• Journal of Powder Materials
• /
• v.17 no.2
• /
• pp.142-147
• /
• 2010

The ultrafine titanium carbonitride ($TiC_xN_y$) particles below 100 nm in mean size, including various carbon and nitrogen contents (x=0.55~0.9, y=0.1~0.5), were successfully synthesized by new Mg-thermal reduction process. Nanostructured sub-stoichiometric titanium carbide ($TiC_x$) particles were initially produced by the magnesium reduction of gaseous $TiCl_4+x/2C_2Cl_4$ at $890^{\circ}C$ and post heat treatments in vacuum were performed for 2 hrs to remove residual magnesium and magnesium chloride mixed with $TiC_x$. Finally, well C/N-controled $TiC_xN_y$ phases were successfully produced by nitrification heat treatment under normal $N_2$ gas atmosphere at $1150^{\circ}C$ for 2 hrs. The values of purity, mean particle size and oxygen content of produced particles were about 99.3%, 100 nm and 0.2 wt.%, respectively.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.691-697
• /
• 1989

Fine TiO2 and BaTiO3 powders having spherical particles were synthesized by ultrasonic spray pyrolysis of alcoholic solution of metal alkoxide in an electric furnace heated at 400-90$0^{\circ}C$. Microstructure and composition of particles synthesized were observed by TEM and XRD respectively. Spectific surface area of powders synthesized was examined through BET specific surface area measurement. TEM observation revealed that the particle size did not change irrespective of pyrolysis temperature but decreased according to the increase of concentration and spherical particle was consisted of primary particles of about 0.02${\mu}{\textrm}{m}$. As for BaTiO3 powder, the ratio of Ti/Ba was 0.987 by EDX analysis.

• Journal of Powder Materials
• /
• v.26 no.6
• /
• pp.481-486
• /
• 2019

Iron oxides currently attract considerable attention due to their potential applications in the fields of lithiumion batteries, bio-medical sensors, and hyperthermia therapy materials. Magnetite (Fe₃O₄) is a particularly interesting research target due to its low cost, good biocompatibility, outstanding stability in physiological conditions. Hydrothermal synthesis is one of several liquid-phase synthesis methods with water or an aqueous solution under high pressure and high temperature. This paper reports the growth of magnetic Fe₃O₄ particles from iron powder (spherical, <10 ㎛) through an alkaline hydrothermal process under the following conditions: (1) Different KOH molar concentrations and (2) different synthesis time for each KOH molar concentrations. The optimal condition for the synthesis of Fe₃O₄ using Fe powders is hydrothermal oxidation with 6.25 M KOH for 48 h, resulting in 89.2 emu/g of saturation magnetization at room temperature. The structure and morphologies of the synthesized particles are characterized by X-ray diffraction (XRD, 2θ = 20°-80°) with Cu-kα radiation and field emission scanning electron microscopy (FE-SEM), respectively. The magnetic properties of magnetite samples are investigated using a vibrating sample magnetometer (VSM). The role of KOH in the formation of magnetite octahedron is observed.

• Journal of the Korean Ceramic Society
• /
• v.44 no.12
• /
• pp.690-695
• /
• 2007

Scandia stabilized zirconia (ScSZ) is adapted for electrolyte material of solid oxide fuel cell (SOFC) because of its high ionic conductivity and chemical stability. ScMnSZ1 powder having a composition of $((ZrO_2)_{0.89}(Sc_2O_3)_{0.1}(MnO_2)_{0.01})$ is synthesized by ultrasonic spray pyrolysis (USP) method. Porous ScMnSZ1 powder is obtained by using a pore forming agent. Microstructure and morphology, particle size distribution of porous powder synthesized with 3wt% pore forming agent are investigated. Sintered ScMnSZ1 sample with ground fine powder are also investigated their microstructure and electrical conductivity. The electrical conductivity of sintered ScMnSZ1 samples with ground fine powder was 0.082 S/cm, 0.127 S/cm and 0.249 S/cm at $750^{\circ}C$, $800^{\circ}C$ and $900^{\circ}C$, respectively.

