• Membrane Journal
• /
• v.17 no.3
• /
• pp.219-232
• /
• 2007

The polyethersulfone(PES)-titanium oxide($TiO_2$) hybrid membranes were prepared by immersion precipitation phase inversion method. The casting solution for the preparation of $PES-TiO_2$ hybrid membrane was provided by adding $TiO_2$ nano particles into the basis polymer solution of 14 wt% and 20 wt% PES/N-methyl-2-pyrrolidone(NMP). The $TiO_2$ loading [wt% ($TiO_2/NMP$)] in eating solution was varied from 0 to 60 wt%. Membrane performance and morphological change of the resulting $PES-TiO_2$ hybrid membranes were discussed in aspect of $TiO_2$ loading, by viscosity, coagulation value and light transmittance of the casting solution, measurement of tensile strength, pore size and contact angle, surface and cross sectional SEM images of the hybrid membrane, and ultrafiltration experiments using the hybrid membrane. According as increase of $TiO_2$ loading in the casting solution, viscosity is increased and coagulation value becomes lower, therefore the thermodynamic instability of the casting solution is increased. It is found that when $TiO_2$ loading is increased, 1) precipitation rate becomes faster while instantaneous demixing is maintained, 2) pure water flux, membrane pore size and compaction stability of the resulting membranes are increased, 3) tensile strength and contact angle are decreased. Dead-end ultrafiltration of bovine serum albumin(BSA) solution using the hybrid membrane shows that membrane performance(flux of BSA solution) enhanced up to 7 times compared with the results obtained using the pure PES membrane(not containing $TiO_2$ particle), due to the increase of hydrophilicity.

• Textile Coloration and Finishing
• /
• v.28 no.1
• /
• pp.48-56
• /
• 2016

Improvement of heat sink technology related to the continuous implementation performance and extension of device-life in circumstance of easy heating and more compact space has been becoming more important issue as multi-functional integration and miniaturization trend of electronic gadgets and products has been generalized. In this study, it purposed to minimize of decline of the heat diffusivity by gluing polymer through compounding of inorganic particles which have thermal conductive properties. We used NH-9300 as base resin and used inorganic fillers such as silicon carbide(SiC), aluminum nitride(AlN), and boron nitride(BN) to improve heat diffusivity. After making film which was made from 100 part of acrylic resin mixed hardener(1.0 part more or less) with inorganic particles. The film was matured at $80^{\circ}C$ for 24h. Diffusivity were tested according to sorts of particles and density of particles as well as size and structure of particle to improve the effect of heat sink in view of morphology assessing diffusivity by LFA(Netzsch/LFA 447 Nano Flash) and adhesion strength by UTM(Universal Testing Machine). The correlation between diffusivity of pure inorganic particles and composite as well as the relation between density and morphology of inorganic particles has been studied. The study related morphology showed that globular type had superior diffusivity at low density of 25% but on the contarary globular type was inferior to non-globular type at high density of 80%.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.2
• /
• pp.174-181
• /
• 2007

In this study, $SiO_2/poly(ethylene-co-vinyl$ alcohol)(EVOH) hybrid coating materials with gas barrier property could be produced using sol-gel method. The biaxially oriented polypropylene (BOPP) substrate with surface pretreatment was coated with the prepared hybrid sols containing various inorganic silicate component by a spin coating method. Crystallization behavior of the hybrids was investigated in terms of analysis of X-ray diffraction and cooling thermogram from DSC experiment. From the morphological observation of the $SiO_2/EVOH$ hybrid gel, it was confirmed that there existed an optimum content of inorganic silicate precursor, Tetraethylorthosilicate (TEOS), to produce hybrid materials with dense microstructure, exhibiting uniformly dispersed silica particles with average size below 100 nm. When TEOS was added at below or above the optimum content, particle clusters with large domain were observed, resulting in phase separation. This morphological result was found to be in good agreement with that of oxygen permeability of the hybrid coated films. In the case of film coated with hybrid prepared from addition of 0.01 - 0.02mol of TEOS, a remarkable improvement in barrier property could be obtained, however, with the addition of TEOS more than 0.04 mol, the barrier property was dramatically reduced because of phase separation and micro-crack formation on the film surface.

