• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.95-98
• /
• 2003

Tin doped indium oxide(ITO) films, which is widely used as a transparent conductor in optoelectronic devices such as solar cell, liquid crystal display, plasma display panel, thermal heater, and other sensors, were prepared by using the capacitively coupled DC magnetron sputtering method. The influence of the substrate temperature, working gas pressure and deposition time on the electrical, optical and morphological properties were investigated experimentally. ITO films with the optimum growth conditions showed resistivity of $2.36{\times}10^{-4}(\Omega}-cm$ and transmittance of 86.28% for a film 680nm thick in the wavelength range of the visible spectrum.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.901-904
• /
• 2001

For the c-axis oriented epitaxial YBa$_2$Cu$_3$O$_{7-{\delta}}$ thin film on r-cut sapphire substrate it is necessary to deposit buffer layers. The CeO$_2$buffer layer was deposited on sapphire substrate using RF magnetron sputtering system. We investigated XRD pattern of CeO$_2$thin films at various sputtering conditions such as sputtering gas ratio, sputtering power, target to substrate distance, sputtering pressure and substrate temperature. The optimum condition was 15 mTorr with deposition pressure, 1:1.2 with $O_2$and Ar ratio and 9cm with target to substrate distance. The CeO$_2$(200) peak was notable for a deposition temperature above 75$0^{\circ}C$. The YBa$_2$Cu$_3$O$_{7-{\delta}}$ was deposited on CeO$_2$buffered r-cut sapphire substrate using pulsed laser ablation. The YBa$_2$Cu$_3$O$_{7-{\delta}}$CeO$_2$(200)/A1$_2$O$_3$thin film was exhibited a critical temperature of 89K.xhibited a critical temperature of 89K.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.7
• /
• pp.600-605
• /
• 2007

Process variables for manufacturing the $CuInSe_2$ thin film were established in order to clarify optimum conditions for growth of the thin film depending upon process conditions (substrate temperature, sputtering pressure, DC/RF Power), and then by changing a number of vapor deposition conditions and Annealing conditions variously, structural and electrical characteristics were measured. Thereby, optimum process variables were derived. For the manufacture of the $CuInSe_2$, Cu, In and Se were vapor-deposited in the named order. Among them, Cu and In were vapor-deposited by using the sputtering method in consideration of their adhesive force to the substrate, and the DC/RF power was controlled so that the composition of Cu and In might be 1 : 1, while the surface temperature having an effect on the quality of the thin film was changed from $100^{\circ}C\;to\;300^{\circ}C$ at intervals of $50^{\circ}C$. The diffract fringe of X-ray, which depended upon the substrate temperature and the Annealing temperature of the manufactured $CuInSe_2$ thin film, was investigated. scanning electron microgaphs of represents a case that a sample manufactured at the substrate temperature of $100^{\circ}C$ was thermally treated at $200{\times}350^{\circ}C$. As a result, at $500^{\circ}C$ of the Annealing temperature, their chemical composition was measured in the proportion of 1 : 1 : 2. It could be known that under this condition, the most excellent thin film was formed, compared with the other conditions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.12a
• /
• pp.119-122
• /
• 2006

Process variables for manufacturing the $CuInSe_2$ thin film were established in order to clarify optimum conditions for growth of the thin film depending upon process conditions (substrate temperature, sputtering pressure, DC/RF Power), and then by changing a number of vapor deposition conditions and Annealing conditions variously, structural and electrical characteristics were measured. Thereby, optimum process variables were derived. For the manufacture of the $CuInSe_2$, Cu, In and Se were vapor-deposited in the named order. Among them, Cu and In were vapor-deposited by using the sputtering method in consideration of their adhesive force to the substrate, and the DC/RF power was controlled so that the composition of Cu and In might be 1:1, while the surface temperature having an effect on the quality of the thin film was changed from 100[$^{\circ}C$] to 300[$^{\circ}C$] at intervals of 50[$^{\circ}C$].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.185-186
• /
• 2008

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/SiO2/Si) using RF sputtering method at various substrate temperature. The optimum conditions of RF power and Ar/O2 ratio were 60[W] and 70/30, respectively. The rougness showed about 4.33[nm]. Deposition rate of SBN thin films was about 4.17[nm/min]. The capacitance of SBN thin films were increased with the increase of substrate temperature.

