• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.3
• /
• pp.263-267
• /
• 2007

We investigate the influence of the ambient gas during thermal annealing on the photoluminescence (PL) properties of europium-silicate thin films. The films were fabricated on substrates by using a radio-frequency magnetron sputtering method and subsequent rapid thermal annealing (RTA). The mechanism for the formation of the europium silicates during the annealing process was investigated by using X-ray diffraction (XRD) spectroscopy, Auger electron spectroscopy (AES) and transmission electron microscopy (TEM). A series of narrow PL spectra from $Eu^{3+}$ ions was observed from the film annealed in $O_2$ ambient. Broad PL spectra associated with $Eu^{2+}$ ions, with a maximum intensity at 600 nm and a FWHM of 110 nm, were observed from the thin film annealed at $1000^{\circ}C$ in $N_2$ ambient.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.418-419
• /
• 2006

We investigate the influence of the ambient gas during thermal annealing on the photoluminescence (PL) properties of europium-silicate thin films. The films were fabricated on substrates by using a radio-frequency magnetron sputtering method and subsequent rapid thermal annealing (RTA). The mechanism for the formation of the europium silicates during the annealing process was investigated by using X-ray diffraction (XRD) spectroscopy, Auger electron spectroscopy (AES) and transmission electron microscopy (TEM). A series of narrow PL spectra from $Eu^{3+}$ ions was observed from the film annealed in $O_2$ ambient. Broad PL spectra associated with $Eu^{2+}$ ions, with a maximum intensity at 600 nm and a FWHM of 110 nm, were observed from the thin film annealed at $1000^{\circ}C$ in $N_2$ ambient.

• Korean Journal of Materials Research
• /
• v.24 no.9
• /
• pp.443-450
• /
• 2014

Amorphous (a-Si) films were epitaxially crystallized on a very thin large-grained poly-Si seed layer by a silicide-enhanced rapid thermal annealing (SERTA) process. The poly-Si seed layer contained a small amount of nickel silicide which can enhance crystallization of the upper layer of the a-Si film at lower temperature. A 5-nm thick poly-Si seed layer was then prepared by the crystallization of an a-Si film using the vapor-induced crystallization process in a $NiCl_2$ environment. After removing surface oxide on the seed layer, a 45-nm thick a-Si film was deposited on the poly-Si seed layer by hot-wire chemical vapor deposition at $200^{\circ}C$. The epitaxial crystallization of the top a-Si layer was performed by the rapid thermal annealing (RTA) process at $730^{\circ}C$ for 5 min in Ar as an ambient atmosphere. Considering the needle-like grains as well as the crystallization temperature of the top layer as produced by the SERTA process, it was thought that the top a-Si layer was epitaxially crystallized with the help of $NiSi_2$ precipitates that originated from the poly-Si seed layer. The crystallinity of the SERTA processed poly-Si thin films was better than the other crystallization process, due to the high-temperature RTA process. The Ni concentration in the poly-Si film fabricated by the SERTA process was reduced to $1{\times}10^{18}cm^{-3}$. The maximum field-effect mobility and substrate swing of the p-channel poly-Si thin-film transistors (TFTs) using the poly-Si film prepared by the SERTA process were $85cm^2/V{\cdot}s$ and 1.23 V/decade at $V_{ds}=-3V$, respectively. The off current was little increased under reverse bias from $1.0{\times}10^{-11}$ A. Our results showed that the SERTA process is a promising technology for high quality poly-Si film, which enables the fabrication of high mobility TFTs. In addition, it is expected that poly-Si TFTs with low leakage current can be fabricated with more precise experiments.

• The Journal of the Korea institute of electronic communication sciences
• /
• v.15 no.4
• /
• pp.665-670
• /
• 2020

Buffer layer in CIGS thin-film solar cells improves energy conversion efficiency through band alignment between the absorption layer and the window layer. ZnS is a non-toxic II-VI compound semiconductor with direct-transition band gaps and n-conductivity as well as with excellent lattice matching for CIGS absorbent layers. In this study, the structural and optical properties of ZnS thin films, deposited by RF magnetron sputtering method and subsequently performed by the rapid thermal annealing treatment, were investigated for the buffer layer. The zincblende cubic structures along (111), (220), and (311) were shown in all specimens. The rapid thermal annealed specimens at the relatively low temperatures were polycrystalline structure with the wurtzite hexagonal structures along (002). Rapid thermal annealing at high temperatures changed the polycrystalline structure to the single crystal of the zincblende cubic structures. Through the chemical analysis, the zincblende cubic structure was obtained in the specimen with the ratio of Zn/S near stoichiometry. ZnS thin film showed the shifted absorption edge towards the lower wavelength as annealing temperature increased, and the mean optical transmittance in the visible light range increased to 80.40% under 500℃ conditions.

