• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 춘계학술대회 논문집
• /
• pp.335-338
• /
• 1998

The effect of glass flit addition on microwave dielectric properties of BaTiO$_3$-3TiO$_2$ ceramic was studied. Addition of glass frit to this system obtained sintered sample below sintering temperature 105$0^{\circ}C$. At BaTiO$_3$-3TiO$_2$+ g1ass frit 3wt% + BaWO$_4$6 wt%m, this ceramic showed excellent microwave properties of dielectric constant 34, Q$\times$f 8,100, temperature coefficient of resonant frequency 4 ppm/$^{\circ}C$ .

• 한국재료학회지
• /
• 제12권1호
• /
• pp.48-53
• /
• 2002

$Al_2O_3-SiC$ and $Al_2O_3-SiC$-TiC composite powders were prepared by SHS process using $SiO_2,\;TiO_2$, Al and C as raw materials. Aluminum powder was used as reducing agent of $SiO_2,\;TiO_2$ and activated charcoal was used as carbon source. In the preparations of $Al_2O_3-SiC$, the effect of the molar ratio in raw materials, compaction pressure, preheating temperature and atmosphere were investigated. The most important variable affecting the synthesis of $Al_2O_3-SiC$ was the molar ratio of carbon. Unreactants remained in the product among all conditions without compaction. The optimum condition in this reaction was $SiO_2$: Al: C=3: 5: 5.5, 80MPa compaction pressure under Preheating of $400^{\circ}C$ with Ar atmosphere. However there remains cabon in the optimum condition. The effect of $TiO_2$ as additive was investigated in the preparations of $Al_2O_3-SiC$. As a result of $TiO_2$ addition, $Al_2O_3-SiC$-TiC composite powder was prepared. The $Al_2O_3$ powder showed an angular type with 8 to $15{\mu}m$, and the particle size of SiC powder were 5~$10{\mu}m$ and TiC powder were 2 to $5{\mu}m$.

• International Journal of Precision Engineering and Manufacturing
• /
• 제5권1호
• /
• pp.19-26
• /
• 2004

The growth of solid particles in TiC-XC-2vo1.% and TiC-XC-30vo1.% Ni alloys, (where X=Zr, W or Mo) was fitted to the equation of the form $d^3$-${do}^3$=Kt during the liquid phase sintering at 1,673K. Also, the grain growth behavior decreased markedly with the addition of ${MO}_2$C or WC and increased with the addition of zrC. The contiguity was greater in the alloys with a smaller growth rate constant and especially, decreased by increasing the Ni content in the TiC-${MO}_2$C-Ni alloy. In addition, the effect of the addition of carbide on the grain growth of 2 vo1.% Ni alloys was found to be similar to that of 30vo1.% Ni alloys. Consequently, the grain growth mechanism cannot be explained by the usual solution / reprecipitation process, but can be explained in terms of a new growth velocity equation, which includes the effects of contiguous carbide grain boundaries in restricting the overall grain growth, as well as the area of the solid / liquid interface in the alloy.

• 대한전기학회논문지
• /
• 제44권8호
• /
• pp.1068-1074
• /
• 1995

Effect of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ addition on the phase changes and microwave dielectric properties of BaTi $O_{3}$-3Ti $O_{2}$ ceramics were investigated. Addition of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ to BaTi $O_{3}$-3Ti $O_{2}$ resulted in the formation of Ba $Ti_{4}$$O_{9}$, $Ba_{2}$ $Ti_{9}$ $O_{20}$, Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_{3}$, and Ti $O_{2}$ phases. Ba $Ti_{4}$$O_{9}$ phase was gradually transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$. This was identified by XRD and microstructure. As the Ba $Ti_{4}$$O_{9}$ phase transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$ phase, the dielectric constant increased to 37.5. Q*f$_{o}$ value was 40000 at x=0.04, and the temperature coefficient of resonant frequency was +10ppm/.deg. C.C.. C.C.

• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1151-1158
• /
• 1997

Fracture of uni-directional carbon fiber reinforced carbon matrix composite is strongly dependent on the orientation of basal plane in graphite matrix when it is limited within matrix. The orientation of basal planes are vertically stacked to carbon fiber which results in the weakness for applied tensile or shear force in thermosetting resin derived-carbon matrix composite. Microtextural control of the matrix was tried through chemical interaction between metal carbides and furan resin derived-carbon matrix. SiC and TiO2 addition made the orientation disordered. However, porosity increased due to decomposition of SiC. Interfacial bonding could be controlled by TiO2 addition, but carbon fiber was considerably reacted with TiC during thermal treatment higher than 2$600^{\circ}C$. Therefore, it is desirable to control the thermal treatment temperature at which decomposition of SiC was not serious and TiC/C was not formed eutectoid.

