiO2 powder with nanotubes was prepared by the digestion of the heat-treated powder in 5M NaOH solution. Nanotube was formed for anatase TiO2 powder digested at 10$0^{\circ}C$ above, and the amount and length of nanotube increased with the digestion temperature. In the case of the powder digested at 15$0^{\circ}C$ for 12h, the formed nanotube was 100~150nm in length, 10~20 nm in diameter, and 2nm in width of the walls on both sides of the nanotube. The powder digested at 15$0^{\circ}C$ for 12h showed the highest specific surface area of 270$m^2$/g.