• 한국재료학회지
• /
• 제30권4호
• /
• pp.169-175
• /
• 2020

Silicon nitride thin films are deposited by RF (13.57 MHz) magnetron sputtering process using a Si (99.999 %) target and with different ratios of Ar/N₂ sputtering gas mixture. Corning G type glass is used as substrate. The vacuum atmosphere, RF source power, deposit time and temperature of substrate of the sputtering process are maintained consistently at 2 ~ 3 × 10^-3 torr, 30 sccm, 100 watt, 20 min. and room temperature, respectively. Cross sectional views and surface morphology of the deposited thin films are observed by field emission scanning electron microscope, atomic force microscope and X-ray photoelectron spectroscopy. The hardness values are determined by nano-indentation measurement. The thickness of the deposited films is approximately within the range of 88 nm ~ 200 nm. As the amount of N₂ gas in the Ar:N₂ gas mixture increases, the thickness of the films decreases. AFM observation reveals that film deposited at high Ar:N₂ gas ratio and large amount of N₂ gas has a very irregular surface morphology, even though it has a low RMS value. The hardness value of the deposited films made with ratio of Ar:N₂=9:1 display the highest value. The XPS spectrum indicates that the deposited film is assigned to non-stoichiometric silicon nitride and the transmittance of the glass with deposited SiO₂-Si_xN_y thin film is satisfactory at 97 %.

• 한국재료학회지
• /
• 제4권6호
• /
• pp.662-668
• /
• 1994

실리콘 질화막을 습식 산화하여 제작한 산화막/질화막 복합층과 이 박막의 산화막을 식각하여 제작한 oxynitride 박막의 물리적, 전기적 특성을 기술하였다. $900^{\circ}C$에서 산화시간이 증가함에 따라 산화막/질화막의 경우에는 축전용량은 급격히 감소하였으나 절연 파괴전장은 증가하였다. Oxynitrite박막은 축전용량과 절연파괴 전장이 모두 증가하였다. Oxynitride박막의 경우 축전 용량의 증가와 절연 파괴 전장이 증가하였는데 이는 유효 주께 감소와 박막의 양질화에 기인하였다. 또한, 산화 시강의 증가에 따라 Oxynitride박막의 TDDB특성과 초기 불량율도 향상되었다. 결론적으로 Oxynitride박막은 dynamic기억소자의 유전체 박막으로 사용하기에 적합하였다.

• 전기의세계
• /
• 제28권9호
• /
• pp.43-50
• /
• 1979

Silicon nitride films were chemically deposited on silicon substrates by reacting SiCl$_{4}$ and NH$_{3}$ in a nitrogen atmosphere at 700~1100 .deg.C. The deposition rate increased rapidly with deposition temperature upto about 1000 .deg.C, and became less temperature dependent above this temperature. The etch rate of films in buffered HF solution decreased, with an increase of deposition temperature, and a heat treatment at a temperature higher than that of the deposition considerably reduced the etch rate. It indicates that the heat treatment resulted in a densification of the films. Surface charge density of 3~4 * 10$^{11}$ /cm$^{2}$ was determined from the C-V characteristics of MNS diode, and it was also found that surface charge density depended on deposition temperature, but not film thickness. The current-voltage characteristics displayed a logI-V$^{1}$2/ dependence in the temperature range of 300~500.deg.K. Measurement of the slope of this characteristics and its dependence on temperature and bias polarity suggest that conduction in sili con nitride films arises from the Poole-Frenkel mechanism.

• 한국표면공학회지
• /
• 제23권4호
• /
• pp.218-224
• /
• 1990

Silicon nitride thin(SiNx) is deposited onto 3 inch silicon wafor using ECR plasma apparatus. For the two different plasma extraction windows size, the thin films which were deposited by changing the SiH4/N2 gas fole at at 1.5mTorr without substrate heating are analyzed through the XPS and wlliposometer measurements. The very uniform and good quality silicon nitride thin film were obtained with the analyzed results of the deposited films, and particularly, ion temperature perpendicular to the magnetic filed was nearly same as the neutral gas temperature. The large amount of plasma loss in the transport process following magnetic field lines could be seen from the plasma emission intensity measurements.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1992년도 하계학술대회 논문집 B
• /
• pp.832-834
• /
• 1992

Using the PECVD method, the silicon nitride films were deposited by changing the $SiH_4/NH_3$ gas flow ratio from 0.2 to 1.4 at an interval of 0.2, AES, FTIR, and Spectroscopic Ellipsomter were used to analyze the film composition and structure, the refractive index, and the deposition rate. Also the C-V analysis was used to estimate the memory performance in the capacitor type MNOS memory devices, which utilized native oxide as the tunneling barrier, with the silicon nitride by the above deposition conditions. As a result, it was confirmed that the performance of MNOS memory devices with PECVD silicon nitride was comparable to that with LPCVD or APCVD silion nitride.

