• E2M - 전기 전자와 첨단 소재
• /
• 제8권2호
• /
• pp.171-175
• /
• 1995

Optimum condition of remote plasma enhanced chemical vapor deposition using orthogonal array method was chosen. Characteristics of oxide films deposited by RPECVD with SiH$_{4}$ and N$_{2}$O gases were investigated. Etching rate of the optimized SiO$_{2}$ films in P-etchant was about 6[A/s] that was almost the same as that the high temperature thermal oxide. The films showed high dielectric breakdown field of more than 7[MV/cm] and a resistivity of 8*10$^{13}$ [.ohmcm] around at 7[MV/cm]. The interface trap density of SiO$_{2}$/Si interface around the midgap derived from the high frequency C-V curve was about 5*10$^{10}$ [/cm$^{2}$eV]. It was observed that the dielectric constant of the optimized SiO$_{2}$ film was 4.29.

• 마이크로전자및패키징학회지
• /
• 제29권1호
• /
• pp.61-66
• /
• 2022

이 연구는 원자층 증착(Atomic Layer Deposition, ALD) 기술을 사용하여 나노미터 크기의 금속 촉매 물질을 연료극 층에 코팅하여 표면적을 늘리고 촉매의 효과를 극대화시키기 위한 연구이다. ALD 공정은 기판 위에 원자 수준에서 잘 제어된 두께를 갖는 균일한 막을 제조하는 것으로 알려져 있다. 우리는 고체산화물 연료전지의 연료극 물질로 가장 널리 알려진 Ni/YSZ 위에 금속(Ni)을 코팅하여 성능을 측정하였다. ALD 코팅은 3 nm 이상의 코팅에서 전지 성능의 감소를 보이기 시작했다

• 열처리공학회지
• /
• 제35권2호
• /
• pp.51-56
• /
• 2022

In this study, we controlled the shape of a carbon layer on gallium oxide templates. Gallium oxide layers were deposited on sapphire substrates using mist chemical vapor deposition. Subsequently, carbon layers were formed using radio frequency plasma chemical vapor deposition. Various shapes of carbon structures appeared according to the fraction of methane gas, used as a precursor. As methane gas concentration was adjusted from 1 to 100%, The shapes of carbon structures varied to diamonds, nanowalls, and spheres. The growth of carbon isotope structures on Ga₂O₃ templates will give rise to improving the electrical and thermal properties in the next-generation electronic applications.

• 한국재료학회지
• /
• 제17권6호
• /
• pp.308-312
• /
• 2007

Chromium oxide thin films have been deposited on silicon substrates using a tabletop 9kJ mathertyped plasma focus (PF) device. Before deposition, pinch behavior with gas pressure was observed. Strength of pinches was increased with increasing working pressure. Deposition was performed at room temperature as a function of working pressure between 50 and 1000 mTorr. Composition and surface morphology of the films were analyzed by Auger Electron Spectroscopy and Scanning Electron Microscope, respectively. Growth rates of the films were decreased with pressure. The oxide films were polycrystalline containing some impurities, Cu, Fe, C and revealed finer grain structure at lower pressure.

• 한국자기학회지
• /
• 제22권4호
• /
• pp.147-156
• /
• 2012

최근 들어 박막의 원자층 두께를 정밀하게 제어하는 여러 가지 박막 성장 방법에 관한 관심이 높다. 그 중에서 원자층 두께를 조절할 수 있는 PLD 방법은 매우 폭넓은 관심을 받고 있다. 우리는 기존의 PLD 방법과 Reflection high energy electron diffraction(RHEED)을 이용하여 원자층 제어 PLD 방법을 구현하였다. 이러한 방법을 이용하여 산화물에서의 원자층 두께를 정밀하게 제어하는 방법에 관한 실험을 수행하였다. 이와 같은 실험방법이 가지는 다양한 조건을 제어하여 최소한의 결함을 가지고 결정의 화학적 조성에 근접하는 고품질의 박막을 구축하여 이를 바탕으로 다양한 실험을 수행하였다. 본 논문에서는 최근 이러한 박막을 이용한 우리의 실험결과와 타 그룹의 실험 동향을 정리하여 보았다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제45회 하계 정기학술대회 초록집
• /
• pp.76.1-76.1
• /
• 2013

