• Journal of Powder Materials
• /
• v.27 no.1
• /
• pp.52-57
• /
• 2020

In this study, we report the microstructure and characterization of Ta₂₀Nb₂₀V₂₀W₂₀Ti₂₀ high-entropy alloy powders and sintered samples. The effects of milling time on the microstructure and mechanical properties were investigated in detail. Microstructure and structural characterization were performed by scanning electron microscopy and X-ray diffraction. The mechanical properties of the sintered samples were analyzed through a compressive test at room temperature with a strain rate of 1 × 10^-4 s^-1. The microstructure of sintered Ta₂₀Nb₂₀V₂₀W₂₀Ti₂₀ high-entropy alloy is composed of a BCC phase and a TiO phase. A better combination of compressive strength and strain was achieved by using prealloyed Ta₂₀Nb₂₀V₂₀W₂₀Ti₂₀ powder with low oxygen content. The results suggest that the oxide formed during the sintering process affects the mechanical properties of Ta₂₀Nb₂₀V₂₀W₂₀Ti₂₀ high-entropy alloys, which are related to the interfacial stability between the BCC matrix and TiO phase.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.5
• /
• pp.181-188
• /
• 2008

A.C. impedance properties of HA/Ti compound layer coated Ti-30Ta-($3{\sim}15$)Nb alloys have been studied by electrochemical method. Ti-30Ta binary alloys contained 3, 7, 10 and 15 wt% Nb were manufactured by the vacuum furnace system. And then specimen was homogenized at $1000^{\circ}C$ for 24 hrs. The sample was cut and polished for corrosion test and coating. It was coated with HA/Ti compound layer by magnetron sputter. The non-coated and coated morphology of Ti alloy were analyzed by X-ray diffractometer (XRD), energy X-ray dispersive spectroscopy (EDX) and filed emission scanning electron microscope (FE-SEM). The corrosion behaviors were investigated using A.C. impedance test (PARSTAT 2273, USA) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. Ti-30Ta-($3{\sim}15\;wt%$)Nb alloys showed the ${\alpha}+{\beta}$ phase, and $\beta$ phase peak was predominantly appeared in the case of increasingly Nb contents. The microstructures of Ti alloy were transformed from needle-like structure to equiaxed structure as Nb content increased. From the analysis of coating surface, HA/Ti composite surface uniformed coating layer with 750 nm thickness. The growth directions of film were (211), (112), (300) and (202) for HA/Ti composite coating on the surface after heat treatment at $550^{\circ}C$, whereas, the growth direction of film was (110) for Ti coating. The polarization resistance ($R_p$) of HA/Ti composite coated Ti-alloys were higher than those of the Ti and HA coated samples in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. Especially, corrosion resistance of Ti-Ta-Nb system increased as Nb content increased.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.10a
• /
• pp.67-68
• /
• 2006

