• Bulletin of the Korean Chemical Society
• /
• 제33권1호
• /
• pp.194-198
• /
• 2012

In this work, we studied the microstructural changes of ITO during the annealing process. ITO nanoparticles were prepared by the sol-gel method using indium tin hydroxide as the precursor. The prepared sample was investigated using TEM, powder XRD, XPS, DRIFT, and 2D correlation analysis. The O 1s XPS spectra suggested that the microstructural changes during the annealing process are closely correlated with the oxygen sites of the ITO nanoparticles. The temperature-dependent in situ DRIFT spectra suggested that In-OH in the terminal sites is firstly decomposed and, then, Sn-O-Sn is produced in the ITO nanoparticles during the thermal annealing process. Based on the 2D correlation analysis, we deduced the following sequence of events: 1483 (due to In-OH bending mode) ${\rightarrow}$ 2268, 2164 (due to In-OH stretching mode) ${\rightarrow}$ 1546 (due to overtones of Sn-O-Sn modes) ${\rightarrow}$ 1412 (due to overtones of Sn-O-Sn modes) $cm^{-1}$.

• 대한화학회지
• /
• 제62권5호
• /
• pp.344-351
• /
• 2018

이 연구에서는 기체 상태 페난트렌, 페난트렌올, 페난트레닐 라디칼, 하이드록실 페난트렌 라디칼에 대한 IR 스펙트럼을 BLYP/6-311++G(d,p)법을 사용하여 얻었다. 이 스펙트럼들을 비교함으로써 ${\cdot}OH$에 의한 페난트렌의 분해 반응 경로를 동정하는데 IR 스펙트럼 측정이 유용하게 사용될 수 있음을 볼 수 있었다. IR 스펙트럼에서 H 원자 제거 과정은 CH의 out-of-plane 굽힘 진동 영역인 $650{\sim}850cm^{-1}$, ${\cdot}OH$ 첨가 과정은 CH 신축 및 굽힘 진동 영역에서 용이하게 확인 할 수 있음을 알 수 있었다. 또한 5종의 페난트렌-n-올 (n = 1, 2, 3, 4, 9) 모두에 대하여 얻어진 IR 스펙트럼 역시 여기에 주어졌다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.335-335
• /
• 2008

눈에 안정한(1.53um) 인산염 레이저 유리를 제조하기 위한 기본 조성 (mole%)은 $55P_2O_5\cdot24BaO\cdot10K_2O\cdot4Al_2O_3\cdot6Yb_2O_3$로 하고, 활성 이온은 $Er^{+3}$로, sensitizer로는 $Cr^{+3}(Yb^{+3})$을 사용하였다. 혼합된 원료 조성은 대기와 원료로부터 혼입되는 OH group을 제거하기 위하여 open 시스템에서 가스 버블을 공급하였으며, 용융물에 공급된 시간 변화에 따라 분광학적 특성 변화를 조사하였다. OH oscillations linear 에 의해 quenching된 $Er^{+3}$ 형광방출 확률은 $3500cm^{-1}$ 에서 OH stretching vibration band의 흡수계수에 의존하고 있으며, 이때 $Er^{+3}$의 농도는 $1.6\times10^{19}$에서 $21.2\times10^{19}$ ion/$cm^2$ 범위에서 존재하였다.

