To obtain available process at low temperature, SiOC thin film was prepared with various flow rates by using the rf magnetron sputtering, and AZO thin film was also deposited on SiOC film by rf magnetron sputtering system. The optical electrical properties of the SiOC film and SiOC/AZO were analyzed by the uv visible spectrometer and PL spectra. SiOC film on n type Si showed various type emission according to the deposition condition. The SiOC film showed the blue shift with increasing the thickness in PL spectra. AZO/SiOC/Si film had a broad emission characteristic, which is enhanced the efficiency in solar cell.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2011.10a
• /
• pp.886-887
• /
• 2011

To obtain a transparent electrode, AZO thin film was deposited on SiOC film with various flow rates by rf magnetron sputtering system. SiOC film was deposited with various DMDMOS/O2 flow rate ratio by CVD, The optical electrical properties of the SiOC film and SiOC/AZO were analyzed by the uv visible spectrometer and 4 point prove system. The reflectance of SiOC/AZO film was changed in compared with that of SiOC film. The resistance was decreased with low RF power because of increasing the concentration of carriers.

• Journal of the Korean Vacuum Society
• /
• v.19 no.5
• /
• pp.347-352
• /
• 2010

To research the reduction of the dielectric constant depending on the ionic and electronic effects, the dielectric constant of SiOC film was obtained by C-V measurement using the structure of metal/SiOC film/Si, and $n^2$ calculated by the refractive index. The dielectric constant of SiOC film consists with dipole, ions and electrons. However, the dipole moment is ignored in the effect of dielectric constant in SiOC film. THe SiOC film was deposited by the plasma energy, and the gas precursor was dissociated and recombined. Therefore, the dielectric constant of the deposited film consisted of the polarity with ions. THe dielectric constant decreased after annealing process, because of the evaporation of OH hydroxyl group with polarity. The ideal SiOC film as low-k materials was annealed film with lowering the polarity, which is suitable for physical-chemical and electrical properties as an inter layer dielectric materials.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.13 no.12
• /
• pp.2505-2510
• /
• 2009

The SiOC films were deposited with the variation of flow rate ratios by chemical vapor deposition. It was researched the reason of decreasing the dielectric constant in SiOC film and the relationship between the dielectric constant and the thickness. The thickness of the deposited films tends to in proportion to the refractive index and the sample with the lowest dielectric constant decreased the thickness. The refractive index was decreased after annealing because of the decreasing of the film's thickness by annealing process.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.282-282
• /
• 2012

본 연구에서 SiOC 박막을 제작하기 위해서 RF 마그네트론 스퍼터링법을 이용하여 유량별 RF 파워의 변화에 따라서 AZO 박막을 성장시켰으며 박막의 광학적 특성을 조사하였고 투명 전도성 박막으로써 AZO 박막을 SiOC 박막 위에 성장시켜서 광학적인 특성을 조사하였다. Si 웨이퍼의 종류에 따라서 광학적인 특성에 조금의 변화가 있는 것을 확인하였으며, n-type Si의 경우 electron transition에 의한 emission 특성이 달라지는 것에 비하여 상대적으로 p-type Si의 경우 변화가 거의 없는 것으로 나타났다. 일반적으로 사용되는 SiO2 산화막 위에 증착한 AZO 박막에 비하여 SiOC 박막 위에 증착할 경우 빛의 흡수가 많이 일어나는 것을 확인할 수 있었으며, AZO/SiOC 박막의 반사도 역시 많이 감소하였으며, 이러한 전기적인 특성은 태양전지에서 전면전극으로 사용할 경우 반사방지막으로서의 특징도 나타낸다는 것을 의미한다. 스퍼터 방법에 의한 증착법은 낮은 온도에서도 공정이 가능하다는 장점이 있으며, 절연특성이 우수한 SiOC 박막을 AZO 박막의 보호막으로 사용할 경우 용도에 따라서 우수한 특성을 나타낼 수 있음을 확인하였다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.12
• /
• pp.7283-7286
• /
• 2014

