• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.115-118
• /
• 1999

Carbon composites with $MoSi_2$ dispersion were prepared by hot-pressing at $1700^{\circ}C$ under 30 MPa for 1 h using polysilazance as binding material. The composites consisted of C, $Mo_{4.8}Si_3C_{0.6}$ and SiC. Bulk density and porosity of the carbon composites with 10 vol% $MoSi_2$ was 1.8g.$\textrm{cm}^{-3}$ and 34%, respectively. This composite was oxidized about 0.05mm from the surface of the carbon composite after oxidation test at $1500^{\circ}C$ for 10h in air. Formation of the $SiO_2$ glass layer was observed by SEM. When this composite suffered damage in the coating layer, it had hardly farther oxidation because of its self-repairing property. The composite prepared in this study indicated good oxidation resistance.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.10
• /
• pp.631-636
• /
• 2017

The degradation mechanism of $Mo_xW_{1-x}Si_2$ ultrahigh-temperature heating elements fabricated by self-propagating high-temperature synthesiswas investigated. The $Mo_xW_{1-x}Si_2$ specimens (with and without post-annealing) were subjected to ADTs (accelerated degradation tests) at temperatures up to $1,700^{\circ}C$ at heating rates of 3, 4, 5, 7, and $14^{\circ}C/min$. The surface loads of all the specimen heaters were increased with the increase in the target temperature. For the $Mo_xW_{1-x}Si_2$ specimens without annealing, many pores and secondary-phase particles were observed in the microstructure; the surface load increased to $23.9W/cm^2$ at $1,700^{\circ}C$, while the bending strength drastically reduced to 242 MPa. In contrast, the $Mo_xW_{1-x}Si_2$ specimens after post-annealing retained $single-Mo_xW_{1-x}Si_2$ phases and showed superior durability after the ADT. Consequently, it is thought that the formation of microcracks and coarse secondary phases during the ADT are the main causes for the degraded performance of the $Mo_xW_{1-x}Si_2$ heating elements without post-annealing.

• Korean Chemical Engineering Research
• /
• v.57 no.4
• /
• pp.553-558
• /
• 2019

In present study, the cylindrical susceptor by the slip casting method was designed to apply high-temperature induction heating by using $(Mo,W)Si_2$ ceramics. $MoSi_2$-based materials were synthesized by SHS (Self-propagating High-temperature Synthesis) method. The phase and crystal structure of $MoSi_2$-based materials were confirmed by XRD analysis. The shape of cylindrical mold was synthesized for various thickness by using the slip casting method. Finally, the susceptor for induction heating was processed by sintering and heat treatment to form $SiO_2$ layer, which was confirmed on the surface of susceptor by SEM/EDS analysis. To evaluate the heating performance of $(Mo,W)Si_2$ cylinder susceptor, we measured the maximum surface temperature and heating rate in comparison with the rod heating element under constantly applied power. The induction heating of the $(Mo,W)Si_2$ cylinder showed excellent heating performance, reaches the maximum temperature of $1457^{\circ}C$, with the average heating rate of $19^{\circ}C/s$ at 2 kW

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.43-43
• /
• 2001

• Applied Chemistry for Engineering
• /
• v.7 no.5
• /
• pp.861-868
• /
• 1996

Skeletal isomerization reaction known as exothermic reaction shows possible maximum yield of i-butene from n-butene at $110^{\circ}C$ over $Pt/MoO_3/SiO_2$. Compared with conventional catalyst such as silica, zeolite, alumina etc., $Pt/MoO_3/SiO_2$ demonstrates higher yield while by-products except 2-butene do not form. Faster H spillover rate over $Pt/MoO_3/SiO_2$ is demonstrated via isothermal reduction experiment at $110^{\circ}C$ compared to the rate over $Pt/MoO_3/Al_2O_3$. Overall isomerization rates are proportional to higher spillover rates from Pt onto $MoO_3$ surface. The skeletal isomerization reaction is composed of two elementary steps. First, carbonium ion formation over Pt crystallites by H spillover. Second, carbenium ion formation over $MoO_3$ followed by formation of i-butene. Moreover, it is suggested that H spillover step from Pt surface onto $MoO_3$ is assumed to be the rate determining step and control the overall isomerization rate.

• Journal of the Korean Vacuum Society
• /
• v.9 no.3
• /
• pp.263-266
• /
• 2000

This paper is focused on the fabrication of reliable Al/$TiO_2-SiO_2$/Mo antifuse, which could operate at low voltage along with the improvement in on/off state properties. Mo metal as the bottom electrode had smooth surface and high melting point, and was being kept as-deposited $SiO_2$film stable. The breakdown voltage of TiO_2-SiO_2$ stacked antifuse was better than that of same-thickness (100 $\AA$) $SiO_2$antifuse because of Ti diffusion in $SiO_2$. The improving breakdown-voltage and on-resistance can be obtained as well as the influence of hillock in the bottom metal is reduced by using double insulator. Low on-resistance (65 $\Omega$) and low programming voltage (9.0 V) can be obtained in these antifuses with 250 $\AA$ double insulator.

