• Journal of Sensor Science and Technology
• /
• v.29 no.2
• /
• pp.89-92
• /
• 2020

Polytetrafluoroethylene (PTFE) fibers are widely used in the textile industry, filter media, membrane distillation, electronic appliances, and construction. In this study, PTFE-polyethylene oxide (PEO) fibrous membranes were fabricated by emulsion electrospinning; subsequently, pure PTFE nanofibers were obtained via sintering. PTFE-PEO electrospinning solutions were prepared using different weight ratios to determine the optimized condition. As the ratio of the PEO increased, the fiber structure improved. Scanning electron microscopy and Fourier-transform infrared spectroscopy observations indicate that PEO is removed and PTFE fused gradually to form bonds among them during sintering. The obtained pristine PTFE membrane demonstrated hydrophobicity at 143.6° water contact angle and oleophilicity at 0° oil contact angle, which is known to be utilized for oil/water separation. A simple separation experiment was performed to remove oil droplets from water. The PTFE membrane exhibited good chemical stability and a high surface-area-to-volume nanofiber ratio. These excellent properties suggest that it is applicable to oil/water separation in harsh chemical environments.

• Membrane Journal
• /
• v.29 no.3
• /
• pp.123-129
• /
• 2019

Environmental pollution caused by the presence of heavy metal ion from growing industrialization or from leaching is increasing area of concern. There are several area of water purifications but among them adsorption on the functionalized polymer fibers is efficient and cost-effective method. Polyacrylonitrile (PAN) is exciting polymer due to the presence of excessive functional group which can be easily transformed for metal ion adsorption. PAN can be easily electrospun to prepare nanofiber that have higher surface area leading to better metal ion removal. Composite PAN fiber is yet another type of polymer covered in this review for waste water treatment.

• Journal of Korean Society of Environmental Engineers
• /
• v.39 no.8
• /
• pp.456-461
• /
• 2017

In this study, nano fibers with various physical properties were materialized by using a variety of polymers [PAN (Polyacrylonitrile), PU (Polyuretane), PSU (Polysulfone)] which are raw materials of dope solution manufactured for electrospinning and solvents [NMP (N-methyl-2 pyrrolidone), DMF (Dimethylformamide)] and evaluated characteristics of their flux and SS (Suspended Solids) separation and then ascertained application of manufactured fibers as separation membrane for water treatment. In this study, analysis of surface of manufactured material was carried out through SEM analysis to ascertain the cause of flux and SS separation performance by checking diameter, uniformity and straightness of fiber. If additive is used in manufacturing nano fiber water treatment separation membrane, it is expected to solve problems such as membrane fouling and mechanical strength and to be used as basic factor for manufacturing separation membrane with catalyst function added.

• Journal of Adhesion and Interface
• /
• v.24 no.1
• /
• pp.17-25
• /
• 2023

In this study, waste polyethylene terephthalate (PET) was recycled to produce a support and then polyetherimide (PEI) was used for environmentally friendly organic solvent nanofiltration. The prepared composite membrane was first prepared by electrospinning a PET support, then casted on the support using PEI having excellent solvent resistance, and organic solvent nanoparticles using a Non-solvent Induced Phase Separation (NIPS) method. A filtration membrane was prepared. First, the fiber diameter and tensile strength of the PET scaffold prepared prior to membrane fabrication were identified through morphology analysis, and the optimal scaffold for the organic solvent nanofiltration membrane was identified. Afterward, the PET/PEI composite membrane prepared was checked for the DEA removal rate of Congo red having a molecular weight of 697 g/mol in ethanol to understand the performance as an organic solvent nanofiltration membrane according to the concentration of PEI. Finally, the removal rate of Congo red was 90% or more.

• 대한치주과학회:학술대회논문집
• /
• 2004.11a
• /
• pp.144-145
• /
• 2004

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.381-382
• /
• 2008

$TiO_2$ colloidal solution was electrosprayed for preparing a conductive thin film with high quality. Electrospray is a technique of liquid dispersion electrically and a good method of manufacturing nanoparticle, nanofiber, porous membrane, film preparation and coating. Water and ethanol were used as solvents and their mixing ratio was varied for studying the influence of solvent volatile on nanoparticle dispersion. Various nozzles to control the thru-put of solutions.were examined. Integrated analytical method and scanning electron microscope were used to analyze integrity and microscopic images.