• 한국정보통신학회논문지
• /
• 제11권11호
• /
• pp.2095-2099
• /
• 2007

본 연구에서는 LCD, 이미지 센서 등의 개별 소자인 비정질 실리콘 박막 트랜지스터에서 게 이트 유전층 및 절연층으로 사용되는 비정질 질화 실리콘 박막을 사일랜($SiH_4$) 및 암모니아가스를 사용해서 PECVD(Plasma Enhanced Chemical Vapor Deposition) 진공 증착장비로 최적의 비정질질화실리콘 박막 증착 조건을 확립한다. 먼저 반응실의 진공도, rf 전력, $SiH_4$ 및 질소 그리고 암모니아가스의 flow rate를 변화시키면서 형성된 박막의 특성을 조사한다. 계속해서 다른 변수를 고정시킨 상태에서 rf 전력을 변화시키고 다음에는 반응실의 진공도 등을 변화시켜 최적의 증착조건을 확립한다. 이렇게 확립된 증착조건을 사용하여 비정질질화실리콘박막을 제작하여 특성을 측정한 결과 우수한 성능을 나타냈음을 확인하였다.

• 전자공학회논문지A
• /
• 제29A권10호
• /
• pp.35-41
• /
• 1992

Ultra-thin silicon nitride films were fabricated with ECR(Electron cyclotron Resonance) nitrogen plasma at room temperature. Film thickness was about 50$\AA$ after nitridation for 1min at microwave power of 1000W, RF power of 500W, and NS12T pressure of ${\times}10^{-3}$ torr. 50$\AA$ fo nitride film was grown within 1 min and no appreciable growth occured thereafter. Dielectric breakdown strength and leakage current density in Al/SiN/Si structure were measured to be about 7-11 MV/cm and ${\times}10^{-10}~5{\times}10^{-10}A/cm^{2}$, respectively. Observed linear relationship in 1n(J/E)-vs-E$^{1/2}$ and no polarity-dependence of the leakage current indicated that the Poole-Frenkel emission is mainly responsible for the conduction in this nitrided silicon films.

• 한국전기전자재료학회논문지
• /
• 제34권1호
• /
• pp.33-38
• /
• 2021

Using facing target magnetron sputtering (FTMS) with a graphite target source, carbon nitride thin films were deposited on silicon and glass substrates at different substrate temperatures to confirm the tribological, electrical, and structural properties of thin films. The substrate temperatures were room temperature, 150℃, and 300℃. The tribology and electrical properties of the carbon nitride thin films were measured as the substrate temperature increased, and a study on the relation between these results and structural properties was conducted. The results show that the increase in the substrate temperature during the fabrication of the carbon nitride thin films increased the hardness and elastic modulus values, the critical load value was increased, and the residual stress value was reduced. Moreover, the increase in the substrate temperature during thin-film deposition was attributed to the improvement in the electrical properties of carbon nitride thin film.

• E2M - 전기 전자와 첨단 소재
• /
• 제7권2호
• /
• pp.145-151
• /
• 1994

The multi-dielectric layer SiOz/Si3N4/SiO2(ONO) is used to scale down the memory device. In this paper, the change of composition in ONO layer due to the process condition and the conduction mechanism are observed. The composition of the oxide film grown through the oxidation of nitride film is analyzed using auger electron spectroscopy(AES). AES results show that oxygen concentration increases at the interface between oxide and nitride layers as the thickness -of the top oxide layer increases. Results of I-V measurement show that the insulating properties improve as the thickness of the top oxide layer increases. But when the thickness of the nitride layer decreases below 63.angs, insulating peoperties of film 28.angs. of top oxide and film 35.angs. turn over showing that insulating property of film 28.angs. of top oxide is better than that of film 35.angs. of top oxide. This phenomenon of turn over is thought as the result of generation of surface state due to oxygen flow into nitride during oxidation process. As the thickness of the top oxide and nitride increases, the electrical breakdown field increases, but when the thickness of top oxide reaches 35.angs, the same phenomenon of turn over occurs. Optimum film thickness for scaled multi-layer dielectric of memory device SONOS is estimated to be 63.angs. of nitride layer and 28.angs. of top oxide layer. In this case, maximum electrical breakdown field and leakage current are 18.5[MV/cm] and $8{\times}{10^-12}$[A], respectively.

• Journal of Information Display
• /
• 제11권3호
• /
• pp.109-112
• /
• 2010

The solid phase compositions and dielectric properties of silicon nitride ($SiN_x$) films prepared using the plasma enhanced chemical vapor deposition (PECVD) technique at a low temperature ($200^{\circ}C$) were studied. Controlling the source gas mixing ratio, R = $[N_2]/[SiH_4]$, and the plasma power successfully produced both silicon-rich and nitrogen-rich compositions in the final films. The composition parameter, X, varied from 0.83 to 1.62. Depending on the film composition, the dielectric properties of the $SiN_x$ films also varied substantially. Silicon-rich silicon nitride (SRSN) films were obtained at a low plasma power and a low R. The photoluminescence (PL) spectra of these films revealed the existence of nano-sized silicon particles even in the absence of a post-annealing process. Nitrogen-rich silicon nitride (NRSN) films were obtained at a high plasma power and a high R. These films showed a fairly high dielectric constant ($\kappa$ = 7.1) and a suppressed hysteresis window in their capacitance-voltage (C-V) characteristics.