• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.26-39
• /
• 1999

Bis-GMA, the representative monomer of bonding resin, contributes to the rigidity of bonding layer. Hydrophilic monomer contributes to the permeability into dentin substrates while weaken the bonding layer due to its small molecular weight. The degree of conversion also contributes to the ultimate strength of the bonding layer. This study was performed for the correlation analysis of monomer ratio and dentin bonding strength via degree of conversion. 7 experimental bonding resins were prepared with Bis-GMA, ratio from 20% to 80% by 10% increment, and hydrophilic HEMA monomer. Their degree of conversion and shear bond strength to dentin were compared with Scotchbond Multi-Purpose adhesive, and the fractured surfaces were examined microscopically. The results were as follows; 1. The degree of conversion increased when, the ratio of Bis-GMA increased from 20% to 70%, whereas it decreased when the ratio of Bis-GMA was 80%. 2. Shear bond strengths of the experimental bonding resins of 80%, 70%, 60% ratio of Bis-GMA were significantly higher than those of the experimental bonding resin of 50% ratio of Bis-GMA and Scotchbond Multi-Purpose adhesive. Lower shear bond strengths were obtained with the experimental bonding resins of 40%, 30%, 20% ratio of Bis-GMA (p<0.05). 3. Adhesive fractures were associated with the bonding resins of the lower bond strength, while cohesive fractures within the bonding resin layer were associated with the bonding resins of higher bond strength. Bonding resins with shear bond strength higher than 18MPa showed some cohesive fractures within the composite resin or within the dentin. 4. Correlations between Bis-GMA ratio and the degree of conversion (r=0.826), between Bis-GMA ratio and shear bond strength (r=0.853), and between the degree of conversion and shear bond strength (r=0.786) were significant (p<0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.23 no.2
• /
• pp.450-460
• /
• 1996

The purpose of this study was to compare shear bond strength of composite resin using several dentin bonding agents and light cured glass ionomer cement(Fuji II LC). 40 Bovine primary anterior teeth were used for this experiment. Labial surface of teeth were flattened. It were divided into four groups. Each group was composed of 10 teeth. The material used for this experiment were Scotchbond Multipurpose-Z-100, Allbond 2-Aelitefil, Gluma-Pekalux, light cured glass ionomer cement(Fuji II LC). Each of the materials was applied to the exposed surfaces of 10 teeth by insertion into a cylindrical shaped matrix which is 3mm diameter and 3mm in height. The completed specimens were stored at $37^{\circ}C$ under 100% humidity for 24 hours : the shear bond strength of each material to dentin surface were measured with INSTRON universal testing machine. The results were as follows : 1. Shear bond strength to dentin surface increased in order of light cured glass ionomer cement(Fuji II LC), Gluma, Allbond 2, Scotchbond Multipurpose. 2. Between shear bond strength of light cured glass ionomer cement(Fuji II LC) and Allbond 2, there was statistical significace(p<0.05) 3. Between shear bond strength of light cured glass ionomer cement(Fuji II LC) and Scotchbond Multipurpose, between shear bond strength of Gluma and Scotchbond Multipurpose, there was statistical significance.(p<0.01) The shear bond strength of dentin bonding agents were higher than light cured glass ionomer cement. The reason is that materials and quality of dentin bonding agent were enhanced. Further investigation is necessary to improve shear bond strength of light cured glass ionomer cement.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.247-256
• /
• 1998

To evalutate the change in shear bond strength according to dentin surface treatment, 4 materials were divided into control group(A) and experimental group(B). Group A was treated according to the instruction of manufacture. Group B was treated with 32% phosphoric acid. After dentin surface treatment, each material was bonded and stored in 100% humidity during 7 days, and then, the shear bond strength was evaluated. The results were as follows: 1. In the case of treatment according to the instruction of manufacture, the shear bond strength according to material showed Z-100 to be highest with 12.42 MPa, Compoglass had the lowest shear bond strength with 4.23 MPa and there was significant difference between Compoglass and Z-100, Dyract (p<0.01). 2. The group treated with 32% phosphoric acid showed lower shear bond strength than that of the group treated according to the instruction of manufacture but there was no statistical significance. 3. As a result of observation under SEM, the fracture pattern was a mixture of cohesive and adhesive failure in group 1, and there was more adhesive failure in group 2, and in group 3 and 4 there was cohesive failure of material or tooth structure. From the results above Dyract showed shear bond strength levels between resin and resin -modified glass ionomer but Compoglass showed much lower shear bond strength than that of resin-modified glass ionomer thus indicating that even though they are the same type of material they show evident differences in physical properties. And it is thought that the treatment of dentin surface with phosphoric acid did not increase the shear bond strength, unlike enamel.

