• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.16-17
• /
• 2006

In this paper, Ni-V alloy was studied with different structures and thickness. In case of Ni-V and Ni-V/Co/TiN, low resistive Ni silicide was formed after one step RTP (Rapid Thermal Process) with temperature range from $400^{\circ}C$ to $600^{\circ}C$ for 30sec in vacuum. After furnace annealing with temperatures range from $550^{\circ}C$ to $650^{\circ}C$ for 30min in nitrogen ambient, Ni-V single structure shows the best thermal stability compare with the other ones. To enhance the thermal stability up to 650oC and find the optimal thickness of Ni silicide, different thickness of Ni-V was studied in this work. Stable sheet resistance was obtained through Ni-V single structure with optimal Ni-V thickness.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.192-193
• /
• 2007

An evaporated Ti/Pd/Ag contact system is most widely used to make high-efficiency silicon solar cells, however, the system is not cost effective due to expensive materials and vacuum techniques. Commercial solar cells with screen-printed contacts formed by using Ag paste suffer from a low fill factor and a high shading loss because of high contact resistance and low aspect ratio. Low-cost Ni and Cu metal contacts have been formed by using electro less plating and electroplating techniques to replace the Ti/Pd/Ag and screen-printed Ag contacts. Ni/Cu alloy is plated on a silicon substrate by electro-deposition of the alloy from an acetate electrolyte solution, and nickel-silicide formation at the interface between the silicon and the nickel enhances stability and reduces the contact resistance. It was, therefore, found that nickel-silicide was suitable for high-efficiency solar cell applications. Cu was electroplated on the Ni layer by using a light induced plating method. The Cu electroplating solution was made up of a commercially available acid sulfate bath and additives to reduce the stress of the copper layer. In this paper, we investigated low-cost Ni/Cu contact formation by electro less and electroplating for crystalline silicon solar cells.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2010년도 춘계학술대회 논문집
• /
• pp.511-512
• /
• 2010

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제37회 하계학술대회 초록집
• /
• pp.226-226
• /
• 2009

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2004년도 제26회 학술발표회 초록집
• /
• pp.172-172
• /
• 2004

• 한국산학기술학회논문지
• /
• 제7권3호
• /
• pp.332-337
• /
• 2006

기판전면에 패턴 없이 15 nm Co/15 nm Ni/70 nm polysilicon/200 nm $SiO_2$/Si(100) 구조로 적층된 구조로부터 급속열처리기 (rapid thermal annealer : RTA)를 이용하여 40초간 700, 900, $1000^{\circ}C$의 실리사이드화 온도를 변화시키면서 CoNi 복합실리사이드를 형성하였다. 완성된 두께 100 nm 정도의 CoNi 복합실리사이드층으로 배선층을 만든다고 상정하여, 이중 집속이온빔(dual beam focused ion beam : FIB)을 써서 30 kV에서 표면전류를 $1{\sim}100$ pA 범위에서 조절하면서 나노급 선폭제작의 가능성을 확인하였다. 각 온도별 복합실리사이드에 동일한 이온빔 조건으로 $100{\mu}m$ 길이의 패턴을 만들고, 이온빔으로 양 끝단에 트렌치를 만들어 FE-SEM으로 각 조건에서의 선폭, 두께, 최종 에칭형상을 확인하였다. 기존 형상변형이 많아서 나노급 선폭 구현이 불리한 폴리사이드 공정에 비해서, 최초로 새로운 저저항 복합실리사이드에 대해서 100 nm 이하의 나노급 피치를 가진 선폭 제작이 $30kV{\sim}30pA$ 범위에서 가능하였다.

