• Microbiology and Biotechnology Letters
• /
• v.38 no.4
• /
• pp.461-466
• /
• 2010

In this study the feasibility of simultaneous electricity generation and treatment of swine farm wastewater using microbial fuel cells (MFCs) was examined. Two single-chamber MFCs containing an anode filled with different ratio of graphite felt and stainless-steel cross strip was used in all tests. The proportion of stainless-steel cross strip to graphite felt in the anode of control microbial fuel cell (CMFC) was higher than that of swine microbial fuel cell (SMFC) to reduce construction costs. SMFCs produced a stable current of 18 mA by swine wastewater with chemical oxygen demand (COD) of $3.167{\pm}80\;mg/L$ after enriched. The maximum power density and current density of SMFCs were $680\;mW/m^3$ and $3,770\;mA/m^3$, respectively. In the CMFC, power density and current density was lower than that of SMFC. CODs decreased by the SMFC and CMFC from $3.167{\pm}80$ to $865{\pm}21$ and $930{\pm}14\;mg/L$, achieving 72.7% and 70.6% COD removal, respectively. The suspended solid (SS) of both fuel cells was also reduced over 99% ($4,533{\pm}67$ to $24.0{\pm}6.0\;mg/L$). The concentration of nutritive salts, ${NH_4}^+$, ${NO_3}^-$, and ${PO_4}^{3-}$, dropped by 65.4%, 57.5%, and 73.7% by the SMFC, respectively. These results were similar with those of CMFC. These results show that the microbial fuel cells using electrode with mix stainless-steel cross strip and graphite felt can treat the swine wastewater simultaneously with an electricity generation from swine wastewater.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.6
• /
• pp.599-610
• /
• 2001

Due to an increasing interest in esthetics and concerns about toxic and allergic reactions to certain alloys, patients and dentists have been looking for metal-free tooth-colored restorations. Recent improvement in technology of new all-ceramic materials and composite materials has broadened the options for esthetic single crown restorations. The aim of this investigation was to study the fracture strength of the metal-free posterior single crowns fabricated using two recently introduced systems, Empress 2 ceramic and Targis-Vectris. Forty premolar-shaped stainless steel dies with the 1mm-wide circumferential shoulder were prepared. Ten cylindrical crowns having a diameter of 8.0mm and total height of 7.5mm were fabricated for each crown system respectively(PFM, Empress staining technique, Empress 2 layering technique, and Targis- Vectris). The crowns were filled with cement and placed on the stainless steel dies with firm finger pressure. The crowns were then stored in distilled water at room temperature for 24 hours before testing. The crowns were tested for fracture strength in an Instron universal testing machine (Instron 6022). With a crosshead speed of 1mm/min the center of the occlusal surface of the crown was loaded using a 4-mm-diameter stainless steel ball until fracture occurred. The fracture surfaces of the crowns were gold coated and examined using scanning electron microscopy(Jeol JSM-840 Joel Ltd., Akishima, Tokyo, Japan). Within the parameters of this study the following conclusions were drawn: 1. The mean fracture strength for PFM crowns was 5829(${\pm}906$)N; for Empress staining technique the fracture strength was 1697(${\pm}604$)N; for Empress 2 Layering technique the fracture strength was 1781N(${\pm}400$)N, and the fracture strength for Targis- Vectris was 3093(${\pm}475$)N. 2. The fracture strength of the PFM crowns was significantly higher than that of the Empress 2 and the Targis-Vectris crowns (P<0.05). 3. The fracture strength of the Targis-Vectris crowns was significantly higher than that of the Empress 2 crowns (P<0.05). 4. No statistical difference was found when Empress staining technique was compared with Empress 2 layering technique. 5. The SEM image of fracture surface of Empress 2 crown showed a very dense microstructure of the lithium disilicate crystals and the SEM image of fracture surface of Targis-Vectris crown showed indentations of Vectris and some fibers tom off from Vectris.

• Journal of Preventive Medicine and Public Health
• /
• v.24 no.4 s.36
• /
• pp.496-506
• /
• 1991

A cross-sectional study was conducted to investigate the effect of long term noise exposure on blood pressure among steel mill workers. The workers participated in periodic medical examinations performed from August 27 to September 6 in 1990. Examined were 1,034 workers with high-level noise exposure(average $91.8{\pm}5.2dB(A)$) and 390 workers with low-level noise exposure(average $75.2{\pm}4.6dB(A)$). No significant difference was found in systolic or diastolic flood pressure between the two exposure groups. Prevalence of hypertension (${\geq}160mmHg\;systolic\;or{\geq}100mmHg\;diastolic$) was higher in a younger age group (${\leq}40$ years old) of high-level noise exposure than of low-level noise exposure. However, the difference was not statistically significant. Furthermore, in younger ages, prevalence of hypertension appeared to be higher in the hearing loss group (${\geq}25dB\;at\;1000Hz\;or{\geq}40dB$ at 4000Hz in at least one ear) than in the normal hearing group. From multiple regression analysis, hearing loss, body mass index, age, alcohol and family history of hypertension were proven to be predictors of diastolic blood Pressure (p<0.02). When regression was performed for each age group, hearing loss was a strong predictor of diastolic pressure in the younger age group (p<0.01).

