This paper, Al-doped ZnO(AZO) thin films for application as transparent conducting oxide films were deposited on the Corning glass substrate by using RF magnetron sputtering system. The effects of various Argon gas flow rates on optical and electrical characteristics of AZO films were investigate sputtering method. The Carrier Concentration is enhanced as Ar gas rate increases, and also the oxygen vacancy concentration. The figure of merit obtained in this study means that AZO films which deposited Ar gas rate of 75 sccm have the highest Carrier concentration and Hall mobility, which have the highest photoelectrical performance that it could be used as transparent electrodes.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.10
• /
• pp.808-813
• /
• 2009

Indium nitride thin films were deposited by the radio-frequency reactive magnetron sputtering method. The indium target was sputtered by the mixture flow ratio of $N_2$ to Ar, 9:1. The effects of growth temperature on the structural, optical, and electrical properties of the films were investigated. With increasing the growth temperature, the crystallinity of the films was improved, and the crystalline size was increased. The energy bandgap for the film grown at $25^{\circ}C$ was 3.63 eV, and the bandgap showed an increasing tendency on the growth temperature. The carrier concentration, Hall mobility and electrical resistivity of the films depended significantly on the growth temperature and the maximum Hall mobility of $32.3\;cm^2$/Vsec was observed for the film grown at $400^{\circ}C$.

• Journal of Astronomy and Space Sciences
• /
• v.30 no.1
• /
• pp.49-58
• /
• 2013

ARGO-M is a satellite laser ranging (SLR) system developed by the Korea Astronomy and Space Science Institute with the consideration of mobility and daytime and nighttime satellite observation. The ARGO-M optical system consists of 40 cm receiving telescope, 10 cm transmitting telescope, and detecting optics. For the development of ARGO-M optical system, the structural analysis was performed with regard to the optics and optomechanics design and the optical components. To ensure the optical performance, the quality was tested at the level of parts using the laser interferometer and ultra-high-precision measuring instruments. The assembly and alignment of ARGO-M optical system were conducted at an auto-collimation facility. As the transmission and reception are separated in the ARGO-M optical system, the pointing alignment between the transmitting telescope and receiving telescope is critical for precise target pointing. Thus, the alignment using the ground target and the radiant point observation of transmitting laser beam was carried out, and the lines of sight for the two telescopes were aligned within the required pointing precision. This paper describes the design, structural analysis, manufacture and assembly of parts, and entire process related with the alignment for the ARGO-M optical system.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.4
• /
• pp.280-286
• /
• 2010

We have investigated the influence of rapid thermal annealing (RTA) temperature on properties of Al-doped zinc oxide (AZO) thin films deposited on glass substrate by using radio-frequency magnetron sputtering. The RTA is performed in a nitrogen ambient in the temperature range from 300 to $600^{\circ}C$ for 1 minute in a rapid thermal annealer after growing the AZO thin films. The crystallographic structure and the surface morphology of AZO thin film are measured by using X-ray diffraction, and atomic force microscopy and scanning electron microscopy, respectively. The optical transmittance of the deposited thin films is examined in the wavelength range of 300-1100 nm, where the average transmittance is above the 90% in the visible and near-infrared regions. The optical bandgap is calculated from the Tauc's model, and it shows a significant dependence on the RTA temperature. As for the electrical properties of the thin films, the AZO thin film annealed at $400^{\circ}C$ shows the lowest electrical resistivity of $8.6{\times}10^{-3}{\Omega}cm$ and the Hall mobility of $11.3cm^2$/V-sec. These results suggest that the RTA temperature is an important parameter to influence on the structural, electrical, and optical properties of AZO thin films.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.4
• /
• pp.129-133
• /
• 2008

