• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.11
• /
• pp.848-853
• /
• 2010

We have grown GaN nanowires by the low pressure MOCVD method on Ni deposited oxidized Si surface and have established optimum conditions by observing surface microstructure and its photoluminescence. Optimum growth temperature of $880^{\circ}C$, growth time of 30 min, TMG source flow rate of 10 sccm have resulted in dense nanowires on the surface, however further increase of growth time or TMG flow rate has not increased the length of nanowire but has formed nanocrystals. On the contrary, the increase of ammonia flow has increased the length of nanowires and the coverage of nanowire over the surface. The shape of nanowire is needle-like with a Ni droplet at its tip; the length is tens of micron with more than 40 nm in diameter. Low temperature photoluminescence obtained from the sample at optimum growth condition has revealed several peaks related to exciton decay near band-edge, but does not show any characteristic originated from one dimensional quantum confinement. Strong and broad luminescence at 2.2 eV is observed from dense nanowire samples and this suggests that the broad band is related to e-h recombination at the surface state in a nanowire. The current result is implemented to the nanowire device fabrication by nanowire bridging between micro-patterned neighboring Ni catalysis islands.

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.3 no.1
• /
• pp.18-25
• /
• 1978

The 1/f noise spectrum of short-circuited output drain current due to the Shockley-Read-Hal] recombination centers with a single lifetime in homogeneous nondegenerate MOS-field effcte transtors with n-type channel is calculated under the assumptions that the quasi-Fermi level for the carriers in each energy band can not be defined if we include the fluctuation for time varying quantities. and so 1/f noise is a majority carrier effect. Under these assumptions the derived 1/f noise in this paper show some essential features of the 1/f noise in MOS-field effect transistors. That is, it has no lowfrequency plateau and is proportionnal to the channel cross area A and to the driain bias voltage Vd and inversely proportional to the channel length L3 in MOS field effect transistors. This model can explain the discrepancy between the transition frequency of the noise spectrum from 1/f- response to 1/f2 and the frequency corresponding to the relaxation time related to the surface centers in p-n junction diodes. In this paper the results show that the functional form of noise spectrum is greatly influenced by the functional forms of the electron capture probability cn (E) and the relaxation time r (E) for scattering and the case of lattice scattering show to be responsible for the 4 noise in MOS fold effect transistors. So we canconclude that the source of 1/f noise is due to lattice scattering.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.21 no.1
• /
• pp.62-70
• /
• 1984

N+NPP+ HLEBSF (high low emitter back surface field) solar cells which have N+N high low junction in the emitter as well as N+PP+ BSF cells were designed and fabricated by using <111> oriented P type Si wafers with the resistivity of 10$\Omega$/$\textrm{cm}^2$ and the thickness of 13-15 mil. Physical parameters (impurity concentration, thickness) at each region of N+PP+ and N+NPP+ cell were made equally through same masks and simultaneous process except N region of HLEBSF cell to investigate the high low emitter junction effect for efficiency improvement. Under the light intensity of 100 mW/$\textrm{cm}^2$, total area (active area) conversion efficiency were typically 10.94% (12.16%) for N+PP+ BSF cells and 12.07% (13.41%) for N+N PP+ cells. Efficiency improvement of N+NPP+ cell which has high low emitter Junction structure is resulted from the suppression of emitter recombination current and the increasement of open circuit voltage (Voc) and short circuit current (Ish) by removing heavy doping effects occurring in N+ emitter region.

• Current Photovoltaic Research
• /
• v.3 no.4
• /
• pp.130-134
• /
• 2015

The high efficiency cell research processes through the KF post deposition treatment (PDT) of the $Cu(In,Ga)Se_2(CIGS)$ thin film has been very actively progress. In this study, it CIGS thin film deposition process when KF PDT 300 to the processing temperature, 350, $400^{\circ}C$ changed to soda-lime glass (SLG) efficiency of the CIGS thin film characteristics, and solar cell according to Na presence of diffusion from the substrate the effects were analyzed. As a result, the lower the temperature of KF PDT and serves to interrupt the flow of current K-CIGS layer is not removed from the reaction surface, FF and photocurrent is decreased significantly. Blocking of the Na diffusion from the glass substrate is significantly increased while the optical voltage, photocurrent and FF is a low temperature (300, $350^{\circ}C$) in the greatly reduced, and in $400^{\circ}C$ tend to reduce fine. It is the presence of Na in CIGS thin film by electron-induced degradation of the microstructure of CIGS thin film is expected to have a significant impact on increasing the hole recombination rate a reaction layer is formed of the K elements in the CIGS thin film surface.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.12 no.1
• /
• pp.59-65
• /
• 2012

A study on the electrical characteristic analysis of solar cell diodes under experimental conditions of varying temperature and frequency has been conducted. From the current-voltage (I-V) measurements, at the room temperature, we obtained the ideality factor (n) for Space Charge Region (SCR) and Quasi-Neutral Region (QNR) of 3.02 and 1.76, respectively. Characteristics showed that the value of n (at SCR) decreases with rising temperature and n (at QNR) increases with the same conditions. These are due to not only the sharply increased SCR current flow but the activated carrier recombination in the bulk region caused by defects such as contamination, dangling bonds. In addition, from the I-V measurements implemented to confirm the junction uniformity of cells, the average current dispersion was 40.87% and 10.59% at the region of SCR and QNR, respectively. These phenomena were caused by the pyramidal textured junction structure formed to improve the light absorption on the device's front surface, and these affect to the total diode current flow. These defect and textured junction structure will be causes that solar cell diodes have non-ideal electrical characteristics compared with general p-n junction diodes. Also, through the capacitance-voltage (C-V) measurements under the frequency of 180 kHz, we confirmed that the value of built-in potential is 0.63 V.