SiOC films were prepared as insulators for displays by sputtering at low temperatures, and the relationship with the electrical properties waaas examined. The electrical properties of SiOC films were affected by the annealing process, and SiOC films annealed at 100oC showed a significant increase in thickness and a decrease in the reflective index. XRD revealed an increase in the degree of the amorphous structure. Moreover, the capacitance and leakage current of the SiOC films annealed at 100oC decreased. These characteristics of SiOC films highlight their potential as ideal insulators. Amorphous SiOC films by the reduction of polarization are dependent on the elongation effect of the bonding lengths in the structure and the thickness. The properties of these SiOC films are suitable for low temperature displays.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.16 no.8
• /
• pp.1747-1752
• /
• 2012

The SiOC film of carbon centered system was prepared using bistrimethylsilylmethane (BTMSM) and oxygen mixed precursor by the chemical vapor deposition. The dielectric constant is measured by MIS(metal/insulator/Si) structure, but it could decrease the reliability because the uniformity is not assured. To research the dielectric constant of SiOC film, the range of low polarization was researched in SiOC film using the optical analysis and hardness, and then calculated the dielectric constant of SiOC film with amorphous structure of high degree. After annealing, the dielectric constant of SiOC film was decreased owing to the lowering of polarization, and FTIR spectra of the main bond was shifted to higher wave number. The main bond of 950~1200 cm-1 was composed of the Si-C and Si-O bonds. The intensity increases in Si-O bond infers the bonding strength became stronger than that of deposited film. Annealed SiOC film showed 2.06 in dielectric constant.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.42 no.6 s.336
• /
• pp.17-22
• /
• 2005

Organic-inorganic hybrid type thin films are the next generation candidates as low-k materials. SiOC films are analyzed the bonding structure by the red and blue chemical shift using the fourier transform infraredspectra. Conventional chemical shift of organic chemistry is a red shift, but hybrid type SiOC films were observed the red and blue shift. The chemical shift originates from the interaction between the C-H bond and high electronegative atoms, and the blue shift in SiOC films is caused by the porosity due to the increase of the electron rich group such as much methyl radicals. The bonding structures of SiOC films are also divided into the Si-O-C cross-link structure and the Si-O-C cage-link structure due to the chemical shifts. The Si-O-C cross-link structure progressed the adhesion attributed to the C-H bond elongation in the reason of the red shift, and the dielectric constant also decreases.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.11
• /
• pp.4468-4472
• /
• 2010

SiOC films made by the inductively coupled plasma chemical vapor deposition were researched the relationship between the dielectric constant and the chemical shift. SiOC film obtained by plasma method had the main Si-O-C bond with the molecule vibration mode in the range of $930{\sim}1230\;cm^{-1}$ which consists of C-O and Si-O bonds related to the cross link formation according to the dissociation and recombination. The C-O bond originated from the elongation effect by the neighboring highly electron negative oxygen atoms at terminal C-H bond in Si-$CH_3$ of $1270cm^{-1}$. However, the Si-O bond was formed from the second ionic sites recombined after the dissociation of Si-$CH_3$ of $1270cm^{-1}$. The increase of the Si-O bond induced the redshift as the shift of peak in FTIR spectra because of the increase of right shoulder in main bond. These results mean that SiOC films become more stable and stronger than SiOC film with dominant C-O bond. So it was researched that the roughness was also decreased due to the high degree of amorphous structure at SiOC film with the redshift after annealing.

• Journal of the Korean Vacuum Society
• /
• v.21 no.4
• /
• pp.212-218
• /
• 2012

The optical properties of AZO thin films prepared by the RF mangnetron sputtering system was studied to research the dependance of chemical properties of substrate. The substrate was the SiOC film deposited by Inductively coupled plasma chemical vapor deposition with various gas flow rate of $O_2$ and Ar (DMDMOS). In accordance with the increase of Ar gas flow rates, the Si-O bond in the SiOC film increased and then progressed the amorphism. The roughness of AZO grown on SiOC film with high degree of amorphism decreased and then improved the flatness of surfaces. Moreover, the ultra violet emission with high intensity was spontaneously induced in the AZO film growed on SiOC film with high degree of amorphism.