• International Journal of Highway Engineering
• /
• v.20 no.1
• /
• pp.87-95
• /
• 2018

PURPOSES : A geo-grid pavement, e.g., a stress-absorbing membrane interlayer (SAMI), can be applied to an asphalt-overlay method on the existing surface-pavement layer for pavement maintenance related to reflection cracking. Reflection cracking can occur when a crack in the existing surface layer influences the overlay pavement. It can reduce the pavement life cycle and adversely affect traffic safety. Moreover, a failed overlay can reduce the economic value. In this regard, the objective of this study is to evaluate the bonding properties between the rigid pavement and a SAMI by using the direct shear test and the pull-off test. The predicted fractural energy functions with the shear stress were determined from a numerical analysis of the moving average method and the polynomial regression method. METHODS : In this research, the shear and pull-off tests were performed to evaluate the properties of mixtures constructed using no interlayer, a tack-coat, and SAMI with fabric and without fabric. The lower mixture parts (describing the existing pavement) were mixed using the 25-40-8 joint cement-concrete standard. The overlay layer was constructed especially using polymer-modified stone mastic asphalt (SMA) pavement. It was composed of an SMA aggregate gradation and applied as the modified agent. The sixth polynomial regression equation and the general moving average method were utilized to estimate the interlayer shear strength. These numerical analysis methods were also used to determine the predictive models for estimating the fracture energy. RESULTS : From the direct shear test and the pull-off test results, the mixture bonded using the tack-coat (applied as the interlayer between the overlay layer and the jointed cement concrete) had the strongest shear resistance and bonding strength. In contrast, the SAMI pavement without fiber has a strong need for fractural energy at failure. CONCLUSIONS : The effects of site-reflection cracking can be determined using the same tests on cored specimens. Further, an empirical-mechanical finite-element method (FEM) must be done to understand the appropriate SAMI application. In this regard, the FEM application analy pavement-design analysis using thesis and bonding property tests using cored specimens from public roads will be conducted in further research.

• International Journal of Highway Engineering
• /
• v.19 no.6
• /
• pp.37-46
• /
• 2017

PURPOSES : A composite pavement utilizes both an asphalt surface and a concrete base. Typically, a concrete base layer provides structural capacity, while an asphalt surface layer provides smoothness and riding quality. This pavement type can be used in conjunction with rollercompacted concrete (RCC) pavement as a base layer due to its fast construction, economic efficiency, and structural performance. However, the service life and functionality of composite pavement may be reduced due to interfacial bond failure. Therefore, adequate interfacial bonding between the asphalt surface and the concrete base is essential to achieving monolithic behavior. The purpose of this study is to investigate the bond characteristics at the interface between asphalt (HMA; hot-mixed asphalt) and the RCC base. METHODS : This study was performed to determine the optimal type and application rate of tack coat material for RCC-base composite pavement. In addition, the core size effect, temperature condition, and bonding failure shape were analyzed to investigate the bonding characteristics at the interface between the RCC base and HMA surface. To evaluate the bond strength, a pull-off test was performed using different diameters of specimens such as 50 mm and 100 mm. Tack coat materials such as RSC-4 and BD-Coat were applied in amounts of 0.3, 0.5, 0.7, 0.9, and $1.1l/m^2$ to determine the optimal application rate. In order to evaluate the bond strength characteristics with temperature changes, a pull-off test was carried out at -15, 0, 20, and $40^{\circ}C$. In addition, the bond failure shapes were analyzed using an image analysis program after the pull-off tests were completed. RESULTS : The test results indicated that the optimal application rate of RSC-4 and BD-Coat were $0.8l/m^2$, $0.9l/m^2$, respectively. The core size effect was determined to be negligible because the bond strengths were similar in specimens with diameters of 50 mm and 100 mm. The bond strengths of RSC-4 and BD-Coat were found to decrease significantly when the temperature increased. As a result of the bonding failure shape in low-temperature conditions such as -15, 0, and $20^{\circ}C$, it was found that most of the debonding occurred at the interface between the tack coat and RCC surface. On the other hand, the interface between the HMA and tack coat was weaker than that between the tack coat and RCC at a high temperature of $40^{\circ}C$. CONCLUSIONS : This study suggested an optimal application rate of tack coat materials to apply to RCC-base composite pavement. The bond strengths at high temperatures were significantly lower than the required bond (tensile) strength of 0.4 MPa. It was known that the temperature was a critical factor affecting the bond strength at the interface of the RCC-base composite pavement.

