• Journal of Welding and Joining
• /
• 제29권1호
• /
• pp.99-106
• /
• 2011

Joint strength between a solder ball and a pad on a substrate is one of the major factors which have effects on electronic device reliability. The effort to improve solder joint strength via surface cleaning, heat treatment and solder composition change have been in progress. This paper will discuss the method of solder ball joint strength improvement using LF hydrogen radical cleaning treatment and focus on the effects of surface treatment condition on the solder ball shear strength and interfacial reactions. In the joint without radical cleaning, voids were observed at the interface. However, the specimens cleaned by hydrogen-radical didn't have voids at the interface regardless of cleaning time. The shear strength between the solder ball and the pad was increased over 120%(about 800gf) when compared to that without the radical treatment (680gf) under the same reflow condition. Especially, at the specimen treated for 5minutes, ball shear strength was considerably increased over 150%(1150gf). Through the observation of fracture surface and cross-section microstructure, the increase of joint strength resulted from the change of fracture mode, that is, from the solder ball fracture to IMC/Ni(P) interfacial fracture. The other cases like radical treated specimen for 1, 3, 7, 9min. showed IMC/solder interfacial fracture rather than fracture in the solder ball.

• 대한금속재료학회지
• /
• 제48권11호
• /
• pp.1035-1040
• /
• 2010

The research efforts on GaN-based light-emitting diodes (LEDs) keep increasing due to their significant impact on the illumination industry. Surface mount technology (SMT) is widely used to mount the LED packages for practical application. In surface mount soldering both the device body and leads are intentionally heated by a reflow process. We studied on the effects of multiple reflows on microstructural variation and joint strength of the solder joints between the LED package and the substrate. In this study, Pb-free Sn-3.0Ag-0.5Cu solder and a finished pad with organic solderability preservatives (OSP) were employed. A $Cu_6Sn_5$ intermetallic compound (IMC) layer was formed during the multiple reflows, and the thickness of the IMC layerincreased with an increasing number of reflows. The shear force decreased after three reflows. From the observation of the fracture surface after a shear test, partially brittle fractures were observed after five reflows.

• 대한금속재료학회지
• /
• 제50권1호
• /
• pp.71-77
• /
• 2012

We studied the effect of heat treatment on the microstructures and mechanical strength of the solder joints in the Light Emitting Diode (LED) packages. The commercial LED packages were mounted on the a flame resistance-4 (FR4) Printed Circuit Board (PCB) in the reflow process, and then the joints were aged at $125^{\circ}C$ for 100, 200, 300, 500 and 1000 hours, respectively. After the heat treatment, we measured the shear strength of the solder joints between the PCB and the LED packages to evaluate their mechanical property. We used Pb-free Sn-3.0Ag-0.5Cu solder to bond between the LED packages and the PCBs using two different surface finishes, Electroless Nickel-Immersion Gold (ENIG) and Electroless Nickel-Electroless Palladium-Immersion Gold (ENEPIG). The microstructure of the solder joints was observed by a scanning electron microscope (SEM). (Cu,Ni)6Sn5 intermetallic compounds (IMCs) formed between the solder and the PCB, and the thickness of the IMCs was increased with increasing aging time. The shear strength for the ENIG finished LED package increased until aging for 300 h and then decreased with increasing aging time. On the other hand, in the case of an ENEPIG finished LED package, the shear strength decreased after aging for 500 h.

• 마이크로전자및패키징학회지
• /
• 제18권2호
• /
• pp.49-55
• /
• 2011

전자기기에서의 고장 중 대부분은 작동 중 발생하는 열과 충격에 기인한다. 이 열과 충격은 PCB(Printed Board) 부품의 접합부 계면에 균열을 야기 시키고, 이 균열은 금속간 화합물(Intermetallic Compound: IMC)의 형성과 밀접한 관계를 가진다. 본 연구에서는 Sn-Ag-Cu계의 Ag함량을 변화한 Sn-1.0Ag-0.5Cu와 Sn-1.2Ag-0.5Cu 및 Sn-3.0Ag-0.5Cu의 3가지 조성의 솔더로 접합한 소재를 대상으로 1000시간 까지 등온시효(Isothermal Aging) 하였다. 등온시효 동 안 솔더(Solder)의 계면에 발생하는 IMC(Intermetallic Compound) 성장이 관찰되었으며, solder 접합부의 기계적 특성은 굽힘충격 시험법을 이용하여 평가되었다. 그 결과 시효처리 전에는 Ag 함량이 낮은 solder의 굽힘충격 특성이 우수하게 나타났으나, 시효처리 후에는 반대의 결과를 나타내었다. 이 결과는 IMC layer 주변에 생성된 미세한 $Ag_3Sn$ 및 조대한 $Cu_6Sn_5$와 관련되어, 미세한 $Ag_3Sn$이 충격을 완화한 것으로 나타나 이에 따라 굽힘충격 특성에 차이가 나타남을 알 수 있었다.