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.3
• /
• pp.47-58
• /
• 2024

This study were conduced experimentally to analyze the heat-generating performance, flexural strength, and microstructure of conductive mortar mixed with micro steel fiber and multi-wall carbon nanotube (MWCNT). In the conductive mortar heat-generating performance and flexural strength tests, the mixing concentration of MWCNT was selected as 0.0wt%, 0.5wt%, and 1.0wt% relative to the weight of cement, and micro steel fibers were mixed at 2.0vol% relative to the volume. The performance experiments were conducted with various applied voltages (DC 10V, 30V, 60V) and different electrode spacings (40 mm, 120 mm) as parameters, and the flexural strength was measured at the curing age of 28 days and compared and analyzed with the normal mortar. Furthermore, the surface shape and microstructure of conductive mortar were analyzed using a field emission scanning electron microscope (FE-SEM). The results showed that the heat-generating performance improved as the mixing concentration of MWCNT and the applied voltage increased, and it further improved as the electrode spacing became narrower. However, even if the mixing concentration of MWCNT was added up to 1.0 wt%, the heat-generating performance was not significantly improved. As a result of the flexural strength test, the average flexural strength of all specimens except the PM specimen and the MWCNT mixed specimens was 4.5 MPa or more, showing high flexural strength due to the incorporation of micro steel fibers. Through FE-SEM image analysis, Through FE-SEM image analysis, it was confirmed that a conductive network was formed between micro steel fibers and MWCNT particles in the cement matrix.

• Transactions of Materials Processing
• /
• v.23 no.6
• /
• pp.345-350
• /
• 2014

The current study elucidates the effects of cementite spheroidization and pro-eutectoid ferrite on the sliding wear resistance in medium carbon (0.45wt%C) and high carbon (1wt%C) steels. Both steels were initially heat treated to obtain a fully pearlite or ferrite + pearlite microstructure. Spheroidizing heat treatments were performed on both steels to spheroidize the pearlitic cementite. Sliding wear tests were conducted using a pin-on-disk wear tester with the steel specimens as the disk and an alumina ($Al_2O_3$) ball as the pin. The sliding wear tests were carried out at room temperature in air with humidity of $40{\pm}2%$. Adapted sliding distance and applied load was 300m and 100N, respectively. Sliding speed was 0.1m/s and the wear-track radius was 9 mm. Worn surfaces and cross-sections of the wear track were examined using an SEM. Micro Vickers hardness of the wear-track subsurface was measured as a function of depth from the worn surface. Hardness and sliding-wear resistance of both steel decreased with increased spheroidization of the cementite. The decrease was more significant in the fully pearlitic steel (1wt%C steel). The steel with the pro-eutectoid ferrite showed relatively higher wear resistance compared to the spheroidized pearlitic steel.

• Composites Research
• /
• v.31 no.1
• /
• pp.12-16
• /
• 2018

Composite material and mold steel can be expanded differently with the temperature gradients during the forming process because their coefficients of thermal expansions are not the same. Therefore, in order to manufacture the product with accuracy, it is necessary to verify that the forming pressure on the surface of the composite material is maintained to the required level from the material supplier. In this paper, the pressure between the composite material and mold due to the temperature difference was predicted by finite element analysis and the accuracy of predicted value was verified by measuring the thermal expansions of mold steel by the ruler. The predicted value by finite element analysis is closely in agreement with one by the experiment within the required tolerance value of ${\pm}0.05mm$.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.4
• /
• pp.406-414
• /
• 2001

Ultrasonic guided waves were explored to apply them to the long range inspection of polyethylene coated steel gas pipes. The steel pipes have such dimensions as 190.7mm inside diameter and 5.3mm thickness. The outside surface of the pipe is coated by a polyethylene layer of $1.9{\pm}0.5mm$ thickness. Non-axisymmetric guided waves were excited on the outside surface of the polyethylene coated pipe by using a 0.5MHz transducer with a variable angle shoe. Frequency and phase velocity tuning was used to find optimum guided wave modes for the inspection. The dispersive characteristics of the modes were analyzed in time-frequency representation obtained by short time Fourier transforms. Sample results were presented for artificial defects such as wall thinning and hole.

