• Journal of the Korean institute of surface engineering
• /
• v.55 no.4
• /
• pp.196-201
• /
• 2022

This paper deals with anodic oxidation behavior of AZ31 Mg alloy in aqueous solutions containing various NaF concentrations from 0.01 M to 1 M. Three different voltage-time curves and anodic oxide formation behaviors appeared with concentration of NaF in deionized water. When NaF concentration is lower than 0.02 M, the voltage of AZ31 Mg alloy increased linearly and then reached a steady-state value more than 200 V, and large size pits and thin oxide layer were formed. When NaF concentration is between 0.05 M and 0.1 M, the voltage of AZ31 Mg alloy showed large periodic fluctuations of about 30 ~ 50 V around more than 200 V and large number of small particles were observed. If NaF concentration is higher than 0.2 M, PEO films can be formed without visible arcs under solution pH 6.5 ~ 7.5 by F^- ions without help of OH^- ions.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.753-758
• /
• 1994

(100) Si and 4$^{\circ}$off (100) Si were oxidized in dry oxygen, and the differences in thermal oxidation behavior and electrical characteristics between two specimens were investigated. Ellipsometer measurements of the oxide thickness produced by oxidation in dry oxygen from 1000 to 120$0^{\circ}C$ showed that the oxidation rates of the 5$^{\circ}$ off (100) Si were more rapid than those of the (100) Si and the differences between them decreased as the oxidation temperature increased. The activation energies based on the parabolic rate constant, B for (100) and 4$^{\circ}$off (100) Si were 25.8, 28.6 kcal/mol and those on the linear rate constant, B/A were 56.8, 54.9 kcal/mol, respectively. Variation of C-V characteristics with the oxidation temperature showed that the flat band voltages were shifted positively and surface state charge densities decreased as the oxidation temperature increased, and the surface state charge density of the 4$^{\circ}$off (100) Si was lower than that of the (100) Si. Also considerable decrease in the density of oxidation induced stacking faults (OSF) for the 4$^{\circ}$off (100) Si was observed through optical microscopy after preferentially etching off the oxide layer.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.3
• /
• pp.152-157
• /
• 2004

Ti-Al-N ($Ti_{75}$ $Al_{25}$ N) and Ti-Al-Si-N ($Ti_{69}$ $Al_{23}$ $Si_{8}$N) coatings synthesized by a DC magnetron sputtering technique were studied comparatively with respect to phase characterization and high-temperature oxidation behavior. $Ti_{69}$ $Al_{23}$ $Si_{ 8}$N coating had a nanocomposite microstructure consisting of nanosized(Ti,Al,Si)N crystallites and amorphous $Si_3$$N_4$, with smooth surface morphology. Ti-Al-N coating of which surface $Al_2$$O_3$ layer formed during oxidation suppressed further oxidation. It was sufficiently stable against oxidation up to about $700^{\circ}C$. Ti-Al-Si-N coating showed better oxidation resistance because both surface Ab03 and near-surface $SiO_2$ layers suppressed further oxidation. XRD, GDOES, XPS, and scratch tests were performed.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.1
• /
• pp.13-20
• /
• 2011

This study investigated the high temperature oxidation behavior of Fe-22%Cr-5.8%Al alloy and the oxidation kinetics of the alloy were discussed. Bulk samples were prepared by VAM (vacuum arc melting) and hot forging. High temperature oxidation testes were isothermally conducted up to 100 hours in 79%$N_2$+21%$O_2$ environment at three different temperatures ($900^{\circ}C$, $1000^{\circ}C$, $1100^{\circ}C$). The weight gain was measured after oxidation according to oxidation time (2, 4, 6, 8, 10, 15, 20, 25, 30, 60, 80, 100 hours). The weight gain significantly increased with increasing oxidation temperature. As the temperature increased, the oxidized samples showed sequential formation of $Al_2O_3$, Cr-rich oxide, Fe-rich oxide. The activation energy of high temperature oxidation was obtained as 306.63 KJ/mol. $Al_2O_3$ were developed on the surface in the early stage of oxidation, representing protective role of oxidation. However, Fe-based and Cr-based oxides leaded to breakaway of oxide layer, thus resulted in the significant increase of additional oxidation.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.4
• /
• pp.392-400
• /
• 2017

An experimental study was conducted to investigate behavior of steel surface oxidation with characteristics of the combustion. The excess entalphy combustion in porous media system was applied to implement the direct radiation heating system. The surface oxidation thickness (SOT) of fuel-lean was thicker than the SOT of fuel-rich. Also, the SOT was increased by increasing residence time. Detailed explanations were given by SEM and EDS analysis.

• Journal of Powder Materials
• /
• v.6 no.3
• /
• pp.209-214
• /
• 1999

The oxidation behavior of the simulated spent fuel of burn up 33 MWD/kgU was investigated to predict that of the spent fuel in the temperature ranges of 400 to $700^{\circ}C$ and was compared with those of $UO_2$. The forms of uranium oxides after the oxidation were conformed by XRD analyses. The oxidation rate at each the temperature and the activation energy were obtained. After complete oxidation, the simulated spent fuel was converted to $U_3O_8$ and pulverized to powder due to the density difference between the simulated spent fuel and uranium oxides. The activation energies were 85.35 and 30.77kJ/mol in the temperature ranges of 400$\leq$T($^{\circ}C$)$\leq$500 and 500$\leq$T($^{\circ}C$)$\leq$700, respectively.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.144-148
• /
• 1999

The relationship between oxidation and sliding wear behavior of Fe-28 at%. Al alloys with B2 ordered structure has been investigated. Sliding wear tests of the alloys have been carried out under various environmental conditions using a pin-on-disk wear tester. The wear rate of the ordered alloys in an oxygen atmoshpere was found to be much lower than in an oxygen atmosphere showed that Fe2O oxides formed on the wearing surface. The oxide layer prevented direct contact of the two mating materials and therefore improved wear resistance of the Fe-Al intermetallic alloy. It was found that the surface Al2O3 oxide layer which provides good oxidation resistance and improved mechanical properties broke down easily and didnot function properly as an oxidation barrier.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.352-353
• /
• 2006

The effect of TiC content on oxidation behavior of the sintered WC-TiC-TaC alloys with 2 mass% TaC and different TiC amounts of 3-45 mass% was investigated through oxidation tests in air at 973K. As a result of the tests, it was revealed that with increasing TiC content in the alloys, mass changes caused by oxidation and thickness of the scale decreased. Thus, it is considered that the main component of the scales changed gradually from $WO_3$ to $TiO_2$ with increasing TiC content in the alloys, and oxygen diffusion through the scale to the alloys was inhibited gradually.

• Korean Journal of Materials Research
• /
• v.9 no.6
• /
• pp.609-614
• /
• 1999

The effect of the amount of $SiO_2$dopant on the behavior of $AlO_2$$O_3$-composite formation by melt oxdation of Al-alloy was examined in this paper. The $SiO_2$powder was spread on the top surface of the Al-1Mg-3-Si-5Zn-1Cu alloy in th alumina crucible. The selected amount of each powder was 0.03, 0.10, 0.16g/$\textrm{cm}^2$. The oxidation behavior was determined by observing the weight gain after the heat treatment for 10 hours at 1373K. The macroscopic structure of formed oxide layer was examined by an optical microscope. The top surface and the cross-section of the grown oxide layer were investigated by SEM and analysed by EDX. The $SiO_2$ powder was determined to enhance oxidation by thermit reaction with Al which reduced the growth incubation period of the oxidation layer. As the amount of the $SiO_2$dopant increased, the growth rate decreased due to the precipitated Si which blocked the Al-alloy channel in the composite materials. However, more uniform layer was obtained due to the occurrance of the enhanced oxidation reaction in the whole alloy surface compared to the case of addition of less amount of dopant.

• Journal of Power System Engineering
• /
• v.10 no.3
• /
• pp.51-57
• /
• 2006

The effect of grain size on corrosion resistance and high temperature oxidation behavior was studied in 22Cr-15Ni-5W super austenitic stainless steels for desulfurization equipment as a heat power station. In the high temperature oxidation test, oxidation rate was increased as the temperature increased from $600^{\circ}C\;to\;800^{\circ}C$. In vapor, oxidation rate was faster than that in air. Because the vapor was inhibited nucleation of $Cr_2O_3$ film. And the high temperature oxidation resistance at $600^{\circ}C{\sim}800^{\circ}C$ was excellent from all specimens and specimen of the smallest grain size was the most excellent. Because increasing of diffusion course through the grain-boundary was promoted nucleation and growth of $Cr_2O_3$ film. In the test temperature at $600^{\circ}C{\sim}800^{\circ}C$, Cr rich round particle oxide was formed in air, whereas Fe rich needle type oxide was developed in vapor.