• Journal of the Optical Society of Korea
• /
• v.20 no.1
• /
• pp.130-134
• /
• 2016

The influence of Au/Ni-based contact formed on a lightly-doped (7.3×1017cm−3, Zn-doped) InGaAsP layer for electrical compensation of surface plasmon polariton (SPP) propagation under various rapid thermal annealing (RTA) conditions has been studied. The active control of SPP propagation is realized by electrically pumping the InGaAsP multiple quantum wells (MQWs) beneath the metal planar waveguide. The metal planar film acts as the electric contact layer and SPP waveguide, simultaneously. The RTA process can lower the metal-semiconductor electric contact resistance. Nevertheless, it inevitably increases the contact interface morphological roughness, which is detrimental to SPP propagation. Based on this dilemma, in this work we focus on studying the influence of RTA conditions on electrical control of SPPs. The experimental results indicate that there is obvious degradation of electrical pumping compensation for SPP propagation loss in the devices annealed at 400℃ compared to those with no annealing treatment. With increasing annealing duration time, more significant degradation of the active performance is observed even under sufficient current injection. When the annealing temperature is set at 400℃ and the duration time approaches 60s, the SPP propagation is nearly no longer supported as the waveguide surface morphology is severely changed. It seems that eutectic mixture stemming from the RTA process significantly increases the metal film roughness and interferes with the SPP signal propagation.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.2
• /
• pp.49-54
• /
• 2002

Cobalt silcides thin films were prepared on Poly-Si/$SiO_2$/Si substrates by Co metal depostion using E-beam evaporation method and rapid thermal annealing for the application of inkjet printing heater. The crystal phases and composition distributions of the films were investigated as functions of the rapid thermal annealing (RTA) temperatures (600~$900^{\circ}C$) and times (20~40 sec). The high temparature thermal stability was also investigated by the analysis of sheet resistance and crystalline properties. The stable $CoSi_2$ phases were obtained by the RTA annealing at $800^{\circ}C$ for 20 seconds showing $0.8 \Omega /\Box$ of sheet resitance. However, the sheet resistances were sharply increased at below $700^{\circ}C$ due to changes of crystalline phases. The temperature resistance coefficient of heating elements was found to be about $0.0014/^{\circ}C$, and the obtained cobalt silicided films can be applied to the printer heating elements.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.333-336
• /
• 2006

High Pressure Annealing System was developed to improve the characteristics of low-temperature poly-silicon thin film transistors.. (TFTs). The high-pressure steam annealing was applied to the poly-silicon film made by rapid thermal annealing method. The carrier lifetime was investigated by Microwave detection of the Photo-Conductive Decay and the increase of carrier lifetime which indicates the reduction of the defect was observed by high-pressure steam annealing of 1MPa 600C 1hour.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.11
• /
• pp.734-739
• /
• 2017

We prepared $SnS_x$ thin films on both soda-lime glass (SLG) and molybdenum(Mo)/SLG substrates by a two-step process using a Sn precursor followed by sulfur reaction in rapid thermal annealing (RTA) at different sulfurization temperatures ($Ts=200^{\circ}C$, $230^{\circ}C$, $250^{\circ}C$, and $300^{\circ}C$) and annealing times ($t_s=10min$ and 30 min). The single SnS phase was dominant for $200^{\circ}C{\leq}T_s$<$250^{\circ}C$, while an additional phase of $SnS_2$ was appeared at $T_s{\geq}250^{\circ}C$ alongside SnS. The SnS grains in all the samples showed strong growth along the preferred [040] direction. The band-gap energy ($E_g$) of the films was estimated to be 1.24 eV.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.31A no.9
• /
• pp.78-88
• /
• 1994

The electrical properties of TiM/TiSi$_{2}$ bilayer formed by rapid thermal anneal in NH$_{3}$ ambient after the Ti film is deposited on silicon cubstrate are investigated. N$^{+}$ contact resistance slightly increases with increasing annealing temperature with P$^{+}$ contact resistance decreases. The contact resistance of N$^{+}$ contance was less than 24[.OMEGA.] but P$^{+}$ thatn that of N$^{+}$ contact but the leakage current indicates degradation of the contact at high annealing temperature for both N$^{+}$ and contacts. The leakage current of N$^{+}$ Junction was less than 0.06[fA/${\mu}m^{2}$] but P$^{+}$ contact was 0.11-0.15[fA/${\mu}m^{2}$]. The junction breakdown voltage for N$^{+}$ junction remains contant with increasing annealing temperature while P$^{+}$ junction slightly decreases. The Electrical properties of a two step annealing are better than that of one step annealing. The Tin/TiSi$_{2}$ bilayer formed by RTA in NH$_{3}$ ambient reveals good electrical properties to be applicable at ULSI contact.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.136-139
• /
• 1999

The post-annealing treatments on RF (Radio Frequency) magnetron sputtered PZI(Pb$\_$1.05/(Zr$\_$0.52/, Ti$\_$0.48/)O$_3$thin films(4000${\AA}$) have been investigated. for a structure of PZT/Pt/Ti/SiO$_2$/Si Crystallization pproperties of PZT films were strongly dependent on RTA(Rapid Thermal Annealing) annealing temperature. We were able to obtain a perovskite structure of PZT at a low temperature of 600$^{\circ}C$. P-E curves of Pd/PZT/Pt capacitor annealed at 700$^{\circ}C$ demonstrate typical hysteresis loops. The measured values of P$\_$r/, E$\_$c/, by post annealed at 700$^{\circ}C$ were 12.1 ${\mu}$C/$\textrm{cm}^2$, 120KV/cm respectively.