• Journal of the Korean Magnetics Society
• /
• v.9 no.5
• /
• pp.256-262
• /
• 1999

Sputter deposited CoCr(Mo)/Si film were studied with emphasis on the correlation between magnetic properties and crystallographic orientation. The perpendicular coercivities of CoCr films decreased with Si underlayer thickness, whereas those of CoCrMo films increased with Si underlayer thickness. It has been explained that additions of the larger atomic radius Mo atoms in CoCr films impedes crystal growth resulting in a decrease in grain size, thus this small grain size may induce high perpendicular coercivity. The c-axis alignment of CoCrMo film was improved due to addition of 2at.%Mo. It means CoCrMo layer grow self-epitaxial directly from orientation and structure of Si underlayer when the main layer grow on underlayer.

• Journal of Industrial Technology
• /
• v.21 no.A
• /
• pp.221-229
• /
• 2001

The effect of Mo underlayer on the magnetic properties of CoCrTa/Cr films deposited on glass substrates were investigated. The coercivity increased and the coercivity squareness decreased by introducing Mo underlayer. The coercivity increase was attributed to the increase of in-plane c-axis orientation and magnetic isolation of Co grains deposited on Cr/Mo underlayer. The decrease of coercivity squarenesses seemed to be caused by the increase of magnetic isolation. The increase of magnetic isolation of Co grains was attributed to the diffusion of Mo atoms into grain boundaries of Co films and the physical isolation of Co grains. The coercivity of CoCrTa/Cr/Mo showed maximum values at Mo thickness of $400{\AA}$. The appearance of the maximum coercivity at that thickness was attributed to the development of strong $Co(10{\bar{1}}0)$ and $Co(10{\bar{1}}1)$ preferred orientation.

• Journal of the Korean Magnetics Society
• /
• v.9 no.4
• /
• pp.203-209
• /
• 1999

Effects of Mo and Si addition in Cr underlayer on magnetic properties of CoCrTa/CrMo and CoCrTa/Si thin films media were investigated. Thin films were prepared with DC magnetron sputtering system. The thickness of CoCrTa magnetic layer and Cr underlayer were fixed at 300 $\AA$ and 700 $\AA$, respectively. The substrate heating temperature was kept constant at 26$0^{\circ}C$ for both magnetic layer and underlayer preparation. The coercivity increase of CoCrTa film was realized due to Mo addition in Cr underlayer. Si addition made a small decrease in coercivity. Coercivity increase seems to be attributed by the improvement of preferred orientation of Cr(200) plane. It is found that lattice fit between Cr(200) and CoCrTa(1120) of CrMo underlayer is better than that of CrSi underlayer. This small misfit may also contribute coercivity increase.

• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.320-324
• /
• 1993

The effect of sputtering conditions on magnetic properties of CoCrMo/Cr magnetic thin film was investigated. Substrate temperature were controlled from R. T to $250^{\circ}C$. The thickness changes of Cr underlayer and CoCrMo magnetic layer were in the range of $1000-2500\AA$ and $300-800\AA$, respectively. Grain size was found to be decreased with increasing magnetic layer thickness(from $500\AA$ to $800\AA$). CoCrMo magnetic layer microstructure showed relatively small dependence on Cr underlayer thickness, substrate temperature. Coercivity increased with increasing Cr underlayer, magnetic layer thickness and substrate temperature. CoCrMo/Cr thin film showed a coercivity of 880 Oe in $700\AA$ magnetic layer thickness and $1000\AA$ Cr underalyer thickness.

• Korean Journal of Materials Research
• /
• v.17 no.9
• /
• pp.484-488
• /
• 2007

Mo(Ti) alloy and pure Cu thin films were subsequently deposited on $SiO_2-coated$ Si wafers, resulting in $Cu/Mo(Ti)/SiO_2$ structures. The multi-structures have been annealed in vacuum at $100-600^{\circ}C$ for 30 min to investigate the outdiffusion of Ti to Cu surface. Annealing at high temperature allowed the outdiffusion of Ti from the Mo(Ti) alloy underlayer to the Cu surface and then forming $TiO_2$ on the surface, which protected the Cu surface against $SiH_4＋NH_3$ plasma during the deposition of $Si_3N_4$ on Cu. The formation of $TiO_2$ layer on the Cu surface was a strong function of annealing temperature and Ti concentration in Mo(Ti) underlayer. Significant outdiffusion of Ti started to occur at $400^{\circ}C$ when the Ti concentration in Mo(Ti) alloy was higher than 60 at.%. This resulted in the formation of $TiO_2/Cu/Mo(Ti)\;alloy/SiO_2$ structures. We have employed the as-deposited Cu/Mo(Ti) alloy and the $500^{\circ}C-annealed$ Cu/Mo(Ti) alloy as gate electrodes to fabricate TFT devices, and then measured the electrical characteristics. The $500^{\circ}C$ annealed Cu/Mo($Ti{\geq}60at.%$) gate electrode TFT showed the excellent electrical characteristics ($mobility\;=\;0.488\;-\;0.505\;cm^2/Vs$, on/off $ratio\;=\;2{\times}10^5-1.85{\times}10^6$, subthreshold = 0.733.1.13 V/decade), indicating that the use of Ti-rich($Ti{\geq}60at.%$) alloy underlayer effectively passivated the Cu surface as a result of the formation of $TiO_2$ on the Cu grain boundaries.

• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.95-98
• /
• 2007

In this paper, the magnetic properties and the annealing behavior of spin valve structures with Mo(MoN) underlayers were studied for various underlayer thickness. The spin valve structure was Si substrate/Mo(MoN)$(t{\AA})/NiFe(21{\AA})/CoFe(28{\AA})/Cu(22{\AA})/CoFe(18{\AA})/IrMn(65{\AA})/Ta(25 {\AA})$. Mo and MoN films were deposited on Si substrates and their thermal annealing behavior was analyzed. The deposition rate of the MoN thin film was decreased and tile resistivity of the MoN thin films were increased as the $N_2$ gas flow was increased. The variations of MR ratio and magnetic exchange coupling field of spin valve structure were smaller with MoN underlayers than that with Mo underlayers up to thickness of $51{\AA}$. MR ratio of spin valves with Mo underlayers was 2.86% at room temperature and increased up to 2.91 % after annealing at $200^{\circ}C$. Upon annealing at $300^{\circ}C$, the MR ratio decreased about 2.16%. The MR ratio of spin valves structure with MoN underlayers for $N_2$ gas flow 1 sccm was 5.27% at room temperature and increased up to 5.56% after annealing at $200^{\circ}C$. Upon annealing at $300^{\circ}C$, the MR ratio decreased about 4.9%.

• Journal of the Korean Magnetics Society
• /
• v.12 no.3
• /
• pp.94-98
• /
• 2002

Sputtering conditions and various underlayer such as Al, Cu, Ni, Cr, Ag, Mg, Fe, Co, Pd, Au, Pt, Mo and Hf were investigated for coercivity enhancement of 20 nm Ti/CoCrPt thin films in order to increase the coercivity of the films thinner than 20 nm. Among them, Ag and Mg were effective to increase the coercivity. Particularly 2 nm Ag was very effective to increase the coercivity and nucleation field as well as to reduce ${\alpha}$ value in CoCrPt thin film such that the coercivity of 2 nm Ag/18 nm Ti/10 nm CoCrPt film was 2200 Oe. However, it seemed that other coercivity enhancement mechanism operated in CoCrPt films because Ti (002) preferred texture was not developed with Ag underlayer contrary to a general expectation. And the coercivity and nucleation field were decreased when glass substrate with rougher surface was used.

• Korean Journal of Materials Research
• /
• v.17 no.1
• /
• pp.25-30
• /
• 2007

The in-situ scanning electron microscopy observation of real-time hillock evolution in pure hi thin films on glass substrate during Isothermal annealing was analyzed quantitatively to understand the compressive stress relaxation mechanism by focusing on the effect of Mo interlayer between Al film and glass substrate. There is a good correlation between the hillock-induced stress relaxation by in-situ scanning electron microscopy observation ana the measured stress relaxation by wafer curvature method. It is also clearly shown that the existence of Mo interlayer plays an important role in hillock formation probably due to the large difference in interfacial diffusivity of Al films.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1999.04a
• /
• pp.120-121
• /
• 1999

• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.314-319
• /
• 1993

The Effects of additional element X (X = Si, Mo, Cu, Gd) on magnetic properties and microstructure of Co-1Zat%Cr-Zat%Ta/Cr-X magnetic thin film were investigated. The thickness changes of Cr-X underlayer and CoCrTa magnetic layer were in the range of $1000~2000\AA$ and $200~800\AA$. respectively. Substrate temperatures were controlled from $100^{\circ}C$ to $200^{\circ}C$. Increase of coercivity by about 100~200 Oe was observed in CoCrTa/Cr-X thin films compared to those without additional X element. Cu was the most effective additional element for increasing coercivity. CoCrTa/Cr-Cu thin film shows relatively high coercivity in $1500\AA$ underlayer thickness and $600\AA$ magnetic layer thickness.