• 한국세라믹학회지
• /
• 제31권11호
• /
• pp.1337-1345
• /
• 1994

Glasses in the system of 45CaO-25TiO2-30P2O5 containing 1 mole% of M2O(M=Li, Na, K) were melted and crystallized. And their crystal phases were Ca3(PO4)2, CaTi4(PO4)6, and TiO2. Porous glass-ceramics with skeleton of two crystal phase CaTi4(PO4)6 and TiO2 were prepared by selective leaching of Ca3(PO4)2 with 0.1 N-HCl. Glass transition temperature(Tg) and crystallization temperature(Tc) were decreased by addition of 1 mole% alkali metal oxide. Pore size of porous glass-ceramics was increased with increasing heat treatment temperature and its dependence on heat treatment temperature was decreased with addition of Na2O and K2O. It was found that porous glass-ceramics of parent glass and containing 1mole% M2O(M=Li, Na, K) composition had maximum specific surface area, porosity and maximum of crystallzed phase by heat treatment at 80$0^{\circ}C$, 76$0^{\circ}C$, 78$0^{\circ}C$, 80$0^{\circ}C$ respectively.

• 한국분말재료학회지
• /
• 제4권4호
• /
• pp.291-297
• /
• 1997

Titanium cabide, TiC-x mole% Al composites, and functionally-graded materials (FGMs) of TiC-x mole% Al were synthesized by an electrothermal combustion (ETC) method. TiC-70 mole% Al composite was not ignited by indirect tungsten coil heating, but can be synthesized by an electrothermal combustion. The velocity of the combustion wave decreased with increasing addition of Al and increased with an increase in the applied electric field. Functionally-graded TiC-Al materials were made from reactant layers with compositions of Ti+C+x moles Al with x ranging from zero to 70 by an electrothermal combustion. In the FGM products a nearly linear change in composition in the graded region was observed in samples with 0$\leq$ x $\leq$ 70 with x being the mole% Al.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.131-134
• /
• 2003

[ $ZnWO_4$ ] shows excellent frequency selectivity due to its high quality factor($Q{\times}f$) at microwave frequencies. However, in order to use $ZnWO_4$ as multilayered wireless communication components, its other properties such as sintering temperature($1050^{\circ}C$), ${\tau}_f$ ($-70ppm/^{\circ}C$) and ${\varepsilon}_r(15.5)$ should be modified. In present study, $TiO_2$ and LiF were used to improve the microwave dielectric and sintering properties of $ZnWO_4$. $TiO_2$ additions to $ZnWO_4$ changed ${\tau}_f$ from negative to positive value, and also increased ${\varepsilon}_r$ due to its high ${\tau}_f$ ($+400ppm/^{\circ}C$) and ${\varepsilon}_r$(100). At 20 mol% $TiO_2$ addition, ${\tau}_f$ was controlled to near zero $ppm/^{\circ}C$ with ${\varepsilon}_r=19.4$ and $Q{\times}f=50000GHz$. However, the sintering temperature was still high to $1100^{\circ}C$. LiF addition to the $ZnWO_4+TiO_2$ mixture was greatly reduced the sintering temperature from $1100^{\circ}C$ to $850^{\circ}C$ due to liquid phase formation. Also LiF addition decreased the ${\tau}_f$ value due to its high negative ${\tau}_f$ value. Therefore, by controlling the $TiO_2$ and LiF amount, temperature stable LTCC material in the $ZnWO_4$-TiO_2-LiF$ system could be fabricated.

• 한국분말재료학회지
• /
• 제28권5호
• /
• pp.381-388
• /
• 2021

Zirconia has excellent mechanical properties, such as high fracture toughness, wear resistance, and flexural strength, which make it a candidate for application in bead mills as milling media as well as a variety of components. In addition, enhanced mechanical properties can be attained by adding oxide or non-oxide dispersing particles to zirconia ceramics. In this study, the densification and mechanical properties of YSZ-TiC ceramic composites with different TiC contents and sintering temperatures are investigated. YSZ - x vol.% TiC (x=10, 20, 30) system is selected as compositions of interest. The mixed powders are sintered using hot pressing (HP) at different temperatures of 1300, 1400, and 1500℃. The densification behavior and mechanical properties of sintered ceramics, such as hardness and fracture toughness, are examined.

• 대한금속재료학회지
• /
• 제56권12호
• /
• pp.854-860
• /
• 2018

In spite of the many attractive properties of (W,Ti)C, its low fracture toughness limits its wide application. To improve the fracture toughness generally a second phase is added to fabricate a nanostructured composite. In this regard, graphene was considered as the reinforcing agent of (W,Ti)C. (W,Ti)C-graphene composites that were sintered within 2 min using pulsed current activated heating under a pressure of 80 MPa. The rapid consolidation method allowed retention of the nano-scale microstructure by blocking the grain growth. The effect of graphene on the hardness and microstructure of the (W,Ti)C-graphene composite was studied using a Vickers hardness tester and FE-SEM. The grain size of (W,Ti)C was reduced remarkably by the addition of graphene. Furthermore, the hardness decreased and the fracture toughness improved with the addition of graphene.