• Journal of Korean Vacuum Science & Technology
• /
• v.1 no.1
• /
• pp.38-44
• /
• 1997

Epitaxial growth of SiC films on Si(111) substrates without carbonization was carried out n the temperature range of 900-100$0^{\circ}C$ under high vacuum conditions by single source chemical vapor deposition (CVD) of 1,3-disilabutane (H$_3$SiCH$_2$SiH$_2$$CH_3$). The monocrystalline nature of the films was confirmed by XRD, RHEED and cross-sectional TED. Cross-sectional TEM image indicated that no void exists and the boundary is clear and smooth at the SiC-Si(111) interface. RBS and AES analyses also showed that the films are stoichiometric and homogeneous in depth, From the results, this single source growth techniqe of using 1,3-disilabutane has been found suitable and effective for epitaxial growth of stoichiometric SiC on Si(111) without carbonization at temperatures below 100$0^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.1
• /
• pp.53-59
• /
• 2003

Using Platinum-silicide (PtSi) formed between silicon substrate and carbon film, we have improved the field emission of electrons from carbon films. Pt films were deposited on n-Si(100) substrates at room temperature by DC sputter technique. After deposition, these PtSi thin films were annealed at 400 ~ $600^{\circ}C$ in a vacuum chamber, and the carbon films were deposited on those Pt/Si substrates by laser ablation at room temperature. The field emission property of C/Pt/Si system is found to be better than that of C/Si system and it is showed that property was improved with increasing annealing temperature. The reasons why the field emission from carbon film was improved can be considered as follows, (1)the resistance of carbon films was decreased due to graphitization, (2)electric field concentration effectively occurred because the surface morphology of carbon film deposited on Pt/si substrates with rough surface, (3)it is showed that annealing induced reaction between Pt film and Si substrate, as a consequence that the interfacial resistance between Pt film and Si substrate was decreased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.175-176
• /
• 2007

This paper describes on the characteristics of Pd thin films deposited on poly-crystalline 3C-SiC buffer layers for microsensors, in which the poly 3C-SiC was grown on Si, $SiO_2$, and AlN substrates, respectively, by APCVD using HMDS, $H_2$, and Ar gas at $1100^{\circ}C$ for 30 min. In this work, a Pd thin film was deposited on the poly 3C-SiC film by RF magnetron sputter. The thickness, uniformity, and quality of these samples were evaluated by SEM. Crystallinity and orientation of the Pd film were analyzed by XRD. Finally, Pd/poly 3C-SiC schottky diodes were fabricated and characterized by current-voltage measurements. From these results, Pd/poly 3C-SiC devices are promising for high temperature hydrogen sensors and other microsensors.

• Journal of Sensor Science and Technology
• /
• v.19 no.3
• /
• pp.197-201
• /
• 2010

This paper describes the fabrication and characteristics of a NO sensor using ZnO thin film integrated 3C-SiC micro heater based on polycrystalline 3C-SiC thin film of operation in harsh environments. The sensitivity, response time, and operating properties in high temperature and voltages of NO sensors based SiC MEMS are measured and analyzed. The sensitivity of device with pure ZnO thin film at the heater operating power of 13.5 mW ($300^{\circ}C$) is 0.875 in NO gas concentration of 0.046 ppm. In the case of Pt doping, the sensitivity of at power consumption of 5.9 mW ($250^{\circ}C$) was 1.92 at same gas flow rate. The ZnO with doped Pt was showed higher sensitivity, lower working temperature and faster adsorption characteristics to NO gas than pure ZnO thin film. The NO gas sensor integrated SiC micro heater is more strength than others in high voltage and temperature environments.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.45-45
• /
• 2009

This paper describes the formation of porous 3C-SiC by anodization. 3C-SiC thin films were deposited on p-type Si(100) substrates by APCVD using HMDS (Hexamethyildisilane: $Si_2(CH_3)_6$). UV-LED(380 nm) was used as a light source. The surface morphology was observed by SEM and the pore size was increased with increase of current density. Pore diameter of 70 ~ 90 nm was achieved at 7.1 $mA/cm^2$ current density and 90 sec anodization time. FT-IR was conducted for chemical bonding of thin film and porous 3C-SiC. The Si-H bonding was observed in porous 3C-SiC around wavenumber 2100 $cm^{-1}$. PL shows the band gap enegry of thin film (2.5 eV) and porous 3C-SiC (2.7 eV).

