• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.2
• /
• pp.73-77
• /
• 2012

Co-(0.8 wt%) and Ce-(0.4 wt%) doped cubic zirconia ($ZrO_2$ : $Y_2O_3$ = 80 : 20, 70 : 30, 60 : 40, 50 : 50 wt%) single crystals grown by a skull melting method were heat-treated in $N_2$ at $1000^{\circ}C$ for 5 hrs. The orange, yellowish brown and brown colored as-grown single crystals were changed into either brownish red, yellow and green color after the heat treatment. Before and after the heat treatment, the YSZ (yttria-stabilized zirconia) single crystals were cut for wafer form (${\phi}6.5mm{\times}t2mm$). The optical and structural properties were examined by UV-VIS spectrophotometer and X-ray diffraction. Absorption by $Ce^{3+}(^2F_{5/2,7/2}(4f){\rightarrow}^2T_g(5d^1))$, $Co^{2+}(^4A_2(^4F){\rightarrow}^4T_1(^4F)$ or $^4T_1(^4P))$ and $Co^{3+}$, change of ionization energy and lattice parameter were confirmed.

• Journal of the Korean Vacuum Society
• /
• v.15 no.2
• /
• pp.194-200
• /
• 2006

Self-assembled InAs/InAl(Ga)As quantum dots (QDs) were grown on InP substrates by a molecular-beam epiaxy, and their structural and optical properties were investigated by atomic force microscopy (AFM), transmission electron microscopy (TEM), and room-temperature photoluminescence (PL). AFM images indicated that the InAs quantum structures showed various shapes such as quantum dashes, asymmetric and symmetric QDs mainly caused by the initial surface conditions of InAl(Ga)As with the intrinsic phase separation. For the buried InAs QDs in an InAlGaAs matrix, the average lateral size and height of QDs were 23 and 2 nm, respectively. By changing the growth conditions for the QD samples, the emission wavelength of $1.55{\mu}m$ was obtained, which is one of the wavelength windows for fiber optic communications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.382-382
• /
• 2012

CIGS thin films have received great attention as a promising material for solar cells due to their high absorption coefficient, appropriate bandgap, long-term stability, and low cost production. CIGS thin films are deposited by various methods such as co-evaporation, sputtering, spray pyrolysis and electro-deposition. The deposition technique is one of the most important processes in preparing CIGS thin film solar cells. Among these methods, co-evaporation is one of the best technique for obtaining high quality and stoichiometric CIGS films. However, co-evaporation method is known to be unsuitable for commercialization. The sputtering is known to be very effective and feasible process for mass production. In this study, CIGS thin films have prepared by rf magnetron sputtering using a $Cu(In_{1-x}Ga_x)Se_2$ single quaternary target without post deposition selenization. This process has been examined by the effects of deposition parameters on the structural and compositional properties of the films. In addition, we will explore the influences of substrate temperature and additional annealing treatment after deposition on the characteristics of CIGS thin films. The thickness of CIGS films will be measured by Tencor-P1 profiler. The crystalline properties and surface morphology of the films will be analyzed using X-ray diffraction and scanning electron microscopy, respectively. The optical properties of the films will be determined by UV-Visible spectroscopy. Electrical properties of the films will be measured using van der Pauw geometry and Hall effect measurement at room temperature using indium ohmic contacts.

• Korean Journal of Materials Research
• /
• v.15 no.8
• /
• pp.491-495
• /
• 2005

(Zn,Mg)O (ZMO) thin films doped with Ga $(0\~0.03mol\%)$ in the target source were prepared by pulsed laser deposition on c-plane sapphire substrates at $500^{\circ}C$, and the effect of Ga contents on the properties of the electrical, optical and crystal properties of the deposited films was investigated. From X-ray diffraction patterns, ZMO film doped with $0.02 mol\%$ Ga showed crystal structure with c-axis preferred orientation, showing only the (0002) and (0004) diffraction peaks. In contrast, ZMO film doped with $Ga=0.03 mol\%$ showed a randomly oriented crystal structure. All the samples were highly transparent, showing the transmittance values of above $85\%$ in the visible region. For all the Ga doped ZMO films, the value of energy band gap was found to be about 3.5 eV, regardless of their Ga contents. From the Hall measurements, the resistivity and the carrier density for the ZMO film doped with $0.01 mol\%$ Ga were about $5\times10^{-4}\Omega-cm$ and $2\times10^{21}cm^{-3}$, respectively.

• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.34-39
• /
• 2008

We have investigated the characteristics of $Al_{0.55}Ga_{0.45}N$/GaN heterostructures with and without low-temperature (LT) AlN interlayer grown by metalorganic chemical vapor deposition. The structural and optical properties were systematically studied by Rutherford backscattering spectroscopy (RBS), X-ray diffraction (XRD), optical microscopy (OMS), scanning electron microscopy (SEM), and photoluminescence (PL). The Al content (x) of 55% and the structural properties of $Al_xGa_{1-x}N$/GaN heterostructures were investigated by using RBS and XRD, respectively. We carried out OMS and SEM experiments and obtained a decrease of the crack network in $Al_{0.55}Ga_{0.45}N$ layer with LT-AlN interlayer. A two-dimensional electron gas (2DEG)-related PL peak located at ${\sim}3.437eV$ was observed at 10 K for $Al_{0.55}Ga_{0.45}N$/GaN with LT-AlN interlayer. The 2DEG-related emission intensity gradually decreased with increasing temperature and disappeared at temperatures around 100 K. In addition, with increasing the excitation power above 3.0 mW, two 2DEG-related PL peaks were observed at ${\sim}3.411$ and ${\sim}3.437eV$. The observed lower-energy and higher-energy side 2DEG peaks were attributed to the transitions from the sub-band level and the Fermi energy level of 2DEG at the AlGaN/LT-AlN/GaN heterointerface, respectively.

