• Bulletin of the Korean Chemical Society
• /
• v.33 no.9
• /
• pp.2910-2916
• /
• 2012

Cadmium sulphide (CdS) nanorods were prepared by a single precursor thermal decomposition (SPTD) method. The formation of CdS nanorods and their structure, morphology and elemental composition were studied by means of FT-IR, XRD, FE-SEM, HR-TEM and EDAX analysis. Photoluminescence (PL) and lifetime measurements were recorded to study the luminescence properties of the material. The PL spectrum of the CdS nanorods showed one broad peak and four shoulders and the cause for this emission was discussed. The PL emissions from the band edge and deep trap state of the CdS nanorods were studied by lifetime measurements. Further, the synthesized CdS nanorods showed an increase in efficiency of photocatalytic degradation of methylene blue (MB) and rhodamine B (RhB). The increase in the photocatalytic activity was attributed to the mixed phase of the CdS nanorods.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.9
• /
• pp.2657-2662
• /
• 2013

Multiwalled carbon nanotube (MWCNT)-g-poly (aniline-co-2,5-diaminobenzenesulfonic acid) (DABSA) reinforced Nafion$^{(R)}$ nanocomposite membranes were prepared and characterized for direct methanol fuel cells (DMFCs). The nanocomposite membranes with approximately $90{\mu}m$ thickness were prepared by the water assisted solution casting method. To evaluate the properties of nanocomposite membranes for DMFC applications, the nanocomposite membranes were characterized by methanol and water uptake, thermal stability, and ion exchange capacity (IEC). Furthermore, oxidative stability measurements in terms of the hydrogen peroxide decomposition rate that represent the oxidative stability of the membranes were examined. The methanol uptake values of the nanocomposite membranes were dramatically decreased compared to the cast Nafion$^{(R)}$ membranes. The IEC values of the nanocomposite membranes were increased about 30% compared to the cast Nafion$^{(R)}$ membrane.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.5
• /
• pp.246-249
• /
• 2013

Graphene was obtained on Cu foil by thermal decomposition method. A gas mixture of $H_2$ and $CH_4$ and an ambient annealing temperature of $1,000^{\circ}C$ were used during the deposition for 30 Min., and for the transfer onto $SiO_2/Si$ and Si substrates. The physical properties of graphene were investigated with regard to the effect ofnitrogen atom doping and the various substrates used. The G/2D ratio decreased when the graphene became monolayer graphene. The graphene grown on $SiO_2/Si$ substrate showed a low intensity of the G/2D ratio, because the polarity of the $SiO_2$ layer improved the quality of graphene. The intensity of the G/2D ratio of graphene doped with nitrogen atoms increased with the doping time. The quality of graphene depended on the concentration of the nitrogen doping and chemical properties of substrates. High-quality monolayer graphene was obtained with a low G/2D ratio. The increase in the intensity of the G/2D ratios corresponded to a blue shift in the 2D peaks.

• Smart Structures and Systems
• /
• v.22 no.1
• /
• pp.105-120
• /
• 2018

In this paper, the nonlinear free and forced vibration responses of sandwich nano-beams with three various functionally graded (FG) patterns of reinforced carbon nanotubes (CNTs) face-sheets are investigated. The sandwich nano-beam is resting on nonlinear Visco-elastic foundation and is subjected to thermal and electrical loads. The nonlinear governing equations of motion are derived for an Euler-Bernoulli beam based on Hamilton principle and von Karman nonlinear relation. To analyze nonlinear vibration, Galerkin's decomposition technique is employed to convert the governing partial differential equation (PDE) to a nonlinear ordinary differential equation (ODE). Furthermore, the Multiple Times Scale (MTS) method is employed to find approximate solution for the nonlinear time, frequency and forced responses of the sandwich nano-beam. Comparison between results of this paper and previous published paper shows that our numerical results are in good agreement with literature. In addition, the nonlinear frequency, force response and nonlinear damping time response is carefully studied. The influences of important parameters such as nonlocal parameter, volume fraction of the CNTs, different patterns of CNTs, length scale parameter, Visco-Pasternak foundation parameter, applied voltage, longitudinal magnetic field and temperature change are investigated on the various responses. One can conclude that frequency of FG-AV pattern is greater than other used patterns.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1501-1506
• /
• 1994

The precipitate of FeCl2.4H2O and NaOH, Fe(OH)2 was rapidly made to oxidize by H2O2 to prepare $\delta$-FeOOH. The particle size, surface and morphology of $\delta$-FeOOH, and the shape and structure of thermally decomposed $\delta$-FeOOH were investigated by the use of high resolution STEM. $\delta$-FeOOH prepared under the condition of reaction temperature of Fe(OH)2 at 4$0^{\circ}C$, [OH-][Fe2+]=5 and aging time of 2 hr Fe(OH)2, had 630$\AA$ mean particle size, 4~5 aspect ratio, 20.8 emu/g saturation magnetization and 210 Oe coercivity. The edges of $\delta$-FeOOH were inclined to (001) about 41$^{\circ}$, 60$^{\circ}$ and coincident with (102), (101) respectively. When $\delta$-FeOOH was thermally decomposed at 25$0^{\circ}C$ for 2 hr in vacuo, which had micropores of 0.9 nm thickness and crystallites of 2.4 nm thickness. (001)hex, [10]hex. of $\delta$-FeOOH parallel with (001)hex, [100]hex. of $\alpha$-Fe2O3 respectively. This showed three dimensional topotaxial structure transition, which was investigated by SADP (Selected Area Diffraction Pattern) of STEM.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.8
• /
• pp.2367-2370
• /
• 2014