• Journal of the Korean Magnetics Society
• /
• v.20 no.5
• /
• pp.196-200
• /
• 2010

$\gamma-Fe_2O_3$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, VSM and Mossbauer spectroscopy. $\gamma-Fe_2O_3$ powder annealed at $150^{\circ}C$ has a spinel structure and superparamagnetical behavior. The estimated size of superparammagnetic $\gamma-Fe_2O_3$ nanoparticle is around 7 nm. The hyperfine fields at $-261^{\circ}C$ for the A and B patterns were found to be 503 and 485 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $\gamma-Fe_2O_3$ nanoparticle is about $-183^{\circ}C$. The magnetic anisotropy constant of $\gamma-Fe_2O_3$ nanoparticle was calculated to be $1.6{\times}10^6ergs/cm^3$. $\gamma-Fe_2O_3$ nanoparticle annealed at $150^{\circ}C$ can be a candidate for biomedicine applications as magnetic carriers.

• Korean Chemical Engineering Research
• /
• v.46 no.3
• /
• pp.626-632
• /
• 2008

The purpose of this study was to enhance gas exchange by producing hemosome, a hemoglobin microencapsulated with phospholipid of egg, and perfluorocarbone(PFC) emulsion solution. In the experiment, stable emulsion solution with 437 nm of mean particle size could be produced by Flusol-DA sonication, and shortening of emulsion time could be attained with higher stability as well. $0.8{\mu}m$ sized hemosome could be produced by microencapsulation of hemoglobin with phospholipid extracted from egg yolk. The pattern of oxygen saturation curve of hemosome was S shape, which is similar to that found in normal blood, and $P_{50}$ was measured to be 24 mmHg. The oxygen saturation in the mixed solution of hemosome and blood in 1:4(V/V%) ratio was similar to that of normal blood, and the same result was found in the mixed solution of PFC emulsion and blood in 1:4(V/V%) ratio.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.4 s.33
• /
• pp.55-59
• /
• 2004

We fabricates the $TiO_2$ thin film from anatase phase $TiO_2$ powder having good photocatalytic property using aerosol deposition method at room temperature. Aerosol deposition method, which sprays an aerosol powder with ultrasonic velocity and deposits a thin film on substrate at low temperature, has the advantages of low thermal stress and low cost. To fabricate the $TiO_2$ thin film, the aerosol bath pressure and chamber pressure were 500 torr and 0.4 torr, respectively. The difference of aerosol bath pressure and chamber pressure accelerated the $TiO_2$ nano powder to ultrasonic velocity through the nozzle of $0.4 mm{\times}10 mm$ and $TiO_2$ thin film was finally formed. SS mesh with diameter of 50 mm was used as a substrate to apply the $TiO_2$ thin film to water quality purification. The raw powder was dehydrated for the good dispersion of $TiO_2$ powder. To suppress the formation of second particle, the powder was dispersed for 90 min in alcohol bath by ultrasonic treatment and desiccated. The grain size of $1 {\mu}m$ was observed in $TiO_2$ thin film deposited on SUS mesh by scanning electron microscopy (SEM). The anatase phase of $TiO_2$ thin film was also observed by X-ray diffraction (XRD) and the anatase phase of raw powder was nicely maintained after aerosol deposition. The results are applicable to water treatment filter having photocatalytic reaction.

