This study compared the microtensile bond strength $({\mu}TBS)$ of single step adhesives to different dentin depths. Superficial or deep dentin was exposed in 30 molar teeth by sectioning immediately under the DEJ or 1.5mm area from central pit, respectively. After polishing with 600-grit SiC paper, the dentin surfaces were assigned to three groups: AQ group-AQ Bond, L-Pop group-Adper Prompt L-Pop, Xeno group-Xeno III. The bonded specimens were sectioned into sticks and subjected to ${\mu}TBS$ testing with a crosshead speed of 1mm/minute. The results of this study were as follows; The ${\mu}TBS$ to superficial dentin was higher than that to deep dentin in all group. The ${\mu}TBS$ of Xeno group was significantly higher than that of L-Pop group and AQ group in both superficial and deep dentin (p<0.05).
Journal of the korean academy of Pediatric Dentistry
/
v.34
no.3
/
pp.420-429
/
2007
The purpose of this study was to compare the micro ensile bond strength to bovine dentin of several adhesives (SM, Scotch $Bond^{TM}$ Multipurpose; SB, $Adper^{TM}$ Single Bond 2; SE, $Clearfil^{(R)}$ SE Bond; AQ, AQ $Bond^{TM}$; TS, $Clearfil^{(R)}$ tri-S Bond). Except SM and SB, they have a simplified one- or two-step application protocols in compare with the dentin adhesives conventional three-step protocols. For the microtensile bond strength test, the labial surfaces of bovine incisors were used. Following exposure of dentin layer, according to their manufacturer's directions, each dentin adhesives were applied and composite resin blocks were constructed. The teeth were sectioned for specimen and tested microtensile bond strength. Also observed the fracture mode of interface. The obtained results were as follows : 1. The microtensile bond strength values ranged from 51.34 to 24.04 MPa on dentin(in decreasing order, SE, SM, SB, AQ and TS). 2. The highest microtensile bond strength was by SE and SM on bovine dentin, and the lowest by AQ and TS. 3. SM, SB and SE showed cohesive failures and adhesive failure but AQ, TS presented almost adhesive failures. In summary, microtensile bond strengths of single-step adhesives (AQ and TS) on bovine dentin were significantly lower than those of multi-step adhesives (SM, SB and SE) (p<0.05).
Journal of the korean academy of Pediatric Dentistry
/
v.27
no.3
/
pp.444-456
/
2000
To test the shear bond strength of a new "one-bottle adhesive" system to primary dentin two commercially available one-bottle adhesives (Prime & Bond NT, Single bond) and conventional three step system(Scotchbond Multi-Purpose Plus) were included for comparison. And We observe the interfacial morphology by scanning electron microscope. 90 primary molar teeth were embedded in acrylic and buccal and lingual surface were polished to 320 grit to create standardized dentin surface for testing. After bonding of composite resin to sample surfaces according to the manufacturer s direction and 1000 times thermocycling in dwell time 30 second, Shear bond strengths of adhesives to dentin were determined using universal testing machine and analyzed by ANOVA test. Another groups of specimens were treated by hydrochloric acid to secure the resin only and those tags were evaluated under SEM for their length and forms and the morphology of the bonding sites were also observed. The result are as follows. 1. Group I(Prime & Bond NT) showed higher shear bond strength than group iI(Single Bond) and III(Scotchbond Multi Purpose Plus) but no statistically significant difference was founded between groups(p>.05). 2. Relating long resin tags of $70-120{\mu}m$ were observed in samples of all groups under SEM. We could observed hybrid layer, resin tag and many lateral branches in every group. But, we observed in group III rare lateral branched than other two group and discontinuous hybrid layer.
In order to explore microleakage in class V cavity based on different kinds of several dentin adhesive and composite resin, 2 kinds of composite resin was restored and exposed after applying 4 kinds of dentin adhesives. Deposited in methylene blue solution for 4 hours and cut in parallel with tooth longitudinal axis. By observing dye penetration level of enamel and dentin margins of each restored resin following conclusion was obtained. 1. In composite resin Filtek Z350XT Universal (3M/ESPE Dental Products, USA) in enamel margin, Easy Bond (3M/ESPE Dental Products) showed the lowest microleakage and this leakage was represented to be high in the order of Single Bond 2 (3M/ESPE Dental Products), Scotchbond Multi-Purpose (3M/ESPE Dental Products) and Cearfil SE Bond (Kuraray Medical Inc., Japan). In case of Filtek Z350XT Flowable (3M/ESPE Dental Products), Scotchbond Multi-Purpose showed the lowest microleakage and this leakage was represented to be high in the order of Single Bond 2, Clearfil SE Bond and Easy Bond. 2. In case of Filtek Z350XT Universal in dentin margin, Easy Bond showed the lowest microleakage and this leakage was represented to be high in the order of Scotchbond Multi-Purpose, Single Bond 2 and Clearfil SE Bond. In case of Filtek Z350XT Flowable, Scotchbond Multi-Purpose and Single Bond showed the lowest microleakage and this leakage was represented to be high in the order of Clearfil SE Bond and Easy Bond. 3. In all the groups excepting S-U group (Single Bond 2+Filtek Z350XT Universal), enamel margin showed more higher microleakage than that of dentin margin. 4. There was a difference between enamel and dentin margin among each group but it was not significant statistically (p>0.05). When summarizing this result, it is considered that composite resin and dentin adhesive could be applied selectively and particularly in case of applying 1-step self-etching dentin adhesive, this method would be advantageous for manipulation convenience and shortening of operation time.
