• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.3
• /
• pp.360-368
• /
• 2003

Statement of Problem: The residual monomer of denture base materials causes hypersensitivity on oral mucosa and intereferes with the mechanical properties of the cured resin. The amount of residual monomer is influenced by materials, curing cycle, processing method, and etc. Purpose: The aim of this study was to investigate the residual methyl methacrylate(MMA) content of injection molded denture base polymer, and to compare this with the self-cured resin and the conventional compression molded heat-cured resin. Materials and Methods: Disc shaped test specimens (50mm in diameter and 3mm thick) were prepared in a conventional flasking technique with gypsum molding. One autopolymerized denture base resins (Vertex Sc. Dentimex. Netherlands) and two heat-cured denture base resins (Vertex RS. Dentimex. Netherlands, Ivocap. Ivoclar Vivadent, USA) were used. The three types of specimens were processed according to the manufacturer's instruction. After polymerization, all specimens were stored in the dark at room temperature for 7 days. There were 10 specimens in each of the test groups. 3-mm twist drills were used to obtain the resin samples and 650mg of the drilled sample were collected for each estimation. Gas chromatography (Agillent 6890 Plus Gas Chromatograph, Agillent Co, USA) was used to determine the residual MMA content of 10 test specimens of each three types of polymer. Results: The residual monomer content of injection molded denture base resins was $1.057{\pm}0.141%$. The residual monomer content of injection molded denture base resins was higher than that of compression molded heat cured resin ($0.867{\pm}0.169%$). However, there was no statistical significant difference between two groups (p>0.01). The level of residual monomer in self cured resin($3.675{\pm}0.791$) was higher than those of injection molded and compression molded heat cured resins (p<0.01). Conclusion: With respect to ISO specification pass / fail test (2.2% mass fraction) of residual monomer, injection molding technique($1.057{\pm}0.141%$) is a clinically useful and safe technique in terms of residual monomer.

• Polymer(Korea)
• /
• v.36 no.4
• /
• pp.536-541
• /
• 2012

The effects of silica content were studied on UV curing characteristics and defect formations in imprinted patterns of hundreads nanometer size for the photo-curable imprinting composites with silica particles. An increase in elasticity and a decrease in shrinkage were observed with an increase in silica content in the imprinting resin which was UV cured at room temperature. However, the patterned nano-pillars were stuck together with neighboring nano-pillars if the amount of silica is more than 7 wt%. This can be ascribed to the increased viscosity of imperfectly cured resin due to the obstruction of the photo-reaction by silica particles. Addition of silica to the imprinting resin is useful in enhancing the strength of the cured resin although it is difficult to get good imprinted patterns for the resin with more than 7 wt% of silica due to the reduction of photo-reaction conversion.

• Polymer(Korea)
• /
• v.33 no.2
• /
• pp.153-157
• /
• 2009

The resin matrix in the dental composite is generally composed of 2,2-bis[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane (Bis-GMA) as a base resin and triethylene glycol dimethacrylate (TEGDMA) as a diluent for the reduction of viscosity. The applications of dental composite were often limited in dentistry due to the relatively large amounts of volumetric shrinkage during polymerization and water uptake caused by the addition of TEGDMA to the resin matrix. In this study, in order to solve problems stemmed from the TEGDMA by reducing amount of diluent added to resin matrix, diethylene glycol dimethacrylate (DEGDMA) and ethylene glycol dimethacrylate (EGDMA) were explored as new diluents. A decrease in the volumetric shrinkage and an increase in the mechanical strength were observed by replacing TEGDMA in the dental composite to DEGDMA (or EGDMA). Reduction in the mechanical strength of the dental composite containing DEGDMA (or EGDMA), was not serious in comparison with that of the dental composite containing TEGDMA after water uptake.