• Composites Research
• /
• v.23 no.2
• /
• pp.31-39
• /
• 2010

In this paper, composite panels with hat-shaped stiffeners were made using the co-curing, co-bonding and secondary bonding methods. Co-curing is a manufacturing method in which the hat part and the plate are cured simultaneously in a manner that is more cost effective than other methods. Co-bonding is a method in which the stacked prepregs are cured with other cured parts, and secondary bonding is a method in which cured parts are bonded together using an adhesive. A rubber mold was manufactured for co-curing of composite panel with hat-shaped stiffeners, and finite element analyses were done to evaluate the expanding pressure of the rubber mold consistent with the curing temperature. The manufactured panels were also evaluated using a 3-D measurement tester and an ultrasonic tester. Pull-off tests were performed to evaluate their mechanical properties.

• Journal of the Korean Geotechnical Society
• /
• v.33 no.10
• /
• pp.59-69
• /
• 2017

The tension load of the ground anchor inserted in the ground gradually changes over time. In this regard the change of the initial tension load is primarily decreased by the fixation condition of the fixing head and the mechanical characteristics of the tensile material. The subsequent additional tension load is a time-dependent loss mostly due to the fixing conditions of the bonded length and the surrounding ground properties of the field. In this paper, therefore, a measurement system using a relative displacement detector that can relatively easily measure the change of tension load is discussed. As a result of the review, it was confirmed that the results using the relative displacement detector are similar to those of the real scale model test, and it was also confirmed that similar results were obtained with the result of the pull-out test conducted on the ground anchors fixed to weathered rocks condition. In addition, a pull-out test was conducted on the test anchors whose initial tension load loss was relatively large and through this test pull-out behavior of the tension type ground anchors was verified.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.40 no.2
• /
• pp.64-71
• /
• 2024

Purpose: The purpose of this study is to evaluate Ti-base abutment's three different heights and three different cement types on the pull-off force of zirconia-based restorations. Materials and Methods: A total of 90 fixture lab analogs were embedded in auto polymerizing resin bloack. 90 Ti-base abutments heights of 3 mm, 5 mm, 7 mm were scanned and zirconia restoration were prepared from scanned files. Zirconia restoration were cemented with three different types of cements (temporary, semi-permanent, permanent) following manufacturer's instructions. All 90 specimens were placed and tested in a universal testing machine for pull-out testing. Retention was measured by recording the force at load drop. Statistical analysis was performed using Kruskal-Wallis test for detecting whether there are any statistical significance along cement types or abutment heights. After that, Mann-Whitney test was used for figuring out differences regarding abutment height and the comparison between 3 cements. Results: Temp bond showed significantly lower pull-off force compared to Fujicem regardless of any abutment height. However, there were significant differences between Cem-implant and Fujicem in abutment height of 3 mm and 7 mm, but there was no significant difference in 5 mm. Temp bond and Cem-implant had significant differences only in abutment height of 5 mm. Conclusion: Although Ti-base abutment height did not influenced zirconia restorations' retentiveness, cement types showed significant differences.

• Tribology and Lubricants
• /
• v.31 no.3
• /
• pp.86-94
• /
• 2015

We perform lacquer formation experiments with various combinations of marine fuel oils and lubricant oils. We also investigate the influences of base number (BN) in lubricant oil and sulfur content in fuel oil. A dissolution test with 10% dilute sulfuric acid and pull-off force test are accomplished to distinguish whether the residual layers are lacquering or not. The lacquering layers are dissolved by dilute sulfuric acid and have a strong pull-off force. Moreover, the calcium content detected in the residual layers is compared by energy dispersive x-ray spectroscopy (EDS). More calcium is detected in the lacquer layers than in other residual layers. Distillate fuels containing low sulfur levels are more prone to lacquering when mixed with lubricant oil with a high BN. On the other hand, residual fuels with a high sulfur content do not form lacquer. We investigate the effect of mixture volume ratio. The mixture with higher fuel oil content is more prone to generate lacquer. These experiments indicate that a lubricant with an appropriate BN should be used to prevent lacquer forming on the surfaces such as cylinder liners depending on the sulfur content of fuel oil.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.979-984
• /
• 2001

