• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.2
• /
• pp.65-70
• /
• 2021

In this study, interfacial properties and mechanical properties of joints were reported after Cu pads finished with organic solderability preservative (OSP) on flame retardant-4 (FR-4) printed circuit board (PCB) and electronic components were joined with a Sn-57Bi-1Ag solder paste by using a laser bonding process. The laser bonding process was performed under various bonding conditions with changing a laser power and a bonding time and effects of bonding conditions on interfacial and mechanical properties of joints were analyzed. In order to apply for industry, properties of bonding joints using a reflow bonding process which are widely used were compared. When the laser bonding process were performed, we observed that Cu₆Sn₅ intermetallic compounds (IMCs) were fully formed at the interface although the bonding times were very short about 2 and 3 s. Furthermore, void formations of the joints by using the laser bonding process were suppressed at the joints with comparing to the reflow bonding process and shear strengths of bonding joints were higher than that by using the reflow bonding process. Therefore, in spite of a very short bonding time, it is expected that joints will be stably formed and have a high mechanical strength by using the laser bonding process.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.9-18
• /
• 1999

In this study, Metallugical properties between Sn-3.5Ag, Sn-37Pb eutectic solders and Au/Ni/cu substrate according to time span above the melting point were investigated. A conventional reflow soldering machine wert used for this study and time span above the melting point was determined by changing peak soldering temperature and conveyor speed. As results, scallop type intermetallic compounds of $Ni_3Sn_4$ were formed at joint interface and no Cu-Sn compounds were found at all; Ni layer performed as a barrier for Cu diffusion. As the peak soldering temperature increased, thickness of the intermetallic compound layer increased; maximum thickness of the scallop-layer was 2.2$\mu\textrm{m}$. The shape of scallops were transformed from hemi-sphere type to elliptical shape with smaller size. Micro-hardness of the solder joint decreased as the eutectic structure of Sn-3.5Ag and Sn-37Pb increased.

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.799-806
• /
• 2000

Cu$_{6}$Sn$_{5}$-dispersed 63Sn-37Pb solder bumps of 760$\mu\textrm{m}$ size were fabricated on Au(0.5$\mu\textrm{m}$)/Ni(5$\mu\textrm{m}$)/Cu(27$\pm$20$\mu\textrm{m}$) BGA substrates by screen printing process, and their shear strength were characterized with variations of dwell time at reflow peak temperature and aging time at 15$0^{\circ}C$ . With dwell time of 30 seconds at reflow peak temperature, the solder bumps with Cu$_{6}$Sn$_{5}$ dispersion exhibited higher shear strength than the value of the 63Sn-37Pb solder bump. With increasing the dwell time longer than 60 seconds, however the shear strength of the Cu$_{6}$Sn$_{5}$-dispersed solder bumps became lower than that the 63Sn-37Pb solder bumps. The failure surface of the solder bumps could be divided into two legions of slow crack propagation and critical crack propagation. The shear strength of the solder bumps was inversely proportional to the slow crack propagation length, regardless of the dwell time at peak temperature, aging time at 150 $^{\circ}C$ and the volume fraction of Cu$_{6}$Sn$_{5}$ dispersion.> 5/ dispersion.

• Design & Manufacturing
• /
• v.2 no.3
• /
• pp.6-9
• /
• 2008

This paper describes the process of structure analysis and injection molding analysis to manufacture the forming injection dies for huge glass insert. Factors such as filling time, filling pressure, material temperature, shrinkage, warpage were investigated by using the analysis software, Moldflow. Runner system and cavity structure were designed and manufactured through the results of deformation analysis data for glass insert. Filling time and filling pressure were analyzed in 3.756sec and 43.37MPa.

• Journal of Wetlands Research
• /
• v.24 no.1
• /
• pp.38-43
• /
• 2022

Smart sewage treatment plant means creating a safe and clean water environment by establishing an ICT-based real-time monitoring, remote control management and intelligent system for the entire sewage treatment process. The core technology of such a smart sewage treatment plant can be operation control technology using measuring instruments. This research team analyzed and suggested the operation control technologies necessary for the establishment of the intelligent business by referring to the intelligent research projects of the sewage treatment plant in progress in Korea. As a result of the analysis, a total of six removal technologies were presented, including control by scale, reflow water control, linked treated water control, chemical quantity control, winter operation control, and total organic carbon control. By size, standards that can be classified into small and medium-sized large-scale are presented, and in the case of reflow water control, the location of water quality and flow sensors capable of managing reflow water is suggested. In the case of the linked treated water control, the influence and control points of the linked treated water on the sewage treatment plant were presented, and in the case of the chemical injection volume control, a system capable of optimizing the amount of chemical injection according to the introduction of an intelligent sewage treatment plant was presented. In the case of winter operation, the sensors and pumps to be controlled are suggested when considering the decrease in nitrification due to the decrease in water temperature. In the case of total organic carbon control, an interlocking system considering the total amount of pollution in the future was proposed. These operation control scenarios are expected to be used as basic data to be used in intelligent sewage treatment algorithms and scenarios in the future.