• Environmental Engineering Research
• /
• v.23 no.4
• /
• pp.383-389
• /
• 2018

Microbial fuel cell (MFC) is an innovative environmental and energy system that converts organic wastewater into electrical energy. For practical implementation of MFC as a wastewater treatment process, a number of limitations need to be overcome. Improving cathodic performance is one of major challenges, and introduction of a current collector can be an easy and practical solution. In this study, three types of current collectors made of stainless steel (SS) were tested in a single-chamber cubic MFC. The three current collectors had different contact areas to the cathode (P $1.0cm^2$; PC $4.3cm^2$; PM $6.5cm^2$) and increasing the contacting area enhanced the power and current generations and coulombic and energy recoveries by mainly decreasing cathodic charge transfer impedance. Application of the SS mesh to the cathode (PM) improved maximum power density, optimum current density and maximum current density by 8.8%, 3.6% and 6.7%, respectively, comparing with P of no SS mesh. The SS mesh decreased cathodic polarization resistance by up to 16%, and cathodic charge transfer impedance by up to 39%, possibly because the SS mesh enhanced electron transport and oxygen reduction reaction. However, application of the SS mesh had little effect on ohmic impedance.

• The Korean Journal of Physiology and Pharmacology
• /
• v.2 no.6
• /
• pp.687-693
• /
• 1998

This study was performed to examine the mean arterial pressure and nociceptive jaw opening reflex after microinjection of glutamate into the amygdala in freely moving rats, and to investigate the mechanisms of antinociceptive action of amygdala. Animals were anesthetized with pentobarbital sodium (40 mg/kg, ip). A stainless steel guide cannula (26 gauge) was implanted in the amygdala and lateral ventricle. Stimulating and recording electrodes were implanted into each of the incisor pulp and anterior digastric muscle. Electrodes were led subcutaneously to the miniature cranial connector sealed on the top of the skull with acrylic resin. After 48 hours of recovery from surgery, mean arterial pressure and digastric electromyogram (dEMG) were monitored in freely moving rats. Electrical shocks (200 ${\mu}sec$ duration, $0.5{\sim}2$ mA intensity) were delivered at 0.5 Hz to the dental pulp every 2 minutes. After injection of 0.35 M glutamate into the amygdala, mean arterial pressure was increased by $8{\pm}2$ mmHg and dEMG was suppressed to $71{\pm}5%$ of the control. Injection of 0.7 M glutamate elevated mean arterial pressure by $25{\pm}5$ mmHg and suppressed dEMG to $20{\pm}7%$ of the control. The suppression of dEMG were maintained for 30 minutes. Naloxone, an opioid receptor antagonist, inhibited the suppression of dEMG elicited by amygdaloid injection of glutamate from $28{\pm}4\;to\;68{\pm}5%$ of the control. Methysergide, a serotonin receptor antagonist, also inhibited the suppression of dEMG from $33{\pm}5\;to\;79{\pm}4%$ of the control. However, phentolamine, an ${\alpha}-adrenergic$ receptor antagonist, did not affect the suppression of dEMG. These results suggest that the amygdala can modulate both cardiovascular and nociceptive responses and that the antinociception of amygdala seems to be attributed to an augmentation of descending inhibitory influences on nociceptive pathways via serotonergic and opioid pathways.

• Particle and aerosol research
• /
• v.19 no.4
• /
• pp.111-128
• /
• 2023

Chungcheongnam-do has various emission sources, including large-scale facilities such as power plants, steel and petrochemical industry complexes, which can lead to the severe PM pollution. Here, we measured concentrations of PM₁₀, PM_2.5, and its metallic elements at a suburban site in Taean, Chungcheongnam-do from September 2017 to June 2022. During the measurement period, the average concentrations of PM₁₀ and PM_2.5 were 58.6 ㎍/m³ (9.6~379.0 ㎍/m³) and 35.0 ㎍/m³ (6.1~132.2 ㎍/m³), respectively. The concentration of PM₁₀ and PM_2.5 showed typical seasonal variation, with higher concentration in winter and lower concentration in summer. When high concentrations of PM_2.5 occurred, particulary in winter, the fraction of Zn and Pb components considerably increased, indicating a significant contribution of Zn and Pb to high-PM_2.5 concentration. In addition, Zn and Pb exhibited the highest correlation coefficient among all other metallic elements of PM_2.5. A backward trajectory cluster analysis and CPF model were performed to examine the origin of PM_2.5. The high concentration of PM_2.5 was primarily influenced by emissions from industrial complexes located in the northeast and northwest areas.