• 한국광물학회지
• /
• 제29권4호
• /
• pp.209-220
• /
• 2016

점토광물은 대기부터 지하수에 이르는 크리티컬존(critical zone) 영역에서 금속과 탄소 순환을 결정짓는 역할을 한다. 계산광물학 연구방법 중에 하나인 분자동역학(molecular dynamics) 시뮬레이션은 지구물질을 원자단위로 계산하기 때문에, 점토광물의 물리화학적 현상들에 대해 원자수준의 자세한 정보를 제공할 수 있다. 이번 연구에서는 clayFF 힘 장(force field)을 사용한 분자동역학 시뮬레이션을 이팔면체 점토광물인 깁사이트(gibbsite, $Al(OH)_3$), 카올리나이트(kaolinite, $Al_2Si_2O_5(OH)_4$), 파이로필라이트(pyrophyllite, $Al_2Si_4O_{10}(OH)_2$)에 적용하여 300 K, 1기압조건에서 각 광물이 가지는 격자상수와 원자간 거리를 계산하고 실험결과와 비교하였다. 더불어 수산기의 방향성 및 수소결합의 양상 그리고 파워스펙트럼(power spectrum)을 추가적으로 계산하였다. 계산 결과, 격자상수는 기존의 실험결과와 약 0.1~3.7% 미만의 오차율을 보였으며, 원자간 거리는 실험결과와 약 5% 미만의 차이를 가졌다. 깁사이트나 카올리나이트의 팔면체층 표면에 존재하는 수산기가 가지는 신축진동파수(stretching vibrational wavenumber)는 실험값 보다 약 $200-300cm^{-1}$ 높게 계산되었지만, 팔면체층 표면에 존재하는 수산기들의 상대적 크기의 경향은 기존 실험 결과와 일치하였다. 팔면체층 표면의 수산기가 (001)면과 이루는 각도도 기존 실험결과와 상당부분 일치한 반면에 내부 수산기의 경우는 다소 차이를 보였다. ClayFF를 사용한 분자동역학 시뮬레이션 연구 방법은 이팔면체 점토광물 표면 내(층간) 금속이온 흡착에 대한 수산기의 역할을 규명하는데 유용한 연구방법이 될 수 있음을 시사한다.

• 대한통합의학회지
• /
• 제1권1호
• /
• pp.61-68
• /
• 2013

Purpose : The purpose of this study is to evaluate the stability and balance of the body, mobility complex exercise group and a student group for FMS tests to compare the differences between the two groups to identify its purpose. Method : The subjects of this study FMS measuring D University Physical Therapy, a student enrolled patients (7:7), and 7 patients total of 14 patients was conducted, compound exercise group weekly stretching 10 minutes, the 24 members who have run a complex exercise, 10 minutes of cool down stretching, 20-minute aerobic exercise were included in the study. Result : The results of this study, according to 1) Deep squat, Inline lunge, Trunk Stability Push-up there was significant difference(p<0.05), compound exercise group came out significantly higher. 2) Hurdle Step, Shoulder Mobility Reaching, Active Straight-leg Raise, Rotary stability in measured target these women flexibility because the test items that did not show a significant difference(p>0.05), the two groups averaged compared to the other items were higher. Complex exercise group, a statistically significant difference was overall average. Conclusion : FMS can not be resolved because of a compensatory mechanism to identify disparities and unbalanced movement patterns can help. Therefore, if the FMS and other tests conducted by splicing, will be utilized more profitably, and you will be able to suggest ways that can have a positive impact injury prevention is added to the side to expand the scope of the physical therapist.

• 폴리머
• /
• 제36권3호
• /
• pp.372-379
• /
• 2012

본 연구에서는 실리카 나노입자의 표면을 실란 커플링제인 bis[3-(trimethoxysilyl)propyl]amine(BTMA)을 사용하여 개질하였다. BTMA의 가수분해 시간, 농도 및 개질 시간의 변화가 실리카 표면 개질 반응에 미치는 영향을 Fourier transform infrared spectroscopy(FTIR), elemental analysis(EA) 및 고체 상태 cross-polarization magic angle spinning(CP/MAS) nuclear magnetic resonance spectroscopy(NMR)법을 사용하여 분석을 수행하였다. 연구결과 BTMA의 가수분해 시간, 농도 및 표면 개질 시간이 증가할수록 3737 $cm^{-1}$에 나타나는 실리카의 고립 실란올(isolated silanol) 피크의 세기는 점점 약해지고, 도입되는 BTMA의 $-CH_2$ 기에 의한 신축(stretching) 및 굽힘(bending) 진동 피크는 점점 강하게 나타났다. EA 분석을 통한 N 및 C의 함량에서도 같은 경향을 나타내었다. BTMA를 사용한 실리카 입자의 처리 조건 중, BTMA의 농도 변화는 실리카 입자 표면과 반응하는 BTMA의 양에 큰 영향을 미치지만, BTMA의 가수분해 시간 및 표면 개질 반응 시간의 영향은 크지 않은 것으로 나타났다.

• 한국항공우주학회지
• /
• 제37권9호
• /
• pp.939-945
• /
• 2009

액체로켓 연소기 재생냉각 챔버의 제작에 사용되는 구리합금의 성형한계 곡선을 얻기 위하여 돔 장출 시험과 인장시험을 수행하였다. 성형한계 곡선에 대한 실험적인 연구를 위하여 인장시편을 사용하여 인장-압축 변형률 상태의 데이터를 얻었으며, 인장-인장의 변형률 상태를 얻기 위하여 돔 장출 시험용 시편을 사용한 돔 장출 시험 또한 수행하였다. 시험에 사용한 모든 시편은 제작방향에 따라 종 방향과 횡 방향시편으로 구분하였다. 시험 결과 인장-인장 변형률 상태에서 최대 주 변형률과 부 변형률은 62.3%와 58.6%이며, 인장-압축 상태에서는 60.5%와 25.8%로 나타났다.

