Reliability study of Sn-Zn lead-free solder for SMT application

표면실장 적용을 위한 Sn-Zn 무연 솔더의 신뢰성 연구

Sn-9Zn solder balls were bonded to Cu, ENIG (Electroless Nickel/Immersion Gold) and electrolytic Au/Ni pads, and the effect of aging on their joint reliability was investigated. The interfacial products were different from the general reaction layer formed in a Sn-base solder. The intermetallic compounds formed in the solder/Cu joint were $Cu_{5}Zn_{8}$ and $Cu_{6}Sn_{5}$. After aging treatment, voids formed irregularly at the bottom side of the solder because of Sn diffusion into the $Cu_{5}Zn_{8}$ IMC. In the case of the solder/ENIG joint, $AuZn_{3}$ IMCs were formed at the interface. In the case of the Au/Ni/Cu substrate, an $AuZn_{3}$ IMC layer formed at the interface due to the fast reaction between Au and Zn. In addition, the $AuZn_{3}$ IMC layer became detached from the interface after reflow. When the aging time was extended to 100 h, $Ni_{5}Zn_{21}$ IMC was observed on the Ni substrate.