• Bulletin of the Korean Chemical Society
• /
• v.18 no.1
• /
• pp.3-5
• /
• 1997

• Bulletin of the Korean Chemical Society
• /
• v.21 no.8
• /
• pp.757-758
• /
• 2000

• Journal of Technologic Dentistry
• /
• v.9 no.1
• /
• pp.51-55
• /
• 1987

One of the primary advantages of acrylic resin teeth is their ability to bond chemically to the denture base resins. Fracture od acrylic resin teeth from a maxillary denture, however, is not uncommon. Bonding failures have been attributed to faulty boil-out procedures that fail to eliminate all traces of wax from the ridge lap surfaces of the teeth and to contamination of the ridge lap surface by careless application of tinfoil substitute. Attempts to increase the strength of the bond between acrylic resin teeth and heat-cured denture base resin include grinding the glossy ridge lap surface (in fluid system), painting the ridgelap surface of the teeth with monomer-polymer solution, and cutting retention grooves in the ridge lap surface of the teeth. This latter method has been tested by applying a tensile force in a labial direction to the incisal part of the lingual surface of the acrylic resin teeth. A progressive shear compressive load was applied at an angle to the lingual surface of acrylic resin teeth bonded to denture base acrylic resin. No statistically singificant advantage was derived by preparing retention grooves of different shapes in the ridgelap surface of the denture teeth.

• Polymer(Korea)
• /
• v.38 no.6
• /
• pp.787-790
• /
• 2014

In this work, the epoxy specimens were prepared from diglycidyl ether of bisphenol F (DGEBF) with silane coupling agents (3-glycidoxypropyl trimethoxysilane (GPTMS)) in different ratios. Thermal stability was studied in terms of polymer decomposition temperature (PDT), temperature of maximum rate of weight loss ($T_{max}$), integral procedural decomposition temperature (IPDT), and decomposition activation energy ($E_a$) using TGA analysis. Adhesion properties of epoxy composite specimens were measured by UTM (universal testing machine) at atmosphere temperature. In this result, the adhesion properties of DGEBF were improved by addition of silane coupling agents compared to non-treated epoxy resin. However, when the content of GPTMS agent is more than 10 phr, adhesion properties decreased with increasing GPTMS agent.

• International Journal of Concrete Structures and Materials
• /
• v.2 no.1
• /
• pp.35-39
• /
• 2008

This experimental study examines the applicability of polymer mortar permanent forms using a methyl methacrylate (MMA) solution of waste expanded polystyrene (EPS) to develop effective recycling processes for the EPS, referring to the flexural behavior of a polymer-impregnated mortar permanent form with almost the same performance as commercial products. An MMA solution of EPS is prepared by dissolving EPS in MMA, and unreinforced and steel fiber-reinforced polymer mortars are mixed using the EPS-MMA-based solution as a liquid resin or binder. Polymer mortar permanent forms (PMPFs) using the EPS-MMA-based polymer mortars without and with steel fiber and crimped wire cloth reinforcements and steel fiber-reinforced polymer-impregnated mortar permanent form (PIMPF) are prepared on trial, and tested for flexural behavior under four-point (third-point) loading. The EPS-MMAbased PMPFs are more ductile than the PIMPF, and have a high load-bearing capacity. Consequently, they can replace PIMPF in practical applications.

• Electrical & Electronic Materials
• /
• v.9 no.7
• /
• pp.702-707
• /
• 1996

In this paper, in order to improve the withstand voltage properties of epoxy resin, IPN(interpenetrating polymer network) method was introduced and the influence was investigated. The single network structure specimen(E series), simultaneous interpenetrating polymer network specimen(EM series) and pseudo interpenetrating polymer network(EMP series) specimen were manufactured. In order to understand the internal structure properties, scanning electron microscopy method was utilized, and glass transition temperature was measured. Also, AC voltage dielectric breakdown strength, tensile strength and impact strength were measured to investigate the influence upon electrical and mechanical properties. As a result, it was confirmed that simultaneous interpenetrating polymer network specimen was the most execellent.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.65-67
• /
• 2002

Resin Transfer Molding(RTM) is increasingly used for producing fiber reinforced polymer composites, the resin has to flow a long distance to impregnate the dry fibers. The measure for the resistance of the fiber preform to the resin flow is the permeability of the fiber preform. Permeability is a key issue in the design of molds and processes and in flow modeling. In this study, permeability measurement for braided preform is presented and compared with the permeability calculated numerically. Experimental techniques being used to measure the permeability are also discussed. Measurement is conducted in radial flow test under constant pressure.