• Progress in Superconductivity and Cryogenics
• /
• v.16 no.2
• /
• pp.20-23
• /
• 2014

We have grown $MgB_2$ on SiC buffer layer by using metallic Hastelloy tape as the substrate. Hastelloy tape was chosen for its potential practical applications, mainly in the power cable industry. SiC buffer layers were deposited on Hastelloy tapes at 400, 500, and $600^{\circ}C$ by using a pulsed laser deposition method, and then by using a hybrid physical-chemical vapor deposition technique, $MgB_2$ films were grown on the three different SiC buffer layers. An enhancement of critical current density values were noticed in the $MgB_2$ films on SiC/Hastelloy deposited at 500 and $600^{\circ}C$. From the surface analysis, smaller and denser grains of $MgB_2$ tapes are likely to cause this enhancement. This result infers that the addition of SiC buffer layers may contribute to the improvement of superconducting properties of $MgB_2$ tapes.

• Journal of Sensor Science and Technology
• /
• v.16 no.6
• /
• pp.462-466
• /
• 2007

Aluminum nitride (AlN) thin films were deposited on Si substrates by using polycrystalline (poly) 3C-SiC buffer layers, in which the AlN film was grown by pulsed reactive magnetron sputtering. Characteristics of grown AlN films were investigated experimentally by means of FE-SEM, X-ray diffraction, and FT-IR, respectively. The columnar structure of AlN thin films was observed by FE-SEM. X-ray diffraction pattern proved that the grown AlN film on 3C-SiC layers had highly (002) orientation with low value of FWHM (${\Theta}=1.3^{\circ}$) in the rocking curve around (002) reflections. These results were shown that almost free residual stress existed in the grown AlN film on 3C-SiC buffer layers from the infrared absorbance spectrum. Therefore, the presented results showed that AlN thin films grown on 3C-SiC buffer layers can be used for various piezoelectric fields and M/NEMS applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.04b
• /
• pp.3-6
• /
• 2009

Aluminum nitride (AIN) thin films were deposited on a polycrystalline 3C-SiC intermediate layer by a pulsed reactive magnetron sputtering system. Characteristics of the AIN/SiC heterostructures were investigated by field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR). The columnar structure of AIN thin films was observed by FE-SEM. The surface roughness of AlN films on the 3C-SiC buffer layer was measured using AFM. The XRD pattern of AlN films on SiC buffer layers was highly oriented at (002). Full width at half maximum (FWHM) of the rocking curve near (002) reflections was $1.3^{\circ}$. The infrared absorbance spectrum indicated that the residual stress of AIN thin films grown on SiC buffer layers was nearly negligible. The 3C-SiC intermediate layers are promising for the realization of nitride based electronic and mechanical devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.346-347
• /
• 2007

Aluminum nitride (AlN) thin films were deposited on Polycrystalline (poly) 3C-SiC buffer layers using pulsed reactive magnetron sputtering. Characteristics of AlN films were investigated experimentally by means of FE-SEM, X-ray diffraction, and FT-IR, respectively. As a result, highly (002) oriented AlN thin films with almost free residual stress were achieved using 3C-SiC buffer layers. Therefore, AlN thin films grown on 3C-SiC buffer layers can be used for various piezoelectric fields and M/NEMS applications.

• Progress in Superconductivity
• /
• v.14 no.1
• /
• pp.30-33
• /
• 2012

We have grown $MgB_2$ superconducting thin films on the SiC buffer layers by means of hybrid physical-chemical vapor deposition (HPCVD) technique. Prior to that, SiC was first deposited on $Al_2O_3$ substrates at various temperatures from room temperature to $600^{\circ}C$ by using the pulsed laser deposition (PLD) method in a vacuum atmosphere of ${\sim}10^{-6}$ Torr pressure. All samples showed a high transition temperature of ~40 K. The grain boundaries of $MgB_2$ samples with SiC layer are greater in amount, compare to that of the pure $MgB_2$ samples. $MgB_2$ with SiC buffer layer samples show interesting change in the critical current density ($J_c$) values. Generally, at both 5 K and 20 K measurements, at lower magnetic field, all $MgB_2$ films deposited on SiC buffer layers have low $J_c$ values, but when they reach higher magnetic fields of nearly 3.5 Tesla, $J_c$ values are enhanced. $MgB_2$ film with SiC grown at $600^{\circ}C$ has the highest $J_c$ enhancement at higher magnetic fields, while all SiC buffer layer samples exhibit higher $J_c$ values than that of the pure $MgB_2$ films. A change in the grain boundary morphologies of $MgB_2$ films due to SiC buffer layer seems to be responsible for $J_c$ enhancements at high magnetic fields.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.237-237
• /
• 2009

Zinc oxide (ZnO) thin film was deposited on Si substrates using polycrystalline (poly) 3C-SiC buffer layer, in which the ZnO film was grown by sol-gel method. Physical characteristics of the grown ZnO film was investigated experimentally by means of SEM, XRD, FT-IR (Furier Transform-Infrared spectrum), and AFM. XRD pattern was proved that the grown ZnO film on 3C-SiC layers had highly (002) orientation with low FWHM (Full width of half maxium). These results showed that ZnO thin film grown on 3C-SiC buffer layers can be used for various piezoelectric fields and M/NEMS applications.