Journal of Dental Rehabilitation and Applied Science
/
v.22
no.2
/
pp.181-191
/
2006
The objectives of this study were to evaluate the tensile strength of resin-infiltrated demineralized dentin according to the demineralization time, and to evaluate the tensile strength of hybrid layer that is formed by infiltrating different priming adhesives or primer/adhesive into demineralizd dentin matrix. Seventy five hour-glass shaped dentin specimens were prepared in mid-coronal dentin from extracted human molars. Thirty specimens were distributed into three groups according to demineralization time - 2 hours, 4 hours and 8 hours. Each specimen was placed in primer/adhesive of All-Bond 2 for 5 hours of infiltration. Another forty-five specimens of them were demineralized in 37% phosphoric acid for 4 hours. They were randomly assigned to three experimental groups - AB, SB and OS - to designate All-Bond 2, Single Bond and One-Step. Each specimen was placed in one of three different adhesives for 5 hours of infiltration. The specimens were visible light-cured for 5 minutes, and then stored for 24 hours in distilled water at $37^{\circ}C$. After that, microtensile bond strength for each specimen was measured, and the fractured surfaces were then observed by SEM. The data were statistically analysed by one-way ANOVA and Tukey's multiple comparison test and Bonferroni's multiple comparison test. The results were as follows; 1. Tensile strength of the group demineralized for 4 hours was significantly higher than that of groups demineralized for 2 hours and 8 hours (P < .01). 3. Tensile strength of the AB group was significantly higher than that of the SB group and OS group (P < .01).
This study investigated that the effect of rewetting agent on dentinal microtensile bond strength(${\mu}TBS$). Human molars were sectioned to expose the superficial dentin surfaces. Samples were divided into two groups according to type of adhesives-Single Bond (S) and One-Step (0)], and again subdivided into five groups by different dentin surface treatment-dry for 15s (D), blot dry (BD) or dry for 15s, and rewet with different rewetting agents [distilled water (DW), Gluma Desensitizer (GD) and Aqua-Prep (AP)] for 30s. After application of adhesive, composite resin was built up on the bonding surface. Each tooth was sectioned to obtain stick with $1\textrm{mm}^2$ cross sectional area and the ${\mu}TBS$ was determined by EZ test. In the S group, the mean ${\mu}TBS$ of GD, AP, and BD group was significantly higher than that of DW and D group (p < 0.05), In the O group, the mean, ${\mu}TBS$ of AP, GD, BD and DW group was significantly higher than that of D group (p < 0.05). The data suggested that Gluma Desensitizer and Aqua-Prep could be successfully used as rewetting agents, and Distilled water could be acceptable in aceton based adhesive system only.
This study analyzed the influence of dental adhesive/primer on the bond strength between indirect resin composite and the resin cement. Seventy disc specimens of indirect resin composite (Tescera Dentin, Bisco) were fabricated. And bonding area of all specimens were sandblasted and silane treated for one minute. The resin cements were used with or without application of adhesive/primer to bonding area of indirect resin restoration, Variolink-II (Ivoclar-Vivadent) : Exite DSC, Panavia-F (Kuraray) : ED-Primer, RelyX Unicorn (3M ESPE) Single- Bond, Duolink (Risco) : One-step, Mulitlink (Ivoclar-Vivadent) : Multilinh Primer. Shear bond strength was measured by Instron universal testing machine. Adhesive application improved shear bond strength (p<0.05) But Variolink II and Panavia-F showed no statistically significant difference according to the adhesive application. With the above results, when resin inlay is luted by resin cement it seems that application of dental adhesive/primer is necessary in order to improve the bond strength.