• Restorative Dentistry and Endodontics
• /
• v.26 no.2
• /
• pp.171-179
• /
• 2001

The purpose of this study was to evaluate the shear bond strength of compomers according to dentin surface treatment. Two materials of compomer were devided into six groups. The compomer used in this study were Dyract AP(D) and F2000(F), Group 1 (DN) and 4(FN) were treated according to manufacturers instructions as control groups. Group 2(DE) and 5(FE) were treated with 37％ phosphoric acid and group 3(DA) and 6(FA) were treated with air abrasion unit (80 psi, 50 m aluminum oxide particles) respectively as experimental groups. After dentin surface treatment, compomers were bonded. Completed samples were stored in 100％ humidity. 37C during 7 days, and then, the shear bond strength of specimens were evaluated. The results were as follows: 1. In the case of Dyract AP, the shear bond strength was showed the highest value of 9.10 MPa in dentin surface treatment with air abrasion unit. but there were no significant differences to the other groups. 2. In the case of F2000. the shear bond strength was showed the highest value of 13.51MPa and there were significant differences to the other groups(p<0.05). 3. The shear bond strength of F2000 was higher than Dyract AP in each dentin surface treatment. and in the case of etching and air abrasion. there were significant differences(p<0.05). 4. As a result of observation of SEM. the most of fracture pattern was adhesive failure in group 1(DN), 2(DE) and 4(FN), and cohesive failure in group 3(DA), S(FE) and 6(FA).

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.6
• /
• pp.654-663
• /
• 2004

Statement of problem. According to the fracture pattern in several reports, fractures most frequently occur in the interface between the ceromer and the substructure. Purpose. The aim of this in vitro study was to compare the macro shear bond strength and microshear bond strength of a ceromer bonded to a fiber reinforced composite (FRC) as well as metal alloys. Material and methods. Ten of the following substructures, type II gold alloy, Co-Cr alloy, Ni-Cr alloy, and FRC (Vectris) substructures with a 12 mm in diameter, were imbedded in acrylic resin and ground with 400, and 1, 000-grit sandpaper. The metal primer and wetting agent were applied to the sandblasted bonding area of the metal specimens and the FRC specimens, respectively. The ceromer was placed onto a 6 mm diameter and 3 mm height mold in the macro-shear test and 1 mm diameter and 2 mm height mold in the micro-shear test, and then polymerized. The macro- and micro-shear bond strength were measured using a universal testing machine and a micro-shear tester, respectively. The macro- and micro-shear strength were analyzed with ANOVA and a post-hoc Scheffe adjustment ($\alpha$ = .05). The fracture surfaces of the crowns were then examined by scanning electron microscopy to determine the mode of failure. Chi-square test was used to identify the differences in the failure mode. Results. The macro-shear strength and the micro-shear strength differed significantly with the types of substructure (P<.001). Although the ceromer/FRC group showed the highest macroand micro-shear strength, the micro-shear strength was not significantly different from that of the base metal alloy groups. The base metal alloy substructure groups showed the lowest mean macro-shear strength. However, the gold alloy substructure group exhibited the least micro-shear strength. The micro-shear strength was higher than the macro-shear strength excluding the gold alloy substructure group. Adhesive failure was most frequent type of fracture in the ceromer specimens bonded to the gold alloys. Cohesive failure at the ceromer layer was more common in the base metals and FRC substructures. Conclusion. The Vectris substructure had higher shear strength than the other substructures. Although the shear strength of the ceromer bonded to the base metals was lower than that of the gold alloy, the micro-shear strength of the base metals were superior to that of the gold alloy.