• The Korean Journal of Ceramics
• /
• v.3 no.3
• /
• pp.163-168
• /
• 1997

Most of heteroepitaxial $\beta$-SiC thin films have been successfully grown on Si(100) adapting a carburizing process, by which a few atomic layers of substrate surface is chemically converted to very thin SiC layer using hydrocarbon gas sources. Using an organo-silicon precursor, bis-trimethylsilymethane (BTMSM, [$C_7H_{20}Si_2$]), heteropitaxial $\beta$-SiC thin films were successfully grown directy on Si substrate without a carburized buffer layer. The defect density of the $\beta$-SiC thin films deposited without a carburized layer was as low as that of $\beta$-SiC films deposited on carburized buffer layer. In addition, void density was also reduced by the formation of self-buffer layer using BTMSM instead of carburized buffer layer. It seems to be mainly due to the characteristic bonding structure of BTMSM, in which Si-C was bonded alternately and tetrahedrally (SiC$_4$).

• Progress in Superconductivity and Cryogenics
• /
• v.17 no.3
• /
• pp.1-4
• /
• 2015

Production of $MgB_2$ film on metallic Hastelloy with SiC as the buffer layer was achieved by means of hybrid physical-chemical vapor deposition technique, whereas SiC buffer layers with varied thickness of 170 and 250 nm were fabricated inside a pulsed laser deposition chamber. Superconducting transition temperature and critical current density were verified by transport and magnetic measurement, respectively. With SiC buffer layer, the reduced delaminated area at the interface of $MgB_2$-Hastelloy and the slightly increased $T_c$ of $MgB_2$ tapes were clearly noticed. It was found that the upper critical field, the irreversibility field and the critical current density were reduced when $MgB_2$ tapes were buffered with SiC buffer layer. Clarifying the mechanism of SiC buffer layer in $MgB_2$ tape in affecting the superconducting properties is considerably important for practical applications.

• Journal of Surface Science and Engineering
• /
• v.42 no.1
• /
• pp.21-25
• /
• 2009

Using an evaporation system, $SiO_2$ was deposited as a buffer layer between a PET substrate and a ITO layer and then ITO/$SiO_2$/PET layers were annealed for 1.5 hours at the temperature of $180^{\circ}C$. Adhesion and electro-optical properties of ITO films were studied with thickness variance of a $SiO_2$ buffer layer. As a result of introduction of the $SiO_2$ buffer layer, sheet resistance and resistivity increased and a ITO film with optimum sheet resistance ($529.3{\Omega}/square$) for an upper ITO film of resistive type touch panel could be obtained when $SiO_2$ of $50{\AA}$ was deposited. And it was found that ITO films with $SiO_2$ buffer layer have higher transmittance of $88{\sim}90%$ at 550 nm wavelength than ITO films with no buffer layers and the transmittance was enhanced as $SiO_2$ thickness increased from $50{\AA}$ to $100{\AA}$. Adhesion property of ITO films with $SiO_2$ buffer layers became better than ITO films with no buffer layers and this property was independent of $SiO_2$ thickness variance ($50{\sim}100{\AA}$). By depositing a $SiO_2$ buffer layer of $50{\AA}$ on the PET substrate and sputtering a ITO thin film on the layer, a ITO film with enhanced adhesion, electro-optical properties could be obtained.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.316-316
• /
• 2008

Using an evaporation method, $SiO_2$ was deposited as a buffer layer between a flexible PET substrate and a ITO film deposited by DC magnetron sputtering and electro-optical properties were investigated with thickness variance of $SiO_2$ layers. After coating a $SiO_2$ layer and a ITO film, the ITO/$SiO_2$/PET was heated up to $200^{\circ}C$ and the resistivity and the transmittance were measured by hall effect measurement system and UV/VIS/NIR spectroscopy. As a result of depositing a $SiO_2$ buffer layer, the resistivity increased and the transmittance and adhesion property were enhanced than ITO films with no buffer layers and the resistivity was lowered as $SiO_2$ thickness increased from 50 $\AA$ to 100 $\AA$. It was found that the transmittance was independent of annealing temperature variance in $150^{\circ}C{\sim}200^{\circ}C$ and the resistivity decreased as the temperature increased and especially decreasing rate of the resistivity was higher as the buffer layer thickness was thinner. So under optimized depositing of $SiO_2$ buffer layers and post-annealing of ITO/$SiO_2$/PET, ITO films with enhanced adhesion, electro-optical properties can obtained.