The purpose of this study was to evaluate the microleakage of 5 current dentin bonding systems which are composed of 2 multi-bottle systems(Scotchbond Multi-Purpose, All Bond2) and 3 one-bottle systems(Single bond, One-Step, Prime & Bond). In this in vitro study, class V cavities were prepared on buccal and lingual surfaces of sixty extracted human premolars and molars on cementum margin. The experimental teeth were randomly divided into six groups of 10 samples (20 surfaces) each, Group 1 : Scotchbond Multi-Purpose ; Group 2 : All Bond 2 ; Group 3 : Single Bond ; Group 4 : One-Step ; Group 5 : Prime & Bond ; Group 6 : no bonding agent(control). The bonding agent and composite resin were applied for each group following the manufacturer's instructions. After 500 thermocycling between $5^{\circ}C$ and $55^{\circ}C$, the 60 teeth were placed in 2% Methylene blue dye for 24 hours, then rinsed with tab water. The specimen were embedded in clear resin, then sectioned buccolingually through the center of restoration with a low speed diamond saw. The dye penetration on each of the specimen were then observed with a stereomicroscope at ${\times}20$. The results of study were statistically analyzed using the Student-Newmann-Keul's Methods and the Mann-Whitney Rank Sum Test. The resin/dentin interfaces were examined under Scanning Electron Microscopy. The results of this study were as follows. 1. None of the dentin bonding systems used in this study showed significant difference in leakage values at both the enamel and the dentin margins (P>0.05). 2. In all groups except the control, leakage value seen at the enamel margin was significantly lower than that seen at the dentin margin (P<0.05). 3. Compared to the control group, all the groups treated with dentin bonding systems showed significantly lower leakage value at both enamel and dentin margins (P<0.05). 4. In the SEM view, gaps were observed in the composite resin / dentin interface in group 6 where no dentin bonding agent was used, and in all the other groups (group 1, 2, 3, 4, 5) composite resin, hybrid layer, and dentin were seen to be closely adhering to each other where there were no leakages. Well-developed resin tags 3~100${\mu}m$ in length infiltrated dentinal tubules past the hybrid layer and a hybrid layer 1~5${\mu}m$ thick had developed between the dentinal surface and the composite resin surface.
Journal of the korean academy of Pediatric Dentistry
/
v.29
no.4
/
pp.632-640
/
2002
The objective of the study was to apply the vibration technique to reduce the viscosity of bonding adhesives and thereby compare the bond strength and resin penetration into dentinal tubules achieved with those gained using the conventional technique. Eighty-eight noncarious extracted human permanent molar teeth were sectioned to remove the coronal enamel and were embedded in 1-inch PVC pipe with acrylic resin. The occlusal surfaces were placed so that the tooth and the embedding medium were at the same level to form one flat surface, and the samples were subsequently polished with silicon carbide abrasive papers. The samples were randomly assigned to 4 groups(n=22). On Group 1 and 2, Single Bond(3M-ESPE, St. Paul, USA) was used, and on Group 3 and 4, One-Step(Bisco Inc., Schaumburg, USA) was used, and each was applied according to its manufacturer's instructions. For Group 2 and Group 4, vibration was applied with ultrasonic scaler for 10 seconds, and the adhesive was light-cured for 10 seconds. Resin composite was condensed on to the prepared surface in two increments using a mold kit(Ultradent Products Inc., USA) and each was light-cured for 40 seconds. After 24 hours in tap water at room temperature the specimens were thermocycled, and shear bond strengths were measured with a universal testing machine(Instron 4465, Canton, USA). To investigate infiltration patterns of the adhesive materials, the surface of specimen was examined with scanning electron microscope. The results were as follows. 1. The shear bond strengths of vibration groups(Group 2, Group 4) were significantly greater than those of the non-vibration groups(Group 1, Group 3)(p<0.05). 2. The shear bond strengths of Single Bond and One-Step were not significantly different (p>0.05). 3. The vibration groups showed greater number of resin tags in tubules and lateral branches under SEM.
Journal of the korean academy of Pediatric Dentistry
/
v.44
no.3
/
pp.358-364
/
2017
For the purpose of convenience and reducing time, newer bonding agents have been developed for composite resin restoration. Recently developed one bottle bonding system including etching, primer and adhesive can make procedures simpler and less technique-sensitive than old generation adhesives. The aim of this study was comparing the shear bond strength of new dentin bonding agents to the 5th generation bonding agent which had an etching step. 78 premolar teeth were randomly divided into three groups which were treated with $Tetric^{(R)}$ N-Bond Universal (Ivoclar Vivadent, Liechtenstein), $GC^{(R)}$ G-Premio BOND (GC Co., Japan) without additional etching step and $3M^{TM}$ Single Bond2 (3M ESPE, USA) with an etching step following manufacturer's instructions. $Filtek^{TM}$ Z-350 (3M ESPE, USA) composite resin was applied and light cured over bonding agents. For shear bond strength evaluation, universal testing machine was used with a wedge technique. As a result, shear bond strength of one step bonding agents was lower than two step bonding agent and there were statistically significant differences between them (p < 0.05). In addition, within the result of two new bonding agents, $Tetric^{(R)}$ N-Bond Universal showed significantly higher shear bond strength than $GC^{(R)}$ G-Premio BOND (p < 0.05).
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.