• 한국광물학회지
• /
• 제9권2호
• /
• pp.102-112
• /
• 1996

The precious serpentine, referring to a rare and highly valuable gem variety of serpentine group minerals, is found to occur in serpentinite from Booyo Gren Jade Mine which is located in Oesan-myun, Booyo-gun of Chungchungnam-do. Geommological properties of the precious serpentine have been investigated by use of polarizing microscope, specific gravity balance, refractometer, hardness pencils, X-ray diffractometer, XRF, ICP-MS analyser, and infrared absorption spectroscope.The precious serpentine from Booyo is colored deep green with oily luster and semi-transparent. It is highly tough and Mohs's scale of hardness is measured to be 5-6. Specific gravity is determined to be 2.67, and a single refractive index ND=1.56 is observed by a spot method, using sodium light source. X-ray powder diffraction data is represented by the reflection lines at 7.40(100), 4.64(25), 3.68(68), 2.757(69), 2.530(49), 2.549(32), and 1.710(21${\AA}$), which compares very well with that of antigorite of serpentine group minerals. The major chemical compositions of the precious serpentine group minerals. The major chemical compositions of the precious serpentine are SiO2 42.49%, MgO 39.08%, Fe2O3 3.85%, and H2O 11.87%. Besides, trace elements such as Cr(2188), Ni(1110ppm), Co(58ppm), and Ta (108ppm) are relatively spectrum shows peaks at 3670, 1190, 1070, 980 and 610cm-1. Strong absorption at 3670cm-1 is due to OH stretching, and 1190, 1070 and 980cm-1 due to SiO stretching. The absorption 610cm-1 is formed by alteration of pre-existing ultramafic rock, namely peridotite, with an introduction of fluid with very little content of CO2, under 400$^{\circ}C$ environment. Magnetite inclusions, finely disseminated in the precious serpentine, may be a result of Fe precipitation, during serpentinization of olivine-bearing country rock.

• 마이크로전자및패키징학회지
• /
• 제26권4호
• /
• pp.55-62
• /
• 2019

Polydimethylsiloxane (PDMS)를 베이스 기판으로 사용하고 이보다 강성도가 높은 flexible printed circuit board (FPCB)를 island 기판으로 사용한 soft PDMS/hard PDMS/FPCB 구조의 강성도 경사형 신축패키지를 형성하고, 이의 탄성특성 및 인장 싸이클과 굽힘 싸이클에 따른 신뢰성을 분석하였다. Soft PDMS, hard PDMS, FPCB의 탄성계수가 각기 0.28 MPa, 1.74 MPa, 2.25 GPa일 때 soft PDMS/hard PDMS/FPCB 신축패키지의 유효 탄성계수는 0.6 MPa로 분석되었다. 0~0.3 범위의 인장 싸이클을 15,000회 인가시 신축패키지의 저항변화률은 2.8~4.3% 이었으며, 굽힘반경 25 mm의 굽힘 싸이클을 15,000회 인가시 저항변화률은 0.9~1.5% 이었다.

• 대한화학회지
• /
• 제29권4호
• /
• pp.372-381
• /
• 1985

치환 8-퀴놀린올의 옥소몰리브덴(V)착물을 합성하고 착물의 원소분석, 자외선스펙트럼, 전자스펙트럼 및 전도도를 측정하였고 옥소몰리브덴(VI)착물과 함께 질량분석을 행하여 비교 검토하였다. 옥소몰리브덴(V) 착물은 비전해질이고 몰리브덴-산소의 신축진동은 $940cm^{-1}$ 부근에서 강한 흡수띠가 나타나고 결정장전이와 전하이동 전이가 일어났다. 질량분석 결과로 Mo(V, VI)착물에서 몰리브덴과 리간드의 조성이 1:2임을 확인할 수 있었고 옥소몰리브덴(VI)착물에서는 1:1조성의 착물의 질량수가 나타나지만 옥소몰리브덴(V)에서는 일부만 확인되었다.