Nitrogen and aluminum codoped ZnO(NAZO) thin films were grown on glass substrates with changing the nitrogen flow ratio by radio-frequency magnetron sputtering. The structural, optical, and electrical properties of the NAZO films were investigated. The surface morphologies and the structural properties of the thin films were analyzed by using the X-ray diffraction and scanning electron microscopy. The NAZO thin film, deposited at nitrogen flow ratio of 0%, showed a strongly c-axis preferred orientation and the lowest resistivity of $3.2{\times}10^{-3}{\Omega}cm$. The intensity of ZnO(002) diffraction peak was decreased gradually with increasing the nitrogen flow ratio. The optical properties of the films were measured by UV-VIS spectrophotometer and the optical transmittances for all the samples were found to be an average 90% in the visible range. Based on the transmittance value, the optical bandgap energy for the NAZO thin film deposited at nitrogen flow ratio of 0% was determined to be 3.46 eV. As for the electrical properties, the carrier concentration and the hall mobility were decreased, but the electrical resistivity was increased as the nitrogen flow ratio was increased.

• 정보저장시스템학회:학술대회논문집
• /
• 2005.10a
• /
• pp.47-52
• /
• 2005

A lot of information storage devices have been introduced and developed for recently years. The trends of those devices are high capacity, compact size, low power consumption, reliability, and removability for data interchange with other device. As a satisfaction of these trends, near-field technique is in the spotlight as the next generation device. In order for a near-field recording to be successfully implemented in the storage device, a slider and suspension is introduced as actuating mechanism. The optical slider is designed considering near-filed optics. Suspension is not only supports slider performance, and tracking servo capacity but also meets the optical characteristics such as tilt aberration, and guarantee to satisfy shock performances for the mobility fir the actuator. In this study, the optical slider and the suspension for near-field probe array are designed and analyzed considering dynamic performance of head-gimbal assembly and shock simulation..

• Journal of the Semiconductor & Display Technology
• /
• v.9 no.4
• /
• pp.83-86
• /
• 2010

The transparent electrode properties of ITO films deposited by RF magnetron sputtering with process pressure were investigated. The ITO thin films was deposited on a glass substrate using a target with 3in diameter sintered at a ratio of $In_2O_3$ : $SnO_2$ (9 : 1). 200-nm-thick ITO thin films were manufactured by various process pressures ($2.0{\times}10^{-2}$, $7.0{\times}10^{-3}$ and $2.0{\times}10^{-3}$ Torr). The optical transmittance and resistivity of the deposited ITO thin films showed a relatively satisfactory result under $10^{-2}$ Torr. For high process pressure, the optical transmittance was below 80%, while for low process pressure, the optical transmittance was above 85%. As a result of of mobility, resistivity and carrier concentration by Hall measurement, we obtained satisfactory properties to apply into a transparent conducting thin film.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.288-289
• /
• 2011

Indium Tin Oxide (ITO) is a typical highly Transparent Conductive Oxide (TCO) currently used as a transparent electrode material. Most widely used deposition method is the sputtering process for ITO film deposition because it has a high deposition rate, allows accurate control of the film thickness and easy deposition process and high electrical/optical properties. However, to apply high quality ITO thin film in a flexible microelectronic device using a plastic substrate, conventional DC magnetron sputtering (DMS) processed ITO thin film is not suitable because it needs a high temperature thermal annealing process to obtain high optical transmittance and low resistivity, while the generally plastic substrates has low glass transition temperatures. In the room temperature sputtering process, the electrical property degradation of ITO thin film is caused by negative oxygen ions effect. This high energy negative oxygen ions(about over 100eV) can be critical physical bombardment damages against the formation of the ITO thin film, and this damage does not recover in the room temperature process that does not offer thermal annealing. Hence new ITO deposition process that can provide the high electrical/optical properties of the ITO film at room temperature is needed. To solve these limitations we develop the Magnetic Field Shielded Sputtering (MFSS) system. The MFSS is based on DMS and it has the plasma limiter, which compose the permanent magnet array (Fig.1). During the ITO thin film deposition in the MFSS process, the electrons in the plasma are trapped by the magnetic field at the plasma limiters. The plasma limiter, which has a negative potential in the MFSS process, prevents to the damage by negative oxygen ions bombardment, and increases the heat(-) up effect by the Ar ions in the bulk plasma. Fig. 2. shows the electrical properties of the MFSS ITO thin film and DMS ITO thin film at room temperature. With the increase of the sputtering pressure, the resistivity of DMS ITO increases. On the other hand, the resistivity of the MFSS ITO slightly increases and becomes lower than that of the DMS ITO at all sputtering pressures. The lowest resistivity of the DMS ITO is $1.0{\times}10-3{\Omega}{\cdot}cm$ and that of the MFSS ITO is $4.5{\times}10-4{\Omega}{\cdot}cm$. This resistivity difference is caused by the carrier mobility. The carrier mobility of the MFSS ITO is 40 $cm^2/V{\cdot}s$, which is significantly higher than that of the DMS ITO (10 $cm^2/V{\cdot}s$). The low resistivity and high carrier mobility of the MFSS ITO are due to the magnetic field shielded effect. In addition, although not shown in this paper, the roughness of the MFSS ITO thin film is lower than that of the DMS ITO thin film, and TEM, XRD and XPS analysis of the MFSS ITO show the nano-crystalline structure. As a result, the MFSS process can effectively prevent to the high energy negative oxygen ions bombardment and supply activation energies by accelerating Ar ions in the plasma; therefore, high quality ITO can be deposited at room temperature.