• Journal of the Korean Vacuum Society
• /
• v.15 no.3
• /
• pp.294-300
• /
• 2006

We fabricated the distributed feedback (DFB) InP/InGaAs/InP grating structures on InP (100) substrates by metal-organic chemical vapor deposition, and their structural properties were investigated by atomic force microscopy and scanning electron microscopy. Self-assembled InAs/InAlGaAs quantum dots (QDs) were grown on the InP/InGaAs/InP grating structures by molecular beam epitaxy, and their optical properties were compared with InAs/InAlGaAs QDs without grating structure. The duty of the grating structures was about 30%. The PL peak position of InAs/InAlGaAs QDs grown on the grating structure was 1605 nm, which was red-shifted by 18 nm from that of the InAs/InAlGaAs QDs without grating structure. This indicates that the formation of InAs/InAlGaAs QDs was affected by the existence of the DFB grating structures.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.6
• /
• pp.267-271
• /
• 2009

Multicomponent transparent conducting oxide films were deposited on glass substrates at 150 by dual magnetron sputtering of AZO and ITO targets. In the case of mixing a limited amount of ITO (10W), resistivity of TCO films was significantly increased compared to the AZO film; from $3.5{\times}10^{-3}$ to $9.7{\times}10^{-3}{\Omega}{\cdot}cm$. Deterioration of the electrical conductivity is attributed to the decreases in carrier concentration and Hall mobility. Improvement of the conductivity could be obtained for the films prepared with ITO powers larger than 40 W. The lowest resistivity ($\rho$) of $7.3{\times}10^{-4}{\Omega}{\cdot}cm$ was achieved when ITO power was 100 W. Effects of $H_2$ incorporation on the electrical and optical properties of AZO-ITO films were investigated in this work. Addition of small amount of hydrogen resulted in the increase of carrier concentration and the improvement of electrical conductivity. It is apparent that the roughness of AZO-ITO films decreases dramatically after the transition of microstructure from polycrystalline to amorphous phase, which gives practical advantages such as an excellent uniformity of surface and a high etching rate. AZO-ITO films grown at sputtering ambient with hydrogen gas are expected to be applicable to optoelectronic devices such as organic light emitting diodes and flexible displays due to their sufficient electrical and structural properties.

• Korean Journal of Materials Research
• /
• v.12 no.6
• /
• pp.452-457
• /
• 2002

Titanium oxide films were prepared by RF reactive magnetron sputtering. The effect of sputtering conditions on structural and optical properties was investigated systemically as a function of sputtering pressure(5~20 mTorr) and $O_2/Ar$ flow ratio(0.08~0.4). The results of the X-ray diffraction showed that all films had only the anatase $TiO_2$ phase. At low sputtering pressure and $O_2/Ar$ flow ratio, the films had preferred orientations along [101] and [200] directions. As the sputtering pressure and $O_2/Ar$ flow ratio increased, the intensity of the 101 and 200 diffraction peaks decreased gradually. The microstructure of the sputtered films showed the fine grain size (20nm~50nm) and columnar microcrystals perpendicular to the substrate. With increasing the sputtering pressure and decreasing $O_2/Ar$ flow ratio, the sputtered films showed the more porous columnar structure. XPS analysis showed that stoichiometric $TiO_2$ films were deposited at 7 mTorr sputtering pressure and 0.2 $O_2/Ar$ flow ratio. The results of the X-ray diffraction showed that all films had only the anatase $TiO_2$ phase. Ellipsometeric analysis showed that the refractive index increased from 2.32 to 2.46 as the sputtering pressure decreased. The packing density calculated using the refractive index varied from 0.923 to 0.976, indicating that $TiO_2$films became denser as the sputtering pressure decreased.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• v.9 no.1
• /
• pp.1013-1016
• /
• 2005

ZnO nanostructure was fabricated by catalyst-free method using Zn powder in air. The growth temperature was controlled from 450$^{\circ}$C to 600$^{\circ}$C, and the structural and optical properties were investigated by scanning electron microscopy (SEM), photoluminescence (PL), energy dispersive X-ray spectroscopy (EDX) and cathodoluminescence (CL). From all samples both ZnO tetrapods and clusters were observed. No significant dispersion was observed from the ZnO tetrapods, however, ZnO clusters show considerable change in density and size. From the EDX results, atomic composition difference was found. The clusters have O-deficiencies, while tetrapods have stoichiometric composition. Strong luminescence was observed at room temperature. From room temperature PL, UV emission at 380 nm and green emission at 500 nm were observed, and the intensity ratio ($I_{uv}/I_{green}$) increased as growth temperature increases. CL measurements show that the UV emission is closely related with tetrapods and the green emission is dominated from the clusters.

• Journal of the Korean Vacuum Society
• /
• v.19 no.4
• /
• pp.281-286
• /
• 2010

Thickness effects on the structural and optical properties of ZnO thin films fabricated by spin coating method have been carried out. With increase in the thickness of the ZnO thin films, the width and density of striation shape are increased. The ZnO thin film with thickness of 450 nm has a smooth surface morphology. For the ZnO thin film with a smooth surface, orientation factor ${\alpha}_{(002)}$ is sharply increased and FWHM of (002) diffraction peak is decreased compared to the ZnO thin films with a striation shape surface. Thickness and surface morphology of the ZnO thin films hardly affect the NBE peak position. However, the DLE peak position is blue-shifted as the surface morphology is changed from striation to smooth surface. The PL intensity ratio of the NBE to DLE is increased and the FWHM of NBE peak is decreased as the thickness of the ZnO thin films is increased.