• Polymer(Korea)
• /
• v.35 no.6
• /
• pp.605-609
• /
• 2011

Composite nanofibers were prepared by electrospinning and thermal treatment from poly (vinylidene fluoride) (PVDF)-$SiO_2$ blend solution. The nanofibers were stacked on layers to produce fully interconnected pores. TEM micrographs and EDX spectra confirmed the presence of $SiO_2$ in the composite nanofibers. The porosity of nanofibers was effectively enhanced by the introduction of electrospinning technique. ATR-FTIR and XRD results revealed that PVDF in the composite nanofibers exhibited the mixture crystal structure of ${\alpha}$-phase and ${\beta}$-phase. The crystal structure of ${\alpha}$-phase and crystallinity increased by the thermal treatment. In addition, the mechanical properties, thermal stability and hydrophobicity were markedly amplified by the thermal treatment.

• Journal of the Korean Ceramic Society
• /
• v.51 no.6
• /
• pp.523-526
• /
• 2014

PZT($Pb(Zr_{0.53}Ti_{0.47})O_3$)/PVDF(poly vinylidene fluoride) nanofibers were prepared based on DMF (dimethylformamide) and acetone solvent by electrospinning. The optimum concentration of a PZT and PVDF composite solution for the formation of nanofibers was found by SEM (scanning electron microscopy) observations. XRD (X-ray diffraction) measurements indicated that the characteristics of PZT and PVDF coexisted. The effects of the PZT concentration on the tensile strength were investigated.

• Journal of Powder Materials
• /
• v.27 no.3
• /
• pp.247-255
• /
• 2020

Recently, interest in technology for eco-friendly energy harvesting has been increasing. Polyvinylidene fluoride (PVDF) is one of the most fascinating materials that has been used in energy harvesting technology as well as micro-filters by utilizing an electrostatic effect. To enhance the performance of the electrostatic effect-based nanogenerator, most studies have focused on enlarging the contact surface area of the pair of materials with different triboelectric series. For this reason, one-dimensional nanofibers have been widely used recently. In order to realize practical energy-harvesting applications, PVDF nanofibers are modified by enlarging their contact surface area, modulating the microstructure of the surface, and maximizing the fraction of the ν-phase by incorporating additives or forming composites with inorganic nanoparticles. Among them, nanocomposite structures incorporating various nanoparticles have been widely investigated to increase the β-phase through strong hydrogen bonding or ion-dipole interactions with -CF₂/CH₂- of PVDF as well as to enhance the mechanical strength. In this study, we report the recent advances in the nanocomposite structure of PVDF nanofibers and inorganic nanopowders.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.47 no.3
• /
• pp.577-592
• /
• 2023

In this study, nanofiber-based textile sensors were developed for motion detection and monitoring. Poly(vinylidene fluoride) (PVDF) nanofibers containing zinc oxide (ZnO) nanoparticles and silver nanowires (AgNW) were fabricated using electrospinning. PVDF was chosen as a piezoelectric polymer, zinc oxide as a piezoelectric ceramic, and AgNW as a metal to improve electric conductivity. The PVDF/ZnO/AgNW nanocomposite fibers were used to develop a textile sensor, which was then incorporated into an elbow band to develop a wearable smart band. Changes in the output voltage and peak-to-peak voltage (V_p-p) generated by the joint's flexion and extension were investigated using a dummy elbow. The β-phase crystallinity of pure PVDF nanofibers was 58% when analyzed using Fourier transform infrared spectroscopy; however, the β-phase crystallinity increased to 70% in PVDF nanofibers containing ZnO and to 78% in PVDF nanocomposite fibers containing both ZnO and AgNW. The textile sensor's output voltage values varied with joint-bending angle; upon increasing the joint angle from 45° to 90° to 150°, the V_p-p value increased from 0.321 V_p-p to 0.542 V_p-p to 0.660 V_p-p respectively. This suggests that the textile sensor can be used to detect and monitor body movements.

• Transactions of the Korean hydrogen and new energy society
• /
• v.18 no.4
• /
• pp.446-451
• /
• 2007

Physicochemical properties of carbon nanofibers were evaluated as a supercacitor electrode materials could store electrochemical energy reversibly. A capacitance of carbon nanofiber electrode was increased gradually, depending on the PVDF binder ratio. A feasibility of EDLC electrode was estimated with specific surface area measurement by BET method and mesopore structure of carbon nanofiber surface could be explained electrochemical absorption-desorption in aqueous electrolyte. PVDF 5 wt.% ratio in electrode was observed a suitable binder amount by CV result.