• Applied Chemistry for Engineering
• /
• v.21 no.5
• /
• pp.527-531
• /
• 2010

The optimized sheet for EMI shielding was prepared by metal power with Fe series. Then various metal powders were deposited on the sheet by PVD method. Moreover, the PVdF nanofiber membrane was used to compare the characteristic of EMI shielding efficiency of various metal powders. The electrical property was measured by the 4-point probe method. The result from EDS confirmed that the metal powder existed on the sheet. EMI shielding efficiency was analysed by EMI shielding measurement apparatus. The lowest electrical resistance, $641.95{\Omega}{wcdot}cm$, was obtained with $1000\;{\AA}$ deposition of Cu on the sheet. It was revealed that the EMI shielding efficiency increased with increase of the metal deposition thickness. The sheet deposited by Cu with $1000\;{\AA}$ showed the highest EMI shielding efficiency, 32.5 dB.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.2
• /
• pp.142-147
• /
• 2009

The influence of graphitization of carbon support on the electrochemical corrosion of carbon and sintering of Pt particles are investigated by measuring $CO_2$ emission at a constant potential of 1.4 V for 30 min using on-line mass spectrometry and cyclic voltammogram. In comparison to commercial Pt/C (from Johnson Matthey), highly graphitized carbon nanofiber (CNF) supported Pt catalyst exhibits lower performance degradation and $CO_2$ emission. As the more carbon corrosion occurred, the more prominent changes were detected in electrochemical characteristics of fuel cell. This indicates that the carbon corrosion affects significantly the fuel cell durability. From the observed results, CNF is considered to be more corrosion resistant material as a catalyst support. However, CNF shows higher aggregation of Pt particles under repeated cyclic voltammetry between 0 and 0.8 V where the carbon corrosion is not initiated.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.2
• /
• pp.181-188
• /
• 2009

Pt catalyst was adsorbed on Carbon nanofiber (CNF) by modified polyol method after acid treatment of the carbon support with $HNO_3$ and $H_{2}SO_{4}$. As the time for acid treatment increases, more oxygen functional groups on carbon surface were produced which improve the loading amount and dispersion of Pt catalyst on carbon supports. In order to inspect the effect of CNF acid treatment time on electrochemical corrosion, constant potential of 1.4 V was applied to a single cell for 30 min and the amount of $CO_2$ emitted was monitored with on-line mass spectrometry. According to the results of our experiment, more $CO_2$ was produced with Pt/ oxidized-CNF catalyst in compared to that with unoxidized-CNF. Increasing acid treatment time also induces the more $CO_2$ emission. Besides, performance degradation after corrosion test expanded with severer carbon corrosion. From the observed results, it can be concluded that the acid treatment of CNF is beneficial to catalyst loading, but it also is a significant factor declining the fuel cell durability by accelerating electrochemical oxidation of carbon support.

• Membrane Journal
• /
• v.30 no.4
• /
• pp.228-241
• /
• 2020

Separators, which produces physical layer between a cathode and anode, are getting enormous attention as the quality of the separator determines the performance of lithium ion batteries (LIBs). Porous membranes based on polyethylene (PE) and polypropylene (PP) are generally utilized as the separator of LIBs because of their high electrochemical stability and suitable mechanical strength. However, low thermal resistance and wettability of PE and PP membranes limited the potential of LIBs. Operating at the temperature exceeding the melting point of membranes, the separators change their structures which lead to short circuit of LIBs. Low wettability of the separators corresponds to low ionic conductivity which increases the cell resistance. To overcome these weaknesses of PE and PP separators, different types of separator were prepared by co-electrospinning, applying coating layer, forming core shell around membrane, and papermaking method. The synthesized separator greatly enhanced the heat resistance and wettability of separator and mechanical properties like flexibility and tensile strength. In this review different type of polymer membrane used as separator in lithium ion battery are discussed.