• Korean Journal of Materials Research
• /
• v.30 no.10
• /
• pp.558-565
• /
• 2020

AZO thin films are grown on a p-Si(111) substrate by RF magnetron sputtering. The characteristics of various thicknesses and heat treatment conditions are investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Hall effect and room-temperature photoluminescence (PL) measurements. The substrate temperature and the RF power during growth are kept constant at 400 ℃ and 200 W, respectively. AZO films are grown with a preferred orientation along the c-axis. As the thickness and the heat treatment temperature increases, the length of the c-axis decreases as Al³⁺ ions of relatively small ion radius are substituted for Zn²⁺ ions. At room temperature, the PL spectrum is separated into an NBE emission peak around 3.2 eV and a violet regions peak around 2.95 eV with increasing thickness, and the PL emission peak of 300 nm is red-shifted with increasing annealing temperature. In the XPS measurement, the peak intensity of Al_2p and O_ll increases with increasing annealing temperature. The AZO thin film of 100 nm thickness shows values of 6.5 × 10¹⁹ cm^-3 of carrier concentration, 8.4 cm^-2/V·s of mobility and 1.2 × 10^-2 Ω·cm electrical resistivity. As the thickness of the thin film increases, the carrier concentration and the mobility increase, resulting in the decrease of resistivity. With the carrier concentration, mobility decreases when the heat treatment temperature increases more than 500 ℃.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.187-187
• /
• 2012

Solution-processed metal-alloy oxides such as indium zinc oxide (IZO), indium gallium zinc oxide (IGZO) has been extensively researched due to their high electron mobility, environmental stability, optical transparency, and solution-processibility. In spite of their excellent material properties, however, there remains a challenging problem for utilizing IZO or IGZO in electronic devices: the supply shortage of indium (In). The cost of indium is high, what is more, indium is becoming more expensive and scarce and thus strategically important. Therefore, developing an alternative route to improve carrier mobility of solution-processable ZnO is critical and essential. Here, we introduce a simple route to achieve high-performance and low-temperature solution-processed ZnO thin film transistors (TFTs) by employing alkali-metal doping such as Li, Na, K or Rb. Li-doped ZnO TFTs exhibited excellent device performance with a field-effect mobility of $7.3cm^2{\cdot}V-1{\cdot}s-1$ and an on/off current ratio of more than 107. Also, in case of higher drain voltage operation (VD=60V), the field effect mobility increased up to $11.45cm^2{\cdot}V-1{\cdot}s-1$. These all alkali metal doped ZnO TFTs were fabricated at maximum process temperature as low as $300^{\circ}C$. Moreover, low-voltage operating ZnO TFTs was fabricated with the ion gel gate dielectrics. The ultra high capacitance of the ion gel gate dielectrics allowed high on-current operation at low voltage. These devices also showed excellent operational stability.