Poor water-proofing integrity is related to many factors : site procedure, workmanship, weather. substrate conditions, installation(including asphalt application) conditions. The evaluation of adhesive properties tested by concrete surface moisture and asphalt application was based on laboratory test and observations. This report describes the pull-off test results of waterproofing systems currently used for installing and reparing for concrete bridge decks. The test results showed that the moisture condition fully affected the adhesive properties of sheet membranes and sealer but partially for liquid membranes.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.32 no.4A
• /
• pp.245-253
• /
• 2012

In the longway tunnel and underground traffic road, the structure of transverse ventilation system is constructed by the airpit slab. In this study, the full scale specimens of the PSC airpit slab that attached fire resistance panel are performed the static and dynamic loading tests for evaluation of bending capacity. The first of all, it confirmed the evaluations about the fundamental efficiency of the fire resistance panel and PSC slab by the 3-point bending test and pull-off test. The tests are performed for evaluation of the bending resistance under ultimate static load and the bonded capacity under dynamic fatigue load. A fatigue test is performed for an investigation of the effect on wind pressure that is developed by transit of traffic. The damage or debonding on surface between fire resistance panel and PSC slab was not developed in dynamic fatigue load test, also the behavior of the specimens is very stable and the debonding of the fire resistance panel attached at the bottom surface of PSC slab was not developed in static load test, too. Therefore, the crack or debonding of the fire resistance panel will be not developed by external loads during the construction or completion of the precast fire resistance system.

• Journal of the Society of Disaster Information
• /
• v.19 no.2
• /
• pp.262-269
• /
• 2023

Purpose: In this study,fire-resistance test were executed to evaluate the effectiveness of the fireproof panel attached to the PSC slab in tunnel. Method: For the fire resistance test, the RWS curve was applied and the furnace of the KICT was used. Result: As a result of the experiment, the maximum temperature measured on the concrete surface of the PSC slab with the fireproof panel was 321.8℃, which was lower than the damage limit temperature of 380℃ for concrete. Also, at the t=25mm, the maximum temperature was 35.2℃, which was lower than the damage temperature of steel, 250℃. The use of precast fire resistance panel(t=30mm) improves fire resistance of PSC structures. Conclusion: As a result of the test, a reinforcement method for attached a fireproof panel in case of fire in a tunnel or an underground roadway is provided to protect a structure from fire. In the future, it is necessary to perform the static performance test of the slab to which the fireproof panel is attached, and to confirm the adhesion performance of the fireproof panel by performing the pull-off test and the fatigue test.

• Tribology and Lubricants
• /
• v.32 no.3
• /
• pp.75-81
• /
• 2016

Future electronics such as electronic paper and foldable cellphone are required to be flexible and transparent and should have a high performance. In order to fabricate the flexible electronics using flexibility transfer process, techniques for transferring various devices from rigid substrate onto flexible substrate by elastomeric stamp, have been developed. Adhesion between the elastomeric stamp and various devices is crucial for successful transfer process. The adhesion can be controlled by the thickness of the stamp, separation velocity, contact load, and stamp surface treatment. In this study, we fabricated the bump shape stamp consisting of a UV-curable polymer and investigated the effects of curing condition, separation velocity, and contact load on the adhesion characteristics of bumps. The bumps with hemispherical shape were fabricated using a dispensing process, which is one of the ink-jet printing techniques. Curing conditions of the bumps were controlled by the amount of UV irradiation energy. The adhesion characteristics of bumps are evaluated by adhesion test. The results show that the pull-off forces of bumps were increased and decreased as UV irradiation energy increased. For UV irradiation energies of 300 and 500 mJ/cm², the pull-off forces were increased as the separation velocity increased. The pull-off forces also increased with the increase of contact load. In the case of UV irradiation energy above 600 mJ/cm², however, the pull-off forces were not changed. Therefore, we believe that the bump shape stamp can be applied to roll-based transfer process and selective transfer process as an elastomeric stamp.