• Journal of the Semiconductor & Display Technology
• /
• v.17 no.4
• /
• pp.42-45
• /
• 2018

As The semiconductor decrease from 10 nanometer to 7 nanometer, It is suggested that "More than Moore" is needed to follow Moore's Law, which has been a guide for the semiconductor industry. Fan-Out Wafer Level Package(FOWLP) is considered as the key to "More than Moore" to lead the next generation in semiconductors, and the reasons are as follows. the fan-out WLP does not require a substrate, unlike conventional wire bonding and flip-chip bonding packages. As a result, the thickness of the package reduces, and the interconnection becomes shorter. It is easy to increase the number of I / Os and apply it to the multi-layered 3D package. However, FOWLP has many issues that need to be resolved in order for mass production to become feasible. One of the most critical problem is the warpage problem in a process. Due to the nature of the FOWLP structure, the RDL is wired to multiple layers. The warpage problem arises when a new RDL layer is created. It occurs because the solder ball reflow process is exposed to high temperatures for long periods of time, which may cause cracks inside the package. For this reason, we have studied warpage in the FOWLP structure using commercial simulation software through the implementation of the reflow process. Simulation was performed to reproduce the experiment of products of molding compound company. Young's modulus and poisson's ratio were found to be influenced by the order of influence of the factors affecting the distortion. We confirmed that the lower young's modulus and poisson's ratio, the lower warpage.

• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.64-69
• /
• 2012

Sn-Bi eutectic alloy has been widely used as one of the key solder materials for step soldering at low temperature. The Sn-58Bi solder paste containing chloride flux was adopted to compare with that using the chloride-free flux. The paste was applied on the electroless nickel-immersion gold (ENIG) surface finish by stencil printing, and the reflow process was then performed at $170^{\circ}C$ for 10 min. After reflow, the solder joints were aged at $125^{\circ}C$ for 100, 200, 300, 500 and 1000 h in an oven. The interfacial microstructures were obtained by using scanning electron microscopy (SEM), and the composition of intermetallic compounds (IMCs) was analyzed using energy dispersive spectrometer (EDS). Two different IMC layers, consisting of $Ni_3Sn_4$ and relatively very thin Sn-Bi-Ni-Au were formed at the solder/surface finish interface, and their thickness increased with increasing aging time. The wettability of solder joints was investigated by wetting balance test. The mechanical property of each aging solder joint was evaluated by the ball shear test in accordance with JEDEC standard (JESD22-B117A). The results show that the highest shear force was measured when the aging time was 100 h, and the fracture mode changed from ductile fracture to brittle fracture with increasing aging time. On the other hand, the chloride flux in the solder paste did not affect the shear force and fracture mode of the solder joints.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.219-221
• /
• 2005

Sn-9Zn solder balls were bonded to Cu, ENIG (Electroless Nickel/Immersion Gold) and electrolytic Au/Ni pads, and the effect of aging on their joint reliability was investigated. The interfacial products were different from the general reaction layer formed in a Sn-base solder. The intermetallic compounds formed in the solder/Cu joint were $Cu_{5}Zn_{8}$ and $Cu_{6}Sn_{5}$. After aging treatment, voids formed irregularly at the bottom side of the solder because of Sn diffusion into the $Cu_{5}Zn_{8}$ IMC. In the case of the solder/ENIG joint, $AuZn_{3}$ IMCs were formed at the interface. In the case of the Au/Ni/Cu substrate, an $AuZn_{3}$ IMC layer formed at the interface due to the fast reaction between Au and Zn. In addition, the $AuZn_{3}$ IMC layer became detached from the interface after reflow. When the aging time was extended to 100 h, $Ni_{5}Zn_{21}$ IMC was observed on the Ni substrate.

• Journal of Welding and Joining
• /
• v.18 no.6
• /
• pp.74-82
• /
• 2000

The fluxless wetting properties of UBM-coated Si-wafer to the binary lead-free solders(Sn-Ag, Sn-Sb, Sjn-In, Sn0Bi) were estimated by wetting balance method. With the new wettability indices from the wetting curves of one side coated specimen, the wetting property estimation of UBM-coated Si-wafer was possible. For UBM of Si-chip, Au/Cu/Cr UBm was better than au/Ni/TI in the point of wetting time/ At general reflow process temperature, the wettability of high melting point solders(Sn-Sb, Sn-Ag) was better than that of low melting point one(Sn-Bi, Sn-In). The contact angle of the one side coated Si-plate to the solder could be calculated from the force balance equation by measuring the static state force and the tilt angle.

• Transactions of the Society of Information Storage Systems
• /
• v.10 no.2
• /
• pp.55-60
• /
• 2014

Laser projector has many advantages of high brightness, high resolution and small size, but the huge drawback of image degradation called speckle which generated by coherence of laser and roughness of surface interrupts their general use. There are many methods to reduce speckle pattern, but they need effective optical systems to realize display to the far field with huge volume. We designed speckle reduction element by using microlens with controlled curvature to reduce spatial coherence. Vibration element was also applied to reduce temporal coherence which considered response time of eye. Designed element was fabricated by simple reflow method and imprinting method. From the results, the fabricated element performed 48.33% of speckle reduction efficiency and 41.29% of optical efficiency with a single doublet lens.