• Current Optics and Photonics
• /
• v.5 no.1
• /
• pp.1-7
• /
• 2021

For higher sensitivity in ultraviolet (UV) and even vacuum ultraviolet (VUV) detection of silicon-based sensors, a sandwich-structured film sensor based on Ag Localized Surface Plasmon Resonance (LSPR) was designed and fabricated. This film sensor was composed of a Ag nanoparticles (NPs) layer, SiO2 buffer and fluorescence layer by physical vapour deposition and thermal annealing. By tuning the annealing temperature and adding the SiO2 layer, the resonance absorption wavelength of Ag NPs matched with the emission wavelength of the fluorescence layer. Due to the strong plasmon resonance coupling and electromagnetic field formed on the surface of Ag NPs, the radiative recombination rate of the luminescent materials and the number of fluorescent molecules in the excited state increased. Therefore, the fluorescent emission intensity of the sandwich-structured film sensor was 1.10-1.58 times at 120-200 nm and 2.17-2.93 times at 240-360 nm that of the single-layer film sensor. A feasible method is provided for improving the detection performance of UV and VUV detectors.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.88.2-88.2
• /
• 2010

Dye-sensitized solar cells (DSSCs) have attracted considerable attention on account of their high solar energy-to-conversion efficiencies and low cost processes compared to conventional p-n junction solar cells. The mechanism of DSSC is based on the injection of electrons from the photo excited dyes into the conduction band of the semiconductor electrode. The oxidized dye is reduced by the hole injection into either the hole conductor or the electrolyte. Thus, the light harvesting effect of dye plays an important role in capturing the photons and generating the electron/hole pair, as well as transferring them to the interface of the semiconductor and the electrolyte, respectively. We used the organic fluorescence materials which can absorb short wavelength light and emit longer wavelength region where dye sensitize effectively. In this work, the DSSCs were fabricated with fluorescence materials added $TiO_2$ photo-electrode which were sensitized with metal-free organic dyes. The photovoltaic performances of fluorescence aided DSSCs were compared, and the recombination dark current curves and the incident photon-to-current (IPCE) efficiencies were measured in order to characterize the effects of the additional light harvesting effect in DSSC. Electro-optical measurements were also used to optimize the fluorescence material contents on TiO2 photo-electrode surface for higher conversion efficiency (${\eta}$), fill factor (FF), open-circuit voltage (VOC) and short-circuit current (ISC). The enhanced light harvesting effect by the judicious choice/design of the fluorescence materials and sensitizing dyes permits the enhancement of photovoltaic performance of DSSC.

• Current Photovoltaic Research
• /
• v.8 no.4
• /
• pp.114-119
• /
• 2020

In this study, Mitigation of Potential-induced degradation (PID) for PERC solar cells using SiO2 Structure of ARC layer. The conventional PID test was conducted with a cell-level test based on the IEC-62804 test standard, but a copper PID test device was manufactured to increase the PID detection rate. The accelerated aging test was conducted by maintaining 96 hours with a potential difference of 1000 V at a temperature of 60℃. As a result, the PERC solar cell of SiO2-Free ARC structure decreased 22.11% compared to the initial efficiency, and the PERC solar cell of the Upper-SiO2 ARC structure decreased 30.78% of the initial efficiency and the PID reliability was not good. However, the PERC solar cell with the lower-SiO2 ARC structure reduced only 2.44%, effectively mitigating the degradation of PID. Na+ ions in the cover glass generate PID on the surface of the PERC solar cell. In order to prevent PID, the structure of SiNx and SiO2 thin films of the ARC layer is important. SiO2 thin film must be deposited on bottom of ARC layer and the surface of the PERC solar cell N-type emitter to prevent surface recombination and stacking fault defects of the PERC solar cell and mitigated PID degradation.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.87.2-87.2
• /
• 2015

Transparent conductors are commonly used in photoelectric devices, where the electric energy converts to light energy or vice versa. Energy consumption devices, such as LEDs, Displays, Lighting devices use the electrical energy to generate light by carrier recombination. Meanwhile, solar cell is the only device to generate electric energy from the incident photon. Most photoelectric devices require a transparent electrode to pass the light in or out from a device. Beyond the passive role, transparent conductors can be employed to form Schottky junction or heterojunction to establish a rectifying current flow. Transparent conductor-embedded heterojunction device provides significant advantages of transparent electrode formation, no need for intentional doping process, and enhanced light-reactive surface area. Herein, we present versatile applications of transparent conductors, such as NiO, ZnO, ITO in photoelectric devices of solar cells and photodetectors for high-performing UV or IR detection. Moreover, we also introduce the growth of transparent ITO nanowires by sputtering methods for large scale application.

• Current Photovoltaic Research
• /
• v.5 no.1
• /
• pp.25-27
• /
• 2017

Nanoscale textured black silicon has attracted intensive attention due to its great potential as applications in multicrystalline silicon-based solar cells. It absorbs sunlight over a broad range of wavelengths but introduces large recombination centers, non-uniform doping into cell. In this study, we present a metal-assisted chemical etching technique plus alkaline etching process to fabricate nanoscale pyramid structures with optimized condition. To make the structures, silver nanoparticles-loaded mc-Si wafer was submerged into $H_2O_2/HF$ solution first for nanohole texturing the wafer and textured wafer etched again with KOH solution for making nanoscale pyramid structures. The average reflectivity (350-1050 nm) is about 8.42% with anti-reflection coating.