• The korean journal of orthodontics
• /
• v.22 no.1
• /
• pp.43-65
• /
• 1992

Bonding orthodontic adhesive resins to glazed porcelain surface is not attainable. The aim of this investigation was to examine, in vitro, the effect of three methods of porcelain surface pretreatment on the shear bond strength of orthodontic adhesives, and to compare the shear strength of orthodontic bracket bonding to porcelain surface by the best results that to human enamel. Porcelain disks ($Ceramco^{(TM)}$ and $Vita^{(TM)}$) baked in the laboratory were roughened by sandpapers, #320, #600, #800, #1000 and #1200, and were pretreated with silane and dried at the various temperatures, room temperature, $50^{\circ}C$, $70^{\circ}C$ and $90^{\circ}C$, and were etched by 3% hydrofluoric acid solution for 1, 3, 5, 7, and 9 minutes, orthodontic adhesives (System $1+^{(TM)}$ and $Unite^{(TM)}$) were applied on them, and shear bond strengths were measured by Instron. The best results of pretreatment of each method were determined by the shear bond strengths. Again, porcelain disks were pretreated by the determined best results and human enamel were etched by 37% hydrofluoric acid solution, orthodontic brackets were bonded on them by the orthodontic adhesives, and the shear bond strengths were measured and compared between them. 1. Roughening porcelain surfaces with coarse sandpaper (#300) showed higher shear bond strength than that with finer sandpapers, but it $(22.44Kgf/cm^2)$ was distinguishably low compared to that from etched human enamel $(144.11Kgf/cm^2)$. 2. There were disparities in shear bond strengths upon the orthodontic resins, which was presumably related to the contents of fillers in orthodontic adhesive resins. Also there were disparities in shear bond strength upon the porcelains which had different composition. 3. Silane enhanced the shear bond strength of orthodontic resins to porcelain surfaces ($25.20Kgf/cm^2$ at $50^{\circ}C$), which was markedly low compared to that from etched human enamel. 4. Etched porcelain surface with 3% hydrofluoric acid solution for 1 to 9 minutes showed no difference in shear bonding strength of orthodontic adhesive resins. Shear bond strength from etched porcelain $(97.43-120.72Kgf/cm^2)$ were as high as clinically available, but low compared to that from etched human enamel. 5. Roughening with #300 sandpaper and etching by 3% hydrofluoric acid followed silane application on porcelain surface showed lower shear bond strength than etched human enamel, but were as high as clinically useful. 6. The results suggest that etching porcelain surface by 3% hydrofluoric acid solution might provide comparatively high shear bond strength as much as clinically favorable.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.4
• /
• pp.697-705
• /
• 1997

The purpose of this study was to evaluate the effects of two metal adhesive primers on the shear bond strengths of self-curing resin to Ni-Cr a]toy and the effects of 1000 thermal cycling on the durability of the bond. The two selected metal adhesive primers were Metal Primer II(G-C corp., Japan) and MR Bond(Tokuyama corp., Japan) and no treatment groups were used as control. All specimens were divided into two groups according to thermal cycling. In the group without thermal cycling, the specimens were stored in water for 24 hours. In the group with thermal cycling, the specimens were thermocycled 1000 times at temperature of $5^{\circ}C\;and\;55^{\circ}C$. Shear bond strengths were measured using the Universal testing machine(Zwick 145641, Germany) with a crosshead speed of 0.5 mm/min. The results were as follows: 1. MR Bond significantly improved the shear bond strength of resin to Ni-Cr alloy before and after thermal cycling. 2. There were no difference in the shear bond strength of resin to Ni-Cr alloy between Metal Primer II treated group and no treatment group. 3. Regardless of the type and the use of adhesive primers, there were tendency of decrease in shear bond strength with 1000 thermal cycling.