• Korean Journal of Materials Research
• /
• v.7 no.9
• /
• pp.763-771
• /
• 1997

이규화몰리브덴 고온발열체의 제조공정을 개발하였다. 원료분말은 상용 MoSi$_{2}$분말이었으며 Bentonite, Si$_{3}$N$_{4}$, B, ThO$_{2}$를 각각 가소제와 첨가제로 사용하였다. 이들은 진공압출, 소결, 단자부 기계가공, U자형 성형, 용접 등의 과정을 거쳐 U자형 발열체로 제조되었다. 사용제품의 분석결과 최근 사용온도가 크게 증가된 것으로 알려진 190$0^{\circ}C$용 발열체는 다량(33wt%)의 W이 Mo을 치환하고 있는 것으로 나타났다. 발열체의 전기비저항은 겉보기 밀도가 증가함에 따라 급격하게 감소하는 경향을 보였으며 첨가물들의 영향은 미미하였다. 1400-1$600^{\circ}C$에서 용접한 경우 용접면에서의 전기비저항은 비용접부보다 낮았으며 용접온도가 증사함에 따라 감소하였다. 발열시험결과 제조된 발열체는 표면온도가 1$700^{\circ}C$이하에서는 문제가 없었으며 175$0^{\circ}C$ 이상의 온도에서는 원형의 융기가 표면에 발생하면서 급속하게 파괴되었다. 이 융기는 X-선 회절분석결과 SiO로 밝혀졌으며 따라서 발열체의 파괴는 MoSi$_{2}$/SiO$_{2}$계면에서의 Si(in MoSi$_{2}$) + SiO$_{2}$=2SiO(g)반응에 으해 일어나는 것으로 판단된다.

• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.653-657
• /
• 2012

In this study, a molybdenum disilicide ($MoSi_2$) coating process was investigated by hydrogen reduction and Si-pack cementation. At first, the metallic Mo coating was carried out by hydrogen reduction of $MoO_3$ powder at $750^{\circ}C$ for various holding times (1, 2, 3 h) in hydrogen atmosphere. A $4.3{\mu}m$ thick metallic molybdenum thin film was formed at 3 h. $MoSi_2$ was obtained by Si-pack cementation on molybdenum thin film through hydrogen reduction processing. It was carried out using $Si:Al_2O_3:NH_4Cl=5:92:3$ (wt%) packs at $900^{\circ}C$ for various holding times (30, 60, 90 min) in Ar atmosphere. When the holding time was 90 min, a $MoSi_2$ layer was coated successfully and a $15.4{\mu}m$ thickness was observed.

• Journal of the Korean Magnetics Society
• /
• v.16 no.5
• /
• pp.240-244
• /
• 2006

In this paper, magnetic properties and annealing behavior of spin valve structures using Mo(MoN) layers as underlayers were studied varying the thickness of the underlayers. The spin valve structure was consisted of Si substrate/$SiO_2(2,000{\AA})/Mo(MoN)(t{\AA})/NiFe(21\;{\AA})/CoFe(28\;{\AA})/Cu(22\;{\AA})/CoFe(18\;{\AA})/IrMn(65\;{\AA})/Ta(25\;{\AA})$. Also, MoN films were deposited on Si substrates and their thermal annealing behavior was analyzed. The resistivity of the MoN film increased as the $N_2$ gas flow rate was increased. After annealing at $600^{\circ}C$, XRD results did not show peaks of silicides. XPS results indicated MoN film deposited with 5 sccm of $N_2$ gas flow rate was more stable than the film deposited with 1 sccm of $N_2$ gas flow rate. The variations of MR ratio and magnetic exchange coupling fold were small for the spin valve structures using Mo(MoN) underlayers up to thickness of45 ${\AA}$. MR ratio of spin valves using MoN underlayers deposited with various $N_2$ gas flow rate was about 7.0% at RT and increased to about 7.5% after annealing at $220^{\circ}C$. Upon annealing at $300^{\circ}C$, the MR ratio decreased to about 3.5%. Variation of $N_2$ gas flow rate up to 5 sccm did not change the MR ratio and $H_{ex}$ appreciably.

• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.6
• /
• pp.299-305
• /
• 2007

The effect of spray deposition of oxide particles on oxidation behaviors of as-cast Mo-14.2Si-9.6B (at%) alloys at $1200^{\circ}C$ up to for 100 hrs has been investigated. Various oxide powders are utilized to make coatings by spray deposition, including $SiO_2,\;TiO_2,\;ZrO_2,\;HfO_2$ and $La_2O_3$. It is demonstrated that the oxidation resistance of the cast Mo-Si-B alloy can be significantly improved by coating with those oxide particles. The growth of the oxide layer is reduced for the oxide particle coated Mo-Si-B alloy. Especially, for the alloy with $ZrO_2$ coating, the thickness of oxide layer becomes only one fifth of that of uncoated alloys when exposed to in air for 100 hrs. The reduction of oxide scale growth of the cast Mo-Si-B alloy due to oxide particle coatings are discussed in terms of the change of viscosity of glassy oxide phases that form during oxidation at high temperature.