• Corrosion Science and Technology
• /
• v.8 no.2
• /
• pp.62-67
• /
• 2009

Ti and Ti-alloys have good biocompatibility, appropriate mechanical properties and excellent corrosion resistance. However, the widely used Ti-6Al-4V is found to release toxic ions (Al and V) into the body, leading to undesirable long-term effects. Ti-6Al-4V has much higher elastic modulus (100 GPa) than cortical bone (20 GPa). Therefore, titanium alloys with low elastic modulus have been developed as biomaterials to minimize stress shielding. The electrochemical behavior of surface-modified and MC3T3-E1 cell-cultured Ti-30(Nb,Ta) alloys with low elastic modulus have been investigated using various electrochemical methods. Surfaces of test samples were treated as follows: $0.3{\mu}m$ polished; $25{\mu}m$, $50{\mu}m$ and $125{\mu}m$ sandblasted. Specimen surfaces were cultured with MC3T3-E1 cells for 2 days. Average surface roughness ($R_a$) and morphology of specimens were determined using a surface profilometer, OM, and FE-SEM. Corrosion behavior was investigated using a potentiostat(EG&G PARSTAT 2273), and electrochemical impedance spectroscopy was performed (10 mHz to 100 kHz) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The microstructures of the Ti-30(Ta,Nb) alloys had a needle-like appearance. The $R_a$ of polished Ti-30Ta and Ti-30Nb alloys was lower than that of the sandblasted Ti alloy. Cultured cells displayed round shapes. For polished alloy samples, cells were well-cultured on all surfaces compared to sandblasted alloy samples. In sandblasted and cell-cultured Ti-30(Nb,Ta) alloy, the pitting potential decreased and passive current density increased as $R_a$ increased. Anodic polarization curves of cell-cultured Ti alloys showed unstable behavior in the passive region compared to non-cell-cultured alloys. From impedance tests of sandblasted and cell-cultured alloys, the polarization resistance decreased as $R_a$ increased, whereas, $R_a$ for cell-cultured Ti alloys increased compared to non-cell-cultured Ti alloys.

• Korean Journal of Materials Research
• /
• v.16 no.5
• /
• pp.277-284
• /
• 2006

The alloys were prepared by a non-consumable vacuum arc melting and homogenized at $1050^{\circ}C$ for 24 hrs. Two kind of surface modifications were performed alkali treatment in 5.0M NaOH solution subsequent and heat treatment in vacuum furnace at $600^{\circ}C$, and were oxidizing treatment at the temperature range of 550 to $750^{\circ}C$ for 30 minutes. After surface modification, these samples were soaked in SBF which consists of nearly the same ion concentration as human blood plasma. Cytotoxicity tests were performed in MTT assay treated L929 fibroblast cell culture, using indirect methods. A porous and thin activated layer was formed on Titanium and Ti-8Ta-3Nb alloy by the alkali treatment. A bone-like hydroxyapatite was nucleated on the activated porous surfaces during the in vitro test. However, Ti-8Ta-3Nb alloys showed better bioactive properties than Titanium. According to XRD results, oxide layers composed of mostly $TiO_2$(rutile) phases. Cytotoxicity test also revealed that moderate oxidation treatment lowers cell toxicity and Ti-8Ta-3Nb alloy showed better results compared with Titanium.

• Journal of Korea Foundry Society
• /
• v.28 no.3
• /
• pp.124-128
• /
• 2008

The nitride layer was formed on Ti and Ti-10 wt.%Ta-10 wt.%Nb alloy by a plasma nitriding method. Temperature was selected as the main experimental parameter for plasma nitriding. XRD, EDX, and hardness test were employed to analyze the evolution and material properties of the layer. The SEM observation of TiN nitride layer revealed that the thickness of nitride layer tended to increase with increasing temperature. ${\delta}-TiN$, ${\varepsilon}-Ti_{2}N$ and ${\alpha}-Ti$ phases were detected by XRD analysis and the preferred orientation of TiN nitride layer was obviously observed at (220) plane with increasing temperature. From XRD analysis after step polishing the nitride specimens treated at $850^{\circ}C$, as polishing from the surface, TiN and $Ti_{2}N$ phases decreased gradually. After polishing the surface by $4{\um}m$, a small amount of $Ti_{2}N$ and ${\alpha}-Ti$ phases were observed. The adhesive strength test result indicated that adhesive strength increased with increasing temperature.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.137-137
• /
• 2015

The purposed of this work was to observe hydroxyapatite precipitation phenomena on micro-pore formed Ti-Nb alloy by PEO technique. The Ti-30Nb and Ti-30Ta alloys were remelted at least ten times in order to avoid inhomogeneity, and then cylindrical specimens (diameter 10 mm, thickness 4 mm) were cut by using laser from cast ingots of the Ti alloys. Heat treatment was carried out at $1050^{\circ}C$ for 2 h for homogenization in argon atmosphere. The morphologic change of the alloys were examined by X-ray diffractometer (XRD) and field emission scanning electron microscopy (FE-SEM).