"Cat's eye"-shaped $[^{57}Co]CoO@SiO_2$ core-shell nanostructure was prepared by the reverse microemulsion method combined with radioisotope technique to investigate a potential imaging agent for a single photon emission computed tomography (SPECT) in nuclear medicine. The core cobalt oxide nanorods were obtained by thermal decomposition of $Co-(oleate)_2$ precursor from radio isotope Co-57 containing cobalt chloride and sodium oleate. The $SiO_2$ coating on the surface of the core cobalt oxide nanorods was produced by hydrolysis and a condensation reaction of tetraethylorthosilicate (TEOS) in the water phase of the reverse microemulsion system. In vivo test, micro SPECT image was acquired with nude mice after 30 min of intravenous injection of $[^{57}Co]CoO@SiO_2$ core-shell nanostructure.

• Journal of Power System Engineering
• /
• v.19 no.3
• /
• pp.22-28
• /
• 2015

A compression ignition type of diesel engine makes fuel efficiency better and $CO_2$ in the exhaust gas lower. Also it is suitable to apply alternative fuels(blended fuel) to the engine. The objective of this study is the emissions reduction of diesel engine with EF(Emulsified fuel). The emulsified fuel consists of diesel and peroxide($H_2O_2$) and Soot reduction without worsening of NOx emissions can be achieved by using thermal decomposition of the peroxide, i.e. the chemical effect of the OH radical in actual engine. For manufacturing emulsified fuel, a surfactant which is comprised of span 80 and tween 80 mixed as 9:1, was mixed with a fixed with 3% of the total volume in the emulsion fuel. In addition, considering the mixing ratio of the surfactant, the mixing ratio of $H_2O_2$ in the emulsified fuel was set as EF0, EF2, EF12, EF22, EF32, and EF42, respectively. Consequently, this study aims to obtain the optimization of fuel design(mixing) for the emulsified fuel applying to the diesel engine.

• Textile Coloration and Finishing
• /
• v.20 no.1
• /
• pp.44-47
• /
• 2008

Organic semi-conductive materials have characteristics such as the advantages of easy formability, low-cost and diversity along with moderate semi-conductive properties. In this paper, we developed a flexible organic-inorganic hybrid solar cell fiber. First, we made a solar cell on the glass and attached the solar cell on the glass fiber similarly. In the latter case, thermal deposition method was employed in order to effectively apply ITO onto fiber surface. The amount of ITO was controlled by varying the temperature from 25, 150 to $300^{\circ}C$. Optimum result was obtained at $150^{\circ}C$ where maximize the deposition amount without significant decomposition of ITO. Despite of maximum open circuit voltage of 0.39V, the resulting current was quite unstable and weak, limiting realistic applications. It was, however, concluded that the flexible solar cell fiber developed showed a possibility of low-weight application from functional clothing for military to space suit mainly due to flexibility and thus wear ability.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.1
• /
• pp.141-146
• /
• 2014

A series of bimetallic Cu-Zn/$SiO_2$ catalysts were prepared via thermal decomposition of the as-synthesized $CuZn(OH)_4(H_2SiO_3)_2{\cdot}nH_2O$ hydroxides precursors. This highly dispersed Cu-solid base catalyst is extremely effective for hydrogenation of ethyl acetate to ethanol. The reduction and oxidation features of the precursors prepared by coprecipitation method and catalysts were extensively investigated by TGA, XRD, TPR and $N_2$-adsorption techniques. Catalytic activity by ethyl acetate hydrogenation of reaction temperatures between 120 and $300^{\circ}C$, different catalyst calcination and reduction temperatures, different Cu/Zn loadings have been examined extensively. The relation between the performance for hydrogenation of ethyl acetate and the structure of the Cu-solid base catalysts with Zn loading were discussed. The detected conversion of ethyl acetate reached 81.6% with a 93.8% selectivity of ethanol. This investigation of the Cu-Zn/$SiO_2$ catalyst provides a recently proposed pathway for ethyl acetate hydrogenation reaction to produce ethanol over Cu-solid base catalysts.

• Korean Journal of Materials Research
• /
• v.24 no.3
• /
• pp.140-144
• /
• 2014

The contact mechanism of devices is usually researched at electrode contacts. However, the contact between a dielectric and channel at the MOS structure is more important. The graphene was used as a channel material, and the thin film transistor with MOS structure was prepared to observe the contact mechanism. The graphene was obtained on Cu foil by the thermal decomposition method with $H_2$ and $CH_4$ mixed gases at an ambient annealing temperature of $1000^{\circ}C$ during the deposition for 30 min, and was then transferred onto a $SiO_2/Si$ substrate. The graphene was doped in a nitrogen acidic solution. The chemical properties of graphene were investigated to research the effect of nitric atoms doping. The sheet resistance of graphene decreased after nitrogen acidic doping, and the sheet resistance decreased with an increase in the doping times because of the increment of negative charge carriers. The nitric-atom-doped graphene showed the Ohmic contact at the curve of the drain current and drain voltage, in spite of the Schottky contact of grapnene without doping.