• Resources Recycling
• /
• v.26 no.1
• /
• pp.16-21
• /
• 2017

This paper relates to the synthesis of a source powder for SiC crystal growth. ${\beta}-SiC$ powders are synthesized at high temperatures (>$1400^{\circ}C$) by a reaction between silicon powder and carbon powder. The reaction is carried out in a graphite crucible operating in a vacuum ambient (or Ar gas) over a period of time sufficient to cause the Si+C mixture to react and form poly-crystalline SiC powder. End-product characterizations are pursued with X-ray diffraction analysis, SEM/EDS, particle size analyzer and ICP-OES. The purity of the end-product was analyzed with the Korean Standard KS L 1612.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.593-600
• /
• 1989

Fine spinel powder was prepared from the Mg-Al double alkoxide synthesized using magnesium powder, aluminum foil and sec-butyl alcohol. This powder was compared with powder prepared by mixing two commercial alkoxides. The spinelization was started at 50$0^{\circ}C$ and was almost completed at 100$0^{\circ}C$ with a good crystallinity in the double alkoxide system. In mixed alkoxide system, homogeneous spinel powder was not obtained and MgO existed as a second phase because of solubility and hydrolysis rate differences of two alkoxides. The relative density of specimen prepared by double alkoxide was 99% and specimen prepared by mixed alkoxide was 95%. The modulus of rupture of specimens prepared by double alkoxide and mixed alkoxide was 49.9kg/$\textrm{mm}^2$ and 41.6kg/$\textrm{mm}^2$, respectively.

• Carbon letters
• /
• v.14 no.4
• /
• pp.206-209
• /
• 2013

Nanocomposites comprised of graphene oxide (GO) nanosheets and magnesium oxide (MgO) nanoparticles were synthesized by a sol-gel process. The synthesized samples were studied by X-ray powder diffraction, atomic force microscopy, transmission electron microscopy, and energy-dispersive X-ray analysis. The results show that the MgO nanoparticles, with an average diameter of 70 nm, are decorated uniformly on the surface of the GOs. By controlling the concentration of the MgO precursors and reaction cycles, it was possible to control the loading density and the size of the resulting MgO particles. Because the MgO particles are robustly anchored on the GO structure, the MgO/GOs nanocomposites will have future applications in the fields of adsorption and chemical sensing.

• Journal of the Korean Ceramic Society
• /
• v.42 no.5 s.276
• /
• pp.314-318
• /
• 2005

The effect of reaction parameters in the characteristic of $Pb(Zr_{0.52}Ti_{0.48})O_3$ (below nominal PZT) powders by SHS was investigated in this study. In the preparation of PZT, the effect of starting material contents, pressure, additive on phase fraction and morphology was investigated respectively. The optimum condition of PZT powders were prepared by SHS is $0.37Pb_3O_4+0.52ZrO_2+0.48TiO_2+0.35KClO_3+0.5C,\;(P_{Ar}= 50 atm)$. The PZT powder synthesized in this condition had an spherical shape and the particle size of 0.8$\mu$m.

• Korean Journal of Materials Research
• /
• v.27 no.5
• /
• pp.248-254
• /
• 2017

In the present work, graphene powder was synthesized by laser scribing method. The resultant flexible light-scribed graphene is very appropriate for use in micro-supercapacitors. The effect of the laser scribing process in reducing graphene oxide (GO) was investigated. GO was synthesized using a chemical mixture of GO solution; then, it was coated onto a LightScribe DVD disk and laser scribed to reduce GO and create laser-scribed graphene (LSG). The CV curves of pristine rGO at various scan rates showed that the ultimate product possesses the ability to store energy at the supercapacitor level. Charge-discharge curves of pristine rGO at two different current densities indicated that the specific capacitance ($C_m$) increases due to the reduction of the discharge current density. Finally, the long-term charge-discharge stability of the LSG was plotted and indicates that the specific capacitance decreases very slightly from its primary capacitance of ${\sim}10F\;cm^{-3}$ and that the cyclic stability is favorable over 1000 cycles.

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.167-170
• /
• 1989

Al2O3/SiC composite-material was synthesized by the birth-spread mechanism through the carbothermal reduction reaction of SiO2 in Ha-Dong Kaolin with carbon powder under H2 gas atmosphere at 1300~140$0^{\circ}C$. Average diameter of synthesized SiC whiskers were 1${\mu}{\textrm}{m}$ and aspect ratio (c/a) was 10~100. Al2O3 particles and SiC whiskers were mixed homogeneously in the reacted pellet.