• Journal of the Korean Ceramic Society
• /
• v.43 no.8 s.291
• /
• pp.492-497
• /
• 2006

SiC coating has been introduced as protective layer in TRISO nuclear fuel particle of High Temperature Gas cooled Reactor (HTGR) due to excellent mechanical stability at high temperature. In order to inhibit the failure of the TRISO particles, it is important to evaluate the fracture strength of the SiC coating layer. ]n present work, thin silicon carbide coating was fabricated using chemical vapor deposition process with different microstructures and thicknesses. Processing condition and surface status of substrate.affect on the microstructure of SiC coating layer. Sphere indentation method on trilayer configuration was conducted to measure the fracture strength of the SiC film. The fracture strength of SiC film with different microstructure and thickness were characterized by trilayer strength measurement method nanoindentation technique was also used to characterize the elastic modulus and th ε hardness of the SiC film. Relationships between microstructure and mechanical properties of CVD SiC thin film were discussed.

• Current Photovoltaic Research
• /
• v.1 no.1
• /
• pp.63-68
• /
• 2013

We investigated the effects of Au eutectic reaction on Si thin film growth by hot wire chemical vapor deposition. Small SiC and Si nano-particles fabricated through a wet etching process were coated and biased at 50 V on micro-textured Si p-n junction solar cells. Au thin film of 10 nm and a Si thin film of 100 nm were then deposited by an electron beam evaporator and hot wire chemical vapor deposition, respectively. The Si and SiC nano-particles and the Au thin film were structurally embedded in Si thin films. However, the Au thin film grew and eventually protruded from the Si thin film in the form of Au silicide nano-balls. This is attributed to the low eutectic bonding temperature ($363^{\circ}C$) of Au with Si, and the process was performed with a substrate that was pre-heated at a temperature of $450^{\circ}C$ during HWCVD. The nano-balls and structures showed various formations depending on the deposited metals and Si surface. Furthermore, the samples of Au nano-balls showed low reflectance due to surface plasmon and quantum confinement effects in a spectra range of short wavelength spectra range.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.36.2-36.2
• /
• 2009

Low dielectric materials have been great attention in the semiconductor industry to develop high performance interlayer dielectrics with low k for Cu interconnect technology. In our study, the dielectric properties of SiOC /SiO2 thin film derived from polyphenylcarbosilane were investigated as a potential interlayer dielectrics for Cu interconnect technology. Polyphenylcarbosilane was synthesized from thermal rearrangement of polymethylphenylsilane around $350^{\circ}C{\sim}430^{\circ}C$. Characterization of synthesized polyphenylcarbosilane was performed with 29Si, 13C, 1H NMR, FT-IR, TG, XRD, GPC and GC analysis. From FT-IR data, the band at 1035 cm-1 is very strong and assigned to CH2 bending vibration in Si-CH2-Si group, indicating the formation of the polyphenylcarbosilane. Number average of molecular weight (Mn) of the polyphenylcarbosilane synthesized at $400^{\circ}C$ for 6hwas 2, 500 and is easily soluble in organic solvent. SiOC/SiO2 thin film was fabricated on ton-type silicon wafer by spin coating using 30wt % polyphenylcarbosilane incyclohexane. Curing of the film was performed in the air up to $400^{\circ}C$ for 2h. The thickness of the film is ranged from $1{\mu}m$ to $1.7{\mu}m$. The dielectric constant was determined from the capacitance data obtained from metal/polyphenylcarbosilane/conductive Si MIM capacitors and show a dielectric constant as low as 2.5 without added porosity. The SiOC /SiO2 thin film derived from polyphenylcarbosilane shows promising application as an interlayer dielectrics for Cu interconnect technology.

• Korean Journal of Materials Research
• /
• v.10 no.4
• /
• pp.276-281
• /
• 2000

Silicon carbide(SiC) films were grown on modified Si(111) surface with a SiNx in the NH$_3$surrounding. Thickness of SiC films was decreased with increasing of the nitridation time. Also, voids having crystal defects were removed at interface of SiC/Si according to growth parameters. SiC films were grown on SiNx/Si substrate of 100, 300 and 500nm thickness. SiC films were deposited along [111] direction and columnar grains of SiC crystal. The void-free film was observed in the interface of SiC/SiNx. This result suggests that fabrication of SiC devices are applied to SiNx replacing silicon oxide in SOI structure.

• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.820-828
• /
• 1995

Ti-sillcides are formed on an atomically clean Si substrate and its phase transition and surface and interface morphologies are examined depending on the Ti-film thicknesses, deposition temperatures and Si substrate orientations. Ti film thicknesses of 400$\AA$ and 200$\AA$ have been deposited at elevated temperatures from 50$0^{\circ}C$ to 90$0^{\circ}C$ with increments of 10$0^{\circ}C$ on Si(100) and Si(111) Ti-silicides are formed and analyzed with using XRD, SEM, and TEM to verify the phase transition and the surface and interface morphologies. The phase transition from C49 to C54 is observed to occur around $650^{\circ}C$ and examined to show some retardation depending on the substrate orientation and film thickness. This retardation of phase transition is explained by the consideration based on the surface and volume free energies. A rough surface of C49 TiSi$_2$is exhibited because of characteristics of nonuniform diffusion across the interface while the smooth surface and island formation of C54 TiSi$_2$is examined.