Atomic Layer Deposition (ALD) has remarkably developed in semiconductor and nano-structure applications since early 1990. Now, the advantages of ALD process are well-known as controlling atomic-level-thickness, manipulating atomic-level-composition control, and depositing impurity-free films uniformly. These unique properties may accelerate ALD related industries and applications in various functional thin film markets. On the other hand, one of big markets, Display industry, just starts to look at the potential to adopt ALD functional films in emerging display applications, such as transparent and flexible displays. Unlike conventional ALD process strategies (good quality films and stable precursors at high deposition processes), recently major display industries have suggested the following requirements: large area equipment, reasonable throughput, low temperature process, and cost-effective functional precursors. In this talk, it will be mentioned some demands of display industries for applying ALD processes and/or functional films, in terms of emerging display technologies. In fact, the AMOLED (active matrix organic light emitting diode) Television markets are just starting at early 2013. There are a few possibilities and needs to be developing for AMOLED, Flexible and transparent Display markets. Moreover, some basic results will be shown to specify ALD display applications, including transparent conduction oxide, oxide semiconductor, passivation and barrier films.

• 한국전기전자재료학회논문지
• /
• 제34권2호
• /
• pp.99-104
• /
• 2021

Ion-beam sputtering (IBS) was used to deposit semiconducting IZTO (indium zinc tin oxide) thin films onto heavily-doped Si substrates using a sintered ceramic target with the nominal composition In0.4Zn0.5Sn0.1O1.5, which could work as a channel layer for oxide TFT (oxide thin film transistor) devices. The crystallization behavior and electrical properties were examined for the films in terms of deposition parameters, i.e. target tilt angle and substrate temperature during deposition. The thickness uniformity of the films were examined using a stylus profilometer. The observed difference in electrical properties was not related to the degree of crystallization but to the deposition temperature which affected charge carrier concentration (n), electrical resistivity (ρ), sheet resistance (Rs), and Hall mobility (μH) values of the films.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.II
• /
• pp.907-912
• /
• 2005

Micro-patterns of $Pb(Zr_{0.53}Ti_{0.47})O_3$, PZT, thin films with a MPB composition were deposited on $Pt/Ti/SiO_2/Si$ substrate from molecular-designed PZT precursor solution by using self-assembledmonolayer(SAM) as a template. This method includes deposition of SAM followed by the optical etching by exposing the SAM to the UV-light, leading to the patterned SAM as a selective deposition template. The pattern of SAM was formed by irradiating UV-light to the SAM on a substrate and/or patterned PZT thin film through a metal mask for the selective deposition of patterned PZT or lanthanum nickel oxide (LNO) precursor films from alkoxide-based precursor solutions. As a result, patterned ferroelectric PZT and PZT/LNO thin film capacitors with good electrical properties in micrometer size could be successfully deposited.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제52권9호
• /
• pp.378-382
• /
• 2003

Transparent conductive oxides (TCO) are necessary as front electrode for most thin film solar cell. In our paper, transparent conducting aluminum-doped Zinc oxide films (ZnO:Al) were prepared by rf magnetron sputtering on glass (Corning 1737) substrate as a variation of the deposition condition. After deposition, the smooth ZnO:Al films were etched in diluted HCI (0.5%) to examine the electrical and surface morphology properties as a variation of the time. The most important deposition condition of surface-textured ZnO films by chemical etching is the processing pressure md the substrate temperature. In low pressures (0.9mTorr) and high substrate temperatures ($\leq$$300^{\circ}C$), the surface morphology of films exhibits a more dense and compact film structure with effective light-trapping to apply the silicon thin film solar cells.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2002년도 International Meeting on Information Display
• /
• pp.714-716
• /
• 2002

Indium tin oxide (ITO) was used as the top anode of top emission inverted organic light emitting diodes (TEIOLEDs). TEIOLEDs were fabricated by deposition of an aluminum bottom cathode, an N,N'-diphenyl-N,N'-bis(3-methylphenyl)-1, 1'-diphenyl-4, 4 1'-diamine (TPD) hole transport layer, a tris-8-hydroxyquinoline aluminum ($Alq_3$) emission layer, and an ITO top anode sequentially. ITO was deposited by r.f. magnetron sputtering without $O_2$ flow during the deposition. After the deposition, the deposited ITO layer was kept under oxygen atmosphere for the oxidation. The characteristics of the TEOILED were affected significantly by the post-deposition oxidation condition.