• Restorative Dentistry and Endodontics
• /
• v.20 no.1
• /
• pp.351-361
• /
• 1995

The purpose of this study was to evaluate the shear bond strength of the composite resin bonded on the bleached enamel surface according to its surface treatment. 90 extracted human premolars were divided into six groups. : enamel unbleached (control group) and enamel bleached with 15% carbamide peroxide for 2 weeks (experimental groups: 1, 2, 3, 4 and 5). The surface of bleached enamel in all experimental groups was treated by following manners. Experimental group 1 : catalase immersion for 3 mimutes. Experimental group 2 : catalase immersion for 15 mimutes. Experimental group 3 : artificial saliva immersion for 1 hour. Experimental group 4 : artificial saliva immersion for 48 hours. Experimental group 5: surface reduction of the bleached enamel about 0.5mm-1mm with superfine diamond bur. Composite resin molds(3mm height, 3mm diameter) were bonded to the untreated enamel and treated. The shear bond strengths of composite resin bonded to enamel of each specimen were tested with universal testing machine at a crosshead speed of 5mm/min and 500Kg in full scale and analyzed statistically. The following results were obtained : 1. Control group had the highest shear bond strength with $19.92{\pm}5.14$ MPa and experimental group 5 had the lowest shear bond strength with $11.15{\pm}4.23$ MPa. 2. Control group showed significant differences in shear bond strength with experimental group 1(P<0.05). 3. Control group showed significant differences in shear bond strength with experimental group 5(P<0.05). 4. Experimental group 4 showed significant differences in shear bond strength with experimental group 5(P<0.05). 5. Experimental group 3 showed no significant differences in shear bond strength with experimental group 4(P<0.05).

• Journal of Technologic Dentistry
• /
• v.43 no.1
• /
• pp.6-12
• /
• 2021

Purpose: This study aimed to compare the shear bond strength between zirconia cores and veneer ceramics as per the sand blasting and liner treatments. Methods: The following 4 groups of zirconia-veneering ceramic specimens were prepared: (1) Group I, untreated; (2) Group II, with 110 ㎛ aluminium oxide (Al2O3) sandblasting; (3) Group III, with liner (IPS e.max ZirLiner; Ivoclar Vivadent); and (4) Group IV, with 110 ㎛ Al2O3 sand blasting and liner. Surface roughness was measured for all the prepared specimens, and the surface morphology was observed using a scanning electron microscope. All the samples (n=40) were fixed with measuring jigs, and shear bond strengths were obtained using a universal testing machine with a crosshead speed of 0.5 mm/min. The shear bond strength data were analyzed using one-way analysis of variance and t-test. The post hoc comparison was performed using the Tukey's test (α=0.05). Results: A significant difference in the surface roughness was observed between the specimens of groups I and II (p<0.05). Surface treatment with liner and sandblasting showed higher shear bond strength between zirconia core and veneering ceramic (p<0.05). Conclusion: The sand blasting and liner treatment increased the shear bond strength between zirconia core and veneering ceramic.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.6
• /
• pp.805-814
• /
• 2007

Statement of problem. Composite resin-veneered metal restorations can be used as an alternative to porcelain-fused-metal restorations. But, because of the relatively low bond strength of veneering composite to metal framework, various surface treatment methods have been introduced to improve the bond strength. Purpose. The object of this study was to compare the shear bond strength of different combinations of each of the two bonding systems and each of the two composite veneering resins to cp-Ti/Co-Cr alloy. Material and methods. Two resin bonding systems (metal conditioner containing MEPS monomer, tribochemical silicoating system) and two composite resins (Gradia, Sinfony) were tested on cp-Ti and Co-Cr alloy. Then, according to manufacturers' instructions, resin bonding systems and composite resins were applied. All test specimens were divided into four groups for each alloy; I) sandblast + Metal Primer II + Gradia (MG), II) sandblast + Metal Primer II + Sinfony (MS), III) Rocatec + Gradia (RG), IV) Rocatec + Sinfony (RS). The shear bond strength was determined using a universal testing machine and all data were statistically analyzed with Mann-Whitney test and Kruskal-Wallis test at the significance level of 0.05. Results. The mean (standard deviations) of shear bond strength according to the combinations of two bonding systems and two composite resins to cp-Ti arranged from 16.44 MPa to 17.07 MPa and the shear bond strength to Co-Cr alloy ranged from 16.26 MPa to 17.70 MPa. The result shows that the difference were not statistically significant. Conclusion. The shear bond strengths of composite resins to both cast cp-Ti and Co-Cr alloy were not significantly different between the metal conditioner and the tribochemical silicoating system. And no differences in bond strength were found between cp-Ti and Co-Cr alloy.