• Macromolecular Research
• /
• v.16 no.3
• /
• pp.212-217
• /
• 2008

PVDF ($Kynar^{(R)}$ 761) nanofibers were made by electrospinning with an external voltage of 6-10 kV, a traveling distance of 7-15 cm and a flow rate of 0.4-1 mL/h. Although the mean diameter of the fibers has not changed significantly, the conditions affected the change in diameter distribution. This was attributed to interactions, both attraction and repulsion, between the positive charges on the polymer solutions and the electrically grounded collector. Higher voltages and traveling distance increased the level of attraction between the positive charge on the polymer solution and the electrically grounded collector, resulting in a narrow diameter distribution, In addition, a high flow rate allowed a high population of uniformly charged solutions to travel to the grounded collector, which resulted in a narrow diameter distribution. The optimum conditions for electrospinning of PVDF in DMAc/acetone (3/7 by wt) were a collector voltage of 6 kV, a syringe tip to collector of 7 cm, a flux rate of 0.4 mL/h and 10 kV, 10 cm, 1 mL/h, Since PVDF is widely used as a filtration membrane, it was electrospun on a PET support with a rotating drum as a grounded collector. Surprisingly, some straight nanofibers were separated from the randomly deposited nanofibers. The straight nanofiber area was transparent, while the randomly deposited nanofiber area was opaque. Both straight nanofibers and aligned nanotibers could be obtained by manipulating the PET drum collector. These phenomena were not observed when the support was changed to an Al sheet. This suggests that a pseudo dual collector was generated on the PET sheet. No negative charge was created because the PET sheet was not a conductive material. However, less charge was created when the sheet was not perfectly attached to the metal drum. Hence, the nanotibers jumped from one grounded site to the nearest one, yielding a straight nanofiber.

• Polymer(Korea)
• /
• v.25 no.3
• /
• pp.367-374
• /
• 2001

The electromagnetic interference (EMI) shielding effectiveness (SE) of poly(vinylidene fluoride) (PVDF) composites was investigated using carbon nanofiber fillers prepared by catalytic chemical vapor deposition of various carbon-containing gases over Ni and Ni-Cu catalysts. The electrical conductivity of carbon nanofiber which was regarded as the key property of filler for the application of EMI shielding ranged from 4.2 to 22.4 S/cm at a pressure of 10000 psi. The electrical conductivity of carbon nanofiber/PVDF composites ranged from 0.22 to 2.46 S/cm and the EMI SE of those was in the range of 2∼13 dB. The electrical conductivity of carbon nanofibers increased with the increase in heat treatment temperature and time, while the electrical conductivity of the composites increased rapidly at the initial heat treatment and then approached a certain value with the further increase of heat treatment. The SE of the composites showed a maximum at the medium heat treatment and was proportional to the electrical conductivity of the composites. It was concluded that the specific surface area of carbon nanofibers decreased with the continual heat treatment and the specific surface area of filler was an important factor for the SE of the composites.

• Composites Research
• /
• v.18 no.4
• /
• pp.21-26
• /
• 2005

Nondestructive damage sensing and load transfer mechanisms of carbon nanotube (CNT) and nanofiber (CNF)/epoxy composites have been investigated by using electro-micromechanical technique. The electrospun PVDF nanofibers were also prepared as a piezoelectric sensor. The electro-micromechanical techniques were applied to evaluate sensing response of carbon nanocomposites by measuring electrical resistance under an uniform cyclic loading. Composites with higher volume content of CNT showed significantly higher tensile properties than neat and low volume$\%$ CNT composites. CNT composites showed humidity sensing within limited temperature range. CNT composites with smaller aspect ratio showed higher apparent modulus due to high volume content in case of shorter aspect ratio. Thermal treated electrospun PVDF nanofiber showed higher mechanical properties than the untreated case due to crystallinity increase, whereas load sensing decreased in heat treated case. Electrospun PVDF nanofiber web also showed sensing effect on humidity and temperature as well as stress transferring. Nanocomposites and electrospun PVDF nanofiber web can be applicable for sensing application.

• Textile Coloration and Finishing
• /
• v.32 no.3
• /
• pp.167-175
• /
• 2020

In this study, the optimum conditions for manufacturing PVDF nano web according to various electrospinning conditions such as solution concentration and applied voltage conditions were confirmed. The optimum spinning conditions were studied by analyzing the changes in the radioactivity of PVDF/TiO₂ nano web according to the TiO₂ content and the content of β-phase closely related to the piezoelectric properties under established conditions. As a result, it was confirmed that the concentration of the spinning solution was 20 wt%, the applied voltage was 25 kV, and the TiO₂ content was 5 phr. PVDF nano web and PVDF/TiO₂ nano web were observed morphologies through Scanning Electron Microscope(SEM) analysis. Formation of β-phase by electrospinning was confirmed by Fourier transform infrared spectroscopy(FT-IR) and X-ray Diffractometer(XRD), and the effect of the trapped nano web structure on the piezoelectric properties was investigated.

• Composites Research
• /
• v.26 no.1
• /
• pp.14-20
• /
• 2013

The electrospun PVDF containing CNT was made for fabricating materials of the actuator. The electrochemical and their actuating movement were evaluated for the actuator performance in the electrochemical environment. The actuator (which was fabricated by electrospinning) had some advantages, i.e., good dispersion and flexible properties. In the electrospinning process, the final product would have different forms based on different essential factors. In this work, electrospun nanofibers were aligned by using the drum-type collector, and the morphology was identified via the field emission-scanning electron microscope (FE-SEM). The uniform dispersion of CNT in PVDF nanofiber was observed by electron probe X-ray micro-analysis (EPMA) test. The results of tensile strength and electrical resistivity provided the aligned state. The electrospun CNT/PVDF nanofiber sheet on the aligned direction showed better mechanical and electrical properties than the case of the vertically-aligned direction. The efficiency and electrical capacities of electrospun CNT/PVDF nanofiber sheets were compared with the cast PVDF sheet for actuator application. Electrospun CNT/PVDF nanofiber sheet exhibited much better the case of actuator performance than cast neat PVDF actuator, due to the excellent electrical connecting areas.