• Journal of the Korean Applied Science and Technology
• /
• v.37 no.5
• /
• pp.1159-1170
• /
• 2020

In this study, to improve the stability of fermented squalene developed using microorganisms, Microsome-SQ20 was prepared, and its physical behavior, properties, and efficacy were studied. The appearance of Microsome-SQ20 was a transparent liquid, no smell, and had a specific smell. The color was a transparent liquid, and the specific gravity was 0.928 and the pH was 5.82 (20% solution), forming a nano-emulsion suitable for use in cosmetics. It was confirmed that the content of the main component of squalene was 20.05%, which was stably sealed. The particle size measured by 0.1% aqueous solution of Microsome-SQ20 was 134.8 nm to obtain a bluish emulsified phase. The antioxidant effects of F-SQ and MF-SQ by DPPH radicals were 80.72% and 81.5%, respectively, showing superior effects compared to L-ascorbic acid. The cell viability of squalene (SQ), fermented squalene (F-SQ) and microsome squalene (MF-SQ) was at 10 ppm, respectively, showing 121.2%, 150.3%, and 129.9% cell viability. It was found that SQ, F-SQ, and MF-SQ had an elastase inhibitory ability of 8.7%, 10.33% and 8.7% at 10 ppm, respectively. In addition, the inhibitory ability of MMP-1 was 1.55%, 41.44%, 31.79% at 10 ppm for SQ, F-SQ, and MF-SQ, respectively, indicating that F-SQ significantly reduced the MMP-1 expression.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.8
• /
• pp.765-772
• /
• 2015

Cast iron is widely used in fields such as the transport and heavy industries. For parts where contact damage is expected to occur, it is necessary to understand the friction and wear characteristics of cast iron. In this study, we use cast iron plates as the specimens to investigate their friction and wear characteristics. We perform various experiments using a reciprocating type tribotester. We assess the frictional characteristics by analyzing the friction coefficient values that were obtained during the sliding tests. We observe the wear surfaces of cast iron and steel balls using a scanning electron microscope, confocal microscope, and 3d profiler. We investigate the friction and wear characteristics of cast iron by injecting sand and alumina particles having various sizes. Furthermore, we estimate the effect of temperature on the friction and wear characteristics. The results obtained are expected to aid in the understanding of the tribological characteristics of cast iron in industry.

• Journal of Oral Medicine and Pain
• /
• v.34 no.1
• /
• pp.39-48
• /
• 2009

Recently there is much interest in the antibacterial activity of nano-sized silver particle (nanosilver) since silver is known to be safe and effective as disinfectant for a long time. Oral malodor is considered to originate in the oral cavity primarily as a result of production of malodorous compounds by oral bacteria. Major compounds responsible for oral malodor are volatile sulfur compounds, which is thought to be generated by the G(-) anaerobic bacteria found normally in the oral cavity, especially on the dorsum of the tongue. The purposes of this study were to investigate the effect of nanosilver on growth of oral malodor generating microorganisms, including Fusobacterium nucleatum, Prevotella melaninogenica, Klebsiella pneumonia, and to determine the optimal culture condition of them. The results were as follows: 1. The optimal culture condition for P. melaninogenica was vacuum culture using desiccator after evacuation of air by vacuum pump in chopped beef meat media. 2. The growth of K. pneumonia was temporarily inhibited by nanosilver (5 ppm and 10 ppm). 3. The morphological alteration and cell damage caused by nanosilver were observed in K. pneumonia.

• Korean Chemical Engineering Research
• /
• v.50 no.1
• /
• pp.50-54
• /
• 2012

In this study, PANI and PANI/$TiO_2$ composites were prepared as electrode materials for a supercapacitor application. Cyclic voltammetry (CV) was performed to investigate the supercapacity properties of these electrodes in an electrolyte solution of 6 M KOH. The PANI/$TiO_2$ composites were polymerized by amount of various ratios through a simple in-situ method. The morphological properties of composites were analyzed by SEM and TEM method. The crystallinity of the composite and $TiO_2$ particle size were identified using X-ray diffraction (XRD). In the electrochemical test, The electrode containing 10 wt% $TiO_2$ content against aniline units showed the highest specific capacitance (626 $Fg^{-1}$) and delivered a capacitance of 286 $Fg^{-1}$ reversibly at a 100 $mVs^{-1}$ rate. According to the surface morphology, the increased capacitance was related to the fact that nano-sized $TiO_2$ particles (~6.5 nm) were uniformly connected for easy charge transfer and an enhanced surface area for capacitance reaction of $TiO_2$ itself.