• 한국태양에너지학회:학술대회논문집
• /
• 한국태양에너지학회 2009년도 춘계학술발표대회 논문집
• /
• pp.230-234
• /
• 2009

It is significant technique to increase competitiveness that solar cells have a high energy conversion efficiency and cost effectiveness. When making high efficiency crystalline Si solar cells, evaporated Ti/Pd/Ag contact system is widely used in order to reduce the electrical resistance of the contact fingers. However, the evaporation process is no applicable to mass production because high vacuum is needed. Furthermore, those metals are too expensive to be applied for terrestrial applications. Ni/Cu/Ag contact system of silicon solar cells offers a relatively inexpensive method of making electrical contact. Ni silicide formation is one of the indispensable techniques for Ni/Cu/Ag contact sytem. Ni was electroless plated on the front grid pattern, After Ni electroless plating, the cells were annealed by RTP(Rapid Thermal Process). Ni silicide(NiSi) has certain advantages over Ti silicide($TiSi_2$), lower temperature anneal, one step anneal, low resistivity, low silicon consumption, low film stress, absence of reaction between the annealing ambient. Ni/Cu/Ag metallization scheme is an important process in the direction of cost reduction for solar cells of high efficiency. In this article we shall report an investigation of rapid thermal silicidation of nickel on silngle crystalline silicon wafers in the annealing range of $350-390^{\circ}C$. The samples annealed at temperatures from 350 to $390^{\circ}C$ have been analyzed by SEM(Scanning Electron Microscopy).

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 추계학술대회 논문집 Vol.15
• /
• pp.198-201
• /
• 2002

In this paper, the dependence of Ni-silicide properties such as sheet resistance and cross-sectional profile on the dopants have been characterized. There was little dependence of sheet resistance on the used dopants such as As, P, $BF_{2}$ and $B_{11}$ just after RTP (Rapid Thermal Process). However, the silicide properties showed strong dependence on the dopants when thermal treatment was applied after formation of Ni-silicide. $BF_{2}$ implanted sample shows the best stable property, while $B_{11}$ implanted one was thermally unstable. The main reason of the excellent property of $BF_{2}$ sample is believed to be the retardation of Ni diffusion by the flourine.

• 한국분말재료학회지
• /
• 제6권2호
• /
• pp.145-151
• /
• 1999

Nickel silicides ($Ni_5$Si$_2$, Ni$_2$Si and NiSi) have been synthesized by mechanical alloying (MA) of Ni-27.9at.9at%Si, Ni-33.3at% and Ni-50.0at% powder mixtures, respectively. From in situ thermal analysis, eash citical milling period for the formation of the three phases was observed to be 40.2, 34.9 and 57.5 min, at which there was a rapid increase in temperature. This indicates that rapid, self-propagating high-temperature synthesis (SHS) reactions were observed to produce the three phases during room-temperature high-energy ball milling of elemental powders. Each Ni silicide, Ni and Si, however, coexisted for an extended milling time even after the critical milling period. The powders mechanically alloyed after the critical period showed the rapid increase in microhardness. The Hv values were found to be higher than 1000kgf/mm$^2$. The formation of nickel silicides by mechanical alloying and the relevant reaction rates appeared to be influenced by the critical milling period and the heat of formation of the products involved ($Ni_5$Si$_2$$\rightarrow$-43.1kJ/mol.at., Ni$_2$Si$\rightarrow$-47.6kJ/mol.at., NiSi$\rightarrow$-42.4kJ/mol.at).

• 한국세라믹학회지
• /
• 제43권4호
• /
• pp.230-234
• /
• 2006

Metal-Induced Crystallization (MIC) of amorphous silicon (a-Si) using aluminum and nickel as catalysts were performed with a variation of metal thickness and temperature. Raman results showed that the crystallization of a-Si depended on the thickness of aluminum while not on nickel. Nickel that forms silicide nodules during annealing simply catalyzed the formation of crystalline silicon (c-Si) while aluminum was consumed and transferred during MIC, which resulted in more complex microstructural characteristics. Crystalline silicons after NIC had elongated shape with a twin along the long axis. Morphological change after Aluminum-Induced Crystallization (AIC) showed more equiaxial grains. The nucleation and growth mechanism of AIC was discussed.