• Journal of Mechanical Science and Technology
• /
• v.20 no.1
• /
• pp.13-18
• /
• 2006

Ti-8Ta-3Nb, as a new biomaterial, was prepared by cast and swaging process. Their deformation behavior of Ti-8Ta-3Nb alloy has been characterized on the basis of its flow stress variation obtained from the true strain rate compression testing in the temperature of $700-900^{\circ}C$ and strain rate of $0.001-10\;s^{-1}$. At the strain rates lower than $0.1\;s^{-1}$ and the all temperature ranges which consist of two phase ${\alpha}+{\beta}$ as well as single ${\beta}$ phase fields, the flow curves show a small degree of flow softening behavior. In contrast, the shapes of the flow curves at other strain rates indicate unstable behavior. The shapes of the flow curves were similar in both as-cast and swaged specimen as well as in both ${\alpha}+{\beta}$ phase and ${\beta}$ phase. The flow stress data did not obey the kinetic rate equation over the entire regime of testing but a good fit has been obtained in the intermediate range of temperatures ($750-850^{\circ}C$). In this range, a stress exponent value of about 7.7 in as-cast specimens and about 6.2 in swaged specimens with an apparent activation energy of about 300 kJ/mol and about 206 kJ/mol respectively have been evaluated.

• Toxicological Research
• /
• v.23 no.4
• /
• pp.331-339
• /
• 2007

Titanium or titanium alloy is a widely used implant material according to its certified biocompatibility, sufficient strength and ready availability. The purpose of this study was to evaluate the relative biocompatibility of titanium and titanium alloy specimens (Ti-29Nb-13Ta, TiNb and Ti-6Al-4V, Ti64) using in vivo and in vitro methods. For in vivo experiment, the specimens were implanted in the abdominal subcutaneous region of female mice for 2 and 4 weeks. The reaction of connective tissue to specimens was evaluated histologically. The specimens were encapsulated by fibrous connective tissue consisting of fibroblast, fibrocyte and other cells including neutrophil, macrophage, giant multinucleated cell and unidentified cells. Some newly formed blood vessels were located in the fibrous capsule surrounding the implant. Cell types and the thickness of fibrous capsules were examined quantitatively. Most of cell types located in the fibrous capsule were fibroblasts and fibrocytes. The average thickness of fibrous capsules for the TiNb specimens was much thinner than that of the titanium alloy, Ti64. The thickness of the fibrous capsule around all titanium specimens decreased at 4 weeks compared to 2 weeks post-implantation. The biocompatibility of titanium and titanium alloy specimens were also investigated in in vitro method using alkaline phosphatase from MG-63 cells. Alkaline phosphatase activity of the TiNb specimen showed higher activity than the titanium alloy, Ti64. In conclusion, the TiNb alloy with thin capsule thickness in vivo and high alkaline phosphatase activity in vitro will be of considerable use in biomedical applications.

• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.3
• /
• pp.145-152
• /
• 2023

β titanium alloys containing β stabilizing elements such as V, Nb, Ta, Mo and Fe are widely used etc, due to their excellent specific strength, corrosion resistance, fatigue strength and easy formability. New metastable β titanium alloys are developed containing low-cost elements (Mo and Fe) in this study. Fe element is a strong β-stabilizer which can affect the mechanical and electrochemical properties of Ti-5Mo-xFe (x = 1, 4 wt%) alloys. These properties were analyzed in connection with microstructure and phase distribution. Ti-5Mo-4Fe alloy showed higher compression yield stress and maximum stress than Ti-5Mo-1Fe alloy due to solid-solution hardening and grain refinement hardening effect. As Fe element increased, Fe oxide formation and reduction of ${\bar{Bo}}$ (bond order) value affect the decrease of corrosion resistance. Ti-5Mo-xFe alloys were more excellent than Ti-6Al-4V ELI alloy.