• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.27-29
• /
• 2005

ZnO and phosphorus doped ZnO thin films (ZnO:P) are deposited by pulsed laser deposition grown on (001) $Al_{2}O_{3}$. ZnO/ZnO:P/ZnO/$Al_{2}O_{3}$ (multi-layer) structure was used for phosphorus doped ZnO fabrication. This multi-layer structure thin film was annealed at $400^{\circ}C$ for 40 min. The electron concentration of that was changed from $10^{19}$ to $10^{16}/cm^{-3}$ after annealing. ZnO thin films with encapsulated structure showed the enhanced structural and optical properties than phosphorus doped ZnO without encapsulated layer. In this study, encapsulated ZnO structure was suggested to enhance electrical, structural and optical properties of phosphorus doped ZnO thin film and it was identified that encapsulated structure could be used to fabricate high quality phosphorus doped ZnO thin film.

• 한국재료학회지
• /
• 제19권8호
• /
• pp.417-420
• /
• 2009

This study develops a highly transparent ohmic contact using phosphorus doped ZnO with current spreading for p-GaN to increase the optical output power of nitride-based light-emitting diodes (LEDs). The phosphorus doped ZnO transparent ohmic contact layer was prepared by radio frequency magnetron sputtering with post-deposition annealing. The transmittance of the phosphorus doped ZnO exceeds 90% in the region of 440 nm to 500 nm. The specific contact resistance of the phosphorus doped ZnO on p-GaN was determined to be $7.82{\times}10^{-3}{\Omega}{\cdot}cm^2$ after annealing at $700^{\circ}C$. GaN LED chips with dimensions of $300\times300{\mu}m$ fabricated with the phosphorus doped ZnO transparent ohmic contact were developed and produced a 2.7 V increase in forward voltage under a nominal forward current of 20 mA compared to GaN LED with Ni/Au Ohmic contact. However, the output power increased by 25% at the injection current of 20 mA compared to GaN LED with the Ni/Au contact scheme.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.55-56
• /
• 2005

The properties of phosphorus doped ZnO thin films deposited on (001) sapphire substrates by pulsed laser deposition (PLD) were investigated depending on various deposition conditions. The phosphorus (P) doped ZnO target was composed of ZnO + x wt% Al (x=1, 3, 5). The structural, electrical and optical properties of the ZnO thin films were measured by X-ray diffraction (XRD), Hall measurements and photoluminescence (PL). As the deposition temperature optimized, the electrical properties of the phosphorus doped ZnO (ZnO:P) layer showed a electron concentration of $7.76\times10^{16}/cm^3$, a mobility of 10.225 $cm^2/Vs$, a resistivity of 7.932 $\Omega$cm. It was observed the electrical property of the film was changed by dopant activation effect as target variations and deposition conditions.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.51-52
• /
• 2005

Phosphorus doped ZnO thin films on (001) $Al_2O_3$ substrate have been prepared by a pulsed laser deposition (PLD) technique using a Nd:YAG laser. After deposition, phosphorus doped ZnO thin films have been annealed in vacuum, air, nitrogen, and oxygen ambients using pulsed Nd:YAG laser. We report the electrical properties of phosphorus doped ZnO thin films with the variation of the laser annealing conditions for the applications of optoelectronic devices.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 춘계학술대회 논문집 디스플레이 광소자 분야
• /
• pp.127-130
• /
• 2005

The properties of phosphorus doped ZnO multilayer thin films deposited on (001) sapphire substrates by pulsed laser deposition (PLD) were investigated by using annealing treatment at various annealing temperature after deposition. The phosphorus doped ZnO multilayer was composed of phosphorus doped ZnO layer and two pure ZnO layers on sapphire substrate. The structural. electrical and optical properties of the ZnOthin films were measured by X-ray diffraction (XRD). Hall measurements and photoluminescence (PL). As the annealing temperature optimized. the electrical properties of the ZnO multilayer showed a electron concentration of $1.56{\times}10^{16}/cm^3$, a resistivity of 17.97 ${\Omega}cm$. It was observed the electrical property of the film was changed by dopant activation effect as thermal annealing process

• 한국재료학회지
• /
• 제23권5호
• /
• pp.255-259
• /
• 2013

An effect of thermal annealing on activating phosphorus (P) atoms in ZnO nanorods (NR) grown using a hydrothermal process was investigated. $NH_4H_2PO_4$ used as a dopant source reacted with $Zn^{2+}$ ions and $Zn_3(PO_4)_2$ sediment was produced in the solution. The fact that most of the input P elements are concentrated in the $Zn_3(PO_4)_2$ sediment was confirmed using an energy dispersive spectrometer (EDS). After the hydrothermal process, ZnO NRs were synthesized and their PL peaks were exhibited at 405 and 500 nm because P atoms diffused to the ZnO crystal from the $Zn_3(PO_4)_2$ particles. The solubility of the $Zn_3(PO_4)_2$ initially formed sediment varied with the concentration of $NH_4OH$. Before annealing, both the structural and the optical properties of the P-doped ZnO NR were changed by the variation of P doping concentration, which affected the ZnO lattice parameters. At low doping concentration of phosphorus in ZnO crystal, it was determined that a phosphorus atom substituted for a Zn site and interacted with two $V_{Zn}$, resulting in a $P_{Zn}-2V_{Zn}$ complex, which is responsible for p-type conduction. After annealing, a shift of the PL peak was found to have occurred due to the unstable P doping state at high concentration of P, whereas at low concentration there was little shift of PL peak due to the stable P doping state.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2009년도 9th International Meeting on Information Display
• /
• pp.540-542
• /
• 2009

Phosphorus doped ZnO (PZO) thin films were deposited on $SiO_2$/n-Si substrates using DC magnetron sputtering system varying oxygen partial pressures from 0 to 40 % under Ar atmosphere. The deposited films showed reduced n-type conductivity due to the compensating donor effects by phosphorus dopant. The bias-time stability shows relatively good stability over bias and time comparing to un-doped ZnO-based TFTs.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.49-50
• /
• 2005

Nitrogen and phosphorus ions were implanted into ZnO thin film fabricated by pulsed laser deposition. ion implanted ZnO thin films were annealed from $700^{\circ}C$ to $1000^{\circ}C$ using rapid thermal annealing process. The electron concentration was changed form $10^{20}$ to $10^{18}/cm^3$. Effect of nitrogen and phosphorus in ZnO thin films was certified and the structural and optical properties of nitrogen and phosphorus doped ZnO thin films depending on concentration of nitrogen and phosphorus were investigated.

• 대한전자공학회논문지SD
• /
• 제46권2호
• /
• pp.9-14
• /
• 2009

본 연구에서는 sapphire 기판위에 P (phosphorus) 도핑된 ZnO 박막을 제작한 후, 산소 분위기에서 후열 처리 온도가 박막의 전기적 및 광학적 특성에 미치는 영향에 대해서 조사하였다. XRD 측정 결과, 후열 처리 온도에 무관하게 모든 박막이 c축 배향성을 나타내었다. Hall 측정 결과, $850^{\circ}C$에서 후열 처리한 박막에서만 p형 전도 특성이 관찰되었다. 이때의 홀 캐리어 농도와 홀 이동도는 각각 $1.18{\times}1016cm^{-3}$과 $0.96cm^2/Vs$의 값을 나타내었다. 저온 PL 측정 결과, $850^{\circ}C$에서 후열 처리한 박막의 경우 p형 특성을 나타내는 상당량의 억셉터가 관련된 A0X (3.351eV), FA(3.283eV) 및 DAP (3.201eV) 피크가 관찰되었다. 향후 P 도핑된 ZnO 박막의 공정 조건과 후열 처리 조건을 최적화시킨다면, 차세대 광소자에 응용될 수 있는 매우 유망한 재료로 주목받을 것으로 기대된다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.97-98
• /
• 2005

To investigate the ZnO thin films which is interested in the next generation of short wavelength LEDs and Lasers, our ZnO thin films were deposited by RF sputtering system. Phosphorus (P) and arsenic (As) were diffused into about 2.1${\mu}m$ ZnO thin films sputtered by RF magnetron sputtering system mn ampoule tube which was below $5\times10^{-7}$ Torr. The dopant sources of phosphorus and arsenic were $Zn_3P_2$ and $ZnAs_2$. Those diffusion was perform at 500, 600, and 700$^{\circ}C$ during 3hr. We find the condition of p-type ZnO whose diffusion condition is 700$^{\circ}C$, 3hr Our p-type ZnO thin film has not only very high carrier concentration of above $10^{19}/cm^3$ but also low resistivity of $5\times10^{-3}{\Omega}cm$.