• Korean Journal of Materials Research
• /
• v.8 no.10
• /
• pp.961-968
• /
• 1998

In order to investigate the effects of substrate bias voltage on the formation of$ZnS-SiO_2$ protective film in phase change optical disk by R.F. magnetron sputtering method, thin dielectric film was formed on Si wafer and Corning glass by using ZnS(80mol%)-$SiO_2$(20mol%)t arget under argon gas. In this study, the Taguchi experimental method was applied in order to obtain optimum conditions with reduced number of experiments and to control numerous variables effectively. At the same time this method can assure the reproducibility of experiments. Optimum conditions for film formation obtained by above method were target RF power of 200 W. substrate RF power of 20 W, Ar pressure of 5 mTorr. sputtering time of 20 min.. respectively. The phase of specimen was determined by using XRD and TEM. The compositional analysis of specimen was performed by XPS test. In order to measure the thermal resistivity of deposited specimen, annealing test was carried out at $300^{\circ}C$ and $600^{\circ}C$. For the account of void fraction in thin film, the Bruggeman EMA(Effective Medium Approximation) method was applied using the optical data obtained by Spectroscopic Ellipsometry. According to the results of this work, the existence of strong interaction between bias voltage and sputtering time was confirmed for refractive index value. According to XRD and TEM analysis of specimen, the film structure formed in bias voltage resulted in more refined structures than that formed without bias voltage. But excess bias voltage resulted in grain growth in thin film. It was confirmed that the application of optimum bias voltage increased film density by reduction of void fraction of about 3.7%.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.354.1-354.1
• /
• 2016

Nanoporous gold (NPG) is a very promising material in various fields such as sensor, actuator, and catalysis because of its high surface to volume ratio and conducting nature. In this study, we fabricated a NPG based amperometric sensor on a glass substrate by means of co-sputtering of Au and Si. During the sputtering process, we found the optimum conditions for heat treatment to reduce the residual stress and to improve adhesion between NPG films and the glass substrate. Subsequently, Si was selectively etched from Au-Si alloy by KOH solution, which forms nanoporous structures. Scanning electron microscopy (SEM) and auger electron spectroscopy (AES) were used to estimate the structure of NPG films and their composition. By employing appropriate heat treatments, we could make very stable NPG films. We tested the performance of NPG sensor with aniline molecules, which shows high sensitivity for sensing low concentration of aniline.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.10
• /
• pp.505-509
• /
• 2004

The (Sr/sub 0.9/Ca/sub 0.1/)TiO₃(SCT) thin films are deposited on Pt-coated electrode(Pt/TiN/SiO₂/Si) using RF sputtering method at various substrate temperature. The optimum conditions of RF power and Ar/O₂ ratio were 140[W] and 80/20, respectively. Deposition rate of SCT thin film was about 18.75[Å/min]. The crystallinity of SCT thin films were increased with increase of substrate temperature in the temperature range of 100～500[℃]. The dielectric constant of SCT thin films were increased with the increase of substrate temperature, and changed almost linearly in temperature ranges of -80～+90[℃]. The current-voltage characteristics of SCT thin films showed the increasing leakage current as the substrate temperature increases.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.11a
• /
• pp.244-247
• /
• 1995

Physical, electrical and optical properties of Aluminum(Al) thin films were investigated in order to establish the optimum sputtering parameters in mirror reflection films. Al. thin films deposited on corning glass substrate by DC magnetron sputtering were grown as a variation of the input power, operation pressure and deposition time. The properties of the Al thin films have been discussed by deposition rate, SEM, XRD, sheet resistivity, resistivity and reflectance. Al thin films were obtained at the deposition conditions as follows: operating pressure, 3 mtorr; DC input power desnsitiy, 3W/$\textrm{cm}^2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.8
• /
• pp.671-676
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various deposition conditions. We investigated the effect of deposition condition on the surface morphology and dielectric properties of SBN thin films. The optimum of the rougness showed about 4.33 nm in 70/30 of Ar/$O_2$ ratio. The crystallinity and rougness of SBN thin films were increased with the increase of rf power. Also, Deposition rate of SBN thin films was about 4.17 nm/min in 70 W of rf power. The capacitance of SBN thin films were increased with the increase of Ar/$